• International Journal of Highway Engineering
• /
• v.19 no.2
• /
• pp.25-34
• /
• 2017

PURPOSES: The purpose of this paper is to evaluate interface performance while using various tack coat materials for asphalt overlay. METHODS : The evaluation was conducted with tracking test, permeability, and interface bond strength. Tracking test was conducted using an image processing technique, to investigate the susceptibility of the tack coat materials. BBS and pull-off test were conducted to evaluate bond strength. The permeability test was conducted to evaluate the effect of tack coat materials. RESULTS : Results reveal that the trackless tack coat material demonstrates less tracking compared to other materials. Moreover, both BBS and pull-off tests can effectively evaluate the bond strength at the interface. RSC-4 was measured less bond strength. Moreover, tack coat prevents water penetration through the surface and aids the extension of the surface life of asphalt pavement. CONCLUSIONS : Trackless tack coat demonstrated a high and consistent bond strength performance. The tack coat types demonstrate marginally different performance as function of curing times. Field applicability was tested based on visual observation. Therefore, these should be considered when trackless tack coat is slightly enhanced the pavement performance based on limited this study results. Finally, it is necessary to allow reasonable time for the tack coat to completely cure.

• Resources Recycling
• /
• v.10 no.1
• /
• pp.32-41
• /
• 2001

Bond shear strengths of recycled asphalt concrete were evaluated under different tack coat applications. Regardless of the new and old mixtures, the bond shear strengths at $30^{\circ}C$ were increased by 10-20% than those at 1$0^{\circ}C$. The bond shear strengths of recycled asphalt concrete without tack coat showed very low ones. These are the main reasons for the frequent longitudinal interface crack in the field. The effect of tack coat curing time on bond shear strengths was inferior to the tack coat construction temperature.

• International conference on construction engineering and project management
• /
• 2022.06a
• /
• pp.784-791
• /
• 2022

Tack coat is a thin layer of asphalt between the existing pavement and asphalt overlay. During construction, insufficient tack coat layering can later cause surface defects such as slippage, shoving, and rutting. This paper proposed a method for tack coat inspection improvement using an unmanned aerial vehicle (UAV) and deep learning neural network for automatic non-uniform assessment of the applied tack coat area. In this method, the drone-captured images are exploited for assessment using a combination of Mask R-CNN and Grey Level Co-occurrence Matrix (GLCM). Mask R-CNN is utilized to detect the tack coat region and segment the region of interest from the surroundings. GLCM is used to analyze the texture of the segmented region and measure the uniformity and non-uniformity of the tack coat on the existing pavements. The results of the field experiment showed both the intersection over union of Mask R-CNN and the non-uniformity measured by GLCM were promising with respect to their accuracy. The proposed method is automatic and cost-efficient, which would be of value to state Departments of Transportation for better management of their work in pavement construction and rehabilitation.

• International Journal of Highway Engineering
• /
• v.18 no.5
• /
• pp.1-9
• /
• 2016

PURPOSES : This study focuses on the evaluation of interface performance with varying surface texture and tack coat application in an asphalt overlay. METHODS : The evaluation is carried out in two phases: tracking test and interface bond strength test. Using an image processing tool, tracking test is conducted to evaluate the susceptibility of the tack coat material to produce excessive tracking during application. Using the pull-off test method, the bond strength test is performed to determine the ability of the interface layer to resist failure. RESULTS : Results show that the underseal application yields less tracking compared to other applications. However, the bond strength is barely within the minimum acceptable value. On the other hand, RSC-4 produces higher bond strength for all surface types, but the drying time is long, which produces excessive tracking. CONCLUSIONS : While underseal application may be suitable for a trackless condition, the bond strength is less appealing compared to the rest of the tack applications available. RSC-4 demonstrated a high and consistent bond strength performance, but more time is required for drying to avoid excessive tracking. Tack coat application and surface type combination produce varying results. Therefore, these should be considered when selecting suitable future tack coat application options.

