• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.356-356
• /
• 2007

Plasma immersion ion beam deposition (PIIBD) technique is a cost-effective process for the deposition of diamond like carbon thin film, the possible solid lubricant on large surface and a complex shape. We used PIIB process for the preparation of DLC thin film on $Al_2O_3$ with deposition conditions of deposition temperature range $200^{\circ}C$, working gas pressure of 1.310-1Pa. DLC thin films were coated by $C_2H_2$ ion beam deposition on $Al_2O_3$ after the ion bombardment of SiH4 as the bonding layer. Energetic bombardment of $C_2H_2$ ions during the DLC deposition to ceramic materials generated mixed layers at the DLC-Si interface which enhanced the interface to be highly bonded. Wear test showed that the low coefficient of friction of around 0.05 with normal load 2.9N and proved the advantage of the low energy ion bombardment in PIIBD process which improved the tribological properties of DLC thin film coated alumina ceramic. Furthermore, PIIBD was recognized as a useful surface modification technique for the deposition of DLC thin film on the irregular shape components, such as molds, and for the improvement of wear and adhesion problems of the DLC thin film, high temperature solid lubricant.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.52 no.2
• /
• pp.56-60
• /
• 2003

In this work, we have fabricated thin film resistors using the DC/RF magnetron sputter of 51wt%Ni-41wt%Cr-8wt%Si alloy target and studied the effect of the process parameters on the electrical properties. In fabrication process, sputtering power, substrate temperature and annealing temperature have been varied as controllable parameters. TCR decreases with increasing the substrate temperature, but TCR increases over 300 [$^{\circ}C$]. The films are annealed to 400 [$^{\circ}C$] in air atmosphere, TCR increases with increasing the annealing temperature. The resistivity was 172 [${\mu}{\Omega}{\cdot}cm$] and 209 [${\mu}{\Omega}{\cdot}cm$] for the RF and DC as a sputtering power sources, respectively. Also, TCR was -52 [$ppm/^{\circ}C$] and -25 [$ppm/^{\circ}C$]. As a results of them, it is suggested that the sheet resistance and TCR of thin films can be controlled by variation of sputter process parameter and annealing of thin film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.207-215
• /
• 1997

Aluminum (Al) thin films were deposited on the Si(100) and TiN(60 nm)/Si (100) substrate by the ionized cluster beam deposition (ICBD) method. The characteristics of thin films were examined by the $\alpha$-step, four-point-probe, Scanning Electron Spectroscopy (SEM), Auger Electron Spectroscopy (AES). The growth rate of the Al thin film increased and the resistivity decreased as the crucible temperature increased. At the crucible temperature $1800^{\circ}C$, the microstructure of Al thin film deposited was smooth and continuous the resistivity decreased as the acceleration voltage increased. Also, the minimum resistivity in Si(100) substrate and TiN(60 nm)/Si(100) substrate were 3.4 $\mu \Omega \textrm {cm}$, 3.6 $\mu \Omega \textrm {cm}$ at the acceleration voltage 4 kV and 2 kV respectively. From the AES spectrumt 14 wasn't detected any impurities In the Al thin film. Therefore the resistivity of Al thin film was affected by the microstructure of film.

• Journal of the Semiconductor & Display Technology
• /
• v.8 no.3
• /
• pp.19-23
• /
• 2009

We have studied dielectric characteristics of low-k interlayer dielectric materials was fabricated by plasma enhanced chemical vapor deposition (PECVD). BTMSM precursor was introduced with the flow rates from 24 sccm to 32 sccm by 2 sccm step in the constant flow rate of 60 sccm $O_2$. Then, SiOCH thin film deposited at room temperature was annealed at temperature of $400^{\circ}C$ and $500^{\circ}C$ for 30 minutes in vacuum. The vibrational groups of SiOCH thin films were analyzed by FT/IR absorption lines, and the dielectric constant of the low-k SiOCH thin films were obtained by measuring C-V characteristic curves. With the result that FTIR analysis, as BTMSM flow rate increase, relative carbon content of SiOCH thin film increased from 29.5% to 32.2%, and increased by 32.8% in 26 sccm specimen after $500^{\circ}C$ annealing. Dielectric constant was lowest by 2.32 in 26 sccm specimen, and decreased more by 2.05 after $500^{\circ}C$ annealing. Also, leakage current is lowest by $8.7{\times}10^{-9}A/cm^2$ in this specimen. In the result, shift phenomenon of chemical bond appeared in SiOCH thin film that BTMSM flow rate is deposited by 26 sccms, and relative carbon content was highest in this specimen and dielectric constant also was lowest value

• Journal of the Microelectronics and Packaging Society
• /
• v.8 no.1
• /
• pp.39-43
• /
• 2001

