• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.1
• /
• pp.72-81
• /
• 2017

The aim of this study was to evaluate the effectiveness of artificial saliva contamination and decontamination procedures at different stages of a bonding procedure on the microtensile bond strength (MTBS) of two one-step self-etch adhesives and a two-step total-etch adhesive to dentin of primary teeth. Forty-two extracted sound primary molars were randomly divided into three groups depending on three adhesives, Scotchbond Universal Adhesive (SBU), All-Bond Universal (ABU) and Prime & Bond NT (PNT). For each adhesive, the teeth were allocated into seven groups. Except for control group, group 1, the groups were contaminated with artificial saliva at three different stages: the groups 2 and 3 - before adhesive application; the groups 4 and 5 - before adhesive polymerization; the groups 6 and 7 - after adhesive polymerization. Decontaminating procedures were rinsing, air-drying (group 2, 4, 6) and air-drying (group 3, 5, 7). The specimens were restored with composite resin (Filtek, Z350) and microtensile bond strength was measured. The data was analyzed with one-way ANOVA and Tukey HSD test (p < 0.05). In the control group, using PNT resulted in significantly higher bond strength than when ABU and SBU were used (p < 0.001). For three adhesives, the groups 2, 4 and 6 had greater bond strength than the groups 3, 5 and 7. Also, when the artificial saliva was contaminated before adhesive polymerization (group 4, 5), it showed a significantly lower bond strength. Generally the two-step total-etch adhesive generated a higher bond strength than the one-step self-etch adhesive. Artificial saliva contamination before adhesive polymerization led to a drastic decrease in bond strength, and rinsing with water followed by air-drying could not recover the bond strength.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.321-334
• /
• 2010

Objectives: The purpose of this study is to evaluate bonding efficacy by means of measuring the effect of remained solvent on Degree of conversion(DC) and ${\mu}TBS$ and FE-SEM examination. Materials and Methods: Two 2-step total etching adhesives and two single-step self etching adhesives were used in this study. First, volume weight loss of 4 dentin adhesives were measured using weighting machine in process of time in normal conditions and calculate degree of evaporation (DE). Reaction/reference intensity ratio were measured using micro-Raman spectroscopy and calculate DC according to DE. Then 2 experimental groups were prepared according to air-drying methods (under, over) and control group was prepared to manufacturer's instruction. Total 12 groups were evaluated by means of micro tensile bond strength and FE-SEM examination. Results: Degree of evaporation (DE) was increased as time elapsed but different features were observed according to the kind of solvents. Acetone based adhesive showed higher DE than ethanol and butanol based adhesive. Degree of conversion (DC) was increased according to DE except for $S^3$ bond. In ${\mu}TBS$ evaluation, bond strength was increased by additional air-drying. Large gaps and droplets were observed in acetone based adhesives by FE-SEM pictures. Conclusions: Additional air-drying is recommended for single-step self etching adhesive but careful consideration is required for 2-step total etching adhesive because of oxygen inhibition layer. Evaporation method is carefully chose and applied according to the solvent type.

• Archives of Plastic Surgery
• /
• v.33 no.1
• /
• pp.107-112
• /
• 2006

If autogenous nail is lost in nail bed injuries, alternative effective nail bed protection material is questionable in postoperative follow up period. The conventional modality with autogenous nail coverage have several disadvantages such as drawback of maintenance, higher chance of loss and complex dressing step (eg. ointment apply for humidification and nail fixation using tape or bandage). So, we have studied the usefulness of adhesive silicone gel sheet for alternative nail bed protection material until the end of nail regeneration. From March 2003 to July 2004, we have experienced 215 traumatic nail bed injuries except fingertip loss. Among these patient, we classified two groups, 30 cases with autogenous nail protection(Group I) and 30 cases with adhesive silicone gel sheet protection(Group II). Mean full nail growth time was 3.6 months in group I and 3.8 months in group II. Mean final nail appearance score(0: poor, 4: excellent) was 3.0 in group I and 3.5 in group II. Adhesive silicone gel sheet protection(Group II) was slightly superior to the autogenous nail protection in final appearance, especially sterile matrix laceration. In conclusion, we believe that adhesive silicone gel sheet application is a simple, acceptable, alternative method for protecting nail bed with loss of autogenous nail. It has a number of advantages compared with autogenous nail such as better humidification, controllable hygiene, less pain, less hospitalization, less frequent visit, less chance of loss, avoiding complex dressing step and more even pressure with adhesiveness, flexibility and durability.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.546-553
• /
• 1999

