• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.32.1-32.1
• /
• 2011

Ultra thin tantalum nitride (TaNx) films with various thicknesses (10 nm to 40 nm) have been deposited by rf magnetron sputtering technique on glass substrates. The as deposited films were systematically characterized by several analytical techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, field emission scanning electron microscopy, atomic force microscopy, UV-Vis-NIR double beam spectrophotometer and four point probe method. From the XRD results, the as deposited films are in amorphous nature, irrespective of the film thicknesses. The films composition was changed greatly with increasing the film thickness. SEM micrographs exhibited the densely pack microstructure, and homogeneous surface covered by small size grains at lower thickness deposited films. The surface roughness of the films was linearly increases with increasing the films thickness, consequently the transmittance decreased. The absorption edge was shifted towards higher wavelength as the film thickness increases.

• 한국전기전자재료학회논문지
• /
• 제17권3호
• /
• pp.272-277
• /
• 2004

The primary aim of this study is to investigate new semi-abrasive free slurry including acid colloidal silica and hydrogen peroxide for copper chemical-mechanical planarization (CMP). In general, slurry for copper CMP consists of colloidal silica as an abrasive, organic acid as a complex-forming agent, hydrogen peroxide as an oxidizing agent, a film forming agent, a pH control agent and several additives. We developed new semi-abrasive free slurry (SAFS) including below 0.5％ acid colloidal silica. We evaluated additives as stabilizers for hydrogen peroxide as well as accelerators in tantalum nitride CMP process. We also estimated dispersion stability and Zeta potential of the acid colloidal silica with additives. The extent of enhancement in tantalum nitride CMP was verified through anelectrochemical test. This approach may be useful for the application of single and first step copper CMP slurry with one package system.

• 산업기술연구
• /
• 제41권1호
• /
• pp.25-30
• /
• 2021

Hydride-dehydride process for efficient recycling of tantalum (Ta) is used for manufacturer of Ta powder. In case of metal powder, Impurities as like nitride, oxygen, hydrogen is decreased of physical properties. For manufacture of Ta powder, control of theses impurities is important. In this study, to decreased of impurities on Ta powder using HDH process optimize dehydride condition. Dehydration behavior of Ta is depended on temperature, time, and atmosphere. Phase transition of Ta hydride is analyzed by X-ray diffraction (XRD). Concentration of hydrogen is decreased with temperature increased. At high temperature, concentration of hydrogen in Ta is similar according to time increased. Size and morphology of powder is not observed after dehydride. Ta powder, which is less than 20 um, concentration of hydrogen under 800 ppm is obtain.

• 센서학회지
• /
• 제13권4호
• /
• pp.303-308
• /
• 2004

This paper descibes on the characteristics of Ta-N(tantalum nitride) ceramic thin-film strain gauges which were deposited on Si substrates by DC reactive magnetron sputtering in an argon-nitrogen atmosphere (Ar-$(4{\sim}16%)N_{2}$) for high-temperature applications. These films were annealed in $2{\times}10^{-6}$ Torr vacuum furnace at the range of $500{\sim}1000^{\circ}C$. Optimum deposition atmosphere and annealing temperature were determined at $900^{\circ}C$ for 1 hr. in 8% $N_{2}$ gas flow ratio. Under optimum formation conditions, the Ta-N thin-film for strain gauges was obtained a high-resistivity of $768.93{\mu}{\Omega}{\cdot}cm$, a low temperature coefficient of resistance (TCR) of -84 ppm/$^{\circ}C$ and a good longitudinal gauge factor (GF) of 4.12.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.1014-1017
• /
• 2001

In recent years, The tantalum nitride(TaN) thin-film has been developed for the electronic resistor and capacitor. In this papers, The effect of thermal annealing in the temperature range of 300∼700$^{\circ}C$ on the sheet resistor properties and microistructure of tantalum nitride(TaN) thin-film deposited by RF sputtering was studied. XRD(X-ray diffractometer) and AFM were used to observe electrical properties and microstructrue of the TaN film and sheet resistance. The TCR properties of the TaN films were discussed in terms of annealing temperature, ratio of nitrogen, crystallization and thin films surface morphology due to annealing temperature. The leakage current of the TaN thin film annealed 400 $^{\circ}C$ was stabilized in the study. How its was found that the sheet resistance in the polycrystalline TaN thin film decreased with increasing the annealing temperature above 600 $^{\circ}C$ after sudden peak upen 400 $^{\circ}C$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2002년도 하계학술대회 논문집 C
• /
• pp.1476-1478
• /
• 2002

In recent years, the tantalum nitride(TaN) thin-film has been developed for the electronic resistor, inductor and capacitor. In this papers, this study presents the surface profile and sheet-resistance property relationship of reactive-sputtered TaN thin film resistor processed by TaN(tantalum nitride) on alumina substrate. The TCR properties of the TaN films were discussed in terms of crystallization and thin films surface morphology due to annealing temperature. It is clear that the TaN thin-films resistor electrical properties are low TCR related with it's annealing temperature and ambient annealing condition. Respectively, at $300{\sim}400^{\circ}C$ on vacuum and nitrogen annealed thin film resistor having a goof thermal stability and lower TCR properties then as deposited thin films expected for the application to the dielectric material of passive component.

