• Journal of the Korean Society for Heat Treatment
• /
• 제13권5호
• /
• pp.324-329
• /
• 2000

Microstructure, mechanical and fatigue behaviors of TiCN and TiN/TiCN thin films, deposited on quenched and tempered STD61 tool steel, were investigated by using XRD, XPS, hardness, adhesion and fatigue tests. The TiCN thin film is grown along the (100), (111) orientation, whereas the TiN/TiCN thin film is grown along the (111) orientation. The preferred orientation of TiN/TiCN thin film strongly depends on the TiN buffer layer whose orientation is (111), as is well-known. The TiN/TiCN thin film showed the higher adhesion compared with TiCN single layer because the TiN buffer layer, having good toughness, reduces the effects of the lower hardness of substrate. In the high cycle tension-tension fatigue test, the fatigue life of the TiCN and the TiN/TiCN coated steel increased approximately two to four times and five to nine times respectively compared with uncoated specimens. The TiN buffer layer in multilayer thin films plays an important role in reducing residual stress and fatigue crack initiation, and then in restraining the fatigue propagation.

• Journal of the Korean Society for Heat Treatment
• /
• 제4권1호
• /
• pp.19-29
• /
• 1991

This study was to investigate the influence of the substrate hardness on the hardness and adhesion of TiN thin film deposited by R.F. PACVD. Although the substrate hardness changed, chemical composition, stoichiometry and structure of TiN thin film did not change. ISE index was 1.96-1.99 for the substrate and was 1.57-1.79 for TiN thin film. And ISE index of TiN thin film was inverse proportion to the substrate hardness. When the substrate hardness was low, TiN thin film had many cracks around the indentation. But as the substrate hardness increased, TiN thin film had a few cracks and the deformation was limited within indentation. In having measured the adhesion of TiN thin film by SAT, the critical load (Lc) generally increased as the substrate hardness decreased.

• Journal of Environmental Science International
• /
• 제16권6호
• /
• pp.683-688
• /
• 2007

In this study, N doped $TiO_2$ (TiO-N) thin film was prepared by DC magnetron sputtering method to show the photocatalytic activity in a visible range. Various gases (Ar, $O_2\;and\;N_2$) were used and Ti target was impressed by 1.2 kW -5.8 kW power range. The hysteresis of TiO-N thin film as a function of discharge voltage wasn't observed in 1.2 and 2.9kW of applied power. Cross sections and surfaces of thin films by FE-SEM were tiny and dense particle sizes of both films with normal cylindrical structures. XRD pattern of $TiO_2$ and TiO-N thin films was appeared by only anatase peak. Red shift in UV-Vis adsorption spectra was investigated TiO-N thin film. Photoactivity was evaluated by removal rate measurement of suncion yellow among reactive dyes. The photodegradation rate of $TiO_2$ thin film on visible radiation was shown little efficiency but TiO-N was about 18%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제11권10호
• /
• pp.826-832
• /
• 1998

In this study the thin films with the structure of Si+SiO$_2$+TiN are made by RF supttering method. TiN, which has small diffusion coefficient and low resistivity, is evaporated between SiO$_2$ and Al layers. It investigates the V-R characteristics depending on the thickness of SiO$_2$ which is used as insulation layer and researches its effects on voltage stability of thin film and varistor. These films show very small resistance valus in negative(-) voltage and large and large value in positive voltage band, and with the increase of voltage, resistance value is rapidly reduced and the satisfactory characteristic of varistor is shown at +1[V]. It is found that resistance value of TiN thin film is small and also TiN thin film has more current than the thin film which is not evaporated by TiN thin film. When Al electrode is evaporated of SiO$_2$ thin film, spiking occurs, but the spiking can be prevented with evaporation of TiN between SiO$_2$ and Al layers and this thin films in made easily because of its good attachment. With the increase of voltage, the resistance is changed into non-linear pattern and the bidirectional varistor characteristic is shown and then its theory can be verified by this experiment. Accordingly, when TiN is evaporated of Si Wafer(n-100), it obtains better voltage-resistance than thin film which is not evaporated and also when varistor character is used electrically to automatic control element such as elimination of flame, power distribution arrestor and constant voltage compensation, satisfactory reproducibilities are expected.

• Proceedings of the KIEE Conference
• /
• 대한전기학회 1996년도 하계학술대회 논문집 C
• /
• pp.1838-1840
• /
• 1996

In order to study the relationship between the physical properties of glow discharge plasma and the physical behavior of TiN thin film, electrical characteristics of RF discharge plasma driven at 13.56MHz in a parallel-plate electrode system were measured. Plasma parameters, such as electron density and temperature, are also studied since they may be considered as one of the very important factors deciding the physical properties of TiN thin film under given conditions of applied biasd voltage and pressure. The TiN thin film were fabricated over a wide range of discharge conditions, and some of the general relationships between the measured plasma parameters and the properties of TiN thin film were discussed.

