• Transactions of the Korean Society of Automotive Engineers
• /
• v.22 no.3
• /
• pp.90-96
• /
• 2014

The conventional SnPb solders were widely used for several decades in the electronic packing system due to the superior mechanical properties such as low melting point, better wettavility and good mechanical fatigue. However, in recent years, owing to adverse effect on the human health and environment, conventional SnPb solders have been replaced by Lead-free solders. In this research, the shear punch(SP) test of Sn-4Ag-(Cu)/Ni pad was performed. Pb-free solder alloys which are the environmentally friendly of the electronic components were performed at $150^{\circ}C$ for 100hr~1000hr to artificial aging processing. In order to evaluate the mechanical properties of solder joints, the SP test was conducted at $30^{\circ}C$ and $50^{\circ}C$. As a result, the maximum shear strength of almost the whole specimens was decreased with the increase in aging time and temperature of SP test. The mechanical properties of Sn-4Ag-0.5Cu solder were most excellent in all Pb-free solder which were produced by the SP test at $30^{\circ}C$.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.20 no.2
• /
• pp.187-192
• /
• 2011

UBM(Under Bump Metallurgy) is very important for successful realization of Flip-Chip technology. In this study, it is investigated the interfacial reactions between various Sn-Ag solder alloys and Ni-P/Au UBM and Cu plate finish. It is also evaluated the shear strength by using the micro shear-punch test method for Sn-37Pb alloy, binary and ternary alloys of environment-friendly Pb-free solder alloys which are applied in the electronic packages. In terms of interfacial microstructure, the Pb-free solder joints have thicker IMCs than the Sn-Pb solder joints. The thickness of IMC is related to Reflow time. The IMC has been observed to grow with the increase in Reflow time. As a result of the shear test, in case of Max. shear strength, Pb-free solder showed the highest strength value and Sn-37Pb showed the lowest strength value 10 be generally condition of Reflow time.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.21 no.3
• /
• pp.134-141
• /
• 2013

Reflow soldering process is essential in electronic package. Reflow process for a long time results from the decrease of reliability because IMC is formed excessively. Solder alloys of Sn-37Pb and Sn-Ag with different kinds of Cu contents (0, 0.5 and 1 wt.%) as compared with Ni and Cu plate joints are investigated according to varying reflow time. The interfaces of solder joints are observed to analyze IMC (intermetallic compound) growth rate by scanning electron microscope (SEM). Shear test is also performed by using SP (Share-Punch) tester. The test results are compared with the solder joints of two different plates (Ni and Cu plate). $Cu_6Sn_5$ IMCs are formed on Cu plate interfaces after reflows in all samples. Ni3Sn4 and $(Cu,Ni)_6Sn_5$ IMCs are also formed on Ni plate interfaces. The IMC layer forms are affected by reflow time and contents of solder alloy. These results show that mechanical strength of solder joints strongly depends on thickness and shape of IMC.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.87-105
• /
• 1996

The purpose of this study is to investigate the characteristics of the compositions and phases of amalgam alloys and amalgams by using EMPA and X-ray diffractometer. Each specimen was made from Caulk Fine Cut Clow copper lathe cut amalgam), Caulk Spherical (low copper spherical amalgam), Tytin (high copper unicorn position amalgam), Dispersally (high copper admixed amalgam) and Valiant (Palladium enriched amalgam). For preparing amalgam alloys, Tytin and Valiant were used as powder forms and the others were used as tablet forms after being polished with polishing machine. For preparing amalgams, each amalgam alloy and Hg were measured, and triturated by mechanical amalgamater according to user's instructions. After triturating, the triturated mass was inserted to cylindrical metal mold and simultaneously adapted by cylindrical condenser with same diameter and condensed by Instron universal testing machine with 80kg pressure & 1mm/min speed. Each specimen was removed from the metal mold and stored at room temperature for a week. The specimen was polished with the same polishing machine for amalgam alloy. For observation of microstructure and analysis of composition of amalgam alloys and amalgams, EMPA was used to get secondary electron images, backscattered images and characteristic X-ray images of Ag, Sn, Cu, Zn, Hg. To analyze compositions of amalgam alloys and amalgams, X-ray diffractometer was used. Amalgam alloys were scanned at the range of 2${\theta}$ of 30-$85^{\circ}$ and the speed of $4^{\circ}$/min with Cuka line and amalgams were scanned at the range of 2${\theta}$ of 28-$44^{\circ}$ and the speed of $4^{\circ}$/min with Cuka line. By comparing obtained d(distance between surfaces) and d of expected phases and atoms in amalgam alloys and amalgams in ASTM card, phases and atoms were identified. The results were as follows, 1. In Caulk Fine Cut amalgam alloy typical ${\gamma}$ phase was shown, and in amalgam, ${\gamma}$, ${\gamma}_1$ and ${\gamma}_2$ phases were observed. 2. In Caulk Spherical amalgam alloy ${\gamma}$, Ag, Cu and $\varepsilon$ phases were shown, and in amalgam ${\gamma}$, ${\gamma}_1$, ${\gamma}_2$ and $\eta$ phases were observed. 3. In Tytin amalgam alloy ${\gamma}$, Cu and $\varepsilon$ phases were shown, and in amalgam ${\gamma}$, ${\gamma}_1$, $\eta$ and $\varepsilon$ phases were observed. 4. In Dispersalloy ${\gamma}$, Ag, Cu and $\varepsilon$ phases were shown, and in amalgam ${\gamma}$, ${\gamma}_1$, $\eta$ and $\varepsilon$ phases were observed. 5. In Valiant alloy ${\gamma}$, Cu and e phases were shown, and in amalgam ${\gamma}$, ${\gamma}_1$, $\eta$ and $\varepsilon$ phases were observed.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.11a
• /
• pp.57-57
• /
• 2000

