• Membrane Journal
• /
• v.20 no.4
• /
• pp.312-319
• /
• 2010

Carbon membrane materials have received considerable attention for the gas separation including hydrocarbon mixture of ingredients of the volatile organic compounds(VOCs) because they possess their higher selectivity, permeability, and thermal stability than the polymeric membranes. The use of activated carbon membranes makes it possible to separate continuously the VOCs mixture by the selective adsorption-diffusion mechanism which the condensable components are preferentially adsorbed in to the micropores of the membrane. The activated carbon hollow fiber membranes with uniform adsorptive micropores on the wall of open pores and the surface of the membranes have been fabricated by the carbonization of a thin film of phenolic resin deposited on porous alumina hollow fiber membrane. Oxidation, carbonization, and activation processing variables were controlled under different conditions in order to improve the separation characteristics of the activated carbon membrane. Properties of activated carbon hollow fiber membranes and the characterization of a gas permeation by pyrolysis conditions were studied. As the result, the activated carbon hollow fiber membranes with good separation capabilities by the molecular size mechanism as well as selective adsorption on the pores surface followed by surface diffusion effective in the recovery hydrocarbons have been obtained. Therefore, these activated carbon membranes prepared in this study are shown as promising candidate membrane for separation of VOCs.

• Membrane Journal
• /
• v.24 no.6
• /
• pp.453-462
• /
• 2014

Thin film composite (TFC) polyamide (PA) membranes were prepared on polyester (PET) nonwoven reinforced polysulfone supports for forward osmosis (FO) processes. PSF (polysulfone) supports were prepared via the phase inversion process from PSF casting solutions in dimethyl formamide (DMF) solvents (19 wt%) by using a PET nonwoven (thickness of $100{\mu}m$) as a mechanical reinforcing material for reverse osmosis (RO) membrane. The PSF support from 19 wt% of DMF/PSF casting solution showed sponge-like morphology and asymmetric internal structure. To reduce the internal concentration polarization in FO operation, thin ($20{\mu}m$ of thickness) nonwoven-supported PSF supports were prepared by using PSF/DMF casting solution (9~19 wt%). A desirable support structure with a highly porous sponge-like morphology were achieved from the thin nonwoven-supported PSF layer prepared with 9~12 wt% casting solution. A crosslinked aromatic polyamide layer was fabricated on top of each support to form a TFC PA membrane. The tested sample from 12 wt% of DMF/PSF casting solution presented outstanding FO performance, almost 5.5 times higher water flux (24.3 LMH) with low reverse salt flux (RDF, 1.5 GMH) compared to a thick nonwoven rainforced membrane (4.5 LMH of flux and 3.47 GMH of RSF). By reducing the thickness of the nonwoven and optimizing PSF concentration of casting solution, the morphology of the prepared membranes were changed from a dense structure to a porous sponge structure in the boundary area between nonwoven and PET support layer.

• Journal of Adhesion and Interface
• /
• v.20 no.3
• /
• pp.110-115
• /
• 2019

Graphene oxide has been gathering interests as a way to exfoliate graphene. Since the oxidation group of graphene oxide can hydrogen bond with various functional groups, tremendous efforts have been actively conducted to apply various applications. However, graphene oxide alone cannot substantially possess the mechanical properties required for the practical application. Therefore, in this study, polydopamine, which is a bio-mimetic mussel protein-inspired material, was combined with graphene oxide to form a large-area composite membrane at the liquid-gas interface. In addition, the morphology of the polydopamine-graphene oxide composite thin film was also controlled to obtain a composite membrane having a nano-wrinkle structure. It can be expected to be used in the next generation seawater desalination membranes or carbon composites because it can form mechanically superior and sophisticated nanostructures.

• Membrane and Water Treatment
• /
• v.2 no.3
• /
• pp.137-145
• /
• 2011

Membrane processes are major breakthrough for the removal of organic pollutants in water remediation. The separations of solutes depend on nature of the membranes and solutes. The separation performance depends on the nature of the solutes (i.e., molecular volume, polarity, and hydrophobicity) for the same membrane. As 4-chlorophenol is of more dipolemoment compared to 2-chlorophenol, the orientation of the molecule enables it pass through the pores of the membrane, which is of negatively charged and thus separation order follows: 2-chlorophenol > 4-chlorophenol. Hydrophobicity factor also supports the order. Addition of sodium dodecyl sulfate (SDS) to chlorophenol solution shows remarkable increase in separation performance of the membrane. The improvement in separation is 1.8 and 1.5 times for 4- and 2- chlorophenol consecutively in case of 0.0082 M SDS (1cmc = 0.0082 M) in the solution. 4-chlorophenol has better attachment tendency with SDS because of its relatively more hydrophobic nature and thus reflects in performance i.e. the separation performance of 4-chlorophenol with SDS through the membrane is better compared to 2-chlorophenol.

• Membrane Journal
• /
• v.14 no.3
• /
• pp.207-217
• /
• 2004

In this study, we prepared nanofiltration membrane by applying the interfacial polymerization method as a way of manufacturing composite membranes. We have examined the effects of various preparation factors such as monomer concentration and composition, thermal curing condition, post treatment condition. In addition to preparation conditions, we also monitored the effects of operation conditions such as feed solution concentration and operation pressure on the permeation properties of the resulting nanofiltration membrane. We intended to increase the permeation rate of nanofiltration membrane by the enlargement of effective surface area using additives during interfacial polymerization step. With increasing the monomer concentration, membrane permeation rate are decreased with maintaining almost constant rejection. With respect to curing condition, with increasing the curing temperature both permeation rate and rejection are decreased. With increasing the ratio of MPD in amino monomer composition, permeation rate decreased drastically with high rejection. With increasing the feed solution concentration, both permeation rate and rejection decreased. Both permeation rates and rejection increased with increasing the operating pressure. Nanofiltration membrane have higher surface roughness with increasing additive concentration in the case of using MPD contained amine composition than using piperazine alone. Permeation rates are much lower than the nanofiltration membrane prepared by piperazine.