• Transactions on Electrical and Electronic Materials
• /
• 제12권4호
• /
• pp.144-147
• /
• 2011

In this work, we present a study regarding the etching characteristics on titanium nitride (TiN) thin films using an inductively coupled plasma system. The TiN thin film was etched using a $N_2/BCl_3$/Ar plasma. The studied etching parameters were the gas mixing ratio, the radio frequency (RF) power, the direct current (DC)-bias voltages, and the process pressures. The baseline conditions were as follows: RF power = 500 W, DC-bias voltage = -150 V, substrate temperature = $40^{\circ}C$, and process pressure = 15 mTorr. The maximum etch rate and the selectivity of the TiN to the $SiO_2$ thin film were 62.38 nm/min and 5.7, respectively. The X-ray photoelectron spectroscopy results showed no accumulation of etching byproducts from the etched surface of the TiN thin film. Based on the experimental results, the etched TiN thin film was obtained by the chemical etching found in the reactive ion etching mechanism.

• Electrical & Electronic Materials
• /
• 제8권1호
• /
• pp.13-20
• /
• 1995

To develope a high precision TiAIN thin film resistor, TiAIN films were deposited on A1$_{2}$03 substrates by reactive planar magnetron cosputtering from Ti and Al targets in an Ar-N$_{2}$ atmosphere. The characteristics of the TiAIN thin film were controlled by changing of the R.F. power on Ti and Al targets, and the N$_{2}$ partial pressure. The high precision TiAIN thin film resistor with TCR(Temperature Coefficient of Resistance) of less than 10ppm/.deg. C was obtained under the R.F. power condition of 160(w)/240(w) to Ti and Al targets at the N$_{2}$ partial pressure of 7*10$^{-5}$ Torr. The composition of these films were investigated by XRD, SEM and EDS.

• Journal of Korean Society of Environmental Engineers
• /
• 제27권1호
• /
• pp.59-66
• /
• 2005

[ $TiO_2$ ] was deposited by DC magnetron sputtering on glass surface under various sputtering parameters such as discharge power($0.6{\sim}5.2\;kW$, substrate temperature($R.T{\sim}350^{\circ}C$), Ar and $O_2$ flow ratio with $0{\sim}50\;sccm$($Ar+O_2$ 90 sccm) and about 1 mtorr of pressure. TiO-N thin film was prepared under same sputtering conditions for $TiO_2$ thin film except flow ratio($Ar+O_2+N_2$ 90 sccm). The sheet resistance of thin films deposited under these parameters was measured to analyze electronic characteristic and thin film's thickness(${\alpha}$-step), surface roughness(AFM) and formation construction(FE-SEM, XRD) were also measured to draw optimal sputtering parameters. In order to evaluate photo-activity of thin film($TiO_2$, TiO-N) made in optimal parameters for removal of pollutants, toluene among VOCs and Suncion Yellow among reactive dyes were chosen to probe organic compounds for photo-degradation. It was shown that the photo-catalytic thin films had a significant photo-activation for the chosen contaminants and especially TiO-N thin film showed maximum efficiency of 33% for toluene(5 ppm) removal in visible-light range.

• Journal of the Korean institute of surface engineering
• /
• 제37권6호
• /
• pp.307-312
• /
• 2004

Extensive efforts have been made in an attempt to utilize photocatalytic properties of $TiO_2$ in visible range. $TiO_2$ and TiO-N thin films were made by the DC reactive magnetron sputtering method at $300^{\circ}C$. Various gases (Ar, $O_2$ and $N_2$) were used and Ti target was impressed by 0.6 kW-5.8 kW power range. The hysteresis phenomenon of the $TiO_2$ thin film as a function of the discharge voltage characteristic was observed to be higher as applied power increases. That of TiO-N thin film was occurred at the 5.8 kW power. The cross section and surface roughness of thin films were observed by FE-SEM and AFM. Average surface roughness of TiO-N thin film was observed as $15.9\AA$ and that of $TiO_2$ as $13.2\AA$. The crystal phases of both $TiO_2$ and TiO-N thin films were found to be anatase structure. The atomic $\beta$-N (396 eV peak in N 1s XPS) was shown in the rutile crystal of TiO-N and was considered acting as the origin of wavelength shift to the visible light.

• Journal of the Korean institute of surface engineering
• /
• 제41권3호
• /
• pp.83-87
• /
• 2008

This study described the effects of RF power, DC bias voltage, chamber pressure and gas mixing ratio on the etch rates of TiN thin film and selectivity of TiN thin film to $SiO_2$ with $BCl_3$/Ar gas mixture. When the gas mixing ratio was $BCl_3$(20%)/Ar(80%) with other conditions were fixed, the maximum etch rate of TiN thin film was 170.6 nm/min. When the DC bias voltage increased from -50 V to -200 V, the etch rate of TiN thin film increased from 15 nm/min to 452 nm/min. As the RF power increased and chamber pressure decreased, the etch rate of TiN thin film showed an increasing tendency. When the gas mixing ratio was $BCl_3$(20%)/Ar(80%) under others conditions were fixed, the intensity of optical emission spectra from radical or ion such as Ar(750.4 nm), $Cl^+$(481.9 nm) and $Cl^{2+}$(460.8 nm) was highest. The TiN thin film was effectively removed by the chemically assisted physical etching in $BCl_3$/Ar ICP plasma.