• 한국세라믹학회지
• /
• 제28권5호
• /
• pp.406-414
• /
• 1991

The composition of base glass was selected as MgO 8, Al2O3 24, SiO2 68 in weight percent. TiO2 and ZrO2 were added to the base glass to investigate their effects as nucleating agents. In the case of ZrO2 addition, the optimum temperature for nucleation, which was related to the precipitation of tetragonal ZrO2, was 80$0^{\circ}C$. The optimum growth condition for the crystal was 87$0^{\circ}C$ for 8 hrs, and the major crystal phases precipitated in the samples were $\beta$-quartz ss. and mullite. The light transmissivity turned out to be around 80 per cent. On the other hand, when the TiO2 was added, it was difficult to determine the nucleating temperature, because the samples turned easily into translucency during the heat treatment. Therefore, it was almost impossible to retain transparency in the samples. The light transmissivity was below 30 per cent.

• 한국세라믹학회지
• /
• 제40권11호
• /
• pp.1078-1084
• /
• 2003

비선형 광학재료 및 광촉매를 개발하기 위하여, $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리를 일반적인 용융 및 급냉하는 방법으로 제조하였다. 그리고 $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리의 광학적 성질과 나노-결정화거동을 조사하였다. $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리의 광학적 성질과 물리적 성질은 다음과 같다. 굴절률(n) 은 2.04$\pm$0.04, 밀도(g/㎤)는 4.87$\pm$0.58, 광 에너지 밴드(eV)는 3.14$\pm$0.04이였다. 나노결정으로 구성된 투명한 결정화유리는 3$50^{\circ}C$에서 l시간 열처리한 후, 이것을 다시 40$0^{\circ}C$에서 l 시간 열처리하여 얻었다. 나노결정으로 구성된 Cubie 결정상은 47$0^{\circ}C$ 이상의 온도에서 새로운 결정상으로 변화하였다.

• 한국세라믹학회지
• /
• 제44권8호
• /
• pp.451-456
• /
• 2007

This paper presents results and observations obtained from a study of sintering behavior and crystallization in $Li_2O-Al_2O_3-SiO_2$ (LAS) Glass by screen printing method. The variable experimental conditions were determined carefully by Thermal-Mechanical Analyzer (TMA), Differential Thermal Analyzer (DTA) for setting the optimum transparent sintering conditions in LAS glass system, $10.5Li_2O-14.7Al_2O_3-58.1SiO_2-16.7B_2O_3(wt%)$, such as glass-ceramics which usually have low crystallization temperatures. Crystallization glasses generated during sintering was observed from diffraction patterns by X-Ray Diffraction (XRD), transmittance by UV-Vis spectrometer. Finally, the optimum sintering condition of LAS glass and the relation between factors and results in several sintering conditions were given by using Response Surface Methodology (RSM). From this study, we confirmed that crystallization interrupted densification during glass powder sintering. Furthermore, we observed that main effect of factors in glass powder sintering with concurrent crystallization depended on experimental conditions from main effects plot by MINTAB-14.

• 자원리싸이클링
• /
• 제32권1호
• /
• pp.42-49
• /
• 2023

Li-Al-Si를 함유한 유리세라믹 순환자원은 인덕션, 방화유리, 비젼냄비 등 리튬의 전체 소비량 중 14%로 리튬이온전지 다음으로 많이 쓰인다. 따라서 리튬의 수요가 폭발하고 있는 현재 새로운 리튬 자원을 찾아야 하고 이로부터 리튬의 회수 연구가 필요하다. 본 연구는 이러한 맥락하에 Li을 함유한 새로운 순환자원인 Li-Al-Si 유리세라믹으로부터 리튬을 회수하기 위한 연구를 수행하였다. 본 연구에서는 1.5% Li, 9.4% Al, 28.9% Si를 함유한 Li-Al-Si 유리세라믹 중 방화유리를 원료물질로 사용하였다. 방화유리로부터 리튬을 회수하기 위한 공정은 크게 칼슘 염을 투입한 건식 배소 공정과 수침출 공정으로 나뉜다. 325 mesh 이하로 분쇄된 방화유리 시료를 열처리 전과 열처리 후 칼슘 염을 투입하여 침출 실험을 비교 진행하였고 칼슘 염과 Li-Al-Si 유리세라의 투입비율에 따른 침출율, 칼슘 염 배소 온도에 따른 침출 연구도 비교 수행하였다. 수침출 연구에서는 온도, 시간, 고액비, 그리고 연속 침출횟수에 따라 리튬의 침출율 및 회수율을 비교하였다. 그 결과 Li-Al-Si를 함유한 유리세라믹 방화유리는 열처리를 반드시 수행하여 베타 형태의 스포듀민으로 상변화 시켜야 하며 이로부터 CaCO₃ 염을 Li-Al-Si를 함유한 유리세라믹 방화유리와 6:1의 비율로 투입하여 1000℃이상에서 배소한 후 4회 이상 연속 침출하여 리튬의 회수율을 98% 이상 획득하였고 이때 리튬의 농도는 200mg/L였다.

