Four different coatings deposited using cold spray process were studied with two different powder agglomerating techniques (spray d교 and evaporated powder) and using $TiO_2$ nano-sized powders with and without a 10wt% addition of ZnO. Characterization was performed by SEM, XRD and roughness test. Also the photocatalytic effect of the coatings was evaluated. Although the change of powder preparation techniques and the addition of ZnO into $TiO_2$ did not show appreciable variations in the surface morphology and Anatase phase transformation, it did show influence on the surface roughness of the coating, the highest roughness being found in the coatings made by spray powder prepared method. Regarding the photocatalytic effect it was observed that the using the spray dry coating and the addition of ZnO are promoter of purification at higher rates.

• 한국분말재료학회지
• /
• 제8권3호
• /
• pp.210-213
• /
• 2001

$Si_3N_4$/TiN nano/nano-type composites were successfully fabricated by the combination of a mechano-chemical grinding (MCG) method and a short time sintering process, and their wear resistance was evaluated. Powder mixtures of $\alpha-Si_3N_4$and Ti were prepared using mechano-chemical grinding process and the resulting nanocomposite powder mixtures were consolidated using pulsed electric current sintering (PECS). TEM observation showed that the nano/nano-type composites consisted of homogeneous and very fine matrix grains with the size less than 100 nm. The obtained $Si_3N_4$-based nano/nano-type showed high wear resistance and electric discharge machinability.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.440-441
• /
• 2006

Several titanate powders ($Al_2TiO_5,\;SrTiO_3$, etc.) were synthesized by an ethylene glycol solution route. Titanium isopropoxide and nitrate salts were dissolved in stoichiometric proportions in liquid-type ethylene glycol without any precipitation. The parent precursor sols were dried to porous gels, and then the gels were calcined and crystallized. All synthesized titanate powders had stable crystallization behavior at low temperature and high specific surface area after a simple ball-milling process. A three-component PZT $(Pb(Zr_{0.52}{\cdot}Ti_{0.48})O_3)$ powder was also synthesized successfully by the ethylene glycol method. In this study, the characteristics of the multi-component titanate powders by the ethylene glycol method are examined.

• 한국분말재료학회지
• /
• 제22권3호
• /
• pp.163-168
• /
• 2015

Ti alloys are extensively used in high-technology application because of their strength, oxidation resistance at high temperature. However, Ti alloys tend to be classified very difficult to cut material. In this paper, The powder synthesis, spark plasma sintering (SPS), bulk material properties such as electrical conductivity and thermal conductivity are systematically examined on $Ti_2AlN$ and $Ti_2AlC$ materials having most light-weight and oxidation resistance among the MAX phases. The bulk samples mainly consisted of $Ti_2AlN$ and $Ti_2AlC$ materials with density close to theoretical value were synthesized by a SPS method. Machining characteristics such as machining time, surface quality are analyzed with measurement of voltage and current waveform according to machining condition of micro-electrical discharge machining with micro-channel shape.

• Ecology and Resilient Infrastructure
• /
• 제3권4호
• /
• pp.215-220
• /
• 2016

A new immobilization technique of nanoscale $TiO_2$ powder to expanded polystyrene (EPS) balls with temperature-controlled melting method was developed, and the photocatalytic activity of $TiO_2$ powder-embedded EPS balls were evaluated using methylene blue (MB) solution under ultraviolet irradiation (${\lambda}=254nm$). Based on the scanning electron microscope (SEM) images and associated energy-dispersive X-ray spectroscopy (EDX) analysis, the components of the intact EPS balls were mainly carbon and oxygen, whereas those of $TiO_2$-immobilized EPS balls were carbon, oxygen, and titanium, indicating that relatively homogenous patches of $TiO_2$ and glycerin film were coated on the surface of EPS balls. Based on the comparison of degradation efficiencies of MB between intact and $TiO_2$-immobilized EPS balls under UVC illumination, the degradation efficiencies of MB can be significantly improved using $TiO_2$-immobilized EPS balls, and surface reactions in heterogeneous photocatalysis were more dominant than photo-induced radical reactions in aqueous solutions. Thus, $TiO_2$-immobilized EPS balls were found to be an effective photocatalyst for photodegradation of organic compounds in aqueous solutions without further processes (i.e., separation, recycling, and regeneration of $TiO_2$ powder). Further study is in progress to evaluate the feasibility for usage of buoyant $TiO_2$-immobilized EPS to inhibit the excessive growth of algae in rivers and lakes.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.399-404
• /
• 1996