In Older to evaluate the effectiveness of 'One-bottle dentin adhesive system', the shear bond strengths of two fourth generation dentin adhesive systems and two One-bottle systems to the occlusal dentin of the freshly extracted third molars were measured by the regulation of the ISO TR 11405. The fourth generation dentin adhesive systems used in this study were Scotchbond Multi-Purpose Plus and All-Bond 2, and the One-bottle systems were Single Bond and One-Step. The effects of the thickness of hybrid layer and adhesive layer, the diameter of resin tag and the ratio between the diameter of resin tag and that of dentinal tubule were analyzed as the contributing factors of the shear bond strength of dentin bonding systems from the Scanning Electron Microscopic images. The results were as follows: 1. The shear bond strengths of Scotchbond Multi-Purpose, All-Bond 2, and Single Bond were 16.98${\pm}$3.40 MPa, 15.10${\pm}$2.77 MPa and 15.05${\pm}$3.18 MPa, respectively. There were no statistical differences(p>0.05). 2. But, the shear bond strength of One-Step were significantly lower than those of the other groups (11.81${\pm}$1.95 MPa, p<0.05). 3. The thicknesses of hybrid layer and adhesive layer of One-Step were significantly thinner than those of the other groups(p<0.05). The differences of the diameter of resin tag(p=0.0685) and the ratio between the diameter of resin tag and that of dentinal tubule(p=0.2401) were not significant among all the material groups. 4. The thickness of hybrid layer and adhesive layer might be considered as contributing factors of the she at bond strengths of dentin bonding systems, but the diameter of resin tag and the ratio between the diameter of resin tag and that of dentinal tubule might not.

• Restorative Dentistry and Endodontics
• /
• v.24 no.2
• /
• pp.381-391
• /
• 1999

A new 5th generation adhesive system(ONE-STEP) has been supplied which operators can apply to conditioned tooth surfaces by one simplified step. The purpose of this study was to determine whether different methods of adhesive application and various air drying duration after applying adhesive affect the shear bond strength of composite resin to dentin, and to evaluate the adhesive pattern of composite resin and dentin under SEM. Seventy-seven extracted human molar teeth were cleaned and mounted in palstic test tubes. The occlusal dentin surfaces were exposed with Diamond Wheel Saw and smoothed with Lapping and Polishing Machine (South Bay Technology Co., U.S.A.). Teeth were randomly divided into 7 groups (n=11), In experimental A group, adhesive was applied to dentin with agitation for 20 sec. In experimental N-A group, adhesive were continuously applied to dentin for 20 sec. Also control and experimental 1, 2, 3, 4 groups were dried for 10, 0, 5, 20, 30 seconds after applying adhesive, respectively, Adhesives were light cured for 10 sec. A gelatin capsule 5mm in diameter was filled with Aelitefil$^{TM}$ composite resin, placed on the treated dentin surface and light cured for 40 see, from three sides, All specimens were stored in distilled water at room temperature for 24 hours. The shear bond strengths were measured using a universal testing machine(AGS-1000 4D, Japan) at a crosshead speed of 5mm/min. An one-way ANOVA and LSD test were used for statistical analysis of the data. For SEM evaluation, seven specimens were made and sectioned. Representive postfracture and seven specimens were mounted on brass stubs, sputter-coated with gold and observed under SEM. The results were as follows : 1. The shear bond strength of experimental A group which adhesive were applied to dentin with agitation was higher than that of experimental N-A group (continuous application), and there was significant difference between two groups (p<0.01). 2. The interface between composite and dentin according to different application methods showed close adaptation in experimental A group and showed tinny gap in experimental N-A group. 3. The shear bond strength accoding to various air drying duration was the lowest value(7.57${\pm}$2.60 MPa) in experimental 1 group, so there was significant difference between experimental 1 group and other four groups (p<0.05). But there was no significant difference of shear bond strength between four groups (p>0.05). 4. The interface between composite and dentin according to various air drying duration showed close adaptation in control group and tinny gap in experimental 3 and 4 groups. But experimental 1 and 2 groups showed $30{\mu}$ and 6 - $10{\mu}m$ thick gaps, respectively.

