• 한국전기전자재료학회논문지
• /
• 제25권7호
• /
• pp.543-551
• /
• 2012

In this study, transparent conducting Al-doped Zinc Oxide (AZO) films with a thickness of 150 nm were prepared on corning glass substrate by the RF magnetron sputtering with using a Al-doped zinc oxide (AZO), ($Al_2O_3$: 2 wt%) target at room temperature. This study investigated the effect of rapid thermal annealing temperature and oxygen ambient on structural, electrical and optical properties of Al-doped zinc oxide (AZO) thin films. The films were annealed at temperatures ranging from 400 to $700^{\circ}C$ by using Rapid thermal equipment in oxygen ambient. The effect of RTA treatment on the structural properties were studied by x-ray diffraction and atomic force microscopy. It is observed that the Al-doped zinc oxide (AZO) thin film annealed at $500^{\circ}C$ at 5 minute oxygen ambient gas reveals the strongest XRD emission intensity and narrowest full width at half maximum among the temperature studied. The enhanced UV emission from the film annealed at $500^{\circ}C$ at 5 minute oxygen ambient gas is attributed to the improved crystalline quality of Al-doped zinc oxide (AZO) thin film due to the effective relaxation of residual compressive stress and achieving maximum grain size.

• Composites Research
• /
• 제15권6호
• /
• pp.8-15
• /
• 2002

본 실험에서는 2관능성 에폭시 수지(2EP)와 생분해성 poly(butylene succinate)(PBS) 블렌드의 유변학적 특성, 경화거동, 열안정성 그리고 기계적 특성을 살펴보았다. 유변학적 특성은 레오미터를 이용하여 등온 조건 하에서 검토하였고, 겔화시간과 경화 온도를 이용한 Arrhenius 방정식을 적용하여 가교 활성화 에너지($\textrm{E}_c$)를 구하였다. $\textrm{E}_c$는 2EP에 대한 PBS의 비율이 10 wt%로 증가함에 따라 증가하였다. DSC 측정 결과, 경화 활성화 에너지($\textrm{E}_a$)는 $\textrm{E}_c$와 유사만 경향을 나타내었는데 이는 2EP와 PBS 사이의 분자상호작용이 증가하였기 때문으로 사료된다. 그리고 열안정성과 관련하이 분해 활성화에너지($\textrm{E}_t$)는 Horowitz-Metzger식을 이용한 적분법을 사용하여 구하였는데 PBS 10 wt%에서 증가하였다. 그리고 20 wt% PBS일 때 가장 높은 임계응력세기 인자를 보이는데, 이는 2EP/PBS 블렌드 시스템의 파괴인성이 증가하였기 때문으로 사료된다.

• Composites Research
• /
• 제15권6호
• /
• pp.16-23
• /
• 2002

본 연구에서는 양극산화 처리에 따른 고강도 PAN계 탄소섬유의 표면 특성 변화가 기계적 계면 물성에 미치는 영향을 조사하였다. 탄소섬유의 표면성질은 산.염기도, SEM, XPS, 그리고 접촉각 측정을 통하여 알아보았으며, 복합재료의 기계적 계면 특성은 ILSS와 $K_{IC}$를 통하여 고찰하였다. 탄소섬유 표면의 산도와 $O_{ls}/C_{IC}$가 증가하였는데, 이는 산소관능기의 발달에 기인하고, 양극산화된 탄소섬유의 표면자유에너지의 증가는 극성요소의 증가에 기인하는 것으로 사료된다. ILSS와 $K_{IC}$ 같은 기계적 계면 성질은 양극산화로 향상되어졌는데, 이러한 결과는 좋은 젖음성이 최종 복합재료의 섬유와 에폭시 수지 매트릭스 사이의 계면결합력을 증가시기는 중요한 역할을 하기 때문으로 사료된다.

