• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.246-249
• /
• 2011

Surface modification before coating nickel by coupling agents and/or etchant of glass did not provide enough adhesive strength of electroless nickel deposits on glass. Effect of heat treatments on hardness as well as adhesion of nickel deposits was studied by using tape test for adhesion, nanoindenter for hardness and glancing angle x-ray diffractometer (GAXRD) for phase characterization. Heat treatment improved hardness as well as adhesion. XRD results give that the improvements of adhesion and hardness are due to the formation of $NiSiO_4$ around the interface between the nickel deposits and the glass and the precipitation of $Ni_3P$ causing precipitation hardening, respectively. The details in effects of heat treatment on adhesion and hardness are described here.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.8
• /
• pp.2367-2370
• /
• 2014

"Cat's eye"-shaped $[^{57}Co]CoO@SiO_2$ core-shell nanostructure was prepared by the reverse microemulsion method combined with radioisotope technique to investigate a potential imaging agent for a single photon emission computed tomography (SPECT) in nuclear medicine. The core cobalt oxide nanorods were obtained by thermal decomposition of $Co-(oleate)_2$ precursor from radio isotope Co-57 containing cobalt chloride and sodium oleate. The $SiO_2$ coating on the surface of the core cobalt oxide nanorods was produced by hydrolysis and a condensation reaction of tetraethylorthosilicate (TEOS) in the water phase of the reverse microemulsion system. In vivo test, micro SPECT image was acquired with nude mice after 30 min of intravenous injection of $[^{57}Co]CoO@SiO_2$ core-shell nanostructure.

• Journal of the Korean Ceramic Society
• /
• v.43 no.8 s.291
• /
• pp.463-468
• /
• 2006

Hydrothermal deposition of hydroxyapatite coatings on two types of $ZrO_2$ substrates (3 mol% $Y_2O_3$-doped and 13 mol% $CeO_2$-doped tetragonal $ZrO_2s$) was studied using aqueous solutions of $Ca(NO_3)_2\;4H_2O$ and $(NH_4)_2HPO_4$ containing EDTA (ethylene diamine tetra acetic acid) disodium salt as a chelating agent for $Ca^{2+}$ ions. For the precipitation of the coatings, the $EDTA-Ca^{2+}$ chelates were decomposed by oxidation with $H_2O_2$ at $90^{\circ}C$. The deposition behavior, morphology, and orientation of the coatings were investigated while varying the solution pH using scanning electron microscopy and X-ray diffractometry. For the two sub-strates, sparse deposition of the coating was obtained at pH 5.5, whereas a uniform deposition was obtained at pH 7.1, 9.8, and 11.4 with a denser microstructure for the higher pH. The coating consisted of thin needle-like or plate-like crystals ($1-2{\mu}m$ length or diameter) at pH 7.1, but fine rod-like crystals ($1-2{\mu}m$ length, $0.1{\mu}m$ diameter) at pH 9.8 and 11.4. The coatings were $1-3{\mu}m$ thick and showed a preferred orientation of the hydroxyapatite crystals with their c axis (i.e., the elongated direction) perpendicular to the substrate surface especially for pH 9.8 and 11.4.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.129-129
• /
• 2006

Conventional solvent-based polyurethane (PU) is well established for wide applications, such as textile treatments, surface coating, adhesive and so on. Due to the demands of safety, economic, and environmental protection, the solvent-based PU is restricted and has been phasing out and aqueous-based PU is becoming the world market trend, which is an environmental friendly product. The chemical resistance, physical and mechanical properties of aqueous-based PU are still not competible with solvent-based PU. Because of aqueous-based PU is a linear thermoplastic polymer with lower average molecular weight. Their improvements are normally performed by a post-curing reaction or a polymer hybridization to enhance the polymer cross-linking density. Hybridization of PU with aqueous-based epoxy resin or acrylate emulsion and then cured by a curing agent for improving the performance properties and reducing the cost of aqueous-based PU.Furthermore, a special function is added to aqueous-based PU increasing the application value, for examples, flame retardation, polymeric dyes, hydrophilic and etc.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1158-1161
• /
• 2006

The toner type paper-like display (PLD) has been developed with two polymer particles having opposite polarity which is composed of polymer, colorant and external additives (nano-sized silica). Nano-sized silica with triboelectric charge was used for the charge control agent (CCA) and influenced on the electrostatic properties of the silica-coated polymer particles. The PLD cell using silica-coated particles (200 seconds) had shown a good white appearance and low driving voltage. The result could be explained in terms of the surface morphology and the cohesiveness depending on the silica coating time.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.4
• /
• pp.546-554
• /
• 2007

