The influence of Cu and Ni on the ductile-brittle transition behavior of metastable austenitic Fe-18Cr-10Mn-N alloys with N contents below 0.5 wt.% was investigated in terms of austenite stability and microstructure. All the metastable austenitic Fe-18Cr-10Mn-N alloys exhibited a ductile-brittle transition behavior by unusual low-temperature brittle fracture, irrespective of Cu and/or Ni addition, and deformation-induced martensitic transformation occasionally occurred during Charpy impact testing at lower temperatures due to reduced austenite stability resulting from insufficient N content. The formation of deformation-induced martensite substantially increased the ductile-brittle transition temperature(DBTT) by deteriorating low-temperature toughness because the martensite was more brittle than the parent austenite phase beyond the energy absorbed during transformation, and its volume fraction was too small. On the other hand, the Cu addition to the metastable austenitic Fe-18Cr-10Mn-N alloy increased DBTT because the presence of ${\delta}$-ferrite had a negative effect on low-temperature toughness. However, the combined addition of Cu and Ni to the metastable austenitic Fe-18Cr-10Mn-N alloy decreased DBTT, compared to the sole addtion of Ni or Cu. This could be explained by the fact that the combined addition of Cu and Ni largely enhanced austenite stability, and suppressed the formation of deformation-induced martensite and ${\delta}$-ferrite in conjunction with the beneficial effect of Cu which may increase stacking fault energy, so that it allows cross-slip to occur and thus reduces the planarity of the deformation mechanism.

• 한국재료학회지
• /
• 제11권6호
• /
• pp.483-491
• /
• 2001

냉간가공된 Zr 합금을 $575^{\circ}C$에서 $650^{\circ}C$의 온도범위에서 유지시간을 달리하여 열처리하는 동안에 발생하는 회복 및 재결정 거동을 TEP(ThermoElectric Power)와 미소경도 분석을 통하여 연구하였다. 냉간가공과 열처리에 따른 합금의 회복 및 재결정온 격자결함, 공공, 전위, 적층결함 등이 소멸함에 따라 TEP가 증가하는 거동을 보였다. 이러한 TEP 분석은 미소경도 분석에 비해 재결정의 완료를 정확하게 예측할 수 있었으며, 특히, Zr-0.4Nb-xSn합금에서는 미소경도 분석으로 쉽게 구분하기 어려운 회복 및 재결정 단계를 명확하게 나타내었다. TBP와 미소경도 분석을 이용한 Zr-base합금의 재결정 거동에 따르면, Sn을 첨가하는 경우에 Sn이 치환형 고용체로 존재하기 때문에 이로 인한 응력장과 전위와의 상호작용에 기인하여 회복이 지연되는 현상을 가져왔으며, Nb함량을 증가시키는 경우에는 재결정 지연 효과가 미미하였으나, 석출물 형성에 의한 결정립 성장의 지연효과가 크게 나타났다.

• 대한금속재료학회지
• /
• 제50권9호
• /
• pp.645-651
• /
• 2012

This study investigated changes in phase fraction caused by the addition of Mo, as well as the subsequent behaviour of N and its effect on the mechanical properties of welded 24Cr-N duplex stainless steel weld metals. Filler metal was produced by fixing the contents of Cr, Ni, N, and Mn while adjusting the Mo content to 1.4, 2.5, 3.5 wt%. The delta ferrite fraction increased as the Mo content increased. In contrast, the ${\gamma}$ fraction decreased and changed from a round to an acicular shape. Secondary austenite (${\gamma}^{\prime}$) was observed in all specimens in a refined form, but it decreased as the Mo content increased to the extent that it was nearly impossible to find any secondary austenite at 3.5 wt% Mo. Both tensile and yield strengths increased with the addition of Mo. In contrast, the highest value of ductility was observed at 1.41 wt% Mo. At all temperatures, impact energy absorption showed the lowest value at 3.5 wt% Mo, at which the amount of ${\delta}$-ferrite was greatest. There was no significant temperature dependence of the impact energy absorption values for any of the specimens. As the fraction of ${\gamma}$ phase decreased, the amount of N stacked in the ${\gamma}$ phase increased. Consequently, the stacking fault energy decreased, while the hardness of ${\gamma}$ increased.

• Current Photovoltaic Research
• /
• 제8권4호
• /
• pp.114-119
• /
• 2020

In this study, Mitigation of Potential-induced degradation (PID) for PERC solar cells using SiO2 Structure of ARC layer. The conventional PID test was conducted with a cell-level test based on the IEC-62804 test standard, but a copper PID test device was manufactured to increase the PID detection rate. The accelerated aging test was conducted by maintaining 96 hours with a potential difference of 1000 V at a temperature of 60℃. As a result, the PERC solar cell of SiO2-Free ARC structure decreased 22.11% compared to the initial efficiency, and the PERC solar cell of the Upper-SiO2 ARC structure decreased 30.78% of the initial efficiency and the PID reliability was not good. However, the PERC solar cell with the lower-SiO2 ARC structure reduced only 2.44%, effectively mitigating the degradation of PID. Na+ ions in the cover glass generate PID on the surface of the PERC solar cell. In order to prevent PID, the structure of SiNx and SiO2 thin films of the ARC layer is important. SiO2 thin film must be deposited on bottom of ARC layer and the surface of the PERC solar cell N-type emitter to prevent surface recombination and stacking fault defects of the PERC solar cell and mitigated PID degradation.