• Fisheries and Aquatic Sciences
• /
• 제18권1호
• /
• pp.51-56
• /
• 2015

A 8-week trial was conducted to evaluate the effects of photoperiod manipulation on the growth performance and hematological parameters of juvenile Caspian roach, Rutilus rutilus caspicus (average weight $1.46{\pm}0.12g$ mean${\pm}$SD) reared under five photoperiods (24 h Light, 24L; 18 h Light & 6 h Dark, 18L:6D; 12 h Light & 12 h Dark, 12L:12D; 6 h Light & 18 h Dark, 6L:18D; 24 h Dark, 24D) with constant light intensity 1,500 lx on the water surface. Triplicate of 20 fish were allocated into each of 15 fiberglass tanks of 50 L capacity and they were fed three times per day with the commercial feed (SFK, Co., Sari - Iran) contains 50.0% protein and 10.5% lipid. At the end of experimental period, final body weight, weight gain and specific growth rates of fish exposed to 24L were significantly higher than those of fish exposed to 12L:12D, 6L:18D and 24D (P < 0.05). Red blood cell and hemoglobin of fish exposed to 24L were significantly higher than those of fish exposed to 24D. No significant difference observed in hematocrit, white blood cell and plasma glucose among the different treatments groups. Therefore, these results demonstrated that the growth performance of juvenile Caspian roach can be significantly stimulated by using 24L and 18L:6D photoperiods without any measurable significant stress response such as plasma glucose concentration.

• 대한기계학회논문집
• /
• 제10권1호
• /
• pp.25-33
• /
• 1986

본 연구에서는 선단요소 해법의 방법을 토대로 소형컴퓨터를 위한 비선형 유한요소의 개발을 시도한 것이다. 주로 참조한 선단요소 해법의 프로그램은 Hinton과 Owen이 작성한 프로그램이며 원판메모리를 최대로 활용하여, 활동변수를 최소화 시키므로써, 실제 소형컴퓨터인 HP-3000II(512KB) 컴퓨터에서 총 자유도가 1000정도 되는 유한요소까지는, 해석이 가능하도록 만들어지게 되었다. 이와같이 완성된 프로그램의 응용성과 신뢰성을 검토해 보기 위해서 표준 CT 시편의 유한요소 를 작성하여(124 element, 428 node, 941 freedom) 크랙선단에 형성되는 소성역의 형상과 소성변형 크기를 수치적으로 추적하여 본 결과, 실험결과와 매우 잘 일치함을 볼 수 있어서 프로그램의 신뢰성을 확인 할 수 있었다. 이때 실험은 SUS-304스테인 레스강단의 소성역을 형성시킨다음, 재결정 방법에 의해 소성역의 형상과 크기를 가시 화 및 정량화 하여서 계산결과와 비교 하였다.

• 대한기계학회논문집A
• /
• 제25권4호
• /
• pp.592-601
• /
• 2001

Fiber reinforced metal laminates(FRMLs) are new types of hybrid materials. FRMLs consists of high strength metal(Al 5052-H34) and laminated fiber with structural adhesive bond. The mixture ratio effect of epoxy resin$.$curing agent$.$accelerator on the fatigue behavior of FRMLs was investigated in this study. The epoxy, diglycidylether of bisphenol A(DGEBA), was cured by methylene dianiline(MDA) with or without an accelerator(K-54). Eight different kinds of resin mixture ratios were selected for the test ; five kinds of FRMLs(1) and three others of FRMLs(2). The relationship between da/dN and ΔK with variation of resin mixture ratio was studied. FRMLs(1) and FRMLs(2) indicated approximately 2 times and 2.2 times more improved maximum bending strengths in comparison with those of Al 5052-H34. The resin mixture ratio <1:1> in case of FRMLs(1) indicated the maximum fatigue life, while the resin mixture ratio <1:1:0.2> in case of FRMLs(2) indicated the maximum fatigue life. As results, FRMLs(2) turned out to have more effective characteristics on the fatigue properties and the bending strength than those of FRMLs(1).

• 대한기계학회논문집A
• /
• 제24권3호
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.