Brazing characteristics of the LTCC(Low Temperature Co-fired Ceramics)/ Kovar(Fe-Ni-Co alloy) was investigated. Kovar is one of the typical material for the lid of MCM and packages. In case of alumina package, Brazing process is done by higher temperature profile than 800 $^{\circ}C$ and Ag-Cu alloy. But, LTCC has sintering temperature near 850 $^{\circ}C$. So, it is difficult to use the same process as alumina brazing. The adhesion strength of the brazed part is affected by brazing alloy and metallization properties between conductor pattern and LTCC material. We investigated brazing characteristics of the LTCC/Kovar using various brazing alloys(Ag-Cu, Au-Sn) and process conditions. And, we examined the influence of the glass contents in conductor on the brazing characteristics of the LTCC/Kovar.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.1
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.

• Journal of dental hygiene science
• /
• v.4 no.3
• /
• pp.103-109
• /
• 2004

The present study prepared 72 test samples - 24 made of amalgam alloy, 24 of Verabond (Ni-Cr alloy) for crown and 24 of Talladium $^{TM}alloy$ for denture - according to the manufacturers' manuals and general method in consideration of the width of the mesial-distal dental crown of the lower $1^{st}$ molar and MOD cavity in clinics, put them in a 200 ml beaker containing 80 ml of artificial saliva, and measured their galvanic corrosion at distances of 0 mm, 7 mm and 40 mm after 7 days. Isolated metals in the electrolyte such as Cu, Ag, Ni, Cr, Sn, Zn and Hg were quantitatively analyzed with Inductively Coupled Plasma - Atomic Emission Spectrometer (ICP-AES, JY-50P, VG Elemental Co. France), and from the results were drawn conclusions as follows. First, Cu, Sn, Ag, Hg and Zn were highly advantageous when amalgam contacted gold alloy compared to Ni-Cr alloy for crown and Talladium alloy for denture. In addition, although gold alloy was finest in terms of oral tissue and biocompatibility, it was most disadvantageous when it was with amalgam. Second, when amalgam contacted gold alloy, heavy metals such as Ni and Cr were not isolated at all because gold alloy did not contain such elements but Sn was isolated as much as $227.1{\pm}18.0035{\mu}g/cm^2$ although it was not included in the composition either. Hg was also isolated. These elements are assumed to have been isolated from amalgam itself. Third, when amalgam alloy was apart from gold alloy 0 mm, 7 mm and 40 mm, Cu and Ag showed significance but Hg did not. This suggests that gold alloy must not be used together with amalgam, and must not be used between dissimilar prostheses regardless of distance. Fourth, when amalgam alloy contacted Ni-Cr alloy for crown, Ag was not isolated from the amalgam, but Zn, Ni, Sn, Hg and Cu were isolated in order of quantity. Significance was observed according to distance - 0 mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Ni-Cr alloy for crown, the isolation Hg was less than that when amalgam alloy contacted Ni-Cr alloy for crown. Fifth, when amalgam alloy contacted Talladium alloy for denture, significance was observed at distances of 0mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Talladium alloy for denture, the isolation Hg was less than that when amalgam alloy contacted Talladium alloy for denture. Sixth, according to the result of ICPES test on Cu, Sn, Ag, Hg, Zn, Ni and Cr of amalgam alloy, gold ally, Verabond and Talladium alloy when these alloys contacted artificial saliva, significance was observed in Cu and Hg. Seventh, when amalgam alloy contracted two non-precious metals Ni-Cr alloy for crown and Talladium alloy for denture in artificial saliva, significance was observed in the isolated by-products of Hg, Ni and Cr according to distance.

