• 마이크로전자및패키징학회지
• /
• 제14권4호
• /
• pp.71-77
• /
• 2007

본 연구에서는 리플로우 횟수를 달리하여 Sn-37Pb, Sn-3.5Ag와 Sn-3.5Ag-0.75Cu (all wt.%) BGA 솔더 접합부들을 OSP가 코팅된 Cu 패드 상에 형성시킨 후, 기계적 전기적 특성을 연구하였다. 주사전자현미경 분석 결과, 접합 계면에 생성된 $Cu_6Sn_5$ 금속간화합물 층의 두께는 리플로우 횟수가 증가함에 따라 증가하였다. Sn-Pb와 Sn-Ag-Cu 솔더 접합부의 경우, 3회 리플로우 후 최대 전단 강도를 나타내었으며, Sn-Ag 솔더 접합부의 경우 4회 리플로우 후 최대 전단 강도를 나타내었다. 이후 리플로우 횟수가 10회까지 증가함에 따라 전단 강도는 점차 감소하였다. 리플로우 횟수가 증가함에 따라 전기적 특성은 점차 감소하였다.

• Journal of Welding and Joining
• /
• 제16권3호
• /
• pp.157-166
• /
• 1998

Recently as environmental pollution caused by Pb has posed a serious threat to the global environment, the trend to regulate the usage of Pb in electronic industry is one the rise. Currently, the solder alloy with high Pb content, Sn-37%Pb, is utilized in the electronic assembly therefore, the objective of this study is to develop an alternative solder alloy for the existing Sn-37%Pb solder alloy. First thing, this work choosed Sn-5%Pb-1.5%Ag, Sn-5%Pb-1.5%Ag-x%Bi(x=1~5%) for candidate solder alloys, and examined their properties such as melting range, wettability, microhardness, tensile property, oxidation behavior and microstructure. Wettability was on the same level of Sn-37%Pb. Dissolution of Pb ion in Sn-5%Pb solder was 0.46ppm. This solder alloy revealed cellular dendrite microstructure $\beta$-Sn matrix, Pb-rich phase, Ag/Sn, and Cu/Sn Intermetallic compounds. The range of solidification temperature was within 3$0^{\circ}C$. Also these alloy displayed higher tensile strength and lower elongation than Sn-37%Pb. The resistance of oxidation in Sn-5%Pb-1.5%Ag solder alloy was superior to that of Sn-37%Pb solder alloy. But that of Sn-5%Pb-1.5%Ag-5%Bi solder alloy was equal to that of Sn-37%Pb solder alloy.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2002년도 춘계 기술심포지움 논문집
• /
• pp.126-129
• /
• 2002

This article presents that the affecting factors to solderability and initial reliability. It was discussed that effect of the solder ball hardness and composition on the reliability of solder joints. In this study, lead free solder alloys with compositions of Sn-Cu, Sn-Ag, Sn-Ag-Cu, Sn-Ag-Cu-Bi were applied to the $\muBGA$ packages. As a result of experiments, the high degree of hardness with the displacement of 0.22mm was obtained Sn-2.0Ag-0.7Cu-3.0Bi. The shear strength of lead free solder was higher than of Sn-37Pb solder, and it was increased about 150% in Sn-2.0Ag-0.7Cu-3.0Bi.

• Journal of Welding and Joining
• /
• 제29권1호
• /
• pp.41-45
• /
• 2011

SnAgCu lead-free solder alloy is considered as the best alternative to eutectic tin-lead solder. However, the detailed material properties of SnAgCu solder are not available in public. Hence, this paper presents an estimation of mechanical properties of SnAgCu lead-free solder. In particular, the weight percent of Ag was varied as 1.0wt%, 2.5wt%, 3.0wt%, and 4.5wt% in order to estimate the effect of Ag in the Sn-xAg-0.5Cu ternary alloy system. For this purpose, four types of SnAgCu bars were first molded by casting and then standard specimens were cut out of molded bars. Micro-Vickers hardness, tensile tests were finally performed to estimate the variations in mechanical properties according to the weight percent of Ag. Test results reveal that the higher the weight percent of Ag is, the higher the hardness, yield strength, and ultimate tensile strength become. More material properties will be further investigated in the future work.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.640-644
• /
• 2000

