• Corrosion Science and Technology
• /
• v.17 no.3
• /
• pp.129-137
• /
• 2018

The resistance to corrosion of additive manufactured (3D printing) Ti-6Al-4V alloys was investigated using micro-electrochemical tests. In terms of corrosion resistance, the acicular martensitic ${\alpha}^{\prime}$ phase in such additive manufactured Ti-6Al-4V was the focus of attention, and its behavior was distinct from that of conventional subtractive manufactured Ti-6Al-4V. To order to identify ${\alpha}^{\prime}$ phase, XRD tests were performed and micro Vickers hardness was measured for different grains (bright and dark grains) in the additive manufactured Ti-6Al-4V alloy. Micro-electrochemical tests were performed to measure corrosion resistance of bright and dark grains in the additive manufactured Ti-6Al-4V alloy with specially designed electrochemical micro-droplet cell. Critical pitting temperature (CPT) measurement was performed to evaluate the resistance to pitting corrosion of additive manufactured Ti-6Al-4V alloys with different volumes of ${\alpha}^{\prime}$ phase and subtractive manufactured Ti-6Al-4V alloy. The dark grains of the laminated Ti-6Al-4V alloy distributed broader than the bright grains measured with low microhardness. The dark grains of the Ti-6Al-4V alloy, which was rich in martensite ${\alpha}^{\prime}$, had lower general corrosion and pitting resistance than bright grains. As the fraction of martensite ${\alpha}^{\prime}$ phase increased, the resistance to the pitting corrosion decreased.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.328-333
• /
• 2004

Hydroxyapatite (HAp) and HAp-Ag composite layers were coated on ZrO$_2$and Si wafer substrates by RF magnetron sputtering technique. The thickness of coating layers was in the range of 0.7∼1.0$\mu\textrm{m}$ and its roughness was 3∼4nm. The heat treated HAp coating layers were composed with nano-sized crystallines. However, the HAp-Ag composite layers showed the mixed structure with crystalline and amorphous phases. The Ca/P ratio of the as-received HAp coating layer was 1.9, but, the value was decreased as the Ag content with increased. Also, the Vickers hardness of HAp coating layer decreased as the Ag content increase.

• Journal of the Korean Ceramic Society
• /
• v.42 no.8 s.279
• /
• pp.582-587
• /
• 2005

AlN-BN ceramic composites were fabricated and their mechanical properties were investigated. The relative density of hot-pressed composites decreased with increasing BN content, but over $99\%$ could be obtained with 30 $vol\%$ BN in AlN. YAG was formed in the composites and monolithic AlN as a second phase by the reaction between $Y_2O_3$, added as sintering aid, and $Al_2O_3$. As expected, Vickers hardness and Young's modulus decreased with increasing BN content. The three-point flexural strength also showed similar behavior decreasing from 500 MPa of monolith down to 250 MPa by the addition 30 $vol\%$ BN. However, interestingly, the standard deviation of the strength values decreased significantly as BN was added to AlN. As a result, the Weibull modulus of the AlN-30 $vol\% BN composite was 21.3, which was extremely high. Fractography and crack path studies revealed that BN platelets induced grain pull-out and crack bridging in a bigger scale during crack propagation. Consequently, fracture toughness increased as more BN was added, reaching 4.5 $MPa\sqrt{m}$ at 40 $vol\%$ BN.

• Korean Journal of Health Education and Promotion
• /
• v.13 no.2
• /
• pp.167-183
• /
• 1996

Human teeth vary widely in color. Practitioner and patients are concerned with preventing and correcting discolored or dark teeth to achieve and maintain stain-free, white teeth. Tooth brushing cannot alter tooth color but it can remove adhering films and stains. The esthetics of natural dentition can be improved by bleaching and this process can be applied to intrinsically and extrinsically stained teeth. The need for a brighter, more attractive smile has made rapid growth in the market for tooth whiteners. There is no doubt these products work as whiteners, at least on mild to moderate stains, but the safety of these products are unclear. In this experiment, the effect of tooth whitener application on the color and microhardness of extracted human enamel was measured. RMS, RMT and NWT were used as tooth whiteners, and tooth paste(ETQ) and hydrogen peroxide solution(HPO) were used as controls. 35 caries-free extracted human molars were embedded and polished with the exposed enamel diameter of 4 mm. The tooth whiteners and control agents were applied according to the manufacturers' instructions or clinically simulated procedures for eight weeks, and measurements were repeated every two weeks. Value(L＊) difference was measured using Differential Colorimeter(Model TC-6FX, Denshoku Co., Japan), and microhardness was measured using microhardness tester(Mitsuzawa Seiki Co., Japan). The results were as follows; 1. After application of agents for eight weeks, the Vickers hardness increased significantly in the ETQ, RMS and RMT application group(p〈0.01), and that decreased significantly in NWT application group(p〈0.01), but in HPO application group there was no significant change. The change in microhardness was greatest in NWT application group(p〈0.01). 2. After application of tooth whiteners and controls for eight weeks, the value change of toothpaste application group was significantly lower than those of other agents groups(p〈0.01), and there was no significant difference in value(L＊) change among tooth whitener groups(p〉0.01). 3. The application of tooth paste and paste type tooth whitener made gradual value change, but hydrogen peroxide gel type tooth whitener and hydrogen peroxide solution made rapid value change during initial application period.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.4
• /
• pp.271-278
• /
• 2018