• 한국세라믹학회지
• /
• 제42권8호
• /
• pp.554-560
• /
• 2005

The engineering ceramic needs the properties of high strength, hardness, corrosion-resistance and heat-resistance in order to withstand thermal shock or applied nonuniform stresses without failure. The densely coated porous ceramics can be used for machine component, electromagnetic component, bio-system component and energy-system component by their high-performances from superior coating properties and light-weight characteristics due to the structure including pore by itself. In this study we controlled the porosity of silica and alumina, $8.2\~25.4\%$ and $23.4\~36.0\%$, respectively, by the control of sintering temperature and starting powder size. We made bilayer structures, consisting of a transparent glass coating layer bonded to a thick substrate of different porous ceramics by a thin layer of epoxy adhesive, facilitated observations of crack initiation and propagation. The elastic modulus mismatch could be controlled using different porous ceramics as the substrate layer. Then we applied 150 N force using WC sphere with a radius of 3.18 mm by Hertzian indentation. As a result, the crack initiation in the coating layer was delayed at lower porosity in the substrate layer, and the damage in the coating layer was relatively smaller at the bilayer structure coated on higher elastic substrate.

• The Korean Journal of Ceramics
• /
• 제6권1호
• /
• pp.15-20
• /
• 2000

Thick inorganic-organic hybrid films were prepared on ITO-coated glass substrates by the electrophoretic sol-gel deposition of polyphenylsilsesquioxane particles. The morphology of the deposited films changed from the aggregate of the spherical particles to monolith by heat treatment at temperatures higher than $200^{\circ}C$. Transparency of the films was significantly improved accompanied by the morphological change of the particles. The degree of the morphological change was governed by two factors; maximum heat treatment temperature and heating rate. Transparent thick films of ca. 3$\mu\textrm{m}$ in thickness were obtained only by heat treatment at $400^{\circ}C$ for 2h with rapid heating from room temperature to $400^{\circ}C$. These films obtained were strongly adhered to the ITO-coated glass substrates and has a very smooth surface.

• The Korean Journal of Ceramics
• /
• 제5권1호
• /
• pp.50-54
• /
• 1999

$(Pb_xLa_{1-x}) (Zr_yTi_{1-y})O_3$ (PLZT) thin films with electrooptic effect are promising for the optical application such as display or light shutter. However, it is difficult to use inexpensive and transparent glass substrates because the conventional process for preparation of PLZT requires temperatures above $600^{\circ}C$. In order to deposit a perovskite PLZT thin films at low processing temperatures through alkoxide route, we have offered several seeding processes which reduce the activation energy for crystallization. In this study, we optimized the stacking structure of multilayered PLZT for obtaining single phase perovskite at lower temperatures. As a result, ferroelectric PLZT thin films with different compositions were successfully prepared at a temperature as low at $500^{\circ}C$.

• 대한기계학회논문집B
• /
• 제37권12호
• /
• pp.1159-1165
• /
• 2013

파우더 블라스팅은 미세 유리가공법으로서 가공속도가 빠르고 저비용의 장점이 있지만 유리를 취성파괴 시키기 때문에 표면거칠기가 좋지않다. 블라스팅된 표면에 저압의 워터젯을 분사하여 표면에서의 연마 슬러리의 흐름을 통해 표면거칠기를 저감할 수 있다. 본 연구에서는 소다라임 유리에 블라스팅으로 마이크로 채널을 가공한 후 워터젯을 연속 적용하고, 마이크로 채널의 표면거칠기 및 단면 형상의 변화의 과정을 관찰하였다. 워터젯의 적용결과, 초기단계에서는 블라스팅에 의한 미세 요철이 제거되었고, 이후 표면하부의 크랙이 제거되어 평균 표면거칠기 50 nm 근방의 매끈한 표면을 얻을 수 있었다. 표면거칠기 저감에 동반하여 채널단면의 확장 과정도 함께 관측하였다. 마지막으로 제안한 방법에 의해 미세유체칩의 가공 결과를 제시하였다.

• 박물관보존과학
• /
• 제26권
• /
• pp.25-34
• /
• 2021

문화재 복원 분야에서 3D 기술이 복원에 적용되고 있다. 그러나 아직까지 유리제 문화재의 복원에 관하여 3D 기술이 활용되어 복원된 사례가 적으며 이에 관한 연구가 필요한 상황이다. 이에 본 연구에서는 국립중앙박물관에서 소장하고 있는 보물인 금강산 출토 이성계 발원 사리장엄구 일괄 중 유리제 사리병의 결손부를 복원하는 과정에 3D 기술을 이용하였다. 보존처리는 3D 프린팅 출력물을 직접적으로 복원제로써 적용하지않고 에폭시계수지로 복제한 복원편으로 결손부를 복원하였다. 보존처리 완료 후 3D 프린팅에 사용되는 재료와 기술방식에 관하여 기존 도자기의 복원재료 중 투명성을 지닌 재료를 선택하여 사용감과 안정성을 비교하고자 하였다. 보존처리 완료 후 SLA(Stereo Lithography Apparatus)방식으로 출력한 광경화성 수지, 에폭시계 수지, 아크릴계 수지등 총 5개의 시편을 제작 한 후 96시간까지 자외선에 노출시켜 황변화를 조사하였고, 광경화성수지의 시편은 출력물에 UV차단제를 분무 여부에 따라 2종으로 나누어 자외선에 노출시켰다. 자외선 노출 결과, SLA방식 시편에 UV차단제를 분무한 시편, 에폭시계수지의 시편의 b^*값의 변화값이 1 미만으로 황변화에 안정적인 것으로 나타났으며 유리제 문화재의 복원제로써 적용 가능한 재료로 보여진다. 유리제 문화재의 형태가 매우 다양하고 복원해야할 부분 또한 다양하고 복잡하여 접근하기 어려울 수 있으므로 복원재료에 대해 여러 가지 재료를 염두해두고 고민해볼 필요가 있다.