• Restorative Dentistry and Endodontics
• /
• v.36 no.1
• /
• pp.50-58
• /
• 2011

Objectives: The purpose of this study was to compare the microshear bond strength (uSBS) of two totaletch and four self-etch adhesive systems and a flowable resin to enamel. Materials and Methods: Enamels of sixty human molars were used. They were divided into one of six equal groups (n = 10) by adhesives used; OS group (One-Step Plus), SB group (Single Bond), CE group (Clearfil SE Bond), TY group (Tyrian SPE/One-Step Plus), AP group (Adper Prompt L-Pop) and GB group (G-Bond). After enamel surfaces were treated with six adhesive systems, a flowable composite resin (Filek Z 350) was bonded to enamel surface using Tygon tubes. the bonded specimens were subjected to uSBS testing and the failure modes of each group were observed under FE-SEM. Results: 1. The uSBS of SB group was statistically higher than that of all other groups, and the uSBS of OS, SE and AP group was statistically higher than that of TY and GB group (p < 0.05). 2. The uSBS for TY group was statistically higher than that for GB group (p < 0.05). 3. Adhesive failures in TY and GB group and mixed failures in SB group and SE group were often analysed. One cohesive failure was observed in OS, SB, SE and AP group, respectively. Conclusions: Although adhesives using the same step were applied the enamel surface, the uSBS of a flowable resin to enamel was different.

• Restorative Dentistry and Endodontics
• /
• v.40 no.1
• /
• pp.68-74
• /
• 2015

Objectives: This study examined the effects of additional acid etching on the dentin bond strength of one-step self-etch adhesives with different compositions and pH. The effect of ethanol wetting on etched dentin bond strength of self-etch adhesives was also evaluated. Materials and Methods: Forty-two human permanent molars were classified into 21 groups according to the adhesive types (Clearfil SE Bond [SE, control]; G-aenial Bond [GB]; Xeno V [XV]; Beauti Bond [BB]; Adper Easy Bond [AE]; Single Bond Universal [SU]; All Bond Universal [AU]), and the dentin conditioning methods. Composite resins were placed on the dentin surfaces, and the teeth were sectioned. The microtensile bond strength was measured, and the failure mode of the fractured specimens was examined. The data were analyzed statistically using two-way ANOVA and Duncan's post hoc test. Results: In GB, XV and SE ($pH{\leq}2$), the bond strength was decreased significantly when the dentin was etched (p < 0.05). In BB, AE and SU (pH 2.4 - 2.7), additional etching did not affect the bond strength (p > 0.05). In AU (pH = 3.2), additional etching increased the bond strength significantly (p < 0.05). When adhesives were applied to the acid etched dentin with ethanol-wet bonding, the bond strength was significantly higher than that of the no ethanol-wet bonding groups, and the incidence of cohesive failure was increased. Conclusions: The effect of additional acid etching on the dentin bond strength was influenced by the pH of one-step self-etch adhesives. Ethanol wetting on etched dentin could create a stronger bonding performance of one-step self-etch adhesives for acid etched dentin.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.4
• /
• pp.251-258
• /
• 2016

