• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.355-356
• /
• 2006

WC-TiC-TaC binderless cemented carbide was oxidized under low partial pressure of oxygen (50ppm) at 873K for 1 to 20 h. Surface roughness was measured using atomic force microscope, and effect of TiC amount on oxidation behavior of the carbide was investigated. WC phase was oxidized more easily than WC-TiC-TaC solid solution phase. With an increase in TiC amount, WC-TiC-TaC phase increased and the oxidation resistance of the carbide increased.

• 한국분말재료학회지
• /
• 제8권1호
• /
• pp.42-49
• /
• 2001

Ti-50Ni(at%) and Ti-40Ni-10Cu(at%) alloy powders have been fabricated by ball milling method, and their microstructure and phase transformation behavior were investigated by means of scanning electron microscopy/energy dispersive spectrometry, differential scanning calorimetry (DSC), X-ray diffractions and transmission electron microscopy. In order to investigate the effect of ball milling conditions on transformation behavior, ball milling speed and time were varied. Ti-50Ni alloy powders fabricated with the milling speed more than 250 rpm were amorphous, while those done with the milling speed of 100rpm were crystalline. In contrast to Ti-50Ni alloy powders, Ti-40Ni-10Cu alloy powders were crystalline, irrespective of ball milling conditions. DSC peaks corresponding to martensitic transformation were almost discernable in alloy powders fabricated with the milling speed more than 250 rpm, while those were seen clearly in alloy powders fabricated with the milling speed of 100 rpm. This was attributed to the fact that a strain energy introduced during ball milling suppressed martensitic transformation.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.343-353
• /
• 1999

2.45 GHz의 microwave가 수열 합성법으로 제조된 BaTiO3 분말의 특성에 미치는 영향을 조사하였다. 700W 출력으로 반응시켰을 때, microwave-autoclave system에서는 약 5분만에 BaTiO3 결정이 형성되기 시작하여, 10분 이상의 반응에서는 더 이상 결정성 증가는 관찰되지 않았다. Microwave-system의 경우에는 15분만에 결정이 형성되기 시작하여, 1시간정도의 반응으로 충분한 BaTiO3 분말을 얻을 수 있었다. Microwave를 이용한 균일가열의 영향으로 분말들은 균일하게 분산되어 있었고, 기존의 전기적인 가열 방법에서 나타나는 응집 현상이나 grain의 성장 등은 보이지 않았다. 제조된 분말의 크기는 보통 30~60 nm정도였는데, 졸 안의 Ba/Ti의 비가 분말의 크기를 결정하는데 중요한 역할을 하였다. 이는 여분의 바륨이 Ba(OH)2등과 같은 다른 상을 형성하여 BaTiO3 분말의 계면에 얇은 막을 형성하여 분말들의 응집 현상이나 grain의 성장을 억제하는 것으로 추정하였다. M1-crowave-autoclave 에서는 15분 정도의 반응만으로도 미량이지만 tetragonal-BaTiO3를 직접적으로 형성할 수 있었고, microwave-reflux에서는 25$0^{\circ}C$의 건조로써 미량의 tetragonal-BaTiO3를 얻을 수 있었다.

• 한국세라믹학회지
• /
• 제39권11호
• /
• pp.1017-1022
• /
• 2002

$(Ba_{1-x}Ca_x)(Ti_{1-y}Zr_y)O_3(BCTZ)$ powders for the Ni-electrode Multilayer Ceramic Capacitor(MLCC) were synthesized via hydrothermal treatment using mixed aqueous solutions of $BaCl_2{\cdot}2H_2O,\Ca(NO_3)2{\cdot}4H_2O,\ ZrOCl_2{\cdot}8H_2O$ and $TiCl_4$. Two component and three component systems were also extensively studied for basic data. BT, CT and BZ powders were crystalline but CZ was determined to be amorphous under the same synthetic condition. In BTZ system, Zr and Ti were completely soluble and Ca would be substituted for Ba up to ∼6 mol% in BCT. The submicron-sized $(Ba_{0.95}Ca_{0.05})(Ti_{0.80}Zr_{0.20})O_3$ powder of the target composition was successfully synthesized at $150{\circ}$ for 12h.

• 한국분말재료학회지
• /
• 제10권6호
• /
• pp.443-447
• /
• 2003

Nano-sized $TiB_2$ was in situ synthesized in copper matrix through self-propagating high temperature synthesis (SHS) with high-energy ball milled Ti-B-Cu elemental mixtures as powder precursors. The size of $TiB_2$ particles in the product of SHS reaction decreases with time of preliminary mechanical treatment ranging from 1 in untreated mixture to 0.1 in mixtures milled for 3 min. Subsequent mechanical treatment of the product of SHS reaction allowed the $TiB_2$ particles to be reduced down to 30-50 nm. Microstructural change of $TiB_2$-Cu nanocomposite during spark plasma sintering (SPS) was also investigated. Under simultaneous action of pressure, temperature and electric current, titanium diboride nanoparticles distributed in copper matrix move, agglomerate and form a interpenetrating phase composite with a fine-grained skeleton.

