• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.8
• /
• pp.474-478
• /
• 2017

We report on thin-film transistors based on $TiO_x$ pre-annealed by femtosecond laser pulses. A 30-nm thick $TiO_x$ active channel layer was initially deposited by an ALD system. The $TiO_x$ semiconducting films were annealed by irradiation with a femtosecond laser (power: $3W/cm^2$) for 5, 25, and 50s. Atomic force microscopy images revealed that the surface of a $TiO_x$ film without femtosecond laser pre-annealing was relatively rough, while after annealing with femtosecond laser pulses, the surface of the $TiO_x$ films became smooth. With increasing radiation time, the surrounding gas atmosphere could have a larger impact on the $TiO_x$ surface; meanwhile, the thin-film roughness decreased. Thin-film transistors with $TiO_x$ active channels pre-annealed at 50s exhibited good transfer characteristics and an on-to-off current ratio of ${\sim}10^3$.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.102-108
• /
• 2008

In this paper, the LiF and polymer thin film as passivation layer have been evaporated on green OLED devices. HDPE, polyacenaphthylene, polytetrafluoroethylene, poly(2,6-dimethyl-1,4-pheneylene oxide), poly sulfone and poly(dimer-acid-co-alkyl poly-amine) have been used as polymer materials. The optical transmittance of evaporated polymer thin film was very good as an above 90% in visible range. The morphology of polymer thin film was measured by AFM. As a result of the measurement average roughness($R_a$) value of the polysulfone was very low as 2.2 nm. The green OLED devices with a structure of ITO/HIL/HTL/EML/Buffer/Al in series of various passivation films were fabricated and analyzed. It was observed that an OLED device with LiF as first passivation film has shown the good electrical and optical property, and all kind of polymer films did not influence on the I-V-L characteristics and the life time of OLED devices. Therefore, we found that polymer layer played a key role as a buffer layer between the inorganic passivation layers to relieve the stress of the inorganic layers.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.2
• /
• pp.98-102
• /
• 2019

Direct plasma-enhanced atomic layer deposition (PEALD) are widely used for $SiO_2$ and SiON thin film process in current semiconductor industry. However, this exhibits poor step coverage for three-dimensional device structure due directionality of plasma species as well as plasma damage on the substrate. In this study, to overcome this issue, low temperature (< $300^{\circ}C$) $SiO_2$ and SiON thin film processes were studied using inductively coupled plasma (ICP) type remote PEALD with various reactant gases such as $O_2$, $H_2O$, $N_2$ and $NH_3$. It was confirmed that the interfacial properties such as fixed charge density and charge trapping behavior of thin films were considerably improved by hydrogen species in $H_2O$ and $NH_3$ plasma compared to the films grown with $O_2$ and $N_2$ plasma. Furthermore, the leakage current density of the thin films was suppressed for same reason.

• Current Photovoltaic Research
• /
• v.11 no.4
• /
• pp.103-107
• /
• 2023

A Nickel oxide (NiO_x) thin films were prepared via sol-gel process on a transparent conductive oxide glass substrate. The NiO_x thin films were spin-coated in ambient air and subsequently annealed for 30 minutes at temperatures ranging from 150℃ to 450℃. The structural and optical characteristics of the NiO_x thin films annealed at various temperatures were measured using X-ray diffraction, field emission scanning electron microscopy, and ultraviolet-visible spectroscopy. After optimizing the NiO_x coating conditions, perovskite solar cells were fabricated with p-i-n inverted structure, and its photovoltaic performance was evaluated. NiO_x thin films annealed at 350℃ exhibited the most favorable characteristics as a hole transport layer, resulting in the highest power conversion efficiency of 17.88 % when fabricating inverted perovskite solar cells using this film.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.93-93
• /
• 2013

In recent years, multifunctional ternary nitride thin films have received extenstive attention due to its versatility in many applications. In particular, noble metal based ternary nitride thin films showed a promising properties in the application of Multifunctional heating resistor films because its good electrical properties and excellent resistance against oxidation and corrosion. In this study, we prepared multifunctional noble metal based ternary nitride thin films by atomic layer deposition (ALD) and plasma-enhanced ALD (PEALD) method. ALD and PEALD techniques were used due to their inherent merits such as a precise composition control and large area uniformity, which is very attractive for preparing multicomponent thin films on large area substrate. Here, we will demonstrate the design concept of multifunctional noble metal based ternary thin films. And, the relationship between microstructural evolution and electrical resistivity in noble metal based ternary thin films will be systemically presented. The useful properties of noble metal based ternary thin films including anti-corrosion and anti-oxidation will be discussed in terms of hybrid functionality.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.455-458
• /
• 2001

The thin films of high pemitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)$TiO_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/$SiO_2/Si$ substrate at 4,000 [rpm] for 10 seconds. The devices of BST thin films to composite $(Ba_{0.7},Sr_{0.3})TiO_3$ were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_2/Si$ substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$, $3800[\AA]$. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency l[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.91-91
• /
• 2012