• 대한기계학회논문집A
• /
• 제41권9호
• /
• pp.853-860
• /
• 2017

본 연구는 균열 발생 및 전파단계에서 하중모드 II의 영향을 평가하기 위해 피로균열 하한계 영역의 혼합모드 I+II 하중을 통해 실험적으로 평가하였다. 균열 발생단계(Stage I)에서는 혼합모드상태에서 하중작용 각도(${\theta}$)가 증가할수록 모드 II 영향으로 인하여 낮은 하중에서 균열이 발생하고, 균열 전파단계 (Stage II)에서는 균열전파 속도는 감소하였다. 다단계 하중작용 각도변화에 따른 하중모드 II영향은 균열전파단계 실험을 통해 평가하였다. 혼합모드 I+II 하중 작용 시 작용각도 ($0^{\circ}{\rightarrow}{\theta}{\rightarrow}60^{\circ}$) 증가에 따라 피로균열전파속도는 감소하였으며 늦게 발생한 균열에서도 마찬가지로 감소하였다. 작용각도가 ${\theta}{\geq}75^{\circ}$ 범위에서는 하중작용각도 증가에 따라 피로균열전파속도가 증가하고 피로수명이 감소하는 것을 확인하였다.

• 공업화학
• /
• 제24권5호
• /
• pp.476-482
• /
• 2013

본 연구에서는 탄소섬유 표면에 가해진 전기화학적 산화처리가 탄소섬유강화 극성화된 폴리프로필렌 기지 복합재료의 기계적 계면 물성에 미치는 영향을 알아보기 위해 전류밀도 변수에 따른 섬유표면의 변화를 관찰하였다. 표면처리 전후의 탄소섬유 표면특성은 주사전자현미경과 원자현미경, 적외선분광법, X선광전자분광법과 접촉각으로 분석하였다. 탄소섬유강화복합재의 기계적 계면특성은 임계응력세기인자를 측정하여 평가하였다. 실험 결과 전기화학적 산화처리 후 섬유 표면의 $O_{1s}$ 피크의 증가를 관찰할 수 있었고, 이는 섬유의 표면자유에너지의 증가를 유도하며, 탄소섬유와 폴리프로필렌의 계면 결합력이 증가된 것으로 판단된다. 결론적으로 탄소섬유강화복합재료의 기계적 물성은 탄소섬유와 극성 폴리프로필렌 기지와의 계면 강도조절을 통해 가능할 것으로 판단된다.

• 대한치과기공학회지
• /
• 제27권1호
• /
• pp.89-95
• /
• 2005

In the manufacture of ceramo-metal crown, difference of fracture strength according to the metal depth has been known to be an important influence on enough intensity and internal stress to endure an occlusion-pressure as well as aesthetics of rehabilitating similar colour such as natural teeth. Depth of ceramic material could be determined by that of metal in three groups: first case of thin depth, second case of thick depth, and third case of constant depth. For the enhancement of the fracture strength between metal and ceramic materials and aesthetic satisfaction, a study on the bonding force, fracture strength, and aesthetics have been required more. In this study, therefore metal coping were made in three groups of A, B and C by using both ceramic powder of Norithe and metal of Columbium, which have been used primarily in the market. A group was made in $0.2mm\times10mm\times10mm$, B group was made in $0.4mm\times10mm\times10mm$, and, C group was made in $0.8mm\times10mm\times10mm$, respectively. The number of metal coping in each group was 10, and total sample numbers used in this study were 30 metal copings. After these metal coping tissue were in the process of build-up in 1.5mm constant depth of porcelain, firing, and glazing, the fracture strength about each metal coping tissue was investigated using oil press. It was found that the average values of durable occlusion pressure for separation of ceramic material in the porcelain fused to metal crown (PFM) in the each group showed the increasing order of A group (30 bar), B group (42 bar), and C group (44 bar), respectively. Proper depth of metal coping in the PFM was considered to be 0.4mm in the B group because this metal size showed higher durable property to the occlusion pressure and better coupling strength in the ceramo-metal crown.