• 한국전기전자재료학회논문지
• /
• 제15권11호
• /
• pp.923-932
• /
• 2002

A stoichiometric mixture of evaporating materials for CdIn$\_$2/S$\_$4/ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CdIn$\_$2/S$\_$4/ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by hot wall epitaxy(HWE) system. The source and substrate temperatures were 630 $\^{C}$ and 420 $\^{C}$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of CdIn$\_$2/S$\_$4/ single crystal thin films measured from Hall effect by van der Pauw method are 9.01$\times$10$\^$16/ cm$\^$-3/ and 219 ㎠/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of energy band gap on CdIn$\_$2/S$\_$4/ single crystal thin films was found to be Eg(T) ＝ 2.7116 eV - (7.74 $\times$ 10$\^$-4/ eV) T$\^$2//(T＋434). After the as-grown CdIn$\_$2/S$\_$4/ single crystal thin films was annealed in Cd-, S-, and In-atmospheres, the origin of point defects of CdIn$\_$2/S$\_$4/ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of V$\_$cd/, V$\_$s/, Cd$\_$int/ and S$\_$int/ obtained by PL measurements were classified as donors or accepters type. And we concluded that the heat-treatment in the S-atmosphere converted CdIn$\_$2/S$\_$4/ single crystal thin films to an optical p-type. Also, we confirmed that In in CdIn$\_$2/S$\_$4/GaAs did not from the native defects because In in CdIn$\_$2/S$\_$4/ single crystal thin films existed in the form of stable bonds.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.175-178
• /
• 2004

The stochiometric mixture of evaporating materials for the $ZnIn_2S_4$ single crystal thin film was prepared from horizontal furnace. To obtain the $ZnIn_2S_4$ single crystal thin film, $ZnIn_2S_4$ mixed crystal was deposited on throughly etched semi-insulating GaAs(100) in the Hot Wall Epitaxy(HWE) system. The source and substrate temperature were $610^{\circ}C$ and $450^{\circ}C$, respectively and the growth rate of the $ZnIn_2S_4$ sing1e crystal thin film was about $0.5\;{\mu}m/hr$. The crystalline structure of $ZnIn_2S_4$ single crystal thin film was investigated by photoluminescence and double crystal X-ray diffraction(DCXD) measurement. The carrier density and mobility of $ZnIn_2S_4$ single crystal thin film measured from Hall effect by van der Pauw method are $8.51{\times}10^{17}\;cm^{-3}$, $291\;cm^2/V{\cdot}s$ at $293_{\circ}\;K$, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c - axis of the $ZnIn_2S_4$ single crystal thin film, we have found that the values of spin orbit splitting ${\Delta}S_O$ and the crystal field splitting ${\Delta}Cr$ were 0.0148 eV and 0.1678 eV at $10_{\circ}\; K$, respectively. From the photoluminescence measurement of $ZnIn_2S_4$ single crystal thin film, we observed free excition $(E_X)$ typically observed only in high quality crystal and neutral donor bound exciton $(D^{o},X)$ having very strong peak intensity The full width at half maximum and binding energy of neutral donor bound excition were 9 meV and 26 meV, respectively, The activation energy of impurity measured by Haynes rule was 130 meV.

• 한국전기전자재료학회논문지
• /
• 제20권10호
• /
• pp.829-838
• /
• 2007

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD).The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}\;cm^{-3},\;345\;cm^2/V{\cdot}s$ at 293 K. respectively. The temperature dependence of the energy band gap of the $CdGa_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $Eg(T)\;=\;2.6400\;eV\;-\;(7.721{\times}10^{-4}\;eV/K)T^2/(T+399\;K)$. After the as-grown single crystal $CdGa_2Se_4$ thin films were annealed in Cd-, Se-, and Ga -atmospheres, the origin of point defects of single crystal $CdGa_2Se_4$ thin films has been investigated by PL at 10 K. The native defects of $V_{Cd}$, $V_{Se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or accepters. We concluded that the heat-treatment in the Cd-atmosphere converted single crystal $CdGa_2Se_4$ thin films to an optical p-type. Also, we confirmed that Ga in $CdGa_2Se_4/GaAs$ did not form the native defects because Ga in single crystal $CdGa_2Se_4$ thin films existed in the form of stable bonds.

