• Korean Journal of Materials Research
• /
• v.10 no.9
• /
• pp.624-628
• /
• 2000

As a power durable-electrode in SAW filter, Al-1%Cu/tungsten nitride multi-layer thin film was fabricated by magnetron sputtering process. Tungsten nitride films had the amorphous phase at the nitrogen ratio, R, ranging from 10~40%. The amorphization could be controlled by nitrogen ratio, R= $N_2$/($N_2$+Ar) as a sputtering process parameter. Residual stress in tungsten nitride abruptly decreased with the formation of amorphous phase. Al-1%Cu thin film was deposited on the amorphous tungsten nitride. After the multi-layed thin film was annealed for 4 hours at 453K, the resistivity decreased as $3.6{\mu}{\Omega}-cm$, which was due to grain growth reduced crystal defects.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.29-33
• /
• 2000

The amorphous tungsten nitrides, WNx, film could be fabricated by reactive sputtering process. The nitrogen concentration for the amorphization ranges from 10 at% to 40at%. The amorphous $W_{67}N_{33}$ film was crystallized into low resistivity $\alpha$-tungsten phase with equiaxed grains and excess nitrogen after the rapid thermal annealing for 1min at 1273K, which was similar to the resistivity of the sputtered pure tungsten film. The excess nitrogen was depleted from $\alpha$-tungsten crystals and then segregated at $\alpha$-tungsten/poly-Si interface. The segregated nitrogen has favored the formation of the homogeneous diffusion barrier layer comprised of silicon nitride, $Si_3N_4$, nano-crystals, which undertaken the inhibition of the high resistivity tungsten silicide reaction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.87-88
• /
• 2007

반도체 소자가 초고집적화 되어감에 따라 반도체 공정에서 선폭은 줄어들고 박막은 다층화 되어가고 있다. 이와 같은 제조 공정 하에서는 Si 기판과 금속 박막간의 확산이 커다란 문제로 부각되어 왔다. 특히 Cu는 높은 확산성에 의하여 Si 기판과 접합에서 많은 확산에 의한 문제가 발생하게 되며, 또한 선폭이 줄어듦에 따라 고열이 발생하여 실리콘으로 spiking이 발생하게 된다. 이러한 확산을 방지하기 위하여 이 논문에서는 Tungsten - Carbon - Nitrogen (W-C-N)에 Boron (B)을 첨가하였고, Boron 타겟 power을 조절하여 다양한 조성을 가지는 W-B-C-N 확산방지막을 제작하여 각 조성에 따른 증착률을 조서하였고 $1000^{\circ}C$까지 열처리하여 그 비저항을 측정하여 각 특성을 확인하였다.

• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.32-35
• /
• 2008

Thermally stable diffusion barrier of tungsten carbon nitride(W-C-N) and of tungsten boron carbon nitride(W-B-C-N) thin films have studied to investigate the impurity behaviors of boron and nitrogen. In this paper we newly deposited tungsten boron carbon nitride(W-B-C-N) thin film for various $W_2B$ target power on silicon substrate. The impurities of the 100nm-thick W-C-N and W-B-C-N thin films provide stuffing effect for preventing the inter-diffusion between W-C-N or W-B-C-N thin films and silicon during the high temperature($700^{\circ}C{\sim}1000^{\circ}C$) annealing process.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.130-132
• /
• 2005

Tungsten carbon nitride (W-C-N) thin films were produced by reactive radio frequency (RF) magnetron sputter-ing of tungsten in $Ar-N_2$ gas mixture. The effects of the variation of nitrogen partial pressure on the composition, and structural properties of these films as well as the influence of post-deposition annealing have been studied. When $La_{0.67}Sr_{0.33}MnO_3$ was coated on the W-C-N/Si substrate, coercivity ($H_c$) and magnetization at room temperature shows 58.73 Oe, and 29.4 emu/cc, respectively. In order to improve the diffusion barrier characteristics, we have studied the impurity behaviors to control the ratios of nitrogen and carbon concentrations.