PURPOSE. The purpose of this in vitro study was to evaluate the effect of abrasive toothbrushing on the surface properties of monolithic computer-assisted design and computer-assisted manufacturing (CAD/CAM) materials stored in food-simulating liquids (FSLs). MATERIALS AND METHODS. Fourty-eight disk-shaped test specimens of each material (Paradigm MZ100/PMZ, Lava Ultimate/LU, Vita Enamic/VE, and Vita Mark II/VMII) with a diameter of 10.0 mm and a thickness of $3.0{\pm}0.05mm$ were prepared. Specimens were divided into 4 subgroups (n=12) and stored in air, distilled water, 0.02 M citric acid, or 75% ethanol/water solution for 7 days at $36.5^{\circ}C$. Then, the specimens were brushed in a multi-station brushing machine under a vertical load of 2.0 N for 3 hours. Surface gloss (GU), roughness (Ra), and hardness (Vickers [VHN]) were measured after storage and brushing simulation. The data sets were statistically analyzed with 2 and 3-way ANOVAs followed by the Tukey's post-hoc comparisons (${\alpha}=.05$). RESULTS. Statistically significant difference was found among the materials concerning the results of surface properties. VMII showed the highest VHN, while PMZ produced the lowest. Storage in FSLs significantly affected the VHN of PMZ and LU. VMII showed the lowest Ra and highest GU irrespective of FSLs and of abrasive toothbrushing. VE, LU, and PMZ produced significant decrease in GU and increase in Ra after toothbrushing. CONCLUSION. Surface properties of monolithic CAD/CAM restorative materials were differently affected by the storage media and abrasive toothbrushing.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.6
• /
• pp.763-769
• /
• 2010

In recent times, there has been considerable interest in HIPS (High Impact Polystyrene) materials for their use in construction of office equipments, home electronics, housing for electronics appliances, packing containers, etc. However, these materials suffer from problems caused by fatigue fracture. Further, their strength is substantially affected by environmental conditions. Therefore, in this study, the effect of temperature was analyzed by performing a tensile test and a fatigue test. It was observed that the yield strength, the ultimate strength, and the fatigue life decreased relatively with an increase in temperature. Further, an S-N curve can be predicted by using the results of the tensile test and a micro-Vickers hardness test.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.396-400
• /
• 2003

A new synthesis process for nano laminating Ti$_3$SiC$_2$ has been developed using TiCx (x=0.67) and Si powder as starting materials by a reaction hot pressing. Bulk Ti$_3$SiC$_2$ was fabricated using a green body consisting of TiCx and Si by a hot pressing under the pressures of 25 MPa at 1420-1550 $^{\circ}C$ for 90 min. The synthesized Ti$_3$SiC$_2$ was consisting of only TiCx and Ti$_3$SiC$_2$. The relative density of sintered bulk Ti$_3$SiC$_2$ was increased as the hot pressing temperature was increased, which was mainly due to the increase in TiCx contents in synthesized Ti$_3$SiC$_2$. The synthesized Ti$_3$SiC$_2$ bulk was consisted of nano sized lamella structure of 20-100 nm in thickness. It was found that TiCx particles in Ti$_3$SiC$_2$ would increase the 3-point bending strength of synthesized Ti$_3$SiC$_2$ bulk. The maximum 3-P. bending strength of synthesized Ti$_3$SiC$_2$ bulk was more than 800 MPa. The Vickers hardness of synthesized Ti$_3$SiC$_2$bulk was as low as 5 Gpa, which was decreased with the indentation load. The quasi-plastic deformation behaviors were observed around indentation mark on Ti$_3$SiC$_2$.

• Journal of Power System Engineering
• /
• v.20 no.3
• /
• pp.43-50
• /
• 2016

The current study was carried to understand the immersion characteristics and mechanical properties of heat treated stainless steels. Stainless steels (STS310S, STS316L and STS347H) were thermally treated at temperature ranges from 480 to $720^{\circ}C$. Nominal stress was determined to be slightly different depending on the heat treatment temperature. The Cr concentration in STS310S was increased at the temperatures of 600 and $660^{\circ}C$, whereas the Cr concentration in STS316L and STS347H were almost constant regardless of heat treatment temperatures. Vickers hardness was found larger as a thermal treatment temperature was increased. Immersion tests of the stainless steels were also carried out in acidic solution and alkaline solution for 240 hours. Among three different stainless steels, the pitting was detected in the acidic solution, not in the alkaline solution. The pitting of STS347H was occurred more than STS310S and STS316L.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.26 no.5
• /
• pp.291-296
• /
• 2006

The residual stress in shot-peened Al 7075 alloy was evaluated using surface acoustic wave (SAW). Shot peening was conducted to produce a variation in the residual stress with the depth below the surface under a shot velocity of 30 m/s. The SAW velocity was measured from the V(z) curve using a scanning acoustic microscopy (SAM). The Vickers hardness profile from the surface showed a significant work hardening near the surface layer with a thickness of about 0.25 mm. As the residual stress became more compressive, the SAW velocity increased, whereas as the residual stress became more tensile, the SAW velocity decreased. The variation in the SAW velocity through the shot peened surface layer was in good agreement with the distribution of the residual stress measured by X-ray diffraction technique.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.32 no.1
• /
• pp.20-26
• /
• 2012

The objective of this study is to assess plastic deformation in aluminium alloy by acoustic nonlinearity of laser-generated surface waves. A line-arrayed laser beam made by high-power pulsed laser and mask slits is utilized to generate the narrowband surface wave and the frequency characteristics of laser-generated surface waves are controlled by varying the slit opening width and slit interval of mask slits. Various degrees of tensile deformation were induced by interrupting the tensile tests so as to obtain aluminum specimens with different degrees of plastic deformation. The experimental results show that the acoustic nonlinear parameter of a laser-generated surface wave increased with the level of tensile deformation and it has a good correlation with the results of micro-Vickers hardness test and electron backscatter diffraction (EBSD) test. Consequently, acoustic nonlinearity of laser-generated surface wave could be potential to characterize plastic deformation of aluminum alloy.