• International Journal of Highway Engineering
• /
• v.16 no.6
• /
• pp.121-128
• /
• 2014

PURPOSES : The objective of this study is to evaluate the tack-coating material's properties using the bitumen bond strength(BBS) test and damping test as function of changed curing times. In this study, bonding strength tests were performed according to the curing time of tack coating materials. METHODS : In order to investigate bonding characteristic of tack coating materials, the Pneumatic Adhesion tensile Testing Instrument(PATTI) device is used to measure the bond strength between the tack coating materials and aggregate substrate based on the AASHTO TP-91. Also, damping test as in situ test was used to determine an appropriate traffic openting time for construction vehicle. Four different tack-coating materials were used in this study. The BBS tests were performed a one hour curing and testing temperatures of $5^{\circ}C$, $15^{\circ}C$, and $25^{\circ}C$. Damping test was conducted at 30min, 60min, 90min, and 120 min of curing times with temperatures of $20^{\circ}C$ and $30^{\circ}C$. RESULTS and CONCLUSIONS : The BBS test results show various bond strength as function of tack coat materials. At the same testing condition, A tack coat material shows almost two times higher than D tack coat materials although both materials are satisfied the criteria of material's physical properties. Also, Dampting test results shows similar trend with BBS test result. The damping test result was significantly changed as function of tack coat materials. Based on this study, the tack coating material's curing time is very important. Therefore, both curing time and the bond strength's characteristic has to be considered in standard specification.

• International Journal of Highway Engineering
• /
• v.18 no.6
• /
• pp.137-143
• /
• 2016

OBJECTIVES : Bituminous materials, such as tack coat, are utilized between pavement layers for improving the bond strength in pavement construction sites. The standards regarding the application of bituminous material are not clearly presented in the Korean construction guideline without RS(C)-4. Hence, the objective of this study is to determine the optimum content of bituminous materials by analyzing interlayer shear strength (ISS) from the direct shear tester, which was developed in this research. The shear strength of tack coat was defined with the sort of bituminous materials. METHODS : The mixtures for the shear test were made using marshall mix design. The specimens were vertically and horizontally separated for the direct shear test. The separated specimens were bonded using bituminous material. The objectives of the experiment are to determine the performance of bond and shear properties resulting from slippage, rutting, shovel, and corrugation of asphalt pavements. A machine based on the Louisiana interlayer shear strength tester (LISST) of NCHRP Report-712 was developed to determine the ISS. The applied types of tack coat were RS(C)-4, AP-3, QRS-4, and BD-coat with contents of $0.3{\ell}/m^2$, $0.45{\ell}/m^2$, $0.6{\ell}/m^2$, and $0.8{\ell}/m^2$, respectively. RESULTS : Table 2 gives the results of the direct shear test using the developed shear machine. The BD-coat type indicated the highest average ISS value compared to the others. Between the surface and binder course, optimum tack coat application rates for AP-3, RS(C)-4, QRS-4, and BD-Coat were $0.6{\ell}/m^2$, $0.3{\ell}/m^2$, $0.6{\ell}/m^2$, and $0.45{\ell}/m^2$, respectively. These optimum contents were determined using the ISS value. CONCLUSIONS : The ISS values of AP-3, RS(C)-4, and QRS-4 showed similar tendencies when ISS increased in the range $0.3{\sim}0.6{\ell}/m^2$, while ISS decreased when the applied rate exceeded $0.6{\ell}/m^2$. Similarly, the highest ISS value of the BD-coat was observed when the applied rate was $0.45{\ell}/m^2$. However, shear strength was similar to the maximum value of ISS when the tack-coat application rate of BD-Coat exceeded $0.45{\ell}/m^2$.

• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.39-46
• /
• 2015

PURPOSES: The objectives of this study were to develop a new polymer-modified emulsion for application to tack coats and to evaluate its properties by comparing it with other types of asphalt emulsions, with the goal of providing an enhanced tack coat material for use in construction. METHODS: Modified asphalt binders were developed from using SBS and SBR latex in the laboratory, and their fundamental properties, such as their penetration index and PG grade, were evaluated. Based on the properties, a new tack coat material was developed. To evaluate the newly developed asphalt emulsion, the bonding strength between the two layers of HMA was measured by applying a uniaxial tensile test and shear test. For the tests, a total of four different conditions were applied to the specimens, including the developed asphalt emulsion, latex modified asphalt emulsion, conventional asphalt emulsion, and non-tack coating. RESULTS AND CONCLUSIONS: Overall, the developed asphalt emulsion exhibits the best bonding strength behavior among all of the three types. Also, the two types of polymer-modified emulsions were found to be better for application for use as a tack coat than a conventional emulsion. Especially, at a high temperature ($50^{\circ}C$), the conventional asphalt emulsion no longer acts as a tack coating material. Therefore, the polymer-modified emulsion should be considered for application to tack coat construction during the summer.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.41 no.6
• /
• pp.737-744
• /
• 2021

Spray paving minimizes material lost during the construction or repair of a road surface, and it can be done in conjunction with tack coating. This approach involves applying the asphalt mixture at the same time as spraying the tack coat by attaching a spraying device to the asphalt paver. When applying an asphalt overlay to an aged concrete surface, it is important to ensure the adhesion performance between different material properties. Accordingly, there is a need for a tack coat that can be applied by spray paving and that exhibits good adhesive performance on different materials. In this study, bonding strength tests under various conditions were performed to evaluate the basic performance of a tack coat developed for use with a spray paver. The bonding performance of the tack coat was observed to be affected by curing conditions and material lost during construction. The test results also showed that the tensile and shear bonding strengths of the developed tack coat were 1.21 and 1.99 times higher than those of a conventional one, respectively. As a result, the developed tack coat is considered suitable for application to spray paving.

