• 한국세라믹학회지
• /
• 제25권5호
• /
• pp.473-478
• /
• 1988

In order to obtain the high purity $\beta$-SiC powder that possesses the excellent sinterability and is close to the spherical shape, the carbon black was mixed into the composition of Si(OC2H5)4-H2O-NH3-C2H5OH which the monodispersed spherical fine particles is formed the hydrolysis of Ethylsilicate and the mixture was carbonized under an argon atmosphere. Particle shpae, size and the yield of $\beta$-SiC powder were investigated according to the molar ratio of carbon/alkoxide and variations of reaction temperature and reaction time. The results of this study are as follow ; 1) The yield of $\beta$-SiC gained from the reaction for one hour at 150$0^{\circ}C$ almost got near 100% and the particle size of $\beta$-SiC from the reaction for 15 hrs at 150$0^{\circ}C$ was 0.2${\mu}{\textrm}{m}$ on the average and close to the spherical shape agglomerate state. 2) When the molar ratio carbon/alkoxide is over 3.1 and the reaction occurs at 145$0^{\circ}C$ for 5hrs, the carbon content has not an effect on the kind of crystal of product.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2007년도 제33회 하계학술대회 초록집
• /
• pp.248-248
• /
• 2007

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.63.2-63.2
• /
• 2010

삼중접합 태양전지에 상부전지로 이용되는 a-SiO:H 태양전지는 PECVD(Plasma Enhanced Chemical Vapour Deposition)을 이용하여 증착하였다. i a-SiO:H는 $CO_2/SiH_4$ 비율을 변화하여 밴드갭을 조절하였다. $CO_2/SiH_4$가 0에서 0.43으로 증가 할수록 밴드갭이 1.74 eV에서 1.94 eV로 증가하는 경향을 보였다. 이는 FTIR에서 나타난 결과인 Si-O-Si 결합의 증가 때문인 것으로 판단한다. 그에 반해서 광 전도도는 감소하는 경향을 보였다.그러나 암전도도와 광전도도의 비율인 광민감도는 $10^5$에서 $10^4$의 값으로 비정질 태양전지에 적용가능한 값을 보였다. 이러한 박막 특성을 가진 i a-SiO:H를 이용하여 비정질 실리콘 태양전지를 제작한 결과 $CO_2/SiH_4$의 비율이 증가함에 따라 태양전지의 $V_{oc}$가 0.8 V에서 0.5 V로 현저하게 감소하였고, $J_{sc}$와 FF 역시 11 $mA/cm^2$에서 4 $mA/cm^2$, 69%에서 50%로 감소하였다. 단위박막 결함을 측정하는 CPM(Constant Photocurrent Method)을 이용하여 i a-SiO:H 내부에 $10^{16}cm^{-3}$ 정도의 내부 결함을 관찰하였고 이는 태양전지의 특성 감소와 관련이 있는 것으로 판단한다.

• 한국재료학회지
• /
• 제9권12호
• /
• pp.1155-1159
• /
• 1999

플라즈마 화학증착 (PECVD) 장비를 이용하여 $SnO_2$ 투명전도막이 피막된 유리기판 위에 p-SiC/i-Si/n-Si 이종접합 태양전지를 제작하였다. p-SiC 층의 증착중에 기체조성 x=$CH_4/\;(SiH_4+CH_4)$의 변화에 대한 태양전지의 광기전 특성을 관찰하였다. 기체조성(x)이 0~0.4의 범위에서 p-SiC 창층의 광학적 밴드갭의 증가로 인하여 태양전지의 효율은 증가하였으나, 그 이상의 기체조성에서는 p-SiC/i-Si 계면에서의 조성불일치가 증가하여 태양전지의 효율이 감소하였다. 이러한 계면문제는 p-SiC 층과 i-Si 계면에서의 조성불일치가 증가하여 태양전지의 효율이 감소하였다. 이러한 계면문제는 p-SiC 층과 I-Si 층 사이에 I-SiC 완충층을 삽입함으로써 크게 감소하였다. 그 결과 유효면적이 $1cm^2$인 glass/$SnO_2$/p-SiC/i-SiC/i-Si/n-Si/Ag 구조의 박막 태양전지는 100mW/$cm^2$ 조도 하에서 8.6%의 효율을 나타내었다. ($V_{oc}$=0.85V, $J_{sc}$=16.42mA/$cm^2$, FF=0.615)

• 한국세라믹학회지
• /
• 제28권2호
• /
• pp.130-140
• /
• 1991

The powders of the system Si3N4-Y2O3-AlN were prepared using Si(OC2H5)4 and YCl3.6H2O together with commercial AlN powder. $\alpha$-Si3N4 was prepared by the carbothermal reduction and nitridation of the hydrolyzed gel at 135$0^{\circ}C$ for 10h in N2 atmosphere. YCl3.6H2O was observed to be changed to Y2O3 during the reaction. $\alpha$-Sialon(X=0.2, 0.4, 0.6) ceramics were obtained by hot-pressing the Si3N4-Y2O3-AlN mixture at 178$0^{\circ}C$ for 1h under 30 MPa. The content of $\alpha$-Sialon increased with increasing metal solubility(x value) and $\alpha$-Sialon single phase was obtained at the metal solubility of 0.6. With increasing metal solubility, flexural strength, fracture toughness and thermal shock resistence were decreased, while the microhardness was increased. Large elongated $\beta$-Si3N4 grains were mainly observed at lower metal solubility. Mechanical prorerties of the sintered ceramics with X=0.2 were measured as follows : flexural strength ; 650 MPa, fracture toughness ; 3.63 MN/m3/2, hardness ; 14.7 GPa, thermal shock resistence temperature ; 58$0^{\circ}C$.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2008년도 제35회 하계학술대회 초록집
• /
• pp.156-156
• /
• 2008

