Abstract
In this study, the fabrication of PZT films was performed from a multilayer structure comprising $TiO_2$, $ZrO_2$ and PbO thin films prepared by rapid themal chemical vapor deposition(RTMOCVD). $TiO_2$, $ZrO_2$ and PbO are the component layers of oxide multilayer system for a single phase PZT thin film. The composition control of PZT thin film was done by the thickness control of individual component layer. The composition ratio of Pb:Ti:Zr with thickness were 1:0.94:0.55. Occurrence of a single-phase of PZT was initiated at around $550^{\circ}C$ and almost completed at $750^{\circ}C$ under the fixed time of 1hr. As the concentration of Pb increased, the roughness and crystallization in the film increased. From the as result of using XPS and TEM, the single phase formation through annealing is evident. The electrical properites of the prepared PZT thin film(Zr/Ti=40/60, 300 nm) on a Pt-coated substrate were as follow: dielectric constant ${\varepsilon}_r=475$, coercive field Ec=320 kV/cm, and remanant polarization $P_r=11{\mu}C/cm^2$ at an applied voltage of 18 V.