• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.125-125
• /
• 2015

Ti-Al-Cr-N thin layer was prepared on Fe-Si thin sheet by arc ion plating to improve corrosion and mechanical properties. The compositions ratios of Fe : Cr : Al : Ti : Si : N of the thin layers at $500^{\circ}C$ was 1.24 : 0.56 : 36.82 : 32.72 : 0.59 : 28.07 [wt.%], respectively. The higher arc ion plating temperature was, the higher corrosion resistance and nano-hardness were observed due to chromium content. Corrosion potential and corrosion rate in artificial sea water of the coating layer were in the range of $-39mV_{SHE}$ and $2mA/cm^2$, respectively. Passivity was not observed in the artificial sea water. Nano-hardnesses of the thin layers was increased by adding Cr from 23.6 to 25.8 [GPa]. The friction coefficients and fatigue limits of the layers were 0.388, 0.031, respectively.

• 한국수소및신에너지학회논문집
• /
• 제16권2호
• /
• pp.122-129
• /
• 2005

The characteristics of hydrogen storage have been investigated in the Ti-Cr-Mo and Ti-Cr-V ternary alloys with bcc structure. The alloys were melted by arc furnace and remelted 4-5 times for homogeneity. The lattice parameters, microstructures and phases of the alloys were examined by SEM, EDX and XRD, and the Pressure-Composition isotherms of the alloys were measured. From these data the relationship of the maximum and effective hydrogen storage capacities vs. chemical composition, lattice parameter and the radius of tetrahedral site were analyzed and discussed. The results showed that all of these alloy, in the range of the this study, had mainly bcc solid solutions with small amount of Ti segregation due to a lower melting point of Ti compared with other elements. Lattice parameters of the alloys were very near to the atomic average values of lattice parameters of the constituent elements. It was also found that maximum hydrogen storage capacities of the Ti-Cr-Mo alloys increased with increasing Ti content and the radius of tetrahedral site but the effective hydrogen storage capacities decreased after showing the maximum. The hydrogen storage capacities of the Ti-Cr-V alloys were almost same even though the V contens were quite different from alloy to alloy and this could be attributed to the almost same Ti/Cr ratio of the alloys. The maximum effective hydrogen storage capacity of the Ti-Cr-Mo alloys was revealed at Ti content of about 40${\sim}$50 at% and radius of tetrahedral site of 0.43${\sim}$0.45 nm. The Ti-Cr-V alloys showed the hydrogen storage capacities of 3.0 wt% and effective hydrogen storage capacities of 1.5 wt%.

• 한국세라믹학회지
• /
• 제45권4호
• /
• pp.196-203
• /
• 2008

Metal-carbon/$TiO_2$ composite photocatalysts were thermally synthesized through the mixing of anatase to metal(Cu, Zn) containing phenol resin in an ethanol solvent coagulation method. The BET surface area increases, with the increase depending on the amount of metal salt used. From SEM images, metal components and carbon derived from phenol resin that contains metal was homogeneously distributed to composite particles with porosity. XRD patterns revealed that metal and titanium dioxide phase can be identified for metal-carbon/$TiO_2$ composites, however, the diffraction peaks of carbon were not observed due to the low carbon content on the $TiO_2$ surfaces and due to the low crystallinity of the amorphous carbon. The results of a chemical elemental analysis of the metal-carbon/$TiO_2$ composites showed that most of the spectra for these samples gave stronger peaks for C, O, treated metal components and Ti metal compared to that of any other elements. According to photocatalytic results, the MB degradation can be attributed to the three types of synergetic effect: photocatalysis, adsorptivity and electron transfer, according to the light absorption between the supporter $TiO_2$, metal species, and carbon layers.

• Journal of Electrical Engineering and Technology
• /
• 제2권1호
• /
• pp.98-101
• /
• 2007

Yttrium(Y)-substituted bismuth titanate $(Bi_{4-x},Y_x)Ti_3O_{12}$ [x=0, 0.25, 0.5, 0.75, 1](BYT) thin films were deposited using an RF sputtering method on the $Pt/TiO_2/SiO_2/Si$ substrates. The structural properties and electrical properties of yttrium-substituted $(Bi_4-xYx)Ti_3O_{12}$ thin films were analyzed. The remanent polarization of $(Bi_4-xYx)Ti_3O_{12}$ films increased with increasing Y-content. The $(Bi_{3.25}Y_{0.75})Ti_3O_{12}$ films fabricated using a top Au electrode showed saturated polarization-electric field(P-E) switching curves with a remanent polarization(Pr) of $8{\mu}C/cm^2$ and coercive field (Ec) of 53 kV/cm at an applied voltage of 7 V. The $(Bi_{3.25}Y_{0.75})Ti_3O_{12}$ films exhibited fatigue-free behavior up to $4.5{\times}10^{11}$ read/write switching cycles at a frequency of 1MHz.

• 한국표면공학회지
• /
• 제35권6호
• /
• pp.415-421
• /
• 2002

Ti-Si-N coating layers were codeposited on silicon wafer substrates by a DC reactive magnetron sputtering technique using separate titanium and silicon targets in $N_2$/Ar gas mixtures. The oxidation behavior of Ti-Si-N coating layers containing 4.0 at.%, 10.0 at.%, and 27.3 at.% Si was investigated at temperatures ranging from 600 to $960^{\circ}C$. The coating layers containing 4.0 at.% Si became fast oxidized from $600^{\circ}C$ while the coating layers containing 10.0 at.% Si had oxidation resistance up to $800^{\circ}C$. It was concluded that an increase in Si content to a level of 10.0 at.% led to the formation of finer TiN grains and a uniformly distributed amorphous Si3N4 phase along grain boundaries, which acted as efficient diffusion barriers against oxidation. However, the coating layers containing 27.3 at.% Si showed relatively low oxidation resistance compared with those containing 10.0 at.% Si. This phenomenon would be explained by the existence of free Si which was not nitrified in the coating layers containing 27.3 at.% Si.

