The multi-dielectric layer SiOz/Si3N4/SiO2(ONO) is used to scale down the memory device. In this paper, the change of composition in ONO layer due to the process condition and the conduction mechanism are observed. The composition of the oxide film grown through the oxidation of nitride film is analyzed using auger electron spectroscopy(AES). AES results show that oxygen concentration increases at the interface between oxide and nitride layers as the thickness -of the top oxide layer increases. Results of I-V measurement show that the insulating properties improve as the thickness of the top oxide layer increases. But when the thickness of the nitride layer decreases below 63.angs, insulating peoperties of film 28.angs. of top oxide and film 35.angs. turn over showing that insulating property of film 28.angs. of top oxide is better than that of film 35.angs. of top oxide. This phenomenon of turn over is thought as the result of generation of surface state due to oxygen flow into nitride during oxidation process. As the thickness of the top oxide and nitride increases, the electrical breakdown field increases, but when the thickness of top oxide reaches 35.angs, the same phenomenon of turn over occurs. Optimum film thickness for scaled multi-layer dielectric of memory device SONOS is estimated to be 63.angs. of nitride layer and 28.angs. of top oxide layer. In this case, maximum electrical breakdown field and leakage current are 18.5[MV/cm] and $8{\times}{10^-12}$[A], respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.276-276
• /
• 2014

High-performance, fully-transparent, and top-gated oxide thin-film transistor (TFT) was successfully fabricated with Ta2O5 high-k gate dielectric on a glass substrate. Through a self-passivation with the gate dielectric and top electrode, the top-gated oxide TFT was not affected from H2O and O2 causing the electrical instability. Heat-treated InSnO (ITO) was used as the top and source/drain electrode with a low resistance and a transparent property in visible region. A InGaZnO (IGZO) thin-film was used as a active channel with a broad optical bandgap of 3.72 eV and transparent property. In addition, using a X-ray diffraction, amorphous phase of IGZO thin-film was observed until it was heat-treated at 500 oC. The fabricated device was demonstrated that an applied electric field efficiently controlled electron transfer in the IGZO active channel using the Ta2O5 gate dielectric. With the transparent ITO electrodes and IGZO active channel, the fabricated oxide TFT on a glass substrate showed optical transparency and high carrier mobility. These results expected that the top-gated oxide TFT with the high-k gate dielectric accelerates the realization of presence of fully-transparent electronics.

• 한국정보통신학회논문지
• /
• 제20권4호
• /
• pp.799-804
• /
• 2016

본 논문에서는 비대칭 이중게이트 MOSFET의 상하단 게이트 산화막 두께에 대한 드레인 유도 장벽 감소 현상을 분석하기 위하여 전위장벽에 영향을 미치는 드레인전압에 따른 문턱전압의 변화를 관찰할 것이다. 비대칭 이중게이트 MOSFET는 상단과 하단의 게이트 산화막 두께를 다르게 제작할 수 있는 특징이 있다. 상단과 하단의 게이트 산화막 두께 변화에 따른 드레인 유도 장벽 감소 현상에 대하여 포아송방정식을 이용하여 분석하였다. 결과적으로 드레인 유도 장벽 감소 현상은 상하단 게이트 산화막 두께에 따라 큰 변화를 나타냈다. 상단과 하단 게이트 산화막 두께가 작을수록 드레인 유도 장벽은 선형적으로 감소하였다. 채널길이에 대한 드레인 유도 장벽 감소 값은 비선형적인 관계가 있었다. 고농도 채널도핑의 경우 상단 산화막 두께가 하단 산화막 두께보다 드레인 유도 장벽 감소에 더 큰 영향을 미치고 있었다.