• Polymer(Korea)
• /
• v.36 no.6
• /
• pp.810-815
• /
• 2012

The cation exchange polymer, poly(styrene sulfonic acid) (PSSA), was coated onto polyamide (PA) thin film composite reverse osmosis (RO) membranes. Then these membranes were investigated for the model foulants, bovine serum albumin (BSA), humic acid (HA), and sodium alginate (SA) to check whether there are some improvement. The contact angle of PSSA coated PA RO membrane showed $58^{\circ}$ from $78^{\circ}$, the value of PA RO membrane, which confirmed successful hydrophilization. As the operating pressure increased (2, 4, 8 atm for BSA, HA and SA 100 ppm in feed solution), the fouling phenomena was worse for both none- and PSSA-coated membranes. The fouling increased in the order of BSA>SA>HA due to the interactions between sulfonic acid in PSSA and functional groups of foulants. On the other hand more significant fouling reduction was observed in the order of HA>SA>BSA. The photographs of scanning electron microscopy showed the same trend. As a result, there was the improvement of fouling phenomena for the PSSA coated RO membranes, distinctly in the case of HA.

• Membrane Journal
• /
• v.22 no.4
• /
• pp.272-279
• /
• 2012

The neutral polymer, poly (vinyl alcohol) (PVA), was coated onto polyamide (PA) thin film composite reverse osmosis (RO) membranes. And then these membranes were investigated for the model foulants, bovine serum albumin (BSA), humic acid (HA), and sodium alginate (SA) whether there are aome improvement. As the operating pressure increased with 2, 4, 8 atm for BSA, HA and SA 100 ppm in feed solution, the fouling phenomena was worse for both none and PSSA coated membranes. The fouling occurred in the sequence of BSA > HA > SA due to the interactions between PVA snd functional groups of foulants, and on the other hand the fouling reduction was observed in the order of HA > BSA > SA. The observation of scanning electron microscopy photographs showed the same trend. As a result, there should be the improvement of fouling phenomena for the PVA coated RO membranes and the case of HA was shown distinct.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.6
• /
• pp.248-256
• /
• 2012

A Pd-based hydrogen membranes for hydrogen purification and separation need high hydrogen perm-selectivity. The surface roughness of the support is important to coat the pinholes free and thin-film membrane over it. Also, The pinholes drastically decreased the hydrogen perm-selectivity of the Pd-based composite membrane. In order to remove the pinholes, we introduced various surface pre-treatment such as alumina powder packing, nickel electro-plating and micro-polishing pre-treatment. Especially, the micro-polishing pretreatment was very effective in roughness leveling off the surface of the porous nickel support, and it almost completely plugged the pores. Fine Ni particles filled surface pinholes with could form open structure at the interface of Pd alloy coating and Ni support by their diffusion to the membrane and resintering. In this study, a $4{\mu}m$ surface pore-free Pd-Cu-Ni ternary alloy membrane on a porous nickel substrate was successfully prepared by micro-polishing, high temperature sputtering and Cu-reflow process. And $H_2$ permeation and $N_2$ leak tests showed that the Pd-Cu-Ni ternary alloy hydrogen membrane achieved both high permeability of $13.2ml{\cdot}cm^{-2}{\cdot}min^{-1}{\cdot}atm^{-1}$ permation flux and infinite selectivity.

• Membrane Journal
• /
• v.27 no.6
• /
• pp.506-510
• /
• 2017

The interfacial polymerization method has been applied to various fields as a reaction in which reactive monomers dissolved in two immiscible solutions cause polymerization at the interface. In the case of water treatment membranes, m-phenylene diamine and trimesoyl chloride are used as reactants. The performance of the membrane is affected by various polymerization factors. In this study, we investigated how the spreading rate of the organic solution influences the surface and structure of the membrane. Spreading rate of organic solutions was adjusted to 7.6 and 25 mm/sec. The solution volume of the organic phase was adjusted to 1~3 drops. The observed results showed that cracks were not found in the polyamide membrane when dropping at a drop of 7.6 mm/sec and dropping two drops at 25 mm/sec. On the other hand, cracks occurred in all cases. Therefore, the spreading rate of the initial organic solvent is expected to greatly affect the performance of the polyamide membrane.

• Membrane Journal
• /
• v.33 no.6
• /
• pp.427-438
• /
• 2023

In this study, in order to improve the performance of the reverse osmosis membrane with high water flux and high salt rejection, a study was conducted on the evaluation of characteristics according to the curing temperature and time during various additives and interfacial polymerization. The morphology of the membrane with no additives and the membrane with additives both showed a "rigid-and-valley" structure, confirming that the polyamide layer was successfully polymerized on the surface of the porous support layer. In addition, the additive of 2-Ethyl-1,3-hexanediol (EHD) had improved hydrophilicity and water flux, which was confirmed by measuring the contact angle. Finally, a highly permeable TFC membrane with NaCl and MgSO₄ salt rejection of 97.78% and 98.7% and a high water flux of 3.31 L/(m²⋅h⋅bar) was prepared.