• Journal of Adhesion and Interface
• /
• v.11 no.1
• /
• pp.35-40
• /
• 2010

In this study, solvent based polyurethane (PU) adhesives were prepared with the hydrocarbon resin and the acrylic modified hydrocarbon resin contents. The solvent based PU adhesive were increased with increasing tackifier concentration. The surface state of films showed good compatibility with increasing the PX-95 concentration but A-1100 series didn't present homogeneous phase more than 10 phr. Mechanical strength and peel strength were maximum at 5 phr tackifier concentration especially PX-95 series in solvent based PU adhesive.

• Journal of Adhesion and Interface
• /
• v.6 no.1
• /
• pp.11-18
• /
• 2005

The capsules were prepared from a phase change material (PCM) of octadecane as a core material and melamine formaldehyde resin as a shell material. The PCM capsule size was varied in the range of $3{\sim}25{\mu}m$. The core contents and sizes of the PCM capsule, were determined by DSC and SEM, respectively. An acrylic coating material which contains butyl acrylate (BA), methyl metacrylate (MMA) and acrylic acid (AA) were synthesized by emulsion polymerization. The films were prepared from the acrylic emulsion and PCM capsules which have various capsule sizes. From the results of SEM experiment, it was observed that the PCM capsules were well dispersed inside the film and the surface of the film became less rough when the PCM capsule size was small. The swelling ratio of the films were not significantly affected by the PCM capsule size. However, the tensile strength and elongation of the films were greatly decreased with increasing the PCM capsule size.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.53.2-53.2
• /
• 2010

In this study, we focused on our specialized electrode process for Si back-contact crystalline solar cell. It is different from other well-known back-contact cell process for thermal aspect and specialized process. In general, aluminum makes ohmic contact to the Si wafer and acts as a back surface reflector. And, silver is used for low series resistance metal grid lines. Aluminum was sputtered onto back side of wafer. Next, silver is directly patterned on the wafer by screen printing. The sputtered aluminum was removed by wet etching process after rear silver electrode was formed. In this process, the silver paste must have good printability, electrical property and adhesion strength, before and after the aluminum etching process. Silver paste also needs low temperature firing characteristics to reduce the thermal budget. So it was seriously collected by the products of several company of regarding low temperature firing (below $250^{\circ}C$) and aluminum etching endurance. First of all, silver pastes for etching selectivity were selected to evaluate as low temperature firing condition, electrical properties and adhesive strength. Using the nano- and micron-sized silver paste, so called hybrid type, made low temperature firing. So we could minimize the thermal budget in metallization process. Also the adhesion property greatly depended on the composition of paste, especially added resin and inorganic additives. In this paper, we will show that the metallization process of back-contact solar cell was realized as optimized nano-paste characteristics.

• Corrosion Science and Technology
• /
• v.15 no.3
• /
• pp.141-146
• /
• 2016

By using Ni-Cr and Co-Cr alloys, porcelain fused to metal (PFM) samples were prepared to examine the interface and the surface corrosion behavior. The potentiodynamic polarization analysis showed that the corrosion current density of Co-Cr alloy ($1.61{\times}10^{-6}A/cm^2$) was three times lower than that of Ni-Cr alloy ($4.83{\times}10^{-6}A/cm^2$) at room temperature. A dental prosthesis consisting of the porcelain fused to Ni-Cr alloy extracted from a patient after approximately four years of usage was examined to assess its resistance to corrosion. OM and SEM images of the metal part revealed a typical pitting corrosion. As compared to porcelain fused to Ni-Cr alloy having a thick layer (${\sim}10{\mu}m$) of oxide at the interface, a relatively thin oxide layer (less than $5{\mu}m$) was formed on Co-Cr alloy, indicating that the interface between Co-Cr alloy and porcelain may have a better adhesion strength than the interface between Ni-Cr alloy and porcelain.

• Journal of Adhesion and Interface
• /
• v.17 no.4
• /
• pp.149-154
• /
• 2016

In this study, natural polymer-based virus neutralizing agent was developed in an attempt to replace the conventional sterilization method for mammalian cell culture. A catechol conjugated heparin was synthesized by using EDC chemistry, and it show unique binding ability to virus which has heparin affinity (adenovirus, adeno-associated virus). To evaluate neutralization ability of catechol conjugated heparin, adeno-associated virus was used for test model, instead of using a pathogenic virus. The catechol conjugated heparin exhibited resistance to high concentration of salt and complete inactivation of adeno-associated virus. The result suggests that the catechol conjugated heparin, which is biocompatible and efficiency, may replace conventional sterilization method for mammalian cell culture.

