• Journal of Welding and Joining
• /
• v.17 no.1
• /
• pp.124-132
• /
• 1999

Thermal fatigue strength of the solder joints is the most critical issue for TSOP(Thin Small Outline Package) because the leads of this package are extremely short and thermal deformation cannot be absorbed by the deflection of the lead. And the TSOP body can be subject to early fatigue failures in thermal cycle environments. This paper was discussed distribution of thermal stresses at near the joint between silicon chip and die pad and investigated their reliability of solder joints of TSOP with 42 alloy clad lead frame on printed circuit board through FEM and 3 different thermal cycling tests. It has been found that the stress concentration around the encapsulated edge structure for internal crack between the silicon chip and Cu alloy die pad. And using 42 alloy clad, The reliability of TSOP body was improved. In case of using 42 alloy clad die pad(t=0.03mm). $$\sigma$_{VMmax}$ is 69Mpa. It is showed that 15% improvement of the strength in the TSOP body in comparison with using Cu alloy die pad $($\sigma$_{VMmax}$=81MPa). In solder joint of TSOP, the maximum equivalent plastic strain and Von Mises stress concentrate on the heel of solder fillet and crack was initiated in it's region and propagated through the interface between lead and solder. Finally, the modified Manson-Coffin equation and relationship of the ratio of $N_{f}$ to nest(η) and cumulative fracture probability(f) with respect to the deviations of the 50% fracture probability life $(N_{f 50%})$ were achieved.

• Journal of Welding and Joining
• /
• v.13 no.2
• /
• pp.82-95
• /
• 1995

This paper discusses distribution of thermal stress, strain at near the joint and investigates the reliability of solder joints of electronic devices on a printed circuit board. As Electronic devices are composed of different materials, thermal stresses generate at near the interface, such as solder joints and interface between lC device and lead frame pad due to the differences of thermal expansion coefficients, As results of thermal stress, strain, micro crack often occurs thermal fatigue fracture at the interface of different materials, The initiation and propagation of micro crack depend on the environmental conditions, such as storage temperature and thermal cycling. Finally, this paper experimentally shows a way to suppress micro cracks by using Fe-Ni alloy clad lead frame, and investigates crack and thermal fatigue fracture of TSOP(Thin small outline package) type on printed circuit board.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.333-337
• /
• 2008

This study investigates crack propagation behavior of Sn-3.0Ag-0.5Cu solder under pull-push loading conditions. Fatigue Crack Growth (FCG) tests were conducted on Center Cracked Plate (CCP) specimens in fast-fast (pp) strain waveform. The fast-slow (pc), slow-fast (cp) and slow-slow (cc) strain waveforms were also used to study the effect of strain rates. The crack propagation rates for the four strain waveforms were correlated with J-integral range and a scatter band of factor 4 was found. The crack growth rates for the pc waveform was highest, followed by cp, cc and then pp waveforms.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.21-23
• /
• 2006

The microstructural investigation and thermo-mechanical reliability evaluation of the Sn-3.0Ag-0.5Cu solder bumped flip chip package were carried out during the thermal shock test of the package. In the initial reaction, the reaction product between the solder and Cu mini bump of chip side was Cu6Sn5 layer, while the two phases which were (Cu,Ni)6Sn5 and (Ni,Cu)3Sn4 were formed between the solder and Ni-P layer of the package side. The cracks were occurred at the corner solder joints after the thermal shocks of 400 cycles. The primary failure mechanism of the solder joints in this type of package was confirmed to be thermally activated solder fatigue failure.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.222-222
• /
• 2007

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.09a
• /
• pp.1-26
• /
• 2004

The implementation of Pb-free solder technology is making good progress in electronic industry. Further understanding on fundamental issues on Pb-free solders/processes is required to reduce reliability risk factors of Pb-free solder joints. Several reliability issues including thermal fatigue, impact reliability, IMC growth, spalling, void formation are reviewed for Pb-free solder joints. Several applications of Pb-free technology are discussed, such as Pb-free, CBGA, CuCGA, flip chips, and wafer bumping by IMS.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.07a
• /
• pp.127-133
• /
• 2001

Package reliability test was conducted to investigate the effect of solder composition on ball fatigue strength. The specimens are first assembled using eutectic Composition S $n_{62}$P $b_{36}$A $g_2$, S $n_{63}$P $b_{34.5}$A $g_2$S $b_{0.5}$ solder and Pre-conditioned at MRT Lv 2a and then conducted under Temperature Cycle test(TC). For each case, the ball shear strength is obtained and micro structure photos are taken. SEM and EDX are used to analyze failure mechanism. The degradation of shear strength of solder balls after reliability test is discussed.d.

• Journal of Welding and Joining
• /
• v.20 no.2
• /
• pp.90-94
• /
• 2002

FC-BGA has advantages over other interconnection methods including high I/O counts, better electrical performance, high throughput, and low profile. But, FC-BGA has a lot of reliability issues. The 2nd level solder joint reliability of the FC-BGA with large chip on laminate substrate was studied in this paper. The purpose of this study is to discuss solder joint failures of 2nd level thermal cycling test. This work has been done to understand the influence of the structure of package, the properties of underfill, the properties and thickness of bismaleimide tiazine substrate and the temperature range of thermal cycling on 2nd level solder joint reliability. The increase of bismaleimide tiazine substrate thickness applied to low modulus underfill was improve of solder joint reliability. The resistance of solder ball fatigue was increased solder ball size in the solder joints of FC-BGA.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.439-449
• /
• 2002

This paper reviews our recent research works on the interconnection technologies in electronic packaging and assembly. At the aspect of advanced joining methods, laser-ultrasonic fluxless soldering technology was proposed. The characteristic of this technology is that the oxide film was removed through the vibration excitated by high frequency laser change in the molten solder droplet. Application researches of laser soldering technology on solder bumping of BGA packages were carried out. Furthermore, interfacial reaction between SnPb eutectic solder and Au/Ni/Cu pad during laser reflow was analyzed. At the aspect of soldered joints' reliability, the system for predicting and analyzing SMT solder joint shape and reliability(PSAR) has been designed. Optimization design method of soldered joints' structure was brought forward after the investigation of fatigue failure of RC chip devices and BGA packages under temperature cyclic conditions with FEM analysis and experimental study. At the aspect of solder alloy design, alloy design method based on quantum was proposed. The macroproperties such as melting point, wettability and strength were described by the electron parameters. In this way, a great deal of the experimental investigations was replaced, so as to realize the design and research of any kinds of solder alloys with low cost and high efficiency.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.3
• /
• pp.31-36
• /
• 2002

The 2nd level solder joint reliability of 153 FC-BGA for high-speed SRAM (Static Random Access Memory) with the large chip on laminate substrate comparing to PBGA(Plastic Ball Grid Array) was studied in this paper. This work has been done to understand an influence as the mounting with single side or double sides, structure of package, properties of underfill, properties and thickness of substrate and size of solder ball on the thermal cycling test. It was confirmed that thickness of BT(bismaleimide tiazine) substrate increased from 0.95 mm to 1.20 mm and solder joint fatigue life improved about 30% in the underfill with the low young's modulus. And resistance against the solder ball crack became twice with an increase of the solder ball size from 0.76 mm to 0.89 mm in solder joints.