Microwave Dielectric Properties of La2O3-B2O3-TiO2 Glass-Ceramic and BaNd2Ti5O14Ceramic System for LTCC Application

The LTCCs (Low-Temperature Co-fired Ceramics) are very important for electronic industry to build smaller RF modules and to fulfill the necessity for miniaturization of devices in wireless communication industry. The dielectric materials with sintering temperature $T_{sint}$＜90$0^{\circ}C$ are required. In this study, BaO-N $d_2$ $O_3$-Ti $O_2$ (BNT ： 20∼40 wt％) for ceramic materials and L $a_2$ $O_3$- $B_2$ $O_3$-Ti $O_2$ (LBT ： 80∼60 wt％) for crystallizable glasses were used. The glass/ceramic composites were investigated for sintering behavior, phase evaluation, densities, interface reaction and microwave dielectric properties. It was found that the addition LBT glass frist significantly lowered the sintering temperature to below 90$0^{\circ}C$ and the densification with increasing addition LBT glass frist developed rapidly which was meant to be namely 90％ of relative density. The sintered bodies ekhibited applicable dielectric properties, namely 15 for $\varepsilon$$_{r}$,, 10000 GHz for Q＊ $f_{0}$. The results suggest that the composites have good potential as a new candidate for LTCC materials.

저온동시소성(LTCC)을 위한 결정화 유리(La2O3-B2O3-TiO2계)와 BaNd2Ti5O14 세라믹을 이용한 마이크로파 유전체 특성

무선 이동통신 산업에서 소형화와 RF모듈을 구현하기 위해 저온 동시 소성 세라믹(LTCC)기술이 부각되고 있다. LTCC용 재료는 90$0^{\circ}C$ 이하의 온도에서 소성이 되어야 한다 본 연구는 BaO-N $d_2$ $O_3$-Ti $O_2$ (BNT：20∼40wt%) 세라믹과 L $a_2$ $O_3$- $B_2$ $O_3$-Ti $O_2$ (LBT：80∼60wt%) 유리를 혼합하여 유리를 결정화시킴으로, 나타나는 부수적인 효과를 얻고자 하였다. 이에 소결 거동, 결정상 분석, 상대밀도 그리고 유전특성을 평가하였다 80wt% 유리의 첨가는 90%에 가까운 상대밀도를 갖는 복합체로서 15에 가까운 유전율과 10000GHz의 품질계수와 같은 우수한 유전특성을 보였다. 이와 같은 결과는 유리 결정화를 이용하여 LTCC용 유전체에 적용될 수 있는 가능성을 부여하였다.