• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.11a
• /
• pp.141-145
• /
• 2001

Sn-3.5Ag 무연 솔더에 Cu를 첨가한 3원계 합금을 만든 후 압연과 열처리한 후 크리프 특성을 연구하였다. 모든 솔더 합금에서 1차 크리프는 거의 관찰되지 않았으며, 2차와 3차 크리프가 대부분을 차지하였고, 최소 크리프 변형율은 Cu 함량이 0.75 wt %에서 최소이었고, 응력 지수는 약 4이었으며, 파단 시간 또한 0.75 wt% Cu에서 가장 길었다. 크리프 기구는 격자 확산에 의한 전위의 상승과 전위 활주에 의한 고온 크리프임을 앞 수 있었으며, Cu의 첨가는 1 wt% 가지 연성에 큰 영향을 주지 않았으나, 1.5 wt% 첨가했을 경우 연성은 크게 감소하였다.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.181-183
• /
• 2006

This paper studies the mechanical behaviors of Sn-3.5Ag solder joint against substrate(such as Au/Ni/Cu, Au/cu, Ni/Cu and Cu pad) after induction heating, a new soldering method. It was found that the solder bump formation depends on the time and current of the induction heating system. Also the heating value of the solder bump were found to vary with respect to the thermal conductivity of the pads on the substrate. In case of Au/Ni/Cu pad and Au/Cu pad, solder bump's shear strength were high for the heating time of $1.5{\sim}2sec$. For Ni/Cu pad, solder bump's shear strength were found to increase with time increment.

• Korean Journal of Materials Research
• /
• v.25 no.3
• /
• pp.125-131
• /
• 2015

Fluorine-doped $SnO_2$ (FTO) thin film/Ag nanowire (NW) double layers were fabricated by means of spin coating and ultrasonic spray pyrolysis. To investigate the optimum thickness of the FTO thin films when used as protection layer for Ag NWs, the deposition time of the ultrasonic spray pyrolysis process was varied at 0, 1, 3, 5, or 10 min. The structural, chemical, morphological, electrical, and optical properties of the double layers were examined using X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, transmission electron microscopy, the Hall effect measurement system, and UV-Vis spectrophotometry. Although pure Ag NWs formed isolated droplet-shaped Ag particles at an annealing temperature of $300^{\circ}C$, Ag NWs covered by FTO thin films maintained their high-aspect-ratio morphology. As the deposition time of the FTO thin films increased, the electrical and optical properties of the double layers degraded gradually. Therefore, the double layer fabricated with FTO thin films deposited for 1 min exhibited superb sheet resistance (${\sim}14.9{\Omega}/{\Box}$), high optical transmittance (~88.6 %), the best FOM (${\sim}19.9{\times}10^{-3}{\Omega}^{-1}$), and excellent thermal stability at an annealing temperature of $300^{\circ}C$ owing to the good morphology maintenance of the Ag NWs covered by FTO thin films.

• Journal of Welding and Joining
• /
• v.30 no.2
• /
• pp.65-69
• /
• 2012

Environmental and health concerns over the lead have led to investigation of the alternative Pb-free solders to replace commonly used Pb-Sn solders in microelectronic packaging application. The leading candidates for lead-free solder alloys are presently the near eutectic Sn-Ag-Cu alloys. Therefore, extensive studies on reliability related with the composition have been reported. However, the insufficient drop property of the near eutectic Sn-Ag-Cu alloys has demanded solder compositions of low Ag content. In addition, the solder interconnections in automobile applications like a smart box require significantly improved vibration resistance. Therefore, this study investigated the effect of alloying elements (Ag, Bi, In) on the vibration fatigue strength. The vibration fatigue was conducted in 10~1000Hz frequency and 20Grms. The interface of the as-soldered cross section close to the Cu pad indicated the intermetallic compound ($Cu_6Sn_5$) regardless of solder composition. The type and thickness of IMC was not significantly changed after the vibration test. It indicates that no thermal activities occurred significantly during vibration. Furthermore, as a function of alloying composition, the vibration crack path was investigated with a focus on the IMCs. Vibration crack was initiated from the fillet surface of the heel for QFP parts and from the plating layer of chip parts. Regardless of the solder composition, the crack during a vibration test was propagated as same as that during a thermal fatigue test.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.1
• /
• pp.47-52
• /
• 2002

Intermetallic compound on the soldered interface plays important role on the bondability and mechanical properties of soldered joint. The formation of intermetallic compounds are influenced by many factors such as temperature, holding time, base metals and so on. On this study the effect of number of reflow times on the intermetallic growth was investigated. For the experimental materials, Sn-3.5Ag-0.7Cu solder ball of 0.3mm diameter and RMA-type flux were used. Thickness of intermetallic compound of solder ball by 2nd reflow showed nearly 60% higher than that of 1st reflow, and shear strength showed 10% higher value. Thickness and shear strength according to the position of interface such as upper side or lower side between two substrates were also investigated.

