• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.6
• /
• pp.259-265
• /
• 2011

This research was performed to stabilize heavy metals in mine tailing using fly ash and clay. Fly ash-clay-mine tailing system were investigated using XRD (X-ray diffractometer), XRF (X-ray fluorescence spectrometer), TG-DTA, SEM (Scanning Electron Microscope), Dilatometer and UTM with various mine tailing contents (~15 wt%). The fly ash used in this research was mainly composed of $SiO_2$ (33.01 wt%), $Al_2O_3$ (28.54 wt%), $K_2O$ (3.32 wt%), $Fe_2O_3$ (1.47 wt%), CaO(9.97 wt%). $SiO_2$ and $Al_2O_3$ composition of the clay was over 61 wt%. And the mine tailing have high composition of $SiO_2$ (26.91 wt%), CaO (24.25 wt%), $Fe_2O_3$ (22.97 wt%). Therefore, it was estimated that fly ash-clay-mine tailing have enough sintering characteristics. The shrinkage of specimens started at around $850^{\circ}C$ and changed little up to $1100^{\circ}C$, but increased markedly at above $1100^{\circ}C$. The shrinkage rate is strongly related to the decarbonization amount of coal fly ash. As the result of SEM, structure of the specimens with mine tailing addition showed more close than the one without mine tailing. Compressive strength of the specimens with mine tailing was highly increased to approximately 200~420 kgf/$cm^2$, it satisfied the first grade criterion for clay brick by KS L 4201. The specification of leaching characteristics of the sintered specimens were within the Korean regulation standard.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.70-74
• /
• 2009

Effect of the processing variables on the formation of $Pb(Sc_{1/2}Nb_{1/2})O_3$(hereafter PSN) thin layers prepared on Pt(111)/Ti/$SiO_2$/Si substrates using the sol-gel and the spin coating method has been studied. After each deposition, the coated films were heated at $370^{\circ}C$ for 5 min. Then they were finally sintered at temperature range of $600{\sim}700^{\circ}C$ by RTA(rapid thermal annealing). The final multilayered films showed a (111) preferred orientation. On a while, the layer-by-layer crystallization of multilayered amorphous thin films without the intermediate heating exhibited a (100) preferred orientation. In case of heat treatment in the tube furnace with the heating rate of $4^{\circ}C/min$, (100) and (111) oriented thin layers were formed simultaneously. The microstructure of the deposited films were dense and crack-free with thickness of 300nm, irrespective of the processing variables.

• Journal of the Korea Concrete Institute
• /
• v.26 no.2
• /
• pp.117-124
• /
• 2014

Globally, there are environmental problems due to greenhouse gas emissions. $CO_2$ emissions rate of the cement industry is very high, but the continued demand of cement is needed in the future. In this study, in order to reduce the environmental impact of $CO_2$ emissions from cement production. The experiments were carried out for the development of non-sintered cement (have not undergone firing burning) by granulated ground blast furnace slag. In order to compare the characteristics by curing, an experiment was conducted by changing the curing conditions such as atmospheric steam curing, observe the mechanical properties for the measurement of flexural compressive strength by mortar, observe the chemical properties such as acid resistance, $Cl^-$ penetrate resistance and analyzed the mechanism of hydration by XRD, SEM experiments. From the experimental results, as compared with portland cement usually confirm the mechanical and chemical properties excellent, it is expected be possible to apply to the undersea, underwater and underground structures that require superior durability. In addition, based on the excellent compressive strength by steam curing, it is expected to be possible to utilize as a cement replacement material in the secondary product of concrete. In the future, to solve the problem through continued research, it will be expected to reduce the effect of environmental load and to be excellent economics.