• Journal of Adhesion and Interface
• /
• v.16 no.3
• /
• pp.116-121
• /
• 2015

In this study, octadecyltrichlorosilane (OTS) has been used to replace fluoro-silanes which are much more expensive than OTS. In order to improve the mechanical and adhesive properties of coating layers, inorganic binders were separately synthesized based on sol-gel reaction in acidic condition. Since the synthesized silica nanoparticles gave only nano-scaled roughness, superhydrophobicity is not well obtained. Here, we present a new simple approach by intentionally inducing particle aggregation in the solution which is controlled by adjusting solvent amount. With selecting suitable sizes of silica nanoparticles, superhydrophobic surfaces were obtained with increasing the amount of organic solvents after surface hydrophobization using OTS, and an extremely water-repellent behavior was observed with zero sliding angle. This superhydrophobicity was achived only for the dielectric constant lower than 25, regardless of the composition of solvent, meaning that the dielectric constant could be an excellent indicator for fabricating superhydrobic surfaces induced by particle aggregation in the solution.

• Applied Chemistry for Engineering
• /
• v.28 no.4
• /
• pp.432-436
• /
• 2017

Carbon blocks were prepared by compression molding process using the mixture of isotropic cokes and binder pitches, which were reformed with different ${\beta}$-resin contents from pyrolysis fuel oil. Physical and chemical properties and also thermal behavior of binder pitches were investigated through elemental analysis, FT-IR and thermogravimetric analysis, respectively. The adhesion of binder pitches to isotropic coke particles was evaluated from SEM images of the fracture surface of carbon blocks. From these results, it is shown that the adhesion between the cokes and binder was enhanced by increasing the ${\beta}$-resin content of binder pitches. The density of the carbon block after carbonization also increased from 1.325 to $1.383g/cm^3$ by increasing the ${\beta}$-resin content of binder pitches from 1.4 to 20.1%.

• Journal of Conservation Science
• /
• v.22
• /
• pp.77-86
• /
• 2008

The pre-treatment for conservation must be needed for the exhumed historic sites. So, the study of conservation and restoration of historical sites has progressed favorably with using various polymers for solving upper problems. The problems which should be essentially solved for conservation of the exhumed historic sites are, however, using reinforcing agents that don't impair their original forms and sorting reinforcing agents on the lines of the historic sites' soil. These agents should be able to use without the effect of outer environments like marsh, winter time or temperature. In this work, we synthesized Epoxy resin and Epoxy hardener for the restoration of historical sites. These products have very good tension strength and adhesion strength and various physical properties that the users want. Particularly, these epoxy with high viscosity have good separation of between Epoxy final product and Urethane pre-surface.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.64 no.3
• /
• pp.182-186
• /
• 2015

We investigated that effects of annealing ambient on the characteristics of functional nano thin film synthesized on glass substrate. The functional nano thin films were annealed by using rapid thermal annealing (RTA) equipment in vacuum, oxygen and nitrogen ambient, respectively. The hardness of the functional nano thin films were measured by a standard hardness testing method (ASTM D3363) such as a H-9H, F, HB and B-6B pencil (Mitsubishi, Japan). Also, the adhesion of the functional nano thin films were measured by a standard adhesion testing method (ASTM D3359) using scotch tape (3M, Korea). The contact angle of the functional nano thin films was measured by a contact angle analyzer (Phoenix 300 Touch, S.E.O.). The optical property of functional nano thin films was measured via UV-visible spectroscopy (S-3100, Scinco).

• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.416-422
• /
• 2013

PURPOSE. This study was performed to define attachment and growth behavior of osteoblast-like cells and evaluate the gene expression on zirconia compared to titanium. MATERIALS AND METHODS. MC3T3-E1 cells were cultured on (1) titanium and (2) zirconia discs. The tetrazolium-based colorimetric assay (MTT test) was used for examining the attachment of cells. Cellular morphology was examined by scanning electron microscopy (SEM) and alkaline phosphatase (ALP) activity was measured to evaluate the cell differentiation rate. Mann-Whitney test was used to assess the significance level of the differences between the experimental groups. cDNA microarray was used for comparing the 20215 gene expressions on titanium and zirconia. RESULTS. From the MTT assay, there was no significant difference between titanium and zirconia (P>.05). From the SEM image, after 4 hours of culture, cells on both discs were triangular or elongated in shape with formation of filopodia. After 24 hours of culture, cells on both discs were more flattened and well spread compared to 4 hours of culture. From the ALP activity assay, the optical density of E1 cells on titanium was slightly higher than that of E1 cells on zirconia but there was no significant difference (P>.05). Most of the genes related to cell adhesion showed similar expression level between titanium and zirconia. CONCLUSION. Zirconia showed comparable biological responses of osteoblast-like cells to titanium for a short time during cell culture period. Most of the genes related to cell adhesion and signal showed similar expression level between titanium and zirconia.