Hydrothemal synthesis of PbTiO3 has been investigated. A comprehensive thermodynamic model for heteroge-nous reacting solid-aquous system has been used to predict the optimum condition for the synthesis. Synthesis were performed using lead acetate trihydrate as Pb source crystalline TiO2 as Ti source and KOH as minerali-zer. The synthesis has been examined at low temperature (16$0^{\circ}C$) Phase pure perovskite PbTiO3 has been obtained at high pH(above 0.5 mol KOH). The morphology of PbTiO3 was acicular shape. It has been found sible for a distortion in the c direction. The water is gradully released on annealing the powder to 40$0^{\circ}C$ and the normal crystallographic properties are restored.

• 한국분말재료학회지
• /
• 제10권2호
• /
• pp.123-128
• /
• 2003

$TiO_2$ nanopowder was synthesized by chemical vapor condensation (CVC) process and its photocatalytic property depending on microstructure was considered in terns of decomposition rate of organic compound. In order to control microstructure of $TiO_2$ nanopowder such as particle size and degree of agglomeration, precursor flow rate representing number concentration was changed as a process variable. In TEM observation, spherical $TiO_2$ nanoparticles with average size of 20 nm showed gradual increases in particle size and degree of agglomeration with increase of precursor flow rate. Also decomposition rate of organic compound increased with decreasing precursor flow rate. Thus, it was concluded that photocatalytic property was enhanced by targe surface area of disperse $TiO_2$ nanoparticles synthesized at lower precursor flow rate condition in CVC process.

• 한국세라믹학회지
• /
• 제23권1호
• /
• pp.27-32
• /
• 1986

This study is aimed at synthsizing high dielectric material (Ba, Sr)$TiO_3$ through direct wet process. Pure and ultra fine particle of (Ba, Sr)$TiO_3$ Powder was synthesized from $BaCl_2$ $SrCl_2$ and TiCl4 aqeous solution at KOH Solution in the $N_2$ gas atmosphere. $BaCl_2$ $SrCl_2$ and TiCl4 were Mixed with the mole ratio of 1:9, 3:7:10, 5:5:10, 7:3:10, 9:1:10 and sythesized at 4$0^{\circ}C$~9$0^{\circ}C$ for 10min~15hrs. The particle size particle shape crystallinity and synthesis condition of (Ba, Sr)$TiO_3$ powder with the variation of temperature and reaction time in the aqueous solution studied by the exprimental instruments of DTA. TGA, X-ray diffratometer SEM.

• 한국세라믹학회지
• /
• 제25권6호
• /
• pp.671-676
• /
• 1988

Preparation of high purity ultrafine Ba2Ti9O20 powder was investigated by coprecipitation method. Formation of Ba2Ti9O20 powder from precipitate of coprecipitation takes place at 120$0^{\circ}C$, which is 20$0^{\circ}C$ lower than that from mechanical mixtures of BaCO3 and TiO2. This is apparently due to the nature of the compounds formed by the reaction of mixtures of aqueous solutions of BaCl2 and TiCl4 with an ammoniacal solution of ammonium carbonate and ammouium hydroxide. In this method, the Ba2Ti9O20 powders show low callcining and sintering temperature and it has good sintering and dielectric constant at room temperature.

• 한국세라믹학회지
• /
• 제33권7호
• /
• pp.743-754
• /
• 1996

In this study (Ba1-xPbx)TiO3 was synthesized by modified oxalate process in order to prevent vaporization of PbO through low temperature synthesis climinate Cl ion reproducibly substitute Pb for by and uniformly distribute ion (Ba1-xPbx)TiO3 was synthesized by coprecipitation of lead acetate barium acetate and ammonium titanyl oxalate have been used as starting materials. The substitution of Pb for Ba was reproducibly possible synthetic temperature of perovskite structure becomes lowed as the Pb concentration increases and fine partic-les (specific surface are :7.2 cm2/g) were obtained, BaTiO3 powders calcined at 90$0^{\circ}C$ for 3 hours were cubic from in XRD analysis and as Pb content was increases evident split of tetragonal peaks could be observed The optimum conditions to synthesize (Ba,Pb)TiO3 powder are the followings ; synthesis temperature (5$^{\circ}C$)