• Journal of the Korean Ceramic Society
• /
• v.40 no.4
• /
• pp.323-327
• /
• 2003

Microwave dielectric properties of (P $b_{0.4}$C $a_{0.6}$)[($Fe_{\frac{1}{2}}$N $b_{\frac{1}{2}}$)$_{1-x}$ (M $g_{1}$ 3/N $b_{2}$ 3/)x] $O_3$ (PCFMN) ceramics were investigated as a function of (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content (0.1$\leq$x$\leq$0.8). A single perovskite phase with the cubic structure was obtained through the given composition range. The unit cell volume was increased with (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$, due to the larger average ionic size of (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ than that of ($Fe_{\frac{1}{2}}$N $b_{\frac{1}{2}}$)$^{4+}$ for B-site ion. Dielectric constant (K) and Temperature Coefficient of Resonant Frequency(TCF) of PCFMN ceramics were dependent on (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content due to the decrease of ionic polarizability and B-site bond valence, respectively. Qf value was decreased with (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content due to the decrease of grain size. Typically, K of 73.56, Qf of 5,074 GHz and TCF of -6.45 ppm/$^{\circ}C$ were obtained for the specimens with x=0.4 sintered at 125$0^{\circ}C$ for 3 h.125$0^{\circ}C$ for 3 h.

• Journal of the Korean Ceramic Society
• /
• v.41 no.8
• /
• pp.599-604
• /
• 2004

The LTCCs (Low-Temperature Co-fired Ceramics) are very important for electronic industry to build smaller RF modules and to fulfill the necessity for miniaturization of devices in wireless communication industry. The dielectric materials with sintering temperature $T_{sint}$＜90$0^{\circ}C$ are required. In this study, BaO-N $d_2$ $O_3$-Ti $O_2$ (BNT ： 20∼40 wt％) for ceramic materials and L $a_2$ $O_3$- $B_2$ $O_3$-Ti $O_2$ (LBT ： 80∼60 wt％) for crystallizable glasses were used. The glass/ceramic composites were investigated for sintering behavior, phase evaluation, densities, interface reaction and microwave dielectric properties. It was found that the addition LBT glass frist significantly lowered the sintering temperature to below 90$0^{\circ}C$ and the densification with increasing addition LBT glass frist developed rapidly which was meant to be namely 90％ of relative density. The sintered bodies ekhibited applicable dielectric properties, namely 15 for $\varepsilon$$_{r}$,, 10000 GHz for Q＊ $f_{0}$. The results suggest that the composites have good potential as a new candidate for LTCC materials.

• Journal of the Korean Ceramic Society
• /
• v.40 no.5
• /
• pp.447-454
• /
• 2003

Samples were prepared by the solid-state reaction method. The nominal composition of the samples was B $i_{1.84}$P $b_{0.34}$S $r_{1.91}$C $a_{2.03}$C $u_{3.06}$ $O_{10+{delta}$ prepared from powder of B $i_2$ $O_3$, PbO, SrC $O_3$, CaC $O_3$, and CuO. They were pulverized, mixed with AgO, A $u_2$ $O_3$and MgO of 50 wt%. Finally, they were sintered at 820 to 85$0^{\circ}C$ in air. The structural characteristics, the microstructure of surface and the critical temperature with respect to the each samples were analyzed by XRD, $T_{c}$, SEM and EDS respectively. It was found that the the critical temperature of the silver oxide additive samples (99.58 K) is higher than those of gold or magnesium oxides additive samples, but all those values are lower than that of pure Bi-2223 phase. The microstructure of surface showed the tendency which the AgO additive samples become more minuteness than A $u_2$ $O_3$ and MgO additive samples.s.samples.s.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.2
• /
• pp.61-69
• /
• 2020

Purpose: Zirconia fixed partial dentures with mandibular 2^nd premolar and 2^nd molar as abutments are fabricated and then the effects of inter-abutment distance on fracture resistance of zirconia fixed partial dentures is studied. Materials and Methods: The materials used in this study are Cameleon S zirconia block and S2 zirconia block, which are divided into CS Group and S2 Group applying different inter-abutment distance for each material, and the sintered zirconia fixed partial denture was luted to the epoxy resin die using a temporary luting cement, and then the fracture resistance was measured by placing a 6 mm diameter hardened steel ball on the occlusal surfaces of the pontics and applying pressure at a cross head speed of 1.0 mm/min on a universal testing machine with a load cell of 5.0 kN. Results: The fracture resistance of zirconia fixed partial dentures is not significantly affected by inter-abutment distance The fracture resistance of zirconia fixed partial dentures in CS Group was significantly higher in 15 mm of inter-abutment distance than in 13 mm and 17 mm of inter-abutment distance (P < 0.05). The fracture resistance of zirconia fixed partial dentures in S2 Group was not significantly different between the three groups (P > 0.05). Conclusion: The fracture resistance of zirconia fixed partial dentures with mandibular 2^nd premolar and 2^nd molar as abutments does not significantly affected by the inter-abutment distance.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.589-598
• /
• 1997