• 한국광학회지
• /
• 제5권4호
• /
• pp.499-504
• /
• 1994

불꽃가수분해 증착방법으로 $SiCl_{4}$, TMB, $TiCL_{4}$등을 사용하여 Ti doped BSG 실리카 입자박막을 실리콘 기판위에 증착하고 증착된 입자층을 녹여서 집적광학용 박막을 제작하였다. 박막의 증착 속도는 $0.5{\mu}m$분 이상으로서 수십 ${\mu}m$의 후막을 빠르게 증착할 수 있었으며 $TiO_{2}$의 첨가량에 따라 BSG 박막의 굴절률을 0.3% 이상 변화시킬 수 있었다. 그 결과 통신용 광섬유와 크기 및 굴절률 분포가 BSG박막의 굴절률을 0.3% 이상 변화시킬 수 있었다. 그 결과 통신용 광섬유와 크기 및 굴절률 분포가 유사한 광도파로를 제작하였다. 보통 B의 도판트로는 $BCl_{3}$를 쓰나 여기서는 TBM를 사용한 결과 TBM도 B의 도판트로 적합함을 알았다. B의 첨가에 의하여 실리카 입자막의 녹는점을 $1200^{\circ}C$로 낮출 수 있었다. 또한 FTIR에 의한 박막의 조성비분석 결과 BSG박막에 $B_2O_3$ 함량이 최대 10mol%로 나타났다.

• 한국표면공학회지
• /
• 제39권6호
• /
• pp.263-267
• /
• 2006

As technology advances, there is a demand for development of hard solid lubricant coating. (Ti, Cr, Zr)N-$MoS_2$ films were deposited on AISI H13 tool steel substrate by co-deposition of $MoS_2$ with (Ti, Cr, Zr)N using a D.C. magnetron sputtering process. The influence of the $N_2Ar$ gas ratio, the amount of $MoS_2$ in the films and the bias voltage on the mechanical and structural properties of the films were investigated. The highest hardness level was observed at the $N_2/Ar$ gas ratio of 0.3. Hardness of the films did not change much with the increase of the $MoS_2$ content in the films. As the substrate bias potential was increased, hardness level of the film reached maximum at -150 V. Surface morphology of these films indicated that high hardness was attributed to the fine dome structure.

• 한국전기전자재료학회논문지
• /
• 제15권1호
• /
• pp.24-29
• /
• 2002

In this paper, the microstructure and the dielectric properties of Sr$\_$1-x/CaxTiO$_3$(0$\leq$x$\leq$0.2)-based grain boundary layer ceramics were investigated. The sintering temperature and time were 1420∼152 0$\^{C}$ and 4 hours in N$_2$ gas, respectively. The average grain size and the lattice constant were decreased with increasing content of Ca, but the average grain size was increased with increase of sintering temperature. The second phase foamed by the thermal diffusion of CuO from the surface leads to verb high apparent dielectric constant, $\xi$$\_$r/>50000 and low dielectric loss, tan$\delta$<0.05. X-ray diffraction patterns of Sr$\_$1-x/CaxTiO$_3$ exhibited cubic structure, and the peaks shifted upward and the peak intensity were decreased with x. This is due to the lattice contraction as Sr is replaced by Ca with a smaller ionic radius. The specimens treated thermal diffusion for 2hrs in 1150$\^{C}$ exhibited nonlinear current-voltage characteristic, and its nonlinear coefficient(a) was overt 7.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.112-112
• /
• 2015

The purposed of this work was to determine nanotube shape variation on the Ti-xNb alloys with alloying elements and applied potentials. Samples were prepared by arc melting, followed by followed by homogenization for 12 hr at $1000^{\circ}C$ in argon atmosphere. This study was evaluated the phase and microstructure of Ti-xNb alloys using an X-ray diffraction (XRD) and optical microscopy (OM). The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). The nanotube on the alloy surface was formed in 1 M $H_3PO_4$ with small additions of NaF 0.8 wt.%. All anodization treatments were carried out using a scanning potentiostat (Model 362, EG&G, USA) at constant voltage 30 V for 120 min, respectively. The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). Surface characteristics of nanotbue formed on Ti-xNb alloys was investigated by potentiodynamic test and potentiostatic in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. It was observed that the changed ${\alpha}$ phase to ${\beta}$ phase with Nb content.

• 한국안광학회지
• /
• 제3권1호
• /
• pp.217-222
• /
• 1998

$SiO_2-TiO_2-AgO$ 코팅박막을 졸-겔법으로 현미경용 슬라이드 유리판과 씰리콘 기판에 제조하였다. 이 박막의 열처리온도는 $500^{\circ}C$가 적절하였으며 5회 반복코팅한 박막의 두께는 310nm였다. AgO가 10mol% 첨가된 박막의 표면은 균일한 구조를 보였으나 첨가량이 많아질수록 박막의 표면에 pin hole과 AgO의 석출에 기인한 cluster를 보였다. 열처리온도의 증가에 따라 IR흡수의 정도가 점차 감소하였고, AgO 첨가량의 증가에 따라 반사율은 점차 감소하였으며 색상은 light yellow에서 무채색 쪽으로 점차 전이하였다.