• Korean Journal of Materials Research
• /
• v.22 no.8
• /
• pp.403-408
• /
• 2012

A sample of ultra low carbon IF steel was processed by six-layer stack accumulative roll-bonding (ARB) and annealed. The ARB was conducted at ambient temperature after deforming the as-received material to a thickness of 0.5 mm by 50% cold rolling. The ARB was performed for a six-layer stacked, i.e. a 3 mm thick sheet, up to 3 cycles (an equivalent strain of ~7.0). In each ARB cycle, the stacked sheets were, first, deformed to 1.5 mm thickness by 50% rolling and then reduced to 0.5 mm thickness, as the starting thickness, by multi-pass rolling without lubrication. The specimen after 3 cycles was then annealed for 0.5 h at various temperatures ranging from 673 to 973 K. The microstructural evolution with the annealing temperature for the 3-cycle ARB processed IF steel was investigated in detail by transmission electron microscopy observation. The ARB processed IF steel exhibited mainly a dislocation cell lamella structure with relatively high dislocation density in which the subgrains were partially observed. The selected area diffraction (SAD) patterns suggested that the misorientation between neighboring cells or subgrains was very small. The thickness of the grains increased in a gradual way up to 873 K, but above 898 K it increased drastically. As a result, the grains came to have an equiaxed morphology at 898 K, in which the width and the thickness of the grains were almost identical. The grain growth occurred actively at temperatures above 923 K.

• Journal of Powder Materials
• /
• v.22 no.6
• /
• pp.385-390
• /
• 2015

We report a synthesis of non-toxic InP nanocrystals using non-pyrolytic precursors instead of pyrolytic and unstable tris(trimethylsilyl)phosphine, a popular precursor for synthesis of InP nanocrystals. In this study, InP nanocrystals are successfully synthesized using hexaethyl phosphorous triamide (HPT) and the synthesized InP nanocrystals showed a broad and weak photoluminescence (PL) spectrum. As synthesized InP nanocrystals are subjected to further surface modification process to enhance their stability and photoluminescence. Surface modification of InP nanocrystals is done at $230^{\circ}C$ using 1-dodecanethiol, zinc acetate and fatty acid as sources of ZnS shell. After surface modification, the synthesized InP/ZnS nanocrystals show intense PL spectra centered at the emission wavelength 612 nm through 633 nm. The synthesized InP/ZnS core/shell structure is confirmed with X-ray diffraction (XRD) and Inductively Coupled Plasma - Atomic Emission Spectrometer (ICP-AES). After surface modification, InP/ZnS nanocrystals having narrow particle size distribution are observed by Field Emission Transmission Electron Microscope (FE-TEM). In contrast to uncapped InP nanocrystals, InP/ZnS nanocrystals treated with a newly developed surface modified procedure show highly enhanced PL spectra with quantum yield of 47%.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.1
• /
• pp.1-11
• /
• 1996

Mechanical alloying is an effective process to finely distribute inert dispersoids in an Al-TM(TM is a transition metal) system. It has been considered that high melting point aluminides are formed by precipitation from supersaturated Al(Ti) powder. This analysis is based on the fact that much higher content of TM than the solubioity can be dissolved in alpha aluminum during the high energy ball milling. Thus, decomposition behavior of Ti in the Al(Ti) was considered very important. But it is confirmed that the higher portion of Ti than Al(Ti) solid solution is existed as nano-sized Ti particles in the MA powders by high energy ball nilling from the XRD spectrum and TEM analysis in this study. Therefore, the role of undissolved TM particles affect the formation of aluminides should be suitably considered. In this study, we present experimental observation on the formation of $Al_3Ti$ fron mechanical alloyed Al-Ti alloys in the hyperperitectic region. This study showed that, in the mechanically alloyed Al-20wt%Ti specimen, intermediate phase of cubic $Al_3Ti$ and tetragonal $Al_{24}Ti_8$ formed at $300{\sim}400^{\circ}C$ and $400{\sim}500^{\circ}C$, respectively, before the MA state reaches to equilibrium at higher temperatures. The formation behavior of $Ll_2-Al_3Ti$ is interpreted by interdiffusion of Al and Ti in solid state based on the fact that large amount of nano-sized Ti particles exist in the milled powder. Present analysis indicated undissolved Ti particles of nanosize should have played an important role initiation the formation of $Al_3Ti$ phase during annealing.

