• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.257-265
• /
• 2002

A stoichiometric mixture of evaporating materials for AgInS$_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, AgInS$_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy(HWE) system. The source and substrate temperatures were 680 $^{\circ}C$ and 410 $^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of AgInS$_2$ single crystal thin films measured from Hall effect by van der Pauw method are 9.35${\times}$10$\^$16/ cm$\^$-3/ and 294 $\textrm{cm}^2$/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of the energy band gap on AgInS$_2$ single crystal thin films was found to be E$\_$g/(T) : 2.1365 eV - (9.89 ${\times}$ 10$\^$-3/ eV) T$^2$/(2930 + T). After the as-grown AgInS$_2$ single crystal thin films was annealed in Ag-, S-, and In-atmospheres, the origin of point defects of AgInS$_2$ single crystal thin films has been investigated by using the photoluminescence(PL) at 10 K. The native defects of V$\_$AG/, V$\_$S/, Ag$\_$int/, and S$\_$int/ obtained from PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the S-atmosphere converted AgInS$_2$ single crystal thin films to an optical p-type. Also, we confirmed that In in AgInS$_2$/GaAs did not form the native defects because In in AgInS$_2$ single crystal thin films did exist in the form of stable bonds.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1572-1575
• /
• 2005

Poly(vinyl phenol)(PVP)/$TiO_2$ nanocomposite the films have been prepared incorporating metal alkoxide with vinyl polymer to obtain high dielectric constant gate insulating material for a organic thin film transistor. The surface composition, the morphology, and the thermal and electrical properties of the hybrid nanocomposite films were observed by ESCA, scanning electron microscopy (SEM), atomic force microscopy(AFM), and thermogravimetric analysis (TGA). Thin hybrid films exhibit much higher dielectric constants (7.79 at 40wt% metal alkoxide).

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2000년도 제18회 학술발표회 논문개요집
• /
• pp.100-100
• /
• 2000

Aluminium oxide (Al2O3) films have been investigated for many applications such as insulating materials, hard coatings, and diffusion barriers due to their attractive electrical and mechanical properties. In recent years, application of Al2O3 films for dielectric materials in integrated circuits as gates and capacitors has attracted much attention. Various deposition techniques such as sol-gel, metalorganic decomposition (MOD), sputtering, evaporation, metalorganic chemical vapor deposition (MOCVD), and pulsed laser ablation have been used to fabricate Al2O3 thin films. Among these techniques, reactive sputtering has been widely used due to its high deposition rate and easy control of film composition. It has been also reported that the sputtered Al2O3 films exhibit superior chemical stability and mechanical strength compared to the films fabricated by other processes. In this study, Al2O3 thin films were deposited on Pt/Ti/SiO/Si2 and Si substrates by DC reactive sputtering at room temperature with variation of the Ar/O2 ratio in sputtering ambient. Crystalline phase of the reactively sputtered films was characterized using X-ray diffractometry and the surface morphology of the films was observed with Scanning election microscopy. Effects of Th Ar/O2 ratio characteristics of Al2O3 films were investigated with emphasis on the thickness dependence of the dielectric properties. Correlation between the dielectric properties and the microstructure was also studied

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.154-154
• /
• 2003

A stoichiometric mixture of evaporating materials for CuGaSe2 single crystal thin films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal CuGaSe2, it was found tetragonal structure whose lattice constant at and co were 5.615 ${\AA}$ and 11.025 ${\AA}$, respectively. To obtain the single crystal thin films, CuGaSe2 mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (MWE) system. The source and substrate temperatures were Slot and 450$^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (UXD). The carrier density and mobility of CuGaSe2 single crystal thin films measured with Hall effect by van der Pauw method are 5.0l${\times}$10$\^$17/ cm$\^$-3/ and 245 $\textrm{cm}^2$/V$.$s at 293K, respectively. The temperature dependence of the energy band gap of the CuGaSe2 obtained from the absorption spectra was well described by the Varshni's relation, Eg(T) = 1.7998 eV - (8.7489${\times}$10$\^$-4/ eV/K)T$^2$/(T + 335 K. After the as-grown CuGaSe2 single crystal thin films was annealed in Cu-, Se-, and Ca-atmospheres, the origin of point defects of CuGaSe2 single crystal thin films has been investigated by the photoluminescence(PL) at 10 K The native defects of V$\_$CU/, V$\_$Se/, Cu$\_$int/, and Se$\_$int/ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Cu-atmosphere converted CuGaSe2 single crystal thin films to an optical n-type. Also, we confirmed that Ga in CuGaSe2/GaAs did not form the native defects because Ga in CuGaSe2 single crystal thin films existed in the form of stable bonds.

• 한국전기전자재료학회논문지
• /
• 제15권11호
• /
• pp.923-932
• /
• 2002

A stoichiometric mixture of evaporating materials for CdIn$\_$2/S$\_$4/ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CdIn$\_$2/S$\_$4/ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by hot wall epitaxy(HWE) system. The source and substrate temperatures were 630 $\^{C}$ and 420 $\^{C}$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of CdIn$\_$2/S$\_$4/ single crystal thin films measured from Hall effect by van der Pauw method are 9.01$\times$10$\^$16/ cm$\^$-3/ and 219 ㎠/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of energy band gap on CdIn$\_$2/S$\_$4/ single crystal thin films was found to be Eg(T) ＝ 2.7116 eV - (7.74 $\times$ 10$\^$-4/ eV) T$\^$2//(T＋434). After the as-grown CdIn$\_$2/S$\_$4/ single crystal thin films was annealed in Cd-, S-, and In-atmospheres, the origin of point defects of CdIn$\_$2/S$\_$4/ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of V$\_$cd/, V$\_$s/, Cd$\_$int/ and S$\_$int/ obtained by PL measurements were classified as donors or accepters type. And we concluded that the heat-treatment in the S-atmosphere converted CdIn$\_$2/S$\_$4/ single crystal thin films to an optical p-type. Also, we confirmed that In in CdIn$\_$2/S$\_$4/GaAs did not from the native defects because In in CdIn$\_$2/S$\_$4/ single crystal thin films existed in the form of stable bonds.