• Journal of the Korean Vacuum Society
• /
• v.22 no.4
• /
• pp.188-192
• /
• 2013

Many studies have been conducted for preventing from diffusion between silicon wafer and metallic thin film due to a decrease of line-width and multi-layer thin film for miniaturization and high integration of semiconductor. This paper has focused on the nano-mechanical property of diffusion barrier which sample is prepared for various gas flow rate of nitrogen with tungsten (W) base from 2.5 to 10 sccm. The deposition rate, resistivity and crystallographic properties were measured by a ${\beta}$-ray back-scattering spectroscopy, 4-point probe and x-ray diffraction (XRD), respectively. We also has investigated the nano-mechanical property using the nano-indenter. As a result, the surface hardness of W-N thin film was increased rapidly from 10.07 to 15.55 GPa when the nitrogen gas flow was increased from 2.5 to 5 sccm. And the surface hardness of W-N thin film had 12.65 and 12.77 GPa at the nitrogen gas flow of 7.5 and 10 sccm respectively. These results were decreased by the comparison with the W-N thin film at nitrogen gas flow of 5 sccm. It was inferred that these severe changes were caused by the stoichiometric difference between the crystalline and amorphous state in W-N thin film. In addition, these results were caused by increased compressive stress.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.200-204
• /
• 2011

In this paper, we deposited the tungsten carbon nitride (W-C-N; nitrogen gas flow of 2 sccm) and tungsten carbon (W-C) thin film on silicon substrate using rf magnetron sputter. Then the thin films annealed at $800^{\circ}C$ during 30 minute ($N_2$ gas ambient) for thermal damage. Nano-indenter was executed 16 points on thin film surface to measure the thermal stability, and we also propose the elastic modulus and the Weibull distribution, respectively. This nanotribology method provides statistically reliable information. From these results, the W-C-N thin film included nitrogen gas flow is more stable for film uniformities, physical properties and crystallinities than that of not included nitrogen gas flow.

• Korean Journal of Materials Research
• /
• v.8 no.2
• /
• pp.147-153
• /
• 1998

Tungsten nitride is very attractive as absorber for X-ray lithographic mask and as a diffusion barrier for interconnecting metallization in Si VLSI technology. Microstructure of tungsten nitride films prepared by RF magnetron sputtering has been investigated as a function of deposition parameter. The crystal structure of sputtered films on silicon nitride membrane depends strongly on the NJAr gas flow ratio(0~18%1, gas pressure(l0~43mTorr). RF power (60~150W), target-substrate distance(4~8cm). Tungsten nitride films deposited at the $N_2/Ar$ gas flow ratio(- 10%). gas pressure(~10mmTorr), RF power(~150W) and target-substrate distance(6cm) are amorphous, but at other conditions are almost rough -surfaced polycrystalline. Amorphous films are very smooth($3.1\AA$ rms) and expected to be excellent absorber for X-ray mask.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.7
• /
• pp.17-25
• /
• 1999

Tungsten nitride($WN_x$) films were deposited by PECVD method on silicon nitride($WSi_3N_4$) substrate. The characteristics of $WN_x$ film were investigated with changing various processing parameters ; substrate temperature, gas flow rate, rf power, and different nitrogen sources. The nitrogen composition in $WN_x$ film varied from 0 to 45% according to the $NH_3$ and $N_2$ flow rate. The highest deposition rate of 160 nm/min was obtained for the $NH_3$ gas and relatively low deposition rate of $WN_x$ films were formed by $N_2$ gas. $WN_x$ films deposited on $WSi_3N_4$ substrate had higher deposition rate than that of TiN and Si substrates. The purity of $WN_x$ film were analyzed by AES and higher purity $WN_x$ films were deposited using $NH_3$ gas. The XRD analysis indicates a phase transition from polycrystalline tungsten(W) to amorphous tungsten nitride($WN_x$), showing improved etching profile of $WN_x$ films Thick $WN_x$ films were deposited on various substrates such as Tin, NiCr and Al and maximum thickness of $1.6 {\mu}m$ was obtained on the Al adhesion layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.72-73
• /
• 2005

Stress behavior was studied to investigate the internal behaviors of boron, carbon, and nitrogen in the 1000${\AA}$-thick tungsten boron carbon nitride (W-B-C-N) thin films. The impurities in the W-B-C-N thin films provide stuffing effects that were very effective for preventing the interdiffusion between interconnection metal and silicon substrate during the subsequent high temperature annealing process. The resistivity of W-B-C-N thin film decreases as an annealing temperature increase. The W-B-C-N thin films have compressive stress, and the stress value decreased up to $4.11\times10^{10}dyne/cm^2$ as an $N_2$ flow rate increases up to 3 sccm.