• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2015년도 제49회 하계 정기학술대회 초록집
• /
• pp.187-187
• /
• 2015

The past thirty years have seen increasingly rapid advances in the field of Indium Tin Oxide (ITO) transparent thin film.[1] However, a major problem with this ITO thin film application is high cost compared with other transparent thin film materials.[2] So far, in order to overcome this disadvantage, we show a transparent ITO/Ag/i-ZnO multilayer thin film electrode can be the solution. In comparison with using amount of ITO as a transparent conducting material, intrinsic-Zinc-Oxide (i-ZnO) based on ITO/Ag/i-ZnO multilayer thin film showed cost-effective and it has not only highly transparent but also conductive properties. The aim of this research has therefore been to try and establish how ITO/Ag/i-ZnO multilayer thin film would be more effective than ITO thin film. Herein, we report ITO/Ag/i-ZnO multilayer thin film properties by using optical spectroscopic method and measuring sheet resistance. At a certain total thickness of thin film, sheet resistance of ITO/Ag/i-ZnO multilayer was drastically decreased than ITO layer approximately $40{\Omega}/{\square}$ at same visible light transmittance.(minimal point $5.2{\Omega}/{\square}$). Tendency, which shows lowly sheet resistive in a certain transmittance, has been observed, hence, it should be suitable for transparent electrode device.

• 반도체디스플레이기술학회지
• /
• 제14권3호
• /
• pp.33-36
• /
• 2015

It has increased several decades in the field of Indium Tin Oxide (ITO) transparent thin film, However, a major problem with this ITO thin film application is high cost compared with other transparent thin film materials[1]. So far, in order to overcome this disadvantage, we show that a transparent ITO/Ag/i-ZnO multilayer thin film electrode would be more cost-effective and it has not only highly transparent but also conductive properties. The aim of this research has therefore been to try and establish how ITO/Ag/i-ZnO multilayer thin film would be more effective than ITO thin film. Herein, we report the properties of ITO/Ag/i-ZnO multilayer thin film by using optical spectroscopic method and measuring sheet resistance. At a certain total thickness of thin film, sheet resistance of ITO/Ag/i-ZnO multilayer was drastically decreased than ITO layer approximately $40{\Omega}/{\Box}$ at same visible light transmittance. (minimal point $5.2{\Omega}/{\Box}$). Tendency, which shows lowly sheet resistive in a certain transmittance, has been observed, hence, it should be suitable for transparent electrode device.

• 한국산업정보학회논문지
• /
• 제6권1호
• /
• pp.70-76
• /
• 2001

NdFeB로 만들어진 permanent magnet dc driver는 많은 분야에서 사용된다. 그중 소형 disk type servo driver는 컴퓨터의 hard disk driver나 floppy driver등과 같은 소형기기의 구동용으로 사용된다. 기존의 dc drive는 coil를 감아 winding으로 사용한다. 만들어진 driver에는 coper printed multilayer winding을 사용하였다. 이 논문에서는 thin film multilayer winding의 제조방법, 특성에 관하여 논한다. 또한 dc driver의 commutation를 위해 사용되는 hallsensor 대신에 비 선형 특성의 MR sensor를 선형화시켜 driver의 commutation에 사용하였으며 이렇게 만들어진 소형 driver의 rpm, torque등의 특성을 연구하였다.

• 한국세라믹학회지
• /
• 제40권3호
• /
• pp.225-228
• /
• 2003

A Bender typed Multilayer Actuator(BMA) for decreasing the depolarization effect was designed and fabricated. Unlike bimorph and multimorph actuators in which depolarization occurred, the BMA did not generate depolarization because the polarization and the electric field directions are the same. The simulated results indicate that higher displacement of the BMA can be achieved by increasing input voltage. Compared with the multimorph actuator, the proposed actuator is expected to extend a life time as well as acceptable voltage range.

• 한국전기전자재료학회논문지
• /
• 제26권5호
• /
• pp.347-350
• /
• 2013

By inserting a very thin metal layer of Ag between two outer oxide layers of amorphous silicon indium zinc oxide (SIZO), we fabricated a highly transparent SIZO/Ag/SIZO multilayer on a glass substrate. In order to find the optimized thickness of Ag layers, we investigated the variation of optical properties depending on Ag thickness. It was found that the transition of Ag layer from island formation to a continuous film occurred at a critical thickness. Continuity of the Ag film is very important for optical properties in SIZO/Ag/SIZO multilayer. With about 15 nm thick Ag layer, the multilayer showed a high optical transmittance of 80% at 550 nm and low emissivity in IR.