• 한국인터넷방송통신학회논문지
• /
• 제9권3호
• /
• pp.173-178
• /
• 2009

금속산화물 박막 소자를 제작하여 전기적 특성을 조사하였다. 소자는 Electrode를 TOP-TOP구조로 제작하였으며 스위칭 특성을 연구하기 위해 전극간의 산화금속박막의 전도특성이 측정되었다. 소자의 저항변화는 전압을 선형적으로 인가하여 측정하였다. 제작된 소자는 MIM구조로써 외부에서 인가하는 전기적 신호에 의하여 전기전도도가 큰 On-state와 전기전도도가 낮은 Off-state로 바뀌는 특성을 나타내었다. $Si/SiO_2/MgO$ 소자는 Forming에 의해 저항이 큰 상태에서 저항이 작은 상태로 전기적 특성이 변화하면서 스위칭 특성을 보였다. 본 연구를 통하여 산화금속은 차세대 비휘발성 메모리로는 물론 다른 전기적 응용이 기대되는 물질임을 확인하게 되었다.

• 전기전자학회논문지
• /
• 제24권1호
• /
• pp.194-199
• /
• 2020

본 논문에서는 비대칭 무접합 이중게이트 MOSFET에 대한 문턱전압이동을 상단과 하단 게이트 산화막 두께에 따라 분석하였다. 비대칭 구조에서는 상단과 하단 게이트 산화막 두께를 달리 제작할 수 있으므로 문턱전압이동을 일정하게 유지하면서 상단 게이트에서 발생할 수 있는 누설전류를 감소시키기 위하여 상단과 하단 산화막 두께를 조정할 수 있다. 이를 위하여 해석학적 문턱전압 모델을 제시하였으며 이 모델은 2차원 시뮬레이션 값과 잘 일치하였다. 결과적으로 일정한 문턱전압이동을 유지하면서 하단 게이트 산화막 두께를 감소시키면 상단 게이트 산화막 두께를 증가시킬 수 있어 상단 게이트에서 발생할 수 있는 누설전류를 감소시킬 수 있을 것이다. 특히 하단 게이트 산화막 두께가 증가하여도 문턱전압이동에는 큰 영향을 미치지 않는다는 것을 관찰하였다.

• 한국전기전자재료학회논문지
• /
• 제31권7호
• /
• pp.481-485
• /
• 2018

In this study, oxide/metal/oxide-type transparent electrodes based on Al and ZnO were investigated. Thin films of these materials were sputter-deposited at room temperature. To evaluate the thickness dependence of the oxide layers, the top and bottom ZnO layers were varied in the range of 5~80 nm and 2.5~20 nm, respectively. When the thicknesses of the top and bottom ZnO layers were fixed at 30 nm and 2.5 nm, a maximum transmitance of 66% and sheet resistance of $16.5{\Omega}/{\square}$ were achieved, which is significantly improved compared with the Al layer without top and bottom ZnO layers showing a maximum transmitance of 44.3% and sheet resistance of $44{\Omega}/{\square}$.

• 한국정보통신학회논문지
• /
• 제20권3호
• /
• pp.571-576
• /
• 2016

비대칭 이중게이트 MOSFET는 다른 상하단 게이트 산화막 두께를 갖는다. 상하단 게이트 산화막 두께 비에 대한 문턱전압이하 스윙 및 전도중심의 변화에 대하여 분석하고자한다. 문턱전압이하 스윙은 전도중심에 따라 변화하며 전도중심은 상하단의 산화막 두께에 따라 변화한다. 비대칭 이중게이트 MOSFET는 문턱전압이하 스윙의 저하 등 단채널효과를 감소시키기에 유용한 소자로 알려져 있다. 포아송방정식의 해석학적 해를 이용하여 문턱전압이하 스윙을 유도하였으며 상하단의 산화막 두께 비가 전도중심 및 문턱전압이하 스윙에 미치는 영향을 분석하였다. 문턱전압이하 스윙 및 전도중심은 상하단 게이트 산화막 두께 비에 따라 큰 변화를 나타냈다. 특히 하단 게이트 전압은 문턱전압이하 스윙에 큰 영향을 미치며 하단게이트 전압이 0.7V 일 때 $0<t_{ox2}/t_{ox1}<5$의 범위에서 문턱전압이하 스윙이 약 200 mV/dec 정도 변화하는 것을 알 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제35권3호
• /
• pp.255-263
• /
• 2022