• 한국재료학회지
• /
• 제11권9호
• /
• pp.802-809
• /
• 2001

Electroplating is an attractive alternative deposition method for copper with the need for a conformal and conductive seed layer In addition, the Cu seed layer should be highly pure so as not to compromise the effective resistivity of the filled copper interconnect structure. This seed layer requires low electrical resistivity, low levels of impurities, smooth interface, good adhesion to the barrier metal and low thickness concurrent with coherence for ensuring void-free fill. The electrical conductivity of the surface plays an important role in formation of initial Cu nuclei, Cu nucleation is much easier on the substrate with higher electrical conductivities. It is also known that the nucleation processes of Cu are very sensitive to surface condition. In this study, copper seed layers deposited by magnetron sputtering onto a tantalum nitride barrier layer were used for electroplating copper in the forward pulsed mode. Prior to electroplating a copper film, the Cu seed layer was cleaned by plasma H$_2$ and $N_2$. In the plasma treatment exposure tome was varied from 1 to 20 min and plasma power from 20 to 140W. Effects of plasma pretreatment to Cu seed/Tantalum nitride (TaN)/borophosphosilicate glass (BPSG) samples on electroplating of copper (Cu) films were investigated.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.158-161
• /
• 2003

The primary aim of this study is to investigate new semi-abrasive free slurry including acid colloidal silica and hydrogen peroxide for copper chemical-mechanical planarization (CMP). In general, slurry for copper CMP consists of colloidal silica as an abrasive, organic acid as a complex-forming agent, hydrogen peroxide as an oxidizing agent, a film forming agent, a pH control agent and several additives. We developed new semi-abrasive free slurry (SAFS) including below 0.5% acid colloidal silica. We evaluated additives as stabilizers for hydrogen peroxide as well as accelerators in tantalum nitride CMP process. We also estimated dispersion stability and Zeta potential of the acid colloidal silica with additives. The extent of enhancement in tantalum nitride CMP was verified through anelectrochemical test. This approach may be useful for the application of single and first step copper CMP slurry with one package system.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 추계학술발표대회
• /
• pp.24.1-24.1
• /
• 2009

Tantalum carbo-nitride($T_aC_xN_y$) films were deposited with chemical vapor deposition(CVD) using tert-butylimido tris-diethylamido tantalum (TBTDET, $^tBu-N=Ta-(NEt_2)_3$, $Et=C_2H_5$, $^tBu=C(CH_3)_3$) between $350^{\circ}C$ and $600^{\circ}C$ with argon as a carrier gas. Fourier transform infrared (FT-IR)spectroscopy was used to study the thermal decomposition behavior of TBTDET in the gas phase. When the temperature was increased, C-H and C-N bonding of TBTDET disappeared and the peaks of ethylene appeared above $450^{\circ}C$ in the gas phase. The growth rate and film density of $T_aC_xN_y$ film were in the range of 0.1nm/min to 1.30nm/min and of $8.92g/cm^3$ to $10.6g/cm^3$ depending on the deposition temperature. $T_aC_xN_y$ films deposited below $400^{\circ}C$ were amorphous and became polycrystal line above $500^{\circ}C$. It was confirmed that the $T_aC_xN_y$ film was a mixture of TaC, graphite, $Ta_3N_5$, TaN, and $Ta_2O_5$ phases and the oxide phase was formed from the post deposition oxygen uptake. With the increase of the deposition temperature, the TaN phase was increased over TaC and $Ta_3N_5$ and crystallinity, work function, conductivity and density of the film were increased. Also the oxygen uptake was decreased due to the increase of the film density. With the increase of the TaC phase in $T_aC_xN_y$ film, the work function was decreased to 4.25eV and with the increase of the TaN phase in $T_aC_xN_y$ film,it was increased to 4.48eV.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 반도체재료
• /
• pp.79-83
• /
• 2001

In order to compare the barrier properties of Ta-N/Si(001) with those of Ta-N/Ta/Si(001), we studied structural properties of films grown by RF magnetron sputtering with various $Ar/N_2$ ratios. To evaluate the barrier properties, the samples were annealed in a vacuum chamber. Ex-situ x-ray scattering measurements were done using an in-house x-ray system. With increasing nitrogen ratio in Ta-N/Si(001), the barrier property of Ta-N/Si(001) was enhanced, finally failed at $750^{\circ}C$ due to the crystallization and silicide formation. Compared with Ta-N/Si(001), Ta-N/Ta/Si(001) forms silicides at $650^{\circ}C$. However it does not crystallize even at $750^{\circ}C$. With increasing nitrogen composition in Ta-N/Ta/Si(001), the formation of tantalum silicide was reduced and the surface roughness was improved. To observe the surface morphology of Ta-N/Ta/Si(001) during annealing, we performed an in-situ x-ray scattering experiment using synchrotron radiation of the 5C2 at Pohang Light Source(PLS). Addition of Ta layer between Ta-N and Si(001) improved the surface morphology and reduced the surface degradation at high temperatures. In addition, increasing $N_2/Ar$ flow ratio reduced the formation of tantalum silicide and enhanced the barrier properties.