• Korean Journal of Materials Research
• /
• v.30 no.6
• /
• pp.285-291
• /
• 2020

Recent advances in technology using ultra-thin noble metal film in oxide/metal/oxide structures have attracted attention because this material is a promising alternative to meet the needs of transparent conduction electrodes (TCE). AZO/Ag/AZO multilayer films are prepared by magnetron sputtering for Cu₂ZnSn(S,Se)₄ (CZTSSe) of kesterite solar cells. It is shown that the electrical and optical properties of the AZO/Ag/AZO multilayer films can be improved by the very low resistivity and surface plasmon effects due to the deposition of different thicknesses of Ag layer between oxide layers fixed at AZO 30 nm. The AZO/Ag/AZO multilayer films of Ag 15 nm show high mobility of 26.4 ㎠/Vs and low resistivity and sheet resistance of 3.58^⁎10^-5 Ωcm and 5.0 Ω/sq. Also, the AZO/Ag (15 nm)/AZO multilayer film shows relatively high transmittance of more than 65 % in the visible region. Through this, we fabricated CZTSSe thin film solar cells with 7.51 % efficiency by improving the short-circuit current density and fill factor to 27.7 mV/㎠ and 62 %, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.2
• /
• pp.25-30
• /
• 2018

Sn-Pb solder has been used in automotive electronics for decades. However, recently, due to the environmental and health concerns, some international environmental organizations such as the end-of-life vehicle (ELV) enacted legislation banning of the Pb usage in automotive electronics. For this reason, many studies to develop and promote Pb-free soldering have been significantly reported. Meanwhile, because of flexibility and lightweight, flexible printed circuit boards (FPCBs) have been increasingly used in automotive electronics for lightweight to improve fuel efficiency and space utilization. Although the properties of lead-free solders for automotive electronics have been widely studied, there is a lack of research on the reliability performance of the lead-free solder joint on FPCB under user conditions. This study reported the properties of solder joints between Pb-free solders such as Sn3.0Ag0.5Cu, Sn0.7Cu and Sn0.5Cu0.01Al (Si), and various FPCBs finished with organic solderability preservative (OSP) and electroless nickel immersion gold (ENIG). To evaluate on joint properties and reliabilities with different solder compositions and surface-finishing materials, pull strength test, thermal shock test, and bending cycle test were performed and analyzed. After the bending cycle test of solder joint on OSP-finishing, the fractures were occurred in solder and the lifetime of Sn3.0Ag0.5Cu solder joint was the longest.

• Journal of Welding and Joining
• /
• v.35 no.3
• /
• pp.7-14
• /
• 2017

The effect of high temperature-moisture on corrosion and mechanical properties for Sn-0.7Cu, Sn-3.0Ag-0.5Cu (SAC305) solders on flexible substrate was studied using Highly Accelerated Temperature/Humidity Stress Test (HAST) followed by three-point bending test. Both Sn-0.7Cu and SAC305 solders produced the internal $SnO_2$ oxides. Corrosion occurred between the solder and water film near flexible circuit board/copper component. For the SAC305 solder with Ag content, furthermore, octahedral corrosion products were formed near Ag3Sn. For the SAC305 and Sn-0.7Cu solders, the amount of internal oxide increased with the HAST time and the amount of internal oxides was mostly constant regardless of Ag content. The size of the internal oxide was larger for the Sn-0.7Cu solder. Despite of different size of the internal oxide, the fracture time during three-point bending test was not significantly changed. It was because the bending crack was always initiated from the three-point corner of the chip. However, the crack propagation depended on the oxides between the flexible circuit board and the Cu chip. The fracture time of the three-point bending test was dependent more on the crack initiation than on the crack propagation.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.1
• /
• pp.47-53
• /
• 2012