• Journal of Surface Science and Engineering
• /
• v.45 no.6
• /
• pp.232-241
• /
• 2012

Cr-Ti-B-N coatings were synthesized by a hybrid coating system combining high power impulse magnetron sputtering (HIPIMS) and DC pulse magnetron sputtering from a $TiB_2$ and a Cr target in argon-nitrogen environment, respectively. By changing the power applied on the Cr and $TiB_2$ cathodes, the Cr-Ti-B-N coatings with various Ti/Cr ratio and B content were deposited. The phase structure, microstructure and chemical compositions of the Cr-Ti-B-N coatings were studied by X-ray diffraction (XRD), transmission scanning electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). With increase of Cr element in the coatings, the nanocomposite microstructure consisting of nano-sized (Cr, Ti) N crystallites and amorphous BN phase were obtained in the coatings. The microhardness of the Cr-Ti-B-N coatings exhibited a peak value of ~41 GPa for the $CrTi_{0.1}B_{0.4}N_{1.3}$, and then decreased with further increase of Cr content in the coatings, and all the coatings exhibited low friction coefficient. The oxidation and corrosion behavior of the Cr-Ti-B-N coatings revealed better properties due to the formation of a nanocomposite microstructure.

• Journal of Sensor Science and Technology
• /
• v.11 no.3
• /
• pp.183-190
• /
• 2002

Photoluminescence(PL) properties of $Si^+$-implanted $SiO_2$ film, which was thermally grown on c-Si substrate, is reported. We have compared room temperature photoluminescence (PL) spectra of the samples which was made in several kinds of implantation, subsequent annealing and $SiO_2$ film thickness. XRD data was correlated with the PL spectra. Silicon nanocrystals in $SiO_2$ film is considered as the origin of the photoluminescence. PL spectra was investigated after wet etching of the $SiO_2$ film by using BOE (Buffered Oxide Etchant) at every one minute. PL peak wavelength was varied as the etching is proceeded. These results indicate that the quantity and the distribution of dominant size of Si nanocrystals in $SiO_2$ film seem to have a direct effect on PL spectrum.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.6
• /
• pp.345-353
• /
• 2009

The precipitates of $L2_1$-type $Ni_2AlHf$ phase in B2-ordered NiAl system has been observed by using transmission electron microscope (TEM). The hardness of as-quenched NiAl-Hf alloys is high due to the larger strengthening. However, age hardening of this alloy is not main effect to increase hardness compared to the large microstructural variations during aging. At the beginning of aging, the $L2_1$-type $Ni_2AlHf$ precipitates keep a lattice coherency with the NiAl matrix. The orientation relationship between the $Ni_2 AlHf$ precipitate and the NiAl matrix is <100>$_{Ni2AlHf}$//<100>$_{NiAl}$, {001}$_{Ni2AlHf}$//{001}$_{NiAl}$. By aging treatment for long time $Ni_2AlHf$ precipitates lost their coherency and change their morphology to the spherical ones surrounded by misfit dislocations. The orientation relationship between the NiAl matrix and the $Ni_2AlHf$ precipitates, however, has been kept even after longer aging time. The lattice misfit between the $Ni_2AlHf$ precipitate and the NiAl matrix has been calculated by the selected electron diffraction patterns, and the spacings of misfit dislocations is about 4.5% at 1173 K.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.5
• /
• pp.242-252
• /
• 2014

A comparative study was performed on the microstructures and the mechanical properties of STD11 and 8Cr steel. The specimens were quenched from $1030^{\circ}C$ and tempered at $240^{\circ}C$ and $520^{\circ}C$. Vickers hardness, impact toughness and tensile tests were conducted at various tempering temperatures. Microstructural characterization to measure grain size, volume fraction of retained austenite and distribution of carbides was carried out by using SEM, EBSD, TEM and X-ray diffraction techniques. Due to finer $M_7C_3$ carbides dispersed, 8Cr steel showed larger impact toughness and plasticity than STD11 irrespective of the tempering temperature. While 8Cr steel had lower hardness in as-quenched state and after tempering at $240^{\circ}C$ owing to smaller carbide content and more retained austenite, it was harder after tempering at $520^{\circ}C$ due to larger precipitation hardening from finer $M_{23}C_6$.

