• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.2 s.43
• /
• pp.35-40
• /
• 2007

The pull strength and fracture mechanism were investigated to evaluate the reliability and compatibility of Sn-8Zn-3Bi joints, the solder paste on lead and lead-free plating under thermal shock conditions. At the Sn-8Zn-3Bi solder joint, no crack initiation was observed during thermal shock test. After 1000 cycles, the strength of the solder joint decreased not sharply but reduced gradually compared with initial conditions. The decrement of strength was affected by ${\gamma}-Cu_5Zn_8$ IMC growth which caused the IMC fracture on the fracture surface and a change in fracture mode and initial crack point. Clearly, the Sn-8Zn-3Bi solder shows good reliability properties and compatibility with lead-free plated Cu LF under thermal shock temperatures between 248K and 423K.

• Journal of Korea Foundry Society
• /
• v.20 no.2
• /
• pp.116-121
• /
• 2000

Interfacial reaction and mechanical properties between Sn-Zn-X ternary alloys(X : 3wt.%In, 4wt.%Bi) and Cu-substrate were studied. Cu/solder joints were subjected to aging treatments for up to 50days to see interfacial reaction at $100^{\circ}C$ and then were examined changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. Cu/solder joints were aged to 30days and then loaded to failure at cross head speed of 0.3 mm $min^{-1}$ to measure tensile strength. According to the results of the solderability test, additions of In and Bi in the Sn-9wt.%Zn solder improve the wetting characteristics of the alloy and lower the melting temperature. Through the EDS and XRD analysis of Cu/Sn-9wt.%Zn solder joint, it was concluded that the intermetallic compound was the ${\gamma}-Cu_5Zn_8$ phase. Cu-Zn intermetallics at Cu/solder interfaces played an important role in both the microstructure evolution and failure of solder joints. Cu/solder joint strength was decreased by aging treatment, and those phenomenon was closely related to the thickening of intermetallic layer at Cu/solder joints.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.481-486
• /
• 2002

We have investigated the effects of plating materials for Cu lead (Sn-lOPb, AwPdJNi, Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu) on properties of QFP joints using a Sn-8Zn-3Bi solder. The results were compared with the joints using Sn-3. 5Ag-0. 7Cu and Sn-37Pb solders. As a result, the joints with the Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu plated Cu lead had the reliability comparable to those of the Sn-3.5Ag-0.7Cu and Sn-37Pb soldered joints with respect to the joint strength after the high temperature holding tests at 348K to 423k. In particular, the joint with the Sn-3.5Ag plated Cu lead had the best reliability. This is caused by the low growth rate of a Cu-Sn interfacial reaction layer that degrades the joint strength of the soldered joints. Consequently, the Sn-3.5Ag plating was found to be most feasible plating for the Sn-8Zn-3Bi soldered joint.

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.61-62
• /
• 1999

• Journal of Welding and Joining
• /
• v.23 no.3
• /
• pp.61-67
• /
• 2005

Since lead (Pb)-free solders for electronics have higher melting points than that of eutectic Sn-Pb solder, they need higher soldering temperatures. In order to decrease the soldering temperature we tried to coat Sn-Bi layer on $Sn-3.5\%Ag$ solder by electroplating, which applies the mechanism of transient liquid phase bonding to soldering. During heating Bi will diffuse into the $Sn-3.5\%Ag$ solder and this results in decreasing soldering temperature. As bonding samples, the 1608 capacitor electroplated with Sn, and PCB, its surface was finished with electroless-plated Ni/Au, were selected. The $Sn-95.7\%Bi$ coated Sn-3.5Ag was supplied as a solder between the capacitor and PCB land. The samples were reflowed at $220^{\circ}C$, which was lower than that of normal reflow temperature, $240\~250^{\circ}C$, for the Pb-free. As experimental result, the joint of $Sn-95.7\%Bi$ coated Sn-3.5Ag showed high shear strength. In the as-reflowed state, the shear strength of the coated solder showed 58.8N, whereas those of commercial ones were 37.2N (Sn-37Pb), 31.4N (Sn-3Ag-0.5Cu), and 40.2N (Sn-8Zn-3Bi). After thermal shock of 1000 cycles between $-40^{\circ}C$ and $+125^{\circ}C$, shear strength of the coated solder showed 56.8N, whereas the previous commercial solders were in the range of 32.3N and 45.1N. As the microstructures, in the solder $Ag_3Sn$ intermetallic compound (IMC), and along the bonded interface $Ni_3Sn_4$ IMC were observed.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.228-230
• /
• 2005