• 센서학회지
• /
• 제8권5호
• /
• pp.421-426
• /
• 1999

본 논문에서는 반절연성 GaAs(semi-insulating GaAs) 기판위에 $Al_2O_3$ 절연막이 게이트 절연막으로 이용된 공핍형모드 p-채널 GaAs MOSFET (depletion mode p-channel GaAs MOSFET)를 제조하였다. 반절연성 GaAs 기판위에 $1\;{\mu}m$의 GaAs 버퍼층(buffer layer), $4000\;{\AA}$의 p형 GaAs 에피층(epi-layer), $500\;{\AA}$의 AlAs층, 그리고 $50\;{\AA}$의 캡층(cap layer)을 차례로 성장시키고 습식열산화시켰으며, 이를 통하여 AlAs층은 완전히 $Al_2O_3$층으로 산화되었다. 제조된 MOSFET의 I-V, $g_m$, breakdown특성 측정을 통하여 AlAs/GaAs epilayer/S I GaAs 구조의 습식열산화는 공핍형 모드 p-채널 GaAs MOSFET를 구현하기에 적합함을 알 수 있다.

• 한국태양에너지학회 논문집
• /
• 제23권2호
• /
• pp.59-70
• /
• 2003

A stoichiometric mixture of evaporating materials for $CuGaSe_2$ single crystal thin films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CuGaSe_2$, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were $5.615{\AA}$ and $11.025{\AA}$, respectively. To obtain the single crystal thin films, $CuGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $450^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuGaSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $5.01\times10^{17}cm^{-3}$ and $245cm^2/V{\cdot}s$ at 293K. respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g$(T)=1.7998 eV-($8.7489\times10^{-4}$ eV/K)$T^2$/(T+335K). After the as-grown $CuGaSe_2$ single crystal thin films was annealed in Cu-, Se-, and Ga-atmospheres, the origin of point defects of $CuGaSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{CU},\;V_{Se},\;Cu_{int}$ and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Cu-atmosphere converted $CuGaSe_2$ single crystal thin films to an optical n-type. Also, we confirmed that Ga in $CuGaSe_2$/GaAs did not form the native defects because Ga in $CuGaSe_2$ single crystal thin films existed in the form of stable bonds.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.98-99
• /
• 2008

To obtain the single crystal thin films, $AgGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $630^{\circ}C$ and $420^{\circ}C$, respectively. The temperature dependence of the energy band gap of the $AgGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g$(T) 1.9501 eV - ($8.79\times10^{-4}$ eV/K)$T^2$/(T + 250 K). After the as-grown $AgGaSe_2$ single crystal thin films was annealed in Ag-, Se-, and Ga-atmospheres, the origin of point defects of $AgGaSe_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10K. The native defects of $V_{Ag}$, $V_{Se}$, $Ag_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Ag-atmosphere converted $AgGaSe_2$ single crystal thin films to an optical p-type. Also, we confirmed that Ga in $AgGaSe_2$/GaAs did not form the native defects because Ga in $AgGaSe_2$ single crystal thin films existed in the form of stable bonds.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.97-98
• /
• 2007

A stoichiometric. mixture of evaporating materials for $CuGaSe_2$ single crystal thin films was prepared from horizontal electric furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CuGaSe_2$, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were $5.615\;{\AA}$ and $11.025\;{\AA}$, respectively. To obtain the single crystal thin films, $CuGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $450^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuGaSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $4.87{\times}10^{17}\;cm^{-3}$ and $129\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;1.7998\;eV\;-\;(8.7489\;{\times}\;10^{-4}\;eV/K)T^2/(T\;+\;335\;K)$.

• 한국결정성장학회지
• /
• 제15권1호
• /
• pp.1-9
• /
• 2005

AgGaS₂ 단결정 박막을 수평 전기로에서 합성한 AgGaS₂ 다결정을 증발원으로하여, hot wall epitaxy(HWE) 방법으로 증발원과 기판(반절연성-GaAs(100))의 온도를 각각 590℃, 440℃로 고정하여 성장하였다. 이때 단결정 박막의 결정성은 광발광 스펙트럼과 이중결정 X-선 요동곡선(DCRC)으로 부터 구하였다. AgGaS₂의 광흡수 스펙트럼으로부터 구한 온도에 의존하는 에너지 밴드갭 E/sub g/(T)는 Varshni 공식에 fitting한 결과 E/sub g/(T) = 2.7284 eV - (8.695×10/sup -4/ eV/K)T²/(T + 332 K)를 잘 만족하였다. 성장된 AgGaS₂ 단결정 박막을 Ag, Ga, S 분위기에서 각각 열처리하여 10K에서 photoluminescience(PL) spectrum을 측정하여 점 결함의 기원을 알아보았다. PL 측정으로 부터 얻어진 V/sub Ag/, V/sub s/, Ag/sub int/, 그리고 S/sub int/는 주개와 받개로 분류되어졌다. AgGaS₂ 단결정 박막을 Ag 분위기에서 열처리하면 n형으로 변환됨을 알 수 있었다. 또한, Ga 분위기에서 열처리하면 열처리 이전의 PL 스펙트럼을 보이고 있어서. AgGaS₂ 단결정 박막에서 Ga은 안정된 결합의 형태로 있기 때문에 자연 결함의 형성에는 관련이 없음을 알았다.