• Journal of the Korean Magnetics Society
• /
• v.26 no.6
• /
• pp.190-195
• /
• 2016

We report the effect of pressure varying from 0 to 1500 bar on the magnetic properties of magnetite nanoparticles synthesized from $Fe(OH)_2$ suspension using a high pressure homogenizer without any dispersing agent and oxidant. The observed X-ray diffraction (XRD) patterns showed that all the synthesized nanoparticles had the inverse spinel structure of magnetite. It was found from transmission electron microscopy (TEM) and XRD analysis that the average size of the synthesized magnetite particles could be controlled by the pressure of the high pressure homogenizer. The average particle size was found to range from 21 to 26 nm and decrease with increasing pressure. Magnetic hysteresis measurements performed at room temperature using a vibrating sample magnetometer (VSM) revealed the appearance of a superparamagnetic behavior in the magnetite nanoparticles synthesized at a pressure of 1500 bar.

• Journal of Korea Foundry Society
• /
• v.15 no.3
• /
• pp.252-261
• /
• 1995

The purposes of this study were to investigate the microstructural changes in alloy ribbons of Al-Fe-Mo-Si quarternary system at $450{\sim}500^{\circ}C$, and to study the coarsening mechanism of fine precipitates. Using the hot stage in TEM, in situ microstructural changes in Al-4Fe-0.5Mo-1.5Si alloy ribbon and Al-8Fe-2Mo-1.5Si alloy ribbon have been examined successively up to 60 hours at $450^{\circ}C$ and $500^{\circ}C$. Cell structure in zone B of Al-4Fe-0.5Mo-1.5Si alloy ribbon was observed to collapse even in 10 minutes by in-situ heating at $450^{\circ}C$ and the size of precipitates in zone B increased twice in 60 hours. The precipitates in zone A of Al-4Fe-0.5Mo-1.5Si alloy ribbon showed slower coarsening rate than those in zone B by in-situ heating at $450^{\circ}C$. The precipitates in zone A of Al-8Fe-2Mo-1.5Si alloy ribbon increased 50% by in-situ heating at $500^{\circ}C$ in 50 hours compared to the initial precipitates while any microstructual change in zone B was not observed by in-situ heating at $500^{\circ}C$ up to 50 hours. Only the precipitates in zone A of Al-4Fe-0.5Mo-1.5Si alloy ribbon satisfied $r^3{\propto}t$ relationship of coarsening mechanism.

• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.31 no.1
• /
• pp.13-23
• /
• 2005

This study was performed to investigate mistletoe extract-induced apoptosis in oral squamous cell carcinoma. In vivo study, HN22 cells were xenografted in nude mice. After tumor was experimentally induced, mistletoe extract was directly injected on the tumor mass. The specimens were evaluated using light and transmission electron microscopes. In vitro study, HN22 cells were cultured and exposed to mistletoe extract. The cells were evaluated using transmissin electron microscope. To evaluate apoptotic cells, flow cytometric analysis was done. The results were obtained as follows: 1. Light microscopic view of tumor mass showed necrosis at 2-4 weeks. 2. Transmission electron micrographs of tumor mass showed apoptosis and necrosis. 3. In TEM view of cell lines, necrosis and apoptosis were shown with mistletoe extract at $300{\mu}g/ml$, apoptosis was shown with mistletoe extract at $100{\mu}g/ml$. 4. In flow cytometric analysis, early and late apoptosis was shown when using caspase-3Ab and annexin-V, but no significant change was noted when using mebstain and Apo2.7 Ab. In this study, mistletoe extract induced necrosis and apoptosis in the tumor mass was induced by HN22 cells, early and late apoptosis in vitro study. Mistletoe extract was likely to induce cell death in oral squamous cell carcinoma through apoptosis.