Statement of problem: Die materials require abrasion resistance, dimensional stability with time, and high surface wettability for adequate material properties. Wear of gypsum materials is a significant problem in the fabrication of accurately fitting cast prosthetic devices. So It has been recommended that the use of die hardener before carving or burnishing of the wax pattern. Purpose: The purpose of this study was to compare the abrasion resistance and surface microhardness(Knoop) with 3 commonly used gypsum die materials(MG Crystal Rock, Super plumstone, GC $FUJIROCK^{(R)}$ EP) with and without the application of 2 die hardeners. Material and methods: Three die materials were evaluated for abrasion resistance and surface microhardness after application of 2 die hardeners(Die hardener and Stone die & plaster hardener). Thirty specimens of each gypsum material were fabricated using an impression of resin die(Pattern resin; GC Corporation, Japan) with 1-mm high ridges, sloped 90 degrees. Gypsum materials were mixed according to manufacturer's recommendations and allowed to set 24 hours before coating. Specimens were arbitrary assigned to 1 of 3 treatment subgroups (n=10/subgroup): no treatment(control), coated with Die hardener, and coated with Stone die & plaster hardener. Abrasion resistance(measured by weight loss) was evaluated using device in 50g mass perpendicular to the ridges. Knoop hardness was determined by loading each specimen face 5 times for 15 seconds with a force of 50g. A scanning electron microscope was used to evaluate the surface of specimens in each treatment subgroup. Conclusions: The obtained results were as follows: 1. 3 types of die stone evaluated in this study did not show significant differences in surface hardness and abrasive resistance(P<.05). 2. In the abrasive resistance test, there were no significant differences between GC $FUJIROCK^{(R)}$ EP and MG Crystal Rock with or without 2 die hardener(P<.05). 3. Super plumstone treated with Stone die & plaster hardener showed increased wear loss(P<.05) 4. Die hardener coatings used in this study decreased the surface hardness of the gypsum material(P<.05).

• Korean Chemical Engineering Research
• /
• v.51 no.6
• /
• pp.666-670
• /
• 2013

Recovery method of silicon wafer from defective products generated from manufacturing process of silicon solar cells was studied. The removal effect of the N layer and antireflection coating (ARC) of the waste solar cell were investigated at room temperature ($25^{\circ}C$) by variation of concentration of $H_3PO_4$, $NH_4HF_2$, and concentration and types of chelating agent. Removal efficiency was the best in the conditions; 10 wt% $H_3PO_4$ 2.0 wt% $NH_4HF_2$, 1.5 wt% Hydantoin. Increasing the concentration of $H_3PO_4$, the surface contamination degree was increased and the thickness of the silicon wafe became thicker than the thickness before surface treatment because of re-adsorption on the silicon wafer surface by electrostatic attraction of the fine particles changed to (+). The etching method by mixed solution of $H_3PO_4$-$NH_4HF_2$-chelating agents was expected to be great as an alternative to conventional RCA cleaning methods and as the recycle method of waste solar cells, because all processes are performed at room temperature, the process is simple, and less wastewater, the removal efficiency of the surface of the solar cell was excellent.

• Journal of Microbiology and Biotechnology
• /
• v.22 no.11
• /
• pp.1568-1574
• /
• 2012

Microbiological calcium carbonate precipitation (MCCP) has been investigated for its ability to improve the durability of cement mortar. However, very few strains have been applied to crack remediation and strengthening of cementitious materials. In this study, we report the biodeposition of Bacillus subtilis 168 and its ability to enhance the durability of cement material. B. subtilis 168 was applied to the surface of cement specimens. The results showed a new layer of deposited organic-inorganic composites on the surface of the cement paste. In addition, the water permeability of the cement paste treated with B. subtilis 168 was lower than that of non-treated specimens. Furthermore, artificial cracks in the cement paste were completely remediated by the biodeposition of B. subtilis 168. The compressive strength of cement mortar treated with B. subtilis 168 increased by about 19.5% when compared with samples completed with only B4 medium. Taken together, these findings suggest that the biodeposition of B. subtilis 168 could be used as a sealing and coating agent to improve the strength and water resistance of concrete. This is the first paper to report the application of Bacillus subtilis 168 for its ability to improve the durability of cement mortar through calcium carbonate precipitation.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.541-541
• /
• 2012

InP quantum dots capped by myristic acid (InP-MA QDs) were synthesized by a typical hot injection method using MA as stablizing agent. The current density across the InP-MA QDs thin film which was fabricated by spin-coating method is about $10^{-4}A/cm^2$ at the electric field of 0.1 MV/cm from I-V measurement on a metal-insulator-metal (MIM) device. The low conductivity of the InP-MA QDs thin film is interpreted as due to the long interdistances among the dots governed by the MA molecules. Therefore, replacing the MA with thioacetic acid (TAA) by biphasic ligand exchange was conducted in order to obtain TAA capped InP QDs (InP-TAA). InP-TAA QDs were designed due to: 1) the TAA is very short molecule; 2) the thiolate groups on the surface of the InP-TAA QDs are expected to undergo condensation reaction upon thermal annealing which connects the QDs within the QD thin film through a very short linker -S-; and 3) TAA provides better passivation to the QDs both in the solution and thin film states which minimizing the effect of surface trapping states.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.6
• /
• pp.291-298
• /
• 1993

In order to substitute for porous nickel anode in Molten Carbonate Fuel Cell(MCFC), porous cermet elec-trode was fabricated with Ni and Ni-P coated ceramic powder. Ni and Ni-P were coated by electroless plat-ing method in the nickel solution containing of hydrazine and sodium hypophosphate as a reducing agent. The plating solution was stirred by air and mechanical agitator. Ultrasonic irradiation was applied to the plating bath to improved the effect of agitation and coating speed. Electorde was formed by pressing method and doc-tor blade method followed by sinterd at$ 800^{\circ}C$ for 6 hours in H2 environment. Anode performance test carried out by potentiodynamic polarization technique in the MCFC operating condition and 154-161mA/$\textrm{cm}^2$ as ob-tained as a anode current density at the+100mV overpotential.