The subthreshold swing (SS) of an asymmetric junctionless double gate (AJLDG) MOSFET is analyzed by the use of Gaussian function. In the asymmetric structure, the thickness of the top/bottom oxide film and the flat-band voltages of top gate (V_fbf) and bottom gate (V_fbb) could be made differently, so the change in the SS for these factors is analyzed with the projected range and standard projected deviation which are parameters for the Gaussian function. An analytical subthreshold swing model is presented from the Poisson's equation, and it is shown that this model is in a good agreement with the numerical model. As a result, the SS changes linearly according to the geometric mean of the top and bottom oxide film thicknesses, and if the projected range is less than half of the silicon thickness, the SS decreases as the top gate oxide film is smaller. Conversely, if the projected range is bigger than a half of the silicon thickness, the SS decreases as the bottom gate oxide film is smaller. In addition, the SS decreases as V_fbb-V_fbf increases when the projected range is near the top gate, and the SS decreases as V_fbb-V_fbf decreases when the projected range is near the bottom gate. It is necessary that one should pay attention to the selection of the top/bottom oxide thickness and the gate metal in order to reduce the SS when designing an AJLDG MOSFET.

• 한국정보통신학회논문지
• /
• 제20권5호
• /
• pp.992-997
• /
• 2016

본 논문에서는 단채널 비대칭 이중게이트 MOSFET의 상하단 산화막 두께비에 대한 터널링 전류의 변화에 대하여 분석하고자 한다. 채널길이가 5 nm까지 감소하면 차단전류에서 터널링 전류의 비율이 크게 증가하게 된다. 이와 같은 단채널효과는 상하단 게이트 산화막 구조를 달리 제작할 수 있는 비대칭 이중게이트 MOSFET에서도 발생하고 있다. 본 논문에서는 상하단 게이트 산화막 두께비 변화에 대하여 차단전류 중에 터널링 전류의 비율 변화를 채널길이, 채널두께, 도핑농도 및 상하단 게이트 전압을 파라미터로 계산함으로써 단채널에서 발생하는 터널링 전류의 영향을 관찰하고자 한다. 이를 위하여 포아송방정식으로부터 해석학적 전위분포를 구하였으며 WKB(Wentzel-Kramers-Brillouin)근사를 이용하여 터널링 전류를 구하였다. 결과적으로 단채널 비대칭 이중게이트 MOSFET에서는 상하단 산화막 두께비에 의하여 터널링 전류가 크게 변화하는 것을 알 수 있었다. 특히 채널길이, 채널두께, 도핑농도 및 상하단 게이트 전압 등의 파라미터에 따라 매우 큰 변화를 보이고 있었다.

• 한국전기전자재료학회논문지
• /
• 제19권5호
• /
• pp.442-449
• /
• 2006

Electrical, optical, and structural properties of indium zinc oxide (IZO) films grown by a box cathode sputtering (BCS) were investigated as a function of oxygen flow ratio. A sheet resistance of $42.6{\Omega}/{\Box}$, average transmittance above 88% in visible range, and root mean spare roughness of $2.7{\AA}$ were obtained even in the IZO layers grown at room temperature. In addition, it is shown that electrical characteristics of the top-emitting organic light emitting diodes (TOLEDs) with the BCS grown-IZO top cathode layer is better than that of TOLEDs with DC sputter grown IZO top cathode, due to absence of plasma damage effect. Furthermore the effects of oxygen flow ratio in IZO films are investigated, based on x-ray photoelectron spectroscopy (XPS), ultra violet/visible (UV/VIS) spectro-meter, scanning electron microscopy (SEM), and atomic force microscopy (AFM) analysis results.