• 한국재료학회지
• /
• 제16권8호
• /
• pp.490-496
• /
• 2006

ITO monolayer and ITO/Ag/ITO multilayer thin films are prepared by D.C. magnetron sputtering method. Ag layer was inserted for applying ITO to a flexible substrate at low temperature. Carrier concentration and carrier mobility of ITO and ITO/Ag/ITO thin films were measured, the transmittance of them also was done. The amorphous phase was confirmed to be combined in addition to (400) and (440) peaks from XRD result of ITO thin film. As the substrate temperature increased, the preferred orientation of (400) appeared. From the result of application of Ag layer at room temperature, the growth of columnar structure was inhibited, and the amorphous phase formed mostly. The ITO/Ag/ITO thin film represented the transmittance of above 80% when the thickness of Ag layer was 50 ${\AA}$, and the concentration of carrier increased up to above 10 times than that of ITO thin film. Finally, since very low resistance of 3.9${\Omega}/{\square}$ was observed, the effective application of low temperature process is expected to be possible for ITO thin film.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.385-386
• /
• 2007

We prepared the Al doped ZnO coating Ag multilayer thin films on glass without substrate heating using FTS system. The structure of multilayer thin films has Al doped ZnO/Ag/Al doped ZnO(AZO/Ag/AZO). The thickness of top and bottom AZO thin films were fixed to 50 nm, respectively and controlled the thickness of Ag thin films with deposition time. As-doped multilayer thin films were prepared at 1mTorr and input power (DC) of 100W at room temperature. To investigate the film properties, we employed four-point probe, UVNIS spectrometer, X-ray diffractometer (XRD), scanning electron microscopy (SEM), Hall Effect measurement system and Atomic Force Microscope (AFM).

• 반도체디스플레이기술학회지
• /
• 제13권2호
• /
• pp.13-16
• /
• 2014

We prepared the ITO/Ag multilayer thin films on soda-lime glass substrate by the Facing Target Sputtering System (FTS) at room temperature. To confirm the effect of Ag layer in ITO/Ag multilayer thin films, we have prepared various range of Ag layer in its thickness and investigated prior to the setting of ITO/Ag multilayer thin films. The thickness of Ag layer was controlled by the sputtering deposition time. Properties of as-prepared samples were investigated by using a four-point probe, UV-Visual spectrometer with a spectral visual range (400 - 800 nm) and X-ray diffractometer (XRD). As a result, the transmittance of as-prepared samples turned out to be very low in the visible range due to light-scattering on the surface of thin film as the thickness of Ag layer got increased. However, reduction of phenomenon of light-reflection in visual range was observed around 20nm of Ag thickness. We prepared the ITO/Ag multilayer thin film with a resistivity of about $8{\times}10^{-5}[{\Omega}-cm]$ and a transmittance of more than 80 % at 550 nm.

• 산업기술연구
• /
• 제25권A호
• /
• pp.157-162
• /
• 2005

In this study, the fabrication of PZT films was performed from a multilayer structure comprising $TiO_2$, $ZrO_2$ and PbO thin films prepared by rapid themal chemical vapor deposition(RTMOCVD). $TiO_2$, $ZrO_2$ and PbO are the component layers of oxide multilayer system for a single phase PZT thin film. The composition control of PZT thin film was done by the thickness control of individual component layer. The composition ratio of Pb:Ti:Zr with thickness were 1:0.94:0.55. Occurrence of a single-phase of PZT was initiated at around $550^{\circ}C$ and almost completed at $750^{\circ}C$ under the fixed time of 1hr. As the concentration of Pb increased, the roughness and crystallization in the film increased. From the as result of using XPS and TEM, the single phase formation through annealing is evident. The electrical properites of the prepared PZT thin film(Zr/Ti=40/60, 300 nm) on a Pt-coated substrate were as follow: dielectric constant ${\varepsilon}_r=475$, coercive field Ec=320 kV/cm, and remanant polarization $P_r=11{\mu}C/cm^2$ at an applied voltage of 18 V.

• 정보저장시스템학회:학술대회논문집
• /
• 정보저장시스템학회 2005년도 추계학술대회 논문집
• /
• pp.254-259
• /
• 2005

In this study, measurement of thermal conductivity of multilayer thin dielectric film has been conducted via differential 3$\omega$ method. Also, verification of differential 3$\omega$ method has been accomplished with various proposed criteria. The target film for measurement is 300 nm silicon dioxide and this thin film is covered with various thicknesses of upper protective layer. The upper protective layer is inserted between the target film and the heater line for purpose of electrical insulator or anti-oxidation barrier since the target film may be a good electrical conductor or a well-oxidizing material. However, the verification of differential 3$\omega$ method has not been conducted. Thus we have shown that the measurement of thermal conductivity of thin films with upper protective layer via differential 3$\omega$ method is verified to be reliable as long as the proposed preconditions are satisfied. Experimental results show that the experimental errors tend to increase with aspect ratio between upper protective layer thickness and width of the heater line due to heat spreading effect.