Nano-crystallization Behavior and Optical Properties of Na2O-Nb2O5-TeO2Glasses (1)

In order to develop a new type of nonlinear optical materials or photocatlaysts, Na$_2$O-Nb$_2$ $O_{5}$-Te $O_2$ glasses were prepared using conventional melt quenching method, and the crystallization behaviors and optical properties of these glasses was investigated. The optical and physical properties for Na$_2$O-Nb$_2$ $O_{5}$-Te $O_2$ glasses are: refractive index, n=2.04$\pm$0.04; density, p (g/㎤)=4.87$\pm$0.58; optical energy band of the transmission cut-off wavelength, E$_{0}$ (eV)=3.14$\pm$0.04. The transparent glass ceramics consisting of the nanocrysatls were obtained when the Na$_2$O-Nb$_2$ $O_{5}$-Te $O_2$ glass was first heat-treated at 3$50^{\circ}C$ for 1 h and than at 40$0^{\circ}C$ for 1 h. A cubic crystalline phase consisting of the nano-crysatls transforms into a stable phase at temperature above 47$0^{\circ}C$ for 1 h.

Na2O-Nb2O5-TeO2계 유리의 광학적 성질과 나노-결정화거동 (1)

비선형 광학재료 및 광촉매를 개발하기 위하여, $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리를 일반적인 용융 및 급냉하는 방법으로 제조하였다. 그리고 $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리의 광학적 성질과 나노-결정화거동을 조사하였다. $Na_2$O-Nb$_2$ $O_{5}$-Te $O_2$계 유리의 광학적 성질과 물리적 성질은 다음과 같다. 굴절률(n) 은 2.04$\pm$0.04, 밀도(g/㎤)는 4.87$\pm$0.58, 광 에너지 밴드(eV)는 3.14$\pm$0.04이였다. 나노결정으로 구성된 투명한 결정화유리는 3$50^{\circ}C$에서 l시간 열처리한 후, 이것을 다시 40$0^{\circ}C$에서 l 시간 열처리하여 얻었다. 나노결정으로 구성된 Cubie 결정상은 47$0^{\circ}C$ 이상의 온도에서 새로운 결정상으로 변화하였다.