• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.220-221
• /
• 2007

Recently, imprint lithography have received significant attention due to an alternative technology for photolithography on high performance microelectronic devices. In this work, we investigated thermal stabilities and dynamic mechanical properties of dielectric materials for thermal imprint lithography. Curing behaviours, thermal stabilities, and dynamic mechanical properties of the dielectric materials cured with various curing agent and spherical filler were studied using dynamic differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), rheometer and universal test machine(UTM).

• 한국세라믹학회지
• /
• 제32권11호
• /
• pp.1269-1275
• /
• 1995

Effects of GeO2 addition on the thermal and structural stabilities of PbO-Bi2O3-Ga2O3 glasses were studied. Thermal stabilities, as assessed by the weighted thermal stability factors [(Tx-Tg)/Tg], increased with GeO2 concentraton from 0.097 to 0.210 with the addition of 20 mol% GeO2. Increasing GeO2 content resulted in the decrease of apparent density, molar volume, refractive index and thermal expansion. On the other hand, IR transmission cut-off (λT=50%) moved from 6.73${\mu}{\textrm}{m}$ for the ternary PbO-Bi2O3-Ga2O3 glass to shorter wavelength side, 5.98${\mu}{\textrm}{m}$ for a glass containing 20mol% GeO2. There were little change with GeO2 content, however, in the activation energies for the viscous flow of approximately 140 kcal/mole within the temperature interval of 300~50$0^{\circ}C$. Addition of GeO2 to PbO-Bi2O3-Ga2O3 glasses enhanced the thermal and structural stabilities significantly at the expense of their infrared transmittance. An appropriate compsomise between these two opposite trends should be made following the specifications of the final applications.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.265-268
• /
• 2002

In this work, the blend system of epoxy and PMR-15 polyimide is investigated in terms of the cure behaviors and thermal stabilities. The cure behaviors are studied in DSC measurements and thermal stabilities are also carried out by TGA analysis. DDM (4, 4'-diamino diphenyl methane) is used as curing agent for EP and the content of PMR-15 is varied within 0, 5, 10, 35, and 20 phr to neat EP. As a result, the cure activation energy ($E_a$) is increased at 10 phr of PMR-15, compared with that of neat EP. From the TGA results of EP/PMR-15 blend system, the thermal stabilities based in the initial decomposed temperature (IDT) and integral procedural decomposition temperature (IPDT) are increased with increasing the PMR-15 content. The fracture toughness, measured in the context of critical stress intensity factor ($K_{IC}$) and critical strain energy release rate ($G_{IC}$), shows a similar behavior with $E_a$. This result is probably due to the crosslinking developed by the interactions between intermolecules in the polymer chains.

• 폴리머
• /
• 제27권2호
• /
• pp.91-97
• /
• 2003

각기 다른 온도에서 불소화 표면처리에 의한 실리카의 표면특성을 X-선 광전 분광법 그리고 접촉각을 통해 관찰하였으며, 복합재료의 기계적 계면물성과 열안정성에 미치는 영향은 인열 에너지와 분해 활성화 에너지를 통해 고찰하였다. 실리카 표면 자유 에너지의 London 비극성 요소와 불소작용기는 불소화 처리 온도에 따라 증가하였으며, 결과적으로 실리카/폴리우레탄 복합재료의 인열 에너지를 향상시켰다. 또한 복합재료의 열안정성은 불소화 함량에 따라 증가하였다. 이러한 결과는 실리카 표면에 도입된 불소작용기가 본 실험의 복합재료 시스템 내에서 실리카와 폴리우레탄 계면 사이의 분자간 상호작용을 향상시키는 주요한 인자로 작용한 것으로 사료된다.

• 한국응용과학기술학회지
• /
• 제6권1호
• /
• pp.9-14
• /
• 1989

Effectiveness of some natural antioxidants were investigated by measuring the physico-chemical charcteristics and fatty acid composition during thermal oxidation in palm oil. Tocopherol showed most enhanced thermal oxidation stabilities compared to the other natural antioxidants. AR spice was no good AOM stability and changes of acid value but the other parameters were obtained desirable results. The changes of linoleic aicd content was slightly decreased during thermal oxidation. Addition of rosemary and glycyrriza extract increased the stabilities of oil less than tocopherol and AR spice. Order of antioxdative effects was tocopherol, AR spice and others. There was no significiant difference in stability of rosemary and glycyrriza extract.