• 한국분말재료학회지
• /
• 제11권6호
• /
• pp.503-509
• /
• 2004

Dispersion stabilities and photocatalytic activities of rutile $TiO_{2}$ powders with unique nano-structure synthesized by homogeneous precipitation process at low temperature(HPPLT) have been investigated in the acrylic resin containing fluorostyrene in the range of 0~0.16 mole. Isoelectric point of $TiO_{2}$ in the acrylic resin placed in the neutral region whereas that of $TiO_{2}$ in the water placed in the acidic region, indicating that zeta potential and agglomeration of $TiO_{2}$ powder is strongly dependent on the pH and the type of solvent. To prepare an adhesion, an acrylic resin containing fluorostyrene was synthesized by a radical polymerization. The adhesion of coating layer was increased with increasing fluorostyrene's contents without changing the dispersion stabilities and degrading photocatalytic properties.

• 한국분말재료학회지
• /
• 제13권3호
• /
• pp.199-204
• /
• 2006

We manufactured the metal hydrides of $(Ti_{0.88}Mg_{0.12})H_2$ using a very easy and cheap way that Ti-12%Mg blending powder was mechanically milled with liquid milling media such as isopropyl alcohol ($C_3H_8O$, containing oxygen) and hexane ($C_6H_{14}$, no oxygen) as hydrogen source. The $(Ti_{0.88}Mg_{0.12})H_2$ synthesized in isopropyl alcohol contained the high oxygen of 11.2%, while one in hexane had the low oxygen content of 0.7%. Such a difference of oxygen content affected the dehydriding behavior, phase transformation, and microstructural evolution at high temperature, which was investigated through X-ray diffraction and DSC measurements, and electron microscope observations.

• 한국분말재료학회지
• /
• 제4권4호
• /
• pp.243-251
• /
• 1997

Engine valve-shaped TiAl-Mn intermetallics containing 43.5 to 47.5at%Al (Mn/Al=0.036) are successively fabricated by reactive sintering the elemental powder mixtures near-net shaped by extrusion and die forging. A duplex structure consisted of lamellar grains and equiaxed $\gamma$ grains is developed for all compositions, and the areal fraction of the lamellar grains(or equiaxed $\gamma$ grains) decreases (or increases) with increasing Al content. As Al content increased, the elongation increases with accompanying decrease in yield strength and ultimate tensile strength at both room temperature and 80$0^{\circ}C$. This indicates that the suitable composition is Ti-45at%Al-1.6at%Mn in considering the balance of ambient and elevated tensile properties. The reactive-sintered Ti-45Al-1.6Mn alloy shows superior oxidation resistance not only to the plasma arc melted one but also to the heat resistance steel STR35(representative exhaust valve head material for automotive engine). The reactive-sintered Ti-45Al-1.6Mn alloy coated with an oxidizing scale exhibits a better wear resistance than induction hardened martensitic steel STR11(representative exhaust valve tip material for automotive engine).

• 한국분말재료학회지
• /
• 제13권2호
• /
• pp.119-123
• /
• 2006

The grain growth behavior of $0.95Na_{1/2}Bi_{1/2}TiO_{3}-0.05BaTiO_{3}$ (NBT-5BT) has been investigated with respect to the grain shape. The powder compacts of NBT-5BT were sintered at 1200 for various times. The corresponding equilibrium shape was a round-edged cube with flat {100}-faces. Abnormal grains were not observed in the specimens sintered for 1 to 12 h but abnormal grains appeared when sintered for 24 h. Before the formation of abnormal grains, a valley was observed in the measured grain size distribution of NBT-5BT, showing that the grain size distribution was a combination of two unimodal distributions. The present result suggests that the grain growth in NBT-5BT was governed by the growth of facet planes which would occur via 2-dimansional nucleation and growth.

• 한국분말재료학회지
• /
• 제17권1호
• /
• pp.29-35
• /
• 2010

We produced cylindrical porous TiNi bodies by Self-propagating High-temperature Synthesis (SHS) process, varying the heating schedule prior to ignition of a loose preform compact made from (Ti+Ni) powder mixture. To investigate the effect of the heating schedule on the behaviour of combustion wave propagation and the structure of porous TiNi shape-memory alloy (SMA) body, change of temperature in the compact during SHS process was measured as a function of time and used for determining combustion temperature and combustion wave velocity. Microstructure of produced porous TiNi SMA body was observed and the results were discussed with the combustion characteristics. From the results it was concluded that the final average pore size could be controlled either by the combustion wave velocity or by the average temperature of the preform compact prior to ignition.