Bonding strength of Sn-3.0Ag-0.5Cu solder joint due to degradation characteristic of OSP surface finish was investigated, compared with SnPb finish. The thickness variation and degradation mechanism of organic solderability preservative(OSP) coating were also analyzed with the number of reflow process. To analyze the degradation degree of solder joint strength, FR-4 PCB coated with OSP and SnPb were experienced preheat treatment as a function of reflow number from 1st to 6th pass, respectively. After 2012 chip resistors were soldered with Sn-3.0Ag-0.5Cu on the pre-heated PCB, the shear strength of solder joints was measured. The thickness of OSP increased with increase of the number of reflow pass by thermal degradation during the reflow process. It was also observed that the preservation effect of OSP decreased due to OSP degradation which led Cu pad oxidation. The mean shear strength of solder joints formed on the Cu pads finished with OSP and SnPb were 58.1 N and 62.2 N, respectively, through the pre-heating of 6 times. Although OSP was degraded with reflow process, the feasibility of its application was proven.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.35.2-35.2
• /
• 2009

최근 본 연구실에서 무연 솔더를 위한 새로운 Cu-Zn 합금 젖음층을 개발하였다. 전해도금을 통하여 Cu-Zn 합금층을 형성한 뒤 그 위에 Sn-4.0wt% Ag-0.5wt% Cu (SAC 405) 솔더를 리플로 솔더링을 통해 솔더접합부를 형성하였으며 계면에서 생성된 금속간 화합물의 형성 및 성장 거동을 연구하였다. SAC/Cu 시스템의 경우, $150^{\circ}C$에서 시효 처리를 실시하는 동안 솔더와 도금된 Cu 계면에서 $Cu_6Sn_5$ 상과 미세한 공공이 형성된 $Cu_3Sn$ 상이 발견되었다. 반면에 SAC/Cu-Zn 시스템에서는 계면에서 $Cu_6Sn_5$ 상만이 형성되었다. 또한 큰 판상형의 $Ag_3Sn$ 상이 SAC/Cu 시스템에 비해 현저하게 억제되었다. SAC/Cu-Zn 계면에서의 금속간 화합물의 성장 속도가 SAC/Cu 계면에서 형성된 금속간 화합물의 성장 속도보다 느리게 나타났다. Cu-Zn 젖음층의 Zn가 솔더와 Cu-Zn 층 사이에서 Cu와 Sn 원자의 상호 확산을 방해하기 때문이다. 본 연구에서는 Cu와 Cu-Zn 층을 이용한 솔더 접합부의 낙하 충격 신뢰성을 연구하였다. 낙하 충격 시험 시편은 두 개의 인쇄 회로 기판을 SAC 405 솔더볼을 이용하여 리플로를 통해 상호연결 하여 제조되었다. 이 때, 각각의 인쇄 회로 기판의 패드에는 Cu 층과 Cu-Zn층을 전해도금을 통하여 각각 $10{\mu}m$두께의 젖음층을 형성하였다. 낙하 시험 시편을 제조한 뒤, 시효 처리에 대한 낙하 저항 신뢰성의 특성을 연구하기 위해 250, 500 시간동안 시효처리를 한 후 각 조건에서 계면에 형성된 금속간 화합물의 성장 거동을 관찰하였으며, 낙하 충격 시험을 실시하였다. 낙하 시험은 daisy chain으로 연결된 시편의 저항이 100 Ohm 이상 측정되었을 때 중단되도록 하였다. Cu-Zn/SAC/Cu-Zn 시편의 경우 초기 리플로를 하였을 때 불량이 발생하는 평균 낙하 수는 350이며, Cu/SAC/Cu 시편의 평균 낙하수는 200 미만으로 나타났다. Cu/SAC/Cu 시편의 경우, 시효처리 시간이 증가함에 따라 평균 낙하수는 큰 폭으로 감소하였지만, Cu-Zn/SAC/Cu-Zn 시편은 불량이 발생하는 평균 낙하수의 감소폭이 보다 완만하게 나타났다. Cu 층에 Zn를 첨가함으로써 솔더와 젖음층 사이에서 형성된 금속간 화합물의 성장 및 미세 공공의 형성이 억제되었고, 솔더 접합부의 과냉을 감소시킴으로써 큰 판상형의 $Ag_3Sn$ 상의 형성을 억제함으로써 Cu-Zn/SAC/Cu-Zn 솔더 접합부에서 Cu/SAC/Cu 솔더 접합부보다 낙하 충격에 대한 저항성 및 신뢰성이 향상되었다. 이는 무연 솔더에 Zn를 첨가하여 낙하 충격 신뢰성을 향상시킨 것과 동일한 효과를 나타냈음을 확인하였다. 본 연구는 한국 과학 기술 재단의 전자패키지 재료 연구 센터(CEPM)와 지식 경제부의 부품 소재 기술 개발 사업의 지원을 받아 수행되었습니다.