• 센서학회지
• /
• 제13권2호
• /
• pp.157-167
• /
• 2004

A stoichiometric mixture of evaporating materials for $CuAlSe_{2}$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CuAlSe_{2}$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $680^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuAlSe_{2}$ single crystal thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}cm^{-3}$ and $295cm^{2}/V{\codt}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuAlSe_{2}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}(T)$ = 2.8382 eV - ($8.68{\circ}10^{-4}$ eV/K)$T^{2}$/(T + 155 K). The crystal field and the spin-orbit splitting energies for the valence band of the $CuAlSe_{2}$ have been estimated to be 0.2026 eV and 0.2165 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_{5}$ states of the valence band of the $CuAlSe_{2}$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1-}$, $B_{1-}$, and $C_{1-}$ exciton peaks for n = 1.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.352-356
• /
• 2003

A stoichiometric mixture of evaporating materials for $CuGaSe_2$ single crystal am films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CuGaSe_2$, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were $5.615\;{\AA}\;and\;11.025\;{\AA}$, respectively. To obtain the single crystal thin films, $CuGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $450^{\circ}C$, respectively, The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuGaSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}\;cm^{-3}$ and $295\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;:\;1.7998\;eV\;-\;(8.7489\;{\times}\;10^{-4}\;eV/K)T^2(T\;+\;335\;K)$. After the as-grown $CuGaSe_2$ single crystal thin films was annealed in Cu-, Se-, and Ga-atmospheres, the origin of point defects of $CuGaSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{CU}$, $V_{Se}$, $CU_{int}$, and $Se_{int}$, obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted $CuGaSe_2$ single crystal thin films to an optical n-type. Also, we confirmed that Ga in $CuGaSe_2/GaAs$ did not form the native defects because Ga in $CuGaSe_2$ single crystal thin films existed in the form of stable bonds.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.111-112
• /
• 2005

To obtain the single crystal thin films, $CuInSe_2$, mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wail epitaxy (HWE) system. The source and substrate temperatures were 620$^{\circ}C$ and 410$^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobilily of $CuInSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $9.62\times10^{16}$ $cm^{-3}$ and $296cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the CulnSe$_2$ obtained from the absorption spectra was well described by the Varshni's relation E$_g$(T) = 1.1851 eV - ($8.99\times10^{-4}$ ev/K)T$_2$/(T + 153K). After the as-grown $CuInSe_2$ single crystal thin films was annealed in Cu-, Se-, and In-atmospheres the origin of point defects of $CuInSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The nat ive defects of V$_{Cu}$, $V_{Se}$, Cu$_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted $CuInSe_2$ single crystal thin films to an optical n-type. Also, we confirmed that In in $CuInSe_2$/GaAs did not form the native defects because In in $CuInSe_2$ single crystal thin films existed in the form of stable bonds.

• 한국재료학회지
• /
• 제13권6호
• /
• pp.347-351
• /
• 2003

II-Ⅵ ZnO compound semiconductor thin films were grown on $\alpha$-Al$_2$O$_3$(0001) single crystal substrate by radical beam assisted molecular beam epitaxy and the optical properties were investigated. Zn(6N) was evaporated using Knudsen cell and O radical was assisted at the partial pressure of 1$\times$10$^{4}$ Torr and radical beam source of 250-450 W RF power. In $\theta$-2$\theta$ x-ray diffraction analysis, ZnO thin film with 500 nm thickness showed only ZnO(0002)and ZnO(0004) peaks is believed to be well grown along c-axis orientation. Photoluminescence (PL) measurement using He-Cd ($\lambda$=325 nm) laser is obtained in the temperature range of 9 K-300 K. At 9 K and 300 K, only near band edge (NBE) is observed and the FWHM's of PL peak of the ZnO deposited at 450 RF power are 45 meV and 145 meV respectively. From no observation of any weak deep level peak even at room temperature PL, the ZnO grains are regarded to contain very low defect density and impurity to cause the deep-level defects. The peak position of free exciton showed slightly red-shift as temperature was increased, and from this result the binding energy of free exciton can be experimentally determined as much as $58\pm$0.5 meV, which is very closed to that of ZnO bulk. By van der Pauw 4-point probe measurement, the grown ZnO is proved to be n-type with the electron concentration($n_{e}$ ) $1.69$\times$10^{18}$$cm^3$, mobility($\mu$) $-12.3\textrm{cm}^2$/Vㆍs, and resistivity($\rho$) 0.30 $\Omega$$\cdot$cm.

