• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.665-668
• /
• 1999

Thin films of Pb(Zr,Ti)O$_3$ were fabricated by means of the sol-gel spin-coating method and the multi-coating of eight coating numbers. The thin films were dried on the temperature range of 250 ~ 400($^{\circ}C$), whenever the specimens were dried after each coating Processing. The fabricated ferroelectric thin films of lead zirconate titanate(PZT) were treated with the rapid thermal annealing(RTA) at 650($^{\circ}C$),or 3(min), and direct insertion thermal annealing(DITA) at 650($^{\circ}C$), for 30(min). The measured properties of dielectric thin films were following: The good results of dielectric properties were shown by the RTA specimen. The saturation polarization(Ps), remanent polarization(Pr), coercive field (Ec), dielectric constant and dielectric loss factor of the RTA specimen were estimated to be about 27.1[ $\mu$ C/$\textrm{cm}^2$], 13.7[ $\mu$ C/$\textrm{cm}^2$], 55.6(kV/cm), 786 and 6.4(%) respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.1
• /
• pp.55-60
• /
• 2018

Transparent conductive thin films (TCFs) are essential materials for solar cells, organic light-emitting diodes, and display panels. Indium tin oxide (ITO) is one of the most widely used commercial materials to create TCFs'; however, new materials that can possibly replace ITO at a lower cost and/or those possessing mechanical flexibility are urgently needed. Silver nanowire (AgNW) is one of those promising materials, as it is less expensive and possesses superior mechanical flexibility as compared to ITO. We used AgNW and sol-gel ZnO to fabricate composite thin films by spray coating. We propose two spray-coating methods: the 'metal-organic chemical vapor deposition (MOCVD)/AgNW' method and the Mixture method. These two methods are expected to be commercialized for high-quality and low-cost products, respectively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.911-919
• /
• 1994

As the study for preparation of single-layer anti-reflective coating on glass, the conditions of synthesis of sol for coating and of reproducible coating procedure were investigated. In case of water-based sol, coating was impossible because of poor wettability of sol. The Substitution of solvent with ethanol improved the wettability of sol on the glass surface, and optimum amount of ethanol for substitution was 70 vol%. Maximum specific surface area and total pore volume of water-based sol were 268.7$m^2$/g and 0.315 cc/g, but after substitution, those values increased to 404.1 $m^2$/g and 0.376 cc/g, respectively. The upper limit withdrawl speed of coating in order to get clean coated films without aggregations or stains was 7 cm/min. In case of addition of 0.1 mol HNO3 and substitution with 70 vol% ethanol and heat-treatment at 40$0^{\circ}C$ for 1 hour, thin film with thickness of 94 nm was obtained at withdrawl speed of 4 cm/min. The thickness of thin film was independent of drying time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05b
• /
• pp.33-36
• /
• 2005

Colloidal Silica(CS)/silane sol solutions were prepared in variation with synthesizing parameters such as ratio of CS to silane and reaction time. In the case of LHSA CS/tetramethoxysilane(TMOS)/methyltrimethoxysilane(MTMS) CS/silane sol, coating film had stable contact angle with increasing reaction time excepting for 48hours. Also, the LHSA CS/TMOS/MTMS coating film had more enhanced flat surface with increasing the amount of MTMS and increasing reaction time. In the case of thermal stability, thermal dissociation of LHSA CS/MTMS sol did not occur up to $550^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.444-447
• /
• 2005

In this study, $Hydroxyapatite+TiO_2(HAp+TiO_2)$ composite sol coatings on Cp-Ti substrates were deposited by using a sol-gel derived precursor. Prior to hydroxyapatite coating, the samples were micropolished and divided into three sets. The first set was coated with hydroxyapatite (HAp) directly on Cp-Ti. The second set was first coated with intermediate titania layer and then coated with HAp. The third set samples were coated with $HAp+TiO_2$ (50:50) composite sol. Each samples were predried at $200^{\circ}C$, and heat treated at $600^{\circ}C$. The formation of hydroxyapatite has been confirmed by XRD analyses and the substrate material was found to be oxidized with negligible amount of CaO in the coating. The NaOH treated samples showed the presence of rutile crystal. The SEM studies revealed surface morphologies of each samples. $HAp+TiO_2$ composite sol coating layer was found to be smooth. The bonding strength of each samples were calculated using pull out tests. The bonding strength of the $HAp+TiO_2$ composite sol coating on substrate was 29.35MPa.