• 보존과학연구
• /
• s.16
• /
• pp.18-40
• /
• 1995

Twelve bronze artifacts and silver earring from Kimhae Yangdong-ri Site were treated by B.T.A(Benzotriazole) for the stabilization of copper alloys and impregnated with Incralac for consolidation. Bronze artifacts were analyzed qualitatively by X-rayfluorescence. It was found that elemental composition of bronze artifacts were Cu-Sn-Pbsystem wint some impurities such as Bi, As, Fem Sb, and Ag.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.79-79
• /
• 2010

저온용 무연 솔더의 대표 조성으로 고려되고 있는 Sn-58Bi(융점: $138^{\circ}C$) 공정(eutectic) 조성은 우수한 강도에도 불구하고 연성(ductility) 측면에서의 문제점이 지속적으로 보고되고 있다. 따라서 이 합금계의 연성을 최대로 개선시킬 수 있으면서도 실제 상용화가 가능한 합금 조성의 개발 연구가 요청된다. 본 연구에서는 Sn-Bi 2원계 조성에서 최대의 연성을 나타내는 것으로 보고된 Sn-40Bi 조성에 미량의 합금원소를 첨가함으로써 최대의 연성을 확보하는 한편, 그 연성 특성이 변형속도에 어느 정도 민감한지를 인장 실험을 통해 결정하고자 하였다. 합금원소로는 0.1~0.5 wt%의 Ag, Mn, In, Cu를 선택하였으며, 인장 시편을 제조하여 $10^{-2}$, $10^{-3}$, $10^{-4}\;s^{-1}$의 3종류로 변형속도를 변형시켜가며 응력-변형 곡선(stress-strain curve)을 측정하였고, 조성별, 변형속도별로 최대인장강도(ultimate tensile stress, UTS) 및 연신율 결과들을 정리하였다. 합금원소를 첨가한 조성의 경우는 모든 시험 조건에서 Sn-40Bi보다 우수한 연신률을 나타내는 것으로 측정되었으나, $10^{-2}\;s^{-1}$의 빠른 변형속도에서는 그 향상 정도가 상대적으로 감소하는 경향이 관찰되었다. 특히 Sn-40Bi-0.5Ag 조성의 경우 느린 변형속도에서 특히 눈에 띄는 연신률 값을 나타내며, 모든 변형속도 조건에서 가장 우수한 연성을 나타내었다. 한편 Sn-40Bi-0.1Cu 조성의 경우 변형속도에 따른 연신률의 변화 정도, 즉, 변형속도에 따른 연신률의 민감도가 매우 커 $10^{-4}\;s^{-1}$ 속도에서는 Sn-40Bi-0.5Ag에 버금가는 연신률 값이 측정되었으나, $10^{-2}\;s^{-1}$ 속도에서는 가장 나쁜 연신률 특성을 보여주었다. Sn-40Bi-0.2Mn 조성은 최고의 연신률 향상 특성을 나타내지는 않았으나, In을 첨가한 경우보다는 대체적으로 우수한 연성을 나타내었다. 이상의 각 합금별 연성 특성은 인장시험 전의 미세조직 관찰 결과와 인장시험 후 파면부의 조직변화 관찰 결과로부터 해석되었다. 그 결과 석출상의 형성 여부, 인장 시험 중 재결정 조직의 형성 여부, 라멜라(lamellar) 조직의 분율과 라멜라 간격(lamellar spacing)의 정도 또는 $\beta$-Sn과 라멜라 조직 사이의 결정립계와 라멜라 조직 내 결정립계에서의 슬라이딩 모드(sliding mode) 변형 정도, 석출상의 크기와 분포 정도 등이 연신률 및 변형속도 민감도와 같은 연성 특성에 가장 큰 영향을 미치는 인자인 것으로 분석되었다.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.75-81
• /
• 2014

Usage of heavy metal element (Pb, Hg and Cd etc.) in electronic devices have been restricted due to the environmental banning of the European Union, such as WEEE and RoHS. Therefore, it is needed to develop the Pb-free solder plated ribbon in photovoltaic (PV) module. This study described that degradation characteristics of PV module under damp heat (DH, $85^{\circ}C$ and 85% R.H.) condition test for 1,000 h. Solar cell ribbons were utilized to hot dipping plate with Pb-free solder alloys. Two types of Pb-free solder plated ribbons, Sn-3.0Ag-0.5Cu (SAC305) and Sn-48Bi-2Ag, and an electroless Sn-40Pb solder hot dipping plated ribbon as a reference sample were prepared to evaluate degradation characteristics. To detect the degradation of PV module with the eutectic and Pb-free solder plated ribbons, I-V curve, electro-luminescence (EL) and cross-sectional SEM analysis were carried out. DH test results show that the reason of maximum power (Pm) drop was mainly due to the decrease fill factor (FF). It was attributed to the crack or oxidation of interface between the cell and the ribbon. Among PV modules with the eutectic and Pb-free solder plated ribbon, the PV module with SAC305 ribbon relatively showed higher stability after DH test than the case of PV module with Sn-40Pb and Sn-48Bi-2Ag solder plated ribbons.