• 한국산학기술학회논문지
• /
• 제21권4호
• /
• pp.596-601
• /
• 2020

SiC는 큰 밴드 갭 에너지를 갖고, 불순물 도핑에 의해 p형 및 n형 전도의 제어가 용이해서 고온용 전자부품소재로 활용이 가능한 재료이다. 따라서 국내 부존 규조토의 고부가가치 활용을 위해 정제 규조토로부터 합성한 β-SiC 분말의 열전물성에 대해 조사하였다. 정제한 규조토 중의 SiO₂ 성분을 카본블랙으로 환원 탄화 반응시켜 β-SiC 분말을 합성하고, 잔존하는 불순물(Fe, Ca 등)을 제거하기 위해서 산처리 공정을 행하였다. 분말의 성형체를 질소 분위기 2000℃에서 1~5시간 소결시켜 n형 SiC 반도체를 제작하였다. 소결시간이 길어짐에 따라 캐리어 농도의 증가 및 입자간의 연결성 향상에 의해 도전율이 향상되었다. 합성 및 산처리한 β-SiC 분말에 내재하는 억셉터형 불순물(Al 등)로 인한 캐리어 보상효과가 도전율 향상에 저해하는 요인으로 나타났다. 소결시간이 증가함에 따라 입자 및 결정 성장과 함께 적층 결함 밀도의 감소에 의해 Seebeck 계수의 절대값이 증가하였다. 본 연구에서의 열전 변환 효율을 반영하는 power factor는 상용 고순도 β-SiC 분말로 제작한 다공질 SiC 반도체에 비해 다소 작게 나타났지만, 산처리 공정을 정밀하게 제어하면 열전물성은 보다 향상될 것으로 판단된다.

• 한국결정성장학회지
• /
• 제25권4호
• /
• pp.127-134
• /
• 2015

AlN 단결정은 넓은 밴드갭(6.2 eV), 높은 열 전도도($285W/m{\cdot}K$), 높은 비저항(${\geq}10^{14}{\Omega}{\cdot}cm$), 그리고 높은 기계적 강도와 같은 장점들 때문에 차세대 반도체 적용을 위한 많은 흥미를 끈다. 벌크 AlN 단결정 또는 박막 템플릿(template)들은 주로 PVT(Physical vapor transport)법, 플럭스(flux)법, 용액 성장(solution growth)법, 그리고 증기 액상 증착(HVPE)법에 의해 성장된다. 단결정이 성장하는 동안에 발생하는 결함들 때문에 상업적으로 어려움을 갖게 된 이후로 결함들 분석을 통한 결정 품질 향상은 필수적이다. 격자결함 밀도(EPD)분석은 AlN 표면에 입자간 방위차와 결함이 존재하고 있는 것을 보여준다. 투과전자현미경(TEM)과 전자후방산란회절(EBSD)분석은 전체적인 결정 퀄리티와 다양한 결함의 종류들을 연구하는데 사용된다. 투과전자현미경(TEM)관찰로 AlN의 형태가 적층 결함, 전위, 이차상 등에 의해 크게 영향을 받는 것을 알 수 있었다. 또한 전자후방산란회절(EBSD)분석은 전위의 생성을 유도하는 성장 결함으로서 AlN의 zinc blende 폴리모프(polymorph)가 존재하고 있는 것을 나타내고 있었다.

• 지구물리
• /
• 제2권1호
• /
• pp.39-44
• /
• 1999

심부 지층구조 연구를 위해 획득된 다중채널 반사파 자료를 재처리하여 제4기 단층 및 해저면 부근 천연 가스층 탐지를 위한 고해상도 단면도를 작성하였다. 사용된 자료는 한국해양연구소에서 동해해역 퇴적분지 지각구조 연구를 목적으로 1994년부터 1997년까지 기록한 총 1900 km의 다중채널 반사파 자료 중 근거리 12채널 자료이다. 고해상도용 재처리과정은 자료복사 및 자료편집, 참진폭 회수, 공심점 분류, 초기 뮤트, 중합전 디컨볼루션, 대역필터, 중합, 고주파 통과필터, 중합후 디컨볼루션, 구조보정, 자동이득조절 등의 순서로 이루어지며, 이 중 예측 디컨볼루션, 고주파 통과필터, 짧은 창길이의 자동이득조절 적용 등이 해상도를 높이는데 가장 중요한 처리단계이다. 해저면 하부 약 1초 정도까지의 지층을 대상으로 처리된 중합 및 구조보정 단면상에는 총 200개 이상의 제4기 단층이 인지되며, 이들 대부분은 대륙사면과 울릉분지 경계부에 밀집되어 나타나지만 분지 내에도 상당수 존재한다. 이들 단층중 상당수는 기반암과 제3기 퇴적층에 발달된 단층의 재활성화와 화산활동을 포함한 지구조 운동에 의해 형성된 것으로 추정되며 동해가 구조적으로 다소 불안정된 상태에 놓여 있을 가능성을 지시한다. 또한 3개소 이상에서 발견된 천부 가스층의 존재는 시추나 해저 케이블 및 파이프라인 등 해양구조물 설치시 반드시 경계해야 할 위험 요소가 존재하고 있음을 보여준다. 이러한 천부 가스층의 발견은 최근 관심이 고조되고 있는 가스수화물의 근원 물질이 동해에 존재한다는 긍정적인 면이 있으나, 해저면에 평행한 반사면 등 가스수화물의 전형적인 탄성파 특징은 울릉분지 서부 대륙사면 및 중앙부의 재처리 단면상에서는 발견되지 않는다.