We aim in synthesizing various functional thin films thinner than ~ 10 nm for environmental applications and photovoltaic devices. Atomic layer deposition is used for synthesizing inorganic thin films with a precise control of the film thickness. Several examples about application of our thin films for removing volatile organic compounds (VOC) will be highlighted, which are summarized in the below. 1) $TiO_2$ thin films prepared by ALD at low temperature ($<100^{\circ}C$) show high adsorption capacity for toluene. In combination with nanostructured templates, $TiO_2$ thin films can be used as building-block of high-performing VOC filter. 2) $TiO_2$ thin films on carbon fibers and nanodiamonds annealed at high temperatures are active for photocatalytic oxidation of VOCs, i.e. photocatalytic filter can be created by atomic layer deposition. 3) NiO can catalyze oxidation of toluene to $CO_2$ and $H_2O$ at $<300^{\circ}C$. $TiO_2$ thin films on NiO can reduce poisoning of NiO surfaces by reaction intermediates below $200^{\circ}C$. We also fabricated inverted organic solar cell based on ZnO electron collecting layers on ITO. $TiO_2$ thin films with a mean diameter less than 3 nm on ZnO can enhance photovoltaic performance by reducing electron-hole recombination on ZnO surfaces.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.455-458
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/SiO$_2$/Si substrate at 4,700 [rpm] for 10 seconds. The devices of BST thin films to composite (Ba$\_$0.7/Sr$\_$0.3/)TiO$_3$ were fabricated by changing of the depositing layer number on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was 2500[${\AA}$], 3500[${\AA}$], 3800[${\AA}$]. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency 1[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Korean Journal of Materials Research
• /
• v.24 no.9
• /
• pp.443-450
• /
• 2014

Amorphous (a-Si) films were epitaxially crystallized on a very thin large-grained poly-Si seed layer by a silicide-enhanced rapid thermal annealing (SERTA) process. The poly-Si seed layer contained a small amount of nickel silicide which can enhance crystallization of the upper layer of the a-Si film at lower temperature. A 5-nm thick poly-Si seed layer was then prepared by the crystallization of an a-Si film using the vapor-induced crystallization process in a $NiCl_2$ environment. After removing surface oxide on the seed layer, a 45-nm thick a-Si film was deposited on the poly-Si seed layer by hot-wire chemical vapor deposition at $200^{\circ}C$. The epitaxial crystallization of the top a-Si layer was performed by the rapid thermal annealing (RTA) process at $730^{\circ}C$ for 5 min in Ar as an ambient atmosphere. Considering the needle-like grains as well as the crystallization temperature of the top layer as produced by the SERTA process, it was thought that the top a-Si layer was epitaxially crystallized with the help of $NiSi_2$ precipitates that originated from the poly-Si seed layer. The crystallinity of the SERTA processed poly-Si thin films was better than the other crystallization process, due to the high-temperature RTA process. The Ni concentration in the poly-Si film fabricated by the SERTA process was reduced to $1{\times}10^{18}cm^{-3}$. The maximum field-effect mobility and substrate swing of the p-channel poly-Si thin-film transistors (TFTs) using the poly-Si film prepared by the SERTA process were $85cm^2/V{\cdot}s$ and 1.23 V/decade at $V_{ds}=-3V$, respectively. The off current was little increased under reverse bias from $1.0{\times}10^{-11}$ A. Our results showed that the SERTA process is a promising technology for high quality poly-Si film, which enables the fabrication of high mobility TFTs. In addition, it is expected that poly-Si TFTs with low leakage current can be fabricated with more precise experiments.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.2
• /
• pp.58-61
• /
• 2009

The electrical stability of ZnO: Al thin films deposited on glass substrate by the RF magnetron sputtering method have been modified by a hydrogen annealing treatment and $SiO_2$ protection layer. AZO thin films were deposited at room temperature and different RF powers of 50, 100, 150, and 200 W to optimize the AZO film growth condition. The lowest value of resistivity of $9.44{\times}10^{-4}{\Omega}cm$ was obtained at 2 mtorr, room temperature, and a power level of 150 W. Then, the AZO thin films were annealed at $250-400^{\circ}C$ for 1 h in hydrogen ambient. The minimum resistivity obtained was $8.32{\times}10^{-4}{\Omega}cm$ as-annealed at $300^{\circ}C$. The electrical properties were enhanced by the hydrogen annealing treatment. After a 72 h damp-heat treatment in harsh conditions of a water steam at $110^{\circ}C$ for four representative samples, a degradation of electrical properties was observed. The sample of hydrogen-annealed AZO thin films with $SiO_2$ protection layer showed a slight degradation ratio(17%) of electrical properties and a preferable transmittance of 90%. The electrical stability of AZO thin films had been modified by hydrogen annealing treatment and $SiO_2$ protection layer.