• 한국결정성장학회지
• /
• 제7권2호
• /
• pp.216-223
• /
• 1997

출발물질로 aluminum iso-propoxide ($Al(OC_3H_7)_3$, AIP)를 사용하여 화학증착법으로 Si-wafer(100)위에 알루미나 박막을 증착하였다. 증착된 박막의 조성을 알아보기 위해 ESCA를 이용하였으며, SEM을 이용하여 박막의 형상 및 두께를 평가하였다. 그리고 굴절율 및 C-V 특성은 각각 ellipsometry와 HP4192A를 사용하였다. ESCA와 SEM의 분석결과에서 상압보다는 저압에서 막이 균일하고 조성이 잘 맞는 것을 알 수 있었으며 열처리를 통해 굴절율의 변화를 볼 수 있었다. 그리고 NMOS소자에서의 C-V특성을 개선하기 위해, $Al_2O_3$와 Si사이에 $SiO_2$층을 형성하는 것이 좋음을 알 수 있었다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1277-1279
• /
• 1994

In the structure of ZnO/nip-SiC: H/metal substrate amorphous silicon (a-Si:H) solar cells, the effects of inserting a rear textured ZnO in the p-SiC:H/metal interface and a graded bandgap buffer layer in the i/p-SiC:H have been analysed by computer simulation. The incident light was taken to have an intensity of $100mW/cm^2$(AM-1). The thickness of the a-Si:H n, ${\delta}$-doped a-SiC:H p, and buffer layers was assumed to be $200{\AA},\;66{\AA}$, and $80{\AA}$, respectively. The scattering coefficients of the front and back ZnO were taken to be 0.2 and 0.7, respectively. Inserting the rear buffer layer significantly increases the open circuit voltage($V_{oc}$) due to reduction of the i/p interface recombination rate. The use of textured ZnO markedly improves collection efficiency in the long wavelengths( above ${\sim}550nm$ ) by back scattering and light confinement effects, resulting in dramatic enhancement of the short circuit current density($J_{sc}$). By using the rear buffer and textured ZnO, the i-layer thickness of the ceil for obtaining the maximum efficiency becomes thinner(${\sim}2500{\AA}$). From these results, it is concluded that the use of textured ZnO and buffer layer at the backside of the ceil is very effective for enhancing the conversion efficiency and reducing the degradation of a-Si:H pin-type solar cells.

• 한국세라믹학회지
• /
• 제31권8호
• /
• pp.934-940
• /
• 1994

Fibers of ZrO2-SiO2 system were prepared from the hydrolysis and condensation of Si(OC2H5)4 and Zr(OnC3H7)4 with different H2O/alkoxide molar ratios. It was found that fibers could be drawn in the viscosity range of 1~100 poise from HCl catalyzed solutions with lower water contents of the mole ratio H2O/alkoxide, r 2. The fibrous gels were converted into the corresponding oxide glass fibers by heating at 80$0^{\circ}C$. Mechanical test was performed on E, A and 20ZrO2-80SiO2 glass fibers reinforced cement in order to investigate the flexural strength. The flexural strength value of 20ZrO2-80SiO2 glass fibers reinforced cement was greater than those of E and A. The chemical durability of the fibers in alkaline solutions increased with ZrO2 content. The weight loss due to the corrosion by 2N-NaOH solutions at $25^{\circ}C$ for 160 hours was about 0.31$\times$10-2 mg/dm2 for the 20ZrO2-80SiO2 glass fibers, which was superior to that of Vycor glass.

• 한국재료학회지
• /
• 제12권8호
• /
• pp.650-655
• /
• 2002

$SiO_2$ gels containing dispersed fine Te metal particles have been prepared by the sol- gel method using a starting solution containing Tetraethoxy Silane (Si($OC_2$ $H_{5}$ )$_4$), $H_2$O, Ethylalchol ($C_2$$H_{5}$OH), Nitric Acid ($HNO_3$) and Tellurium Tetracholoride ($TeCl_4$) in a several molar ratio. Gelling time of sols was about 3 days and viscosity of solution was very low about 2~3 cP for 3 days. Heat-treatments of the gel have been performed at 500, 700, 900, 1100 and $1300^{\circ}C$ for 1 hour, respectively. We have investigated TG-DTA, X-ray diffraction patterns and SEM of heat-treatmented gels. The size of Te fine particles dispersed in $SiO_2$ gel was about 0.8~1 $\mu\textrm{m}$ and the shape was almost quadrangle.