Sn-8wt%Zn-3wt%Bi (이하, Sn-8Zn-3Bi) 솔더의 장기 신뢰성을 평가하기 위하여 고용고습시험을 행하였다. 고온 고습 시험은 $85^{\circ}C$/85RH 조건에서 1000 시간 동안 하였다. 접합 기판으로는 각각 OSP (Organic Solderability Preservative), Sn 그리고 Ni/Au 처리를 한 PCB(Printed Circuit Board) 패드를 사용하였다. 접합에 사용한 부품은 1608Chip 으로 MLCC(Multi Layer Ceramic Capacitor 이하, 1608C) 와 Chip Resister(이하, 1608R)을 사용하였으며, 이 두 부품의 전극부위에 Sn-10wt%Pb(이하 Sn-l0PB), Sn을 각각 도금하였다. 솔더링 후 1608C 와 1608R의 전단 접합 강도와 솔더링부에서 Zn상의 변화를 관찰하였다. 측정결과, Sn-8Zn-3Bi 솔더의 초기 전단 접합 강도는 기판의 표면처리에 상관없이 약 40N 이었다. 그러나 고온 고습 시험 1000 시간 후에는 기판의 표면처리에 상관없이 약 30N 까지 감소하였다. 하지만 이는 reference인 Sn-37Pb 솔더의 강도값과 거의 유사하며, 이는 Sn-8Bi-3Zn 솔더의 고온 고습 시험 후 전단강도 특성은 기존 유연솔더와 비교하여 동등이상이라고 평가할 수 있다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.11a
• /
• pp.33-33
• /
• 2004

• Journal of Welding and Joining
• /
• v.23 no.4
• /
• pp.34-40
• /
• 2005

There have been numerous approaches to examine the bonding strengths of solder joints. However, despite the technical and practical limitations, the precedent test methods such as the ball shear and ball pull tests are being used in industrial applications. In this study, the optimum jaw pressure with the modified protrusion jaw was introduced in order to obtain higher successful rate f3r ball pull testing. Furthermore, the pull strengths and fracture modes of Sn-8Zn-3Bi, Sn-4Ag-0.7Cu, and Sn-37Pb eutectic solder after isothermal aging tests ($100^{\circ}C,\;150^{\circ}C$), were evaluated with the protrusion jaw. The pull strength-displacement hysteresis curves and fracture surfaces were carefully investigated to evaluate the correlation between the pull strengths and the fracture modes of each solder. In conclusion, it is verified that Au-Zn IMCs (Intermetallic Compounds) have a detrimental effect on the pull strengths and changed fracture modes of Sn-8Zn-3Bi solder. Meanwhile, the microstructure transformation influences the degradation of pull strengths of Sn-4Ag-0.7Cu and Sn-37Pb solders.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.225-227
• /
• 2005

Sn-8wt%Zn-3wt%Bi (이하, Sn-8Zn-3Bi) 솔더의 장기 신뢰성을 평가하기 위하여 열 충격 시험을 행하였다. 열 충격 시험은 $-40^{\circ}C$에서 $80^{\circ}C$범위에서 1000 사이클 동안 하였다. 접합 기판으로는 각각 OSP(Organic Solderability Preservative), Sn 그리고 Ni/Au 처리를 한 PCB(Printed Circuit Board) 패드를 사용하였다. 접합에 사용한 부품은 1608 Chip(Multi Layer Chip Capacitor, Chip Resistor) 으로 전극 부위에 Sn-37wt%Pb, Sn 도금하여 사용하였다. 솔더링 후 1608 Chip의 전단 강도와 솔더링부에서 미세조직 및 IMC(Inter Metallic Compound) 변화를 관찰하였다. 측정결과, Sn-8Zn-3Bi 솔더의 초기 전단 강도는 기판의 표면처리에 상관없이 약 40N 이상이었다. 그리고 열충격 시험 1000 사이클 후에는 모든 기판에서 2N 정도 약간의 강도 저하를 보였다.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.28-30
• /
• 2005