• Korean Journal of Optics and Photonics
• /
• v.11 no.4
• /
• pp.255-260
• /
• 2000

We report that the crack-free organic-inorganic hybrid silica thin films were fabricated by sol-gel process using organometallic compounds as a precursor and that we have established very reproducible fabrication condition with systematic investigation of thickness and refractive index variations for various control parameters, such as, coating type, coating speed, chemical composition, prebake and postbake temperature. Additionally, we measured and compared the change of optical property with the UV exposure dose for three different kinds of photoinitiators. Furthermore, the fabrication of Ix4 MMI optical power splitter using the sol-gel thin film provides the possibility of various applications to the optical waveguide devices. vices.

• Journal of Electrical Engineering and Technology
• /
• v.8 no.1
• /
• pp.163-167
• /
• 2013

Aluminum doped zinc oxide (AZO) thin films have been prepared on the glass substrates (Corning 1737) by sol-gel dip-coating method employing zinc acetate and aluminum chloride hexahydrate for the transparent conducting oxide (TCO) applications. 1 at% Al was doped to the ZnO thin films. The effects of post-heating temperature on the crystallization, optical and electrical properties of the AZO films have been investigated. Experimental results showed that post-heating temperature affected the microstructure, electrical resistance, and optical transmittance of the AZO films. From the X-ray diffraction analysis, all films have hexagonal wurtzite crystal structure. Optical transmittance spectra of the AZO films exhibited transmittance higher than about 80% within the visible wavelength region and the optical direct band gap ($E_g$) of these films was increased with increasing post-heating temperature. A minimum resistivity of $2.5{\times}10^{-3}{\Omega}cm$ was observed at $650^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.83-86
• /
• 1998

Ferroelectric PZT(40/67)/PZT(60/40)heterolayered thin films were Prepared by the alkoxide-based Sol-Gel method. PZT(40/60) and PZT(60/40) stock solutions were made and spin-coated on the P7Ti/Si02/Si substrate alternately. These PZT(40/60) and PZT(60/40) films were dried at 300$^{\circ}C$ for 30min to remove organic materials and were sintered at 650$^{\circ}C$ for 1 hour to crystalize into a perovskite structure. The coating and heating procedure were repeated 6 times to form heterolayered films. Increasing the number of coating, coercive field was decreased. The relative dielectric constant, loss, remanent polarization and coercive field of the 4-coated PZT heterolayered were 1200, 4.1[%], 30.794[${\mu}$C/㎡] and 147.22[kV/cm], respectively.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.338-344
• /
• 2000

Grain boundary chemistry and electrical characteristics of polycrystalline BaTiO3 ceramics, which were prepared with sol-gel surface-coated semiconducting powders, were investigated. Mn ions were coated on the powder surface by sol-gel coating-techniques. The additives coated on the surface of the powders were observed to be present near the grain boundaries of the ceramics. The ceramics exhibit the PTCR characteristics with a resistivity jump ratio(Pmax/Pmin) of about 2$\times$103. With raising the temperature from room temprature to 20$0^{\circ}C$, the oxidation state of the Mn ions varied from Mn3+ to Mn2+ in the coating layers. Near the grain boundaries an excessive negative charge layer of about 20nm was formed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.192-195
• /
• 2000

Antimony doped tin oxyde thin films have been deposited by sol-gel method using non-alkoxide precursor SnCl$_2$$.$2H$_2$O as host and SbC1$_3$ as dopant material. Using spin coating method, thin films of thickness up to 200nm have been uniformly deposited on Corning 1737F non-alkali glass substrates. Effect of Sb doping concentration and heat treatment on electrical and optical properties was investigated. Heat treatment was performed at the temperature from 350$^{\circ}C$ to 650$^{\circ}C$ in flowing O$_2$. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition and firing condition.