• International Journal of Highway Engineering
• /
• v.19 no.6
• /
• pp.37-46
• /
• 2017

PURPOSES : A composite pavement utilizes both an asphalt surface and a concrete base. Typically, a concrete base layer provides structural capacity, while an asphalt surface layer provides smoothness and riding quality. This pavement type can be used in conjunction with rollercompacted concrete (RCC) pavement as a base layer due to its fast construction, economic efficiency, and structural performance. However, the service life and functionality of composite pavement may be reduced due to interfacial bond failure. Therefore, adequate interfacial bonding between the asphalt surface and the concrete base is essential to achieving monolithic behavior. The purpose of this study is to investigate the bond characteristics at the interface between asphalt (HMA; hot-mixed asphalt) and the RCC base. METHODS : This study was performed to determine the optimal type and application rate of tack coat material for RCC-base composite pavement. In addition, the core size effect, temperature condition, and bonding failure shape were analyzed to investigate the bonding characteristics at the interface between the RCC base and HMA surface. To evaluate the bond strength, a pull-off test was performed using different diameters of specimens such as 50 mm and 100 mm. Tack coat materials such as RSC-4 and BD-Coat were applied in amounts of 0.3, 0.5, 0.7, 0.9, and $1.1l/m^2$ to determine the optimal application rate. In order to evaluate the bond strength characteristics with temperature changes, a pull-off test was carried out at -15, 0, 20, and $40^{\circ}C$. In addition, the bond failure shapes were analyzed using an image analysis program after the pull-off tests were completed. RESULTS : The test results indicated that the optimal application rate of RSC-4 and BD-Coat were $0.8l/m^2$, $0.9l/m^2$, respectively. The core size effect was determined to be negligible because the bond strengths were similar in specimens with diameters of 50 mm and 100 mm. The bond strengths of RSC-4 and BD-Coat were found to decrease significantly when the temperature increased. As a result of the bonding failure shape in low-temperature conditions such as -15, 0, and $20^{\circ}C$, it was found that most of the debonding occurred at the interface between the tack coat and RCC surface. On the other hand, the interface between the HMA and tack coat was weaker than that between the tack coat and RCC at a high temperature of $40^{\circ}C$. CONCLUSIONS : This study suggested an optimal application rate of tack coat materials to apply to RCC-base composite pavement. The bond strengths at high temperatures were significantly lower than the required bond (tensile) strength of 0.4 MPa. It was known that the temperature was a critical factor affecting the bond strength at the interface of the RCC-base composite pavement.

• International Journal of Highway Engineering
• /
• v.17 no.3
• /
• pp.35-47
• /
• 2015

PURPOSES : A tack coat has been utilized to increase the bond performance between the surface layer and base course (intermediate course) at various road pavement sites. This is similarly true in other nations. Based on this connection, the objective of the present study is to evaluate the properties of hot mix asphalt (HMA) mixtures with an RSC-4 or BD-Coat and determine the application rate of the tack coat. METHODS : The HMA specimens were manufactured using superpave gyratory compaction. The HMA mixtures were composed of a 5-cm thick surface layer and a 10-cm thick base course. An impact hammer resonance test (IHRT) and a static load shear test were conducted to evaluate the performance of the HMA mixtures with a tack coat. From these tests, the dynamic moduli related to the high-frequency resistance and interlayer shear strength (ISS) of HMA could be obtained. RESULTS : The results of the dynamic moduli of HMA are discussed based on the resonance frequency (RF). To check the accuracy of the IHRT, we conducted a coherence analysis. A direct shear test using the application of a static load test was carried out to evaluate the interlayer shear strength (ISS) of HMA. CONCLUSIONS : The maximum ISS was demonstrated at an RSC-4 application rate of 462 gsm, and the maximum dynamic modulus was demonstrated at an RSC-4 application rate of 306 gsm. By averaging the results of the ISS, the maximum ISS values were obtained when a BD-Coat application rate of 602 gsm was applied.