The effects of PT/PZ ratio variations in a modified PZT system on crystal structure and electrical properties were studied. $0.05Pb(Sn_{0.5}Sb_{0.5})O_3＋xPbTiO_3＋yPbZrO_3$＋0.4Wt% $MnO_2$(＝0.55PSS＋0.11PT＋0.84PZ＋0.4wt%$MnO_2$ ; x＋y=0.95) systems with variations of PT/PZ from 0.50/0.45 to 0.l1/0.84 were sintered at $1250^{\circ}C$ for 2 hr, and then sintering density, crystal structure, dielctric, piezoelectric, pyroelectic and voltage responsity to infrared were investigated. Sintering density was increased from 7.52g/$\textrm {cm}^3$ to 7.82g/$\textrm {cm}^3$ with increasing PZ content. Dielectric constants at 1 KHz were decreased from 1147 to 193 with variation of PT/PZ from 0.50/0.45 to 0.l1/0.84 after poling of $4 KV_{DC}$/mm at $140^{\circ}C$ for 20 minutes. All Dielectric losses at 1 KHz were less than 1 % in all specimens. $K_{p}$ was increased near to 1 of PT/PZ, and maximun value of 48.2 % was .at 0.45/0.50. Pyroelectric coefficient of PT/PZ with 0.l1/0.84 was maximun value, 0.0541 C/$\m^2$K, and voltage responsity to infrared was 1.5 V.

• Economic and Environmental Geology
• /
• v.37 no.6 s.169
• /
• pp.603-612
• /
• 2004

Pyrochlore is known as one of the most promising materials for the immobilization of radionuclide in high level waste. This study included the synthesis, phase relation and characteristics of $pyrochlore(CaCeZr_xTi_{2-x}O_{7,\;x=0.2\~2.0)$ in the system of Ca-Ce-Zr-Ti-O. Using the CPS(Cold pressing and sintering) method, the mixtures of $CaCO3_,\;CeO_2,\;ZrO_2\;and\;TiO_2$ oxides were pressed, and sintered at $1100\~1600^{\circ}C$ for 20 hours. The optimal synthetic conditions at various compositions were differed from 1300 to $1600^{\circ}C$ Even in the optimal temperatures, pyrochlore or fluorite coexisted with minor amount of perovskite, $CeO_2\;or\;Ce_{0.75}Zr_{0.25}O_2$. It was confirmed that pyrochlore and fluorite structures were stable at $x\leq0.6\;and\;x\geq1.0$, respectively. Especially, the compositions of pyrochlore or fluorite showed non-stoichiometric compositions in that contents of Ca and Ti were more deficient and those of Zr and Ce were more excess than batch compositions with the increase of x value. These characteristics stemmed from the behavior of elements occupied at eight- and six-coordinated site, and then caused the coexistence of perovskite, $CeO_2\;or\;Ce_{0.75}Zr_{0.25}O_2$ along with pyrochlore or fluorite.

• Applied Chemistry for Engineering
• /
• v.20 no.4
• /
• pp.402-406
• /
• 2009

$TiO_2$ thin films were surface-modified with atmospheric plasma and their photocatalytic activities were evaluated. The films were deposited on glass plates by dip-coating in a $TiO_2$ sol-gel solution and sintered at various temperatures for various times. Nitrogen plasma was used for the modification and the experiments were carried out varying operational parameters such as discharge power and treatment time. Photocatalytic activity was evaluated based on the degradation efficiency of methylene blue (MB) under irradiation of UV-A and fluorescent light. According to XPS analysis, a little amount of nitrogen was found to be doped in the film surface after the modification. As a result, photocatalytic activity increased under irradiation of UV-A and fluorescent light, especially fluorescent light.