Sn-3.5Ag 무연합금을 Cu 및 Alloy42 리드프레임에 납땜접합(solder joint)하고 미세조직, 젖 음성, 전단강도, 시효효과를 측정하여 비교하였다. CU의 경우, 납땜의 Sn기지상안에 Ag$_3$Sn$_{5}$상이, 그리고 땜납/리드프레임의 경계면에는 1~2$\mu\textrm{m}$ 두께의 Cu$_{6}$Sn$_{5}$상이 형성되었다. Alloy42의 경우, 기지상내에는 낮은 밀도의 Ag$_3$Sn상만이, 그리고 계면에는 0.5~1.5$\mu\textrm{m}$ 두께의 FeSn$_2$이 형성되었다. 한편. Cu에 비해 Alloy42 리드프레임에서 전단강도는 낮았으며, 시효 시간에 따라 전단강도는 모두 감소하였다. 18$0^{\circ}C$에서 1주일간 시효처리 후, Cu 리드프레임에는 계면에 η-Cu$_{6}$Sn$_{5}$ 층이 15-20$\mu\textrm{m}$ 성장하였고, A11oy42 리드프레임에는 기지상내에 AgSn$_3$이 조대하게 성장하였으며, 계면에는 FeSn$_2$층만이 약 $1.5\mu\textrm{m}$로 성장하였다.성장하였다.

• Journal of Welding and Joining
• /
• 제20권4호
• /
• pp.505-509
• /
• 2002

Pb is considered to be eliminated from solder, due to its toxicity. However, melting temperatures of most Pb-free solders are known higher than that of Sn37Pb. Therefore, there is a difficulty to apply Pb-free solders to electronic industry. Since Sn3Ag8Bi5In has relatively lower melting range as $188~200^{\circ}C$, on this study. Wettability and soldering characteristics of Sn3Ag8Bi5In solder in BGA were investigated to solve for what kind of problem. Zero cross time, wetting time, and equilibrium force of Sn3Ag8Bi5In solder for Cu and plated Cu such as Sn, Ni, and Au/Ni-plated on Cu were estimated. Plated Sn on Cu showed best wettability for zero cross time, wetting time and equilibrium farce. Shear strength of the reflowed joint with Sn3Ag8Bi5In ball in BGA was investigated. Diameter of the ball was 0.5mm, UBM(under bump metallurgy) was $Au(0.5\mu\textrm{m})Ni(5\mu\textrm{m})/Cu(18\mu\textrm{m})$ and flux was RMA type. For the reflow soldering, the peak reflow temperature was changed in the range of $220~250^{\circ}C$, and conveyor speed was 0.6m/min.. The shear strength of Sn3Ag8Bi5In ball showed similar level as those of Sn37Pb. The soldered balls are aged at $110^{\circ}C$ for 36days and their shear strengths were evaluated. The shear strength of Sn3Ag8Bi5In ball was increased from 480gf to 580gf by aging for 5 days.

• 한국공작기계학회논문집
• /
• 제16권5호
• /
• pp.151-156
• /
• 2007

In this paper, the creep characteristics of lead and lead-free solder joint were investigated using the QFP(Quad Flat Package) creep test. Two kind of solder pastes(Sn-3Ag-0.5Cu, Sn-0.2Sb-0.4Ag-37.4Pb) were applied to the QFP solder joints and each specimen was checked the external and internal failures(i.e., wetting failure, void, pin hole, poor-heel fillet) by digital microscope and X-ray inspection. The creep test was conducted at the temperatures of $100^{\circ}C$ and $130^{\circ}C$ under the load of 15$\sim$20% of average pull strength in solder joints. The creep characteristics of each solder joints were compared using the creep strain-time curve and creep strain rate-stress curves. Through the comparison, the Sn-3Ag-0.5Cu solder joints have higher creep resistance than that of Sn-0.3Sb-0.4Ag-37.4Pb. Also, the grain boundary sliding in the fracture surface and the necking of solder joint were observed by FE-SEM.