• Composites Research
• /
• 제17권5호
• /
• pp.47-53
• /
• 2004

본 연구에서는 열잠재성 양이온 촉매인 N-benzylpyrazinium hexafluoroantimonate (BPH)와 benryl-2,5-dimethylpyrazinium hexafluoroantimonate (BDPH)를 합성하였고, 이관능성 에폭시 수지(diglycidylether of bisphenol A, DGEBA)에 개시제로 1 wt.%의 촉매를 혼합하여 DSC, NIR TGA 그리고 DMA를 이용하여 경화거동과 열안정성을 알아보았다. 촉매의 잠재특성은 $100∼180^{\circ}$의 반응 온도에 따른 전환율을 near-IR로부터 조사하였다. NIR 분석으로부터, BPH에 의한 에폭시 수지의 전환율은 BDPH와 비교하여 높은 전환율을 나타내는 것을 확인할 수 있었다. 그리고 TGA 분석 결과, 초기 열분해 온도(IDT)와 적분 열분해 온도(IPDT)에 입각하여 DGEBA/BDPH 시스템의 열안정성이 DGEBA/BPH 시스템보다 상대적으로 낮은 값을 나타냈다. 이는 BDPH 구조의 입체 장애로 인해 BPH보다 열안정성 인자이 더 낮게 측정된 것으로 판단된다.

• Elastomers and Composites
• /
• 제40권1호
• /
• pp.22-28
• /
• 2005

본 연구에서는 실리카/고무 복합재료의 기계적 계면 물성과 열안정성에 대한 산소플라즈마의 영향에 대하여 살펴보았다. 실리카의 표면특성은 XPS와 접촉각 측정을 통하여 살펴보았다. 실리카/고무 복합재료의 기계적 물성과 열안정성은 각각 인열에너지 ($G_{IIIC}$)와 열중량분석(TGA)를 통하여 관찰하였다. 실험결과, 플라즈마 처리시간이 증가함에 따라 실리카 표면에 산소가 함유된 극성 관능기의 도입량이 증가하였으며, 이에 따라 고무 복합재료의 인열에너지와 열안정성이 향상되었다. 이러한 결과는 NBR과 같은 극성고무가 산소가 함유된 관능기가 도입된 실리카와 상대적으로 높은 상호작용을 하기 때문으로 판단된다.

• 한국안전학회지
• /
• 제25권3호
• /
• pp.61-65
• /
• 2010

Most of the chemical reactions performed in the chemical industry are exothermic, meaning that thermal energy is released during the reaction. It is also important to understand the thermal hazards such as thermal stabilities and runaway reactions, which are governed by thermodynamics and reaction kinetics of the mixed materials. The paper was described the evaluation of thermal behavior caused by an exothermic batch process in manufacture of the vinyl acetate resin. The aim of the study was to evaluate the thermal stabilities of raw materials with operating conditions such as a reaction inhibitor, heating rate, reaction atmosphere and the mount of methanol charged in the vinyl acetate polymerization process. The experiments were performed in the differential scanning calorimeter(DSC), C 80 calorimeter, and thermal screening unit($TS^u$). It was suggested that we should provide the thermal characteristics for raw materials to present safe precautions with operating conditions in the vinyl acetate polymerization process.

• 한국가스학회지
• /
• 제15권2호
• /
• pp.82-87
• /
• 2011

열매체유는 화학공장의 가열시스템, 열교환 시스템, 가스플랜트 공정, 사출성형 시스템 및 펄프제지 공정 등에 사용된다. 열매체유는 고열이나 산화분해에 아주 안정하고 저항성이 있으며, 누출이나 방출의 경우 점화원을 만나면 쉽게 발화한다. 본 논문은 열메체유의 신유와 사용유에 대해 인화성과 열적 안정성을 고찰하였다. 열매체유의 인화성은 인화점과 자연발화점을 측정하여 평가하였고, 열적안정성은 열안정성시험기와 시차주사열량기를 사용하여 평가하였다. 실험결과로부터 열매체유의 적절한 사용과 취급과 관련된 안전대책 수립을 위해 화재 위험 특성을 제시하였다.

• 폴리머
• /
• 제38권4호
• /
• pp.441-448
• /
• 2014

멜라민포스페이트(MP)가 분산된 폴리우레탄폼 복합체(MP-PUF)를 만들고, MP-PUF의 모폴로지, 독립기포율, 열전도율, 열분해온도 등을 분석하였다. MP-PUF는 MP가 분산된 폴리아디페이트디올(f=2), 폴리에테르-폴리올(f=4.6)과 PMDI(f=2.5)를 원료로 사용하고 발포제로 $H_2O$ 양을 변화시키며 제조하였다. 폴리우레탄폼의 MP 함량은 $1.43{\pm}0.30wt%$로 고정하였다. $H_2O$의 양이 증가할수록 순수한 폴리우레탄폼(PUF)의 열전도율은 낮아지고 MP-PUF의 열전도율은 커졌다. PUF와 MP-PUF의 열안정성은 $H_2O$ 양이 5 php에서 최대가 되었다가 그 이상에서는 낮아졌다. 특히, MP-PUF는 발포과정에 생성된 우레아기와 MP의 영향으로 열안정성이 크게 향상되어 MP-PUF의 잔량이 50%가 되는 온도가 $370{\sim}450^{\circ}C$, 잔량이 30%가 되는 온도는 $700^{\circ}C$ 이상으로 PUF에 비하여 각각 25, $70^{\circ}C$ 이상 높아졌다.