PURPOSE. This study was undertaken to investigate whether use of an adhesive penetration enhancer, dimethyl sulfoxide (DMSO), improves bond stability of fiber posts to root dentin using two two-step etch-and-rinse resin cements. MATERIALS AND METHODS. Forty human maxillary central incisor roots were randomly divided into 4 groups after endodontic treatment and post space preparation, based on the fiber post/cement used with and without DMSO pretreatment. Acid-etched root dentin was treated with 5% DMSO aqueous solution for 60 seconds or with distilled water (control) prior to the application of Excite DSC/Variolink II or One-Step Plus/Duolink for post cementation. After micro-slicing the bonded root dentin, push-out bond strength (P-OBS) test was performed immediately or after 1-year of water storage in each group. Data were analyzed using three-way ANOVA and Student's t-test (${\alpha}$=.05). RESULTS. A significant effect of time, DMSO treatment, and treatment${\times}$time interaction were observed (P<.001). DMSO did not affect immediate bonding of the two cements. Aging significantly reduced P-OBS in control groups (P<.001), while in DMSO-treated groups, no difference in P-OBS was observed after aging (P>.05). CONCLUSION. DMSO-wet bonding might be a beneficial method in preserving the stability of resin-dentin bond strength over time when fiber post is cemented with the tested etch-and-rinse adhesive cements.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.4
• /
• pp.283-292
• /
• 2007

Two-step or one-step bonding systems generally inhibit curing process of dual-cured core build-up resin composite for their adhesive acidity. In addition this dual-cured core build-up resin composite can be applied to dentin of pulp chamber and root at the time that complete the endodontic treatment. The purpose of this investigation was to determine the influence of sodium hypochlorite on rnicrotensile bond strength of dual-cured core build-up resin composite. Extracted human molars were horizontally sectioned with 1mm thickness using low speed diamond saw. After the sectioned specimens were divided into 8 groups, adhesive systems (Clearfil SE-Bond, Prime&Bond NT[2-step, 1-step], Adper Prompt L-Pop) were then applied with or without sodium hypochlorite pretreatment. The treated specimen was filled with dual-cured core build-up resin composite (Luxacore, DMG corp., German). Then light cured for 40 seconds and soaked in $37^{\circ}C$ water bath for 24 hours. After the treated specimen was grinded with 1mm width and measured rnicrotensile bond strength by testing machine. Additionally 8 teeth were prepared for SEM evaluation. The results were as follows. : NaOCl treated groups generally had lower rnicrotensile bond strength but did not show any difference statistically except Adper Prompt L-Pop. When the teeth were treated by NaOCl, though the difference of applied adhesive system, it had no statistically significant difference within the NaOCl treated groups except the relation of between ClearFil SE-Bond adhesive system and Adper Prompt L-Pop adhesive system. In the SEM evaluation, NaOCl treated groups presented relatively long resin tags and incomplete hybrid layer formation generally.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.2
• /
• pp.161-174
• /
• 2011

The purpose of this study was to evaluate the effect of ethanol addition on efficacy of two-step total-etch adhesive under over-wet condition by measurement of remaining volatile part (RVP), microtensile bond strength (${\mu}TBS$), and degree of conversion (DC). Two-step total-etch adhesive, Optibond Solo Plus (Kerr, Orange, USA), was used. Experimental groups were divided into 8 groups: Group 1 (only 10 ${\mu}l$ adhesive), Group 2 (mixture of 3 ${\mu}l$ distilled water and 10 ${\mu}l$ adhesive), From Group 3 to Group 8 (mixture of 3 ${\mu}l$ distilled water, 10 ${\mu}l$ adhesive, and ethanol added in 1 ${\mu}l$ increment from 1 ${\mu}l$ to 6 ${\mu}l$). The mixtures were placed on slide glass and evaporated for 10 s, 30 s, and 60 s by air-drying. The weight of RVP was measured by precision weight. Same procedures were performed for ${\mu}TBS$ test and measurement of DC. The condition of mixed solution was observed under light microscope. For RVP weight, the weights of experimental groups except for group 1 decreased with the increase of air-drying time (p<0.05). The DC increased with the increase of air-drying time in only group 5 and 6 (p<0.05). The ${\mu}TBS$ increased with the increase of air-drying time in group only 5, 6, and 7 (p<0.05). The phase separation was examined and water blisters were diminished with the increase of air-drying time in group 5, 6, 7, and 8. Within the limits of this study, ethanol additionally applied to adhesive decreased RVP and increased DC and ${\mu}TBS$ under over-wet condition. It was shown that the addition of ethanol to two-step total-etch adhesive under over-wet condition would remove water and increase the efficacy of adhesive.