• 센서학회지
• /
• 제23권2호
• /
• pp.134-141
• /
• 2014

A stoichiometric mixture of evaporating materials for $BaIn_2Se_4$ epilayers was prepared from horizontal electric furnace. To obtain the single crystal thin films, $BaIn_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $620^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the epilayers was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $BaIn_2Se_4$ epilayers measured from Hall effect by van der Pauw method are $8.94{\times}10^{17}cm^{-3}$ and 343 $cm^2/vs$ at 293 K, respectively. The temperature dependence of the energy band gap of the $BaIn_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)$=2.6261 eV-$(4.9825{\times}10^{-3}eV/K)T^2/(T+558 K)$. The crystal field and the spin-orbit splitting energies for the valence band of the $BaIn_2Se_4$ have been estimated to be 116 meV and 175.9 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $BaIn_2Se_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1-$, $B_1$-exciton for n = 1 and $C_{21}$-exciton peaks for n=21.

• 태양에너지
• /
• 제13권1호
• /
• pp.49-58
• /
• 1993

승화방법에 의해 $CdS_{0.46}Se_{0.54}$ 단결정을 성장하여 결정구조를 조사하고, Van der Pauw 방법으로 Hall effect를 측정하여 carrier density의 온도 의존성과 mobility의 온도 의존성을 조사하였다. 성장된 $CdS_{0.46}Se_{0.54}$ 단결정을 치환반응하여 $n-CdS_{0.46}Se_{0.54}/p-Cu_{2-X}S_{0.46}Se_{0.54}$ 이종접합 태양전지를 제작하였다. Spectral response, 전류-전압특성 및 전력변환 효율을 조사하여 그 결과로부터 개방전압은 0.48V, 단락 전류 밀도는 $21mA/cm^2$, fill factor와 전력변환효율은 각각 0.75와 9.5%를 얻었다.

• 한국자기학회지
• /
• 제19권4호
• /
• pp.121-125
• /
• 2009

비정질 $Ge_{1-x}Mn_x$ 박막을 $400^{\circ}C$에서 $700^{\circ}C$까지 온도범위에서 각 3분씩 고진공챔버($10^{-8}$ torr)에서 열처리하였고, as-grown 시료와 열처리한 시료의 전기적 특성과 자기수송특성을 연구하였다. 성분함량은 energy dispersive X-ray spectroscopy(EDS)와 x-ray photoelectron spectroscopy(XPS)로 측정하였으며, 박막의 구조분석은 x-ray diffractometer(XRD)와 transmission electron microscopy(TEM)를 이용하였다. 자성특성은 여러 범위의 자기장에서 Magnetic property measure system(MPMS)를 이용하였다. 박막의 전기적 특성은 standard four-point probe와 Physical property measurement system(PPMS)로 측정하였으며, van der Pauw 방법을 사용하여 Anomalous Hall effect를 측정하였다. X-ray 회절 패턴 분석을 통해 $500^{\circ}C$에서 3분 동안 열처리한 시료는 여전히 비정질 상태인 것을 알 수 있었으며, $600^{\circ}C$의 열처리 온도에서 결정화를 확인할 수 있었다. as-grown $Ge_1$_$_xMn_x$ 박막과 열처리한 $Ge_{1-x}Mn_x$ 박막을 온도에 따른 비저항 값의 변화를 측정하였고, 반도체의 특성을 보이는 것을 확인할 수 있었다. 또한 열처리 온도가 높을수록 비저항도 증가하는 것을 관찰할 수 있었다. $700^{\circ}C$에서 열처리한 $Ge_1$_$_xMn_x$ 박막은 저온에서 negative magnetoresistance(MR)을 확인할 수 있었고, MR ratio는 10 K에서 약 8.5 %를 보였다. 모든 MR 그래프에서 curve의 비대칭을 확인 할 수 있었으며, anomalous Hall Effect는 약하지만 250 K까지 관측이 되었다.