• 대한금속재료학회지
• /
• 제47권3호
• /
• pp.202-208
• /
• 2009

The effects of aging time on the microstructure and shear strength of the Low Temperature Co-fired Ceramic (LTCC)/Ag pad/Electroless Nickel Immersion Gold (ENIG)/BGA solder joints were investigated through isothermal aging at $150^{\circ}C$ for 1000 h with conventional Sn-37Pb and Sn-3Ag-0.5Cu. $Ni_3Sn_4$ intermetallic compound (IMC) layers was formed at the interface between Sn-37Pb solder and LTCC substrate as-reflowed state, while $(Ni,Cu)_3Sn_4$ IMC layer was formed between Sn-3Ag-0.5Cu solder and LTCC substrate. Additional $(Cu,Ni)_6Sn_5$ layer was found at the interface between the $(Ni,Cu)_3Sn_4$ layer and Sn-3Ag-0.5Cu solder after aging at $150^{\circ}C$ for 500 h. Thickness of the IMC layers increased and coarsened with increasing aging time. Shear strength of both solder joints increased with increasing aging time. Failure mode of BGA solder joints with LTCC substrate after shear testing revealed that shear strength of the joints depended on the adhesion between Ag metallization and LTCC. Fracture mechanism of Sn-37Pb solder joint was a mixture of ductile and pad lift, while that of Sn-3Ag-0.5Cu solder joint was a mixture of ductile and brittle $(Ni,Cu)_3Sn_4$ IMC fracture morphology. Failure mechanisms of LTCC/Ag pad/ENIG/BGA solder joints were also interpreted by finite element analyses.

• 한국주조공학회지
• /
• 제28권4호
• /
• pp.184-189
• /
• 2008

Ag-Cd alloy has been widely used as an electrical contact material, since Ag-Cd alloy has a good wear resistance and stable contact resistance. But nowadays Ag-Cd alloy is not considered as electrical contact material any more due to detrimental effect on environments. Currently, active researches are being performed on ($Ag-SnO_2$ and $Ag-SnO_{2}-In_{2}O_{3}$) as an alternative solution which can fix the remaining environmental problems. However, $In_{2}O_{3}$ is relatively expensive and Ag-Sn alloy has low wear resistance. Our recent research results show that Ag-X%Zn-Y%Sn has similar physical and chemical properties. In the present study, so we tried to change and to optimize the Zn oxide content to over 6 wt% and Sn oxide content with 0.5, 1.0, 1.5 wt%. Results obtained from the experiments on the Ag-X%ZnO-Y%$SnO_2$ are discussed.

• 한국생산제조학회지
• /
• 제20권2호
• /
• pp.193-201
• /
• 2011

Recently, mechanical reliabilities including a drop test have been a hot issue. In this paper, solder balls with new components which are Sn-3.0Ag-0.5Cu and Sn-1.0Ag-0.5Cu-0.05N are introduced, and board level drop test for them are conducted under JEDEC standard in which the board with 15 flip chips is dropped as 1,500g acceleration during 0.5ms. The drop simulations are studied by using a implicit method in the ANSYS LS-DYNA, and modal analysis is made. Through both analyses, the solder balls with new components are evaluated under the drop. It is found that the maximum stress of each chip is occurred between the solder ball and the PCB, and the highest value among the maximum stresses in the chips is occurred on the chip nearest to fixed holes on the board in the drop tests and simulations.