$SiC_{x}N$_{y}$ film is deposited by electron cyclotron resonance plasma chemical vapor deposition system using $SiH_4$(5% in Ar), $CH_4$ and $N_2$. Ternary phase $SiC_{x}N$_{y}$ thin film deposited at the microwave power of 600 W and substrate temperature of 700 contains considerable amount of strong C-N bonds. Change in $CH_4$flow rate can effectively control the residual film stress, and typical surface roughness of 34.6 (rms) was obtained. Extreme]y high hardness (3952 Hv) and optical transmittance (95% at 633 nm) was achieved, which is suitable for a LIGA mask membrane application.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.9
• /
• pp.121-127
• /
• 1994

The capability for application of rf magnetron sputterred and post annealed BaTiO$_{3}$ thin films in dielectrics AC drived TFELD(thin film electroluminescent device) was investigated. The dielectric constant of the thin films slightly increased up to about 25 with increase fothe post annealing temperature in the range of 210$^{\circ}C$-480$^{\circ}C$. The dielectric loss was about 0.005-0.01 except for the high frequency range above 100kHz and nearly independent on post annealing temperature. The BaTiO$_{3}$ thin film used for TFELD was annealed at 480.deg. C and Si$_{3}$N$_{4}$ thin film was inserted between BaTiO$_{3}$, lower dielecrics and ZnS:Mn, phosphor layer for stable driving of the device and for fear of interdiffusion. Regardless of the frequency of the applied sine wave voltage, the threshold voltage of the prepared TFELD was 65volt and saturated brightness was about 3000cd/m$^{2}$ at 130volt(2kHz sine wave), 65volt above V$_{TH}$.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2002.11a
• /
• pp.477-480
• /
• 2002

Si-O-C(-H) thin film with a tow dielectric constant were deposited on a P-type Si(100) substrate by an inductively coupled plasma chemical vapor deposition (ICPCVD). Bis-trimethylsilymethane (BTMSM, H$_{9}$C$_3$-Si-CH$_2$-Si-C$_3$H$_{9}$) and oxygen gas were used as Precursor. Hybrid type Si-O-C(-H) thin films with organic material have been generated many voids after annealing. Consequently, the Si-O-C(-H) films can be made a low dielectric material by the effect of void. The surface characterization of Si-O-C(-H) thin films were performed by SEM(scanning electron microscope). The characteristic analysis of Si-O-C(-H) thin films were performed by X-ray photoelectron spectroscopy (XPS).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.4
• /
• pp.362-367
• /
• 2008

We have Manufactured the low-k dielectric interlayer fabricated by plasma enhanced chemical vapor deposition (PECVD), The thin film of SiOCH is studied correlation between components and Dielectric constant. The precursor was evaporated and introduced with the flow rates from 16 sccm to 25 sccm by 1sccm step in the constant flow rate of 60 sccm $O_2$ in process chamber. The chemical characteristics of SiOCH were analyzed by measuring FT/IR absorption lines and obtained each dielectric constant measuring C-V. Then compare respectively. ILD of BTMSM/$O_2$ could have low dielectric constant about $k\sim2$, and react sensitively. Also dielectric constant could be decreased by the effects of decreasing $CH_3$ and growing Si-O-Si(C) after annealing process.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.171-171
• /
• 2011

Atmospheric pressure- plasma enhanced chemical vapor deposition(AP-PECVD)Processes are recognized as promising and cost effective methods for wide-area coating on sheets of steel, glass, polymeric web, etc. In this study, $SiO_xC_y$ thin films were deposited by using AP-PECVD with a dielectric barrier discharge(DBD). The characteristic of $SiO_xC_y$ thin films were investigated as afunction of the HMDSO/O2/He flow rate. And the moisture permeability of $SiO_xC_y$ thin films was studied. The $SiO_xC_y$ thin films were characterized by the Fourier-transformed Infrared(FT-IR) spectroscopy and also investigated by X-ray photo electron spectroscopy(XPS), Auger Electron Spectroscopy(AES). The moisture permeability of $SiO_xC_y$ thin films was investigated by $H_2O$ permeability tester Detailed experimental results will be demonstrated through th present work.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.172-175
• /
• 2009

n-type crystalline silicon wafers were passivated with intrinsic a-Si:H thin films on both sides using HWCVD. Minority carrier lifetime measurement was used to verify interface passivation properties between a-Si:H thin film and crystalline Si wafer. Thin film interface characteristics were investigated depending on $H_2/SiH_4$ ratio and hot wire deposition temperature. Vacuum annealing were processed after deposition a-Si:H thin films on both sides to investigate thermal effects from post process steps. We noticed the effect of interface passivation properties according to $H_2/SiH_4$ ratio and hot wire deposition temperature, and we had maximum point of minority carrier lifetime at H2/SiH4 10 ratio and $1600^{\circ}C$ wire temperature.