• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.52-61
• /
• 2003

$SrBi_2Ta_2O_9(SBT)$and$ZrO_2$thin films for MFIS structure(Metal-Ferroelectric-Insulator-Semiconductor) were deposited by RF magnetron sputtering method. In order to investigate the effect of heat treatment of insulator layers and MFIS structure, the insulator layers were heat treated from $550^{circ}C;to; 850^{\circ}C$in conventional furnace or RTA furnace under$O_2$and Ar ambient, respectively. After then, C-V characteristics and leakage current were measured. The capacitor with 20 nm thick $ZrO_2$layer treated at RTA$750^{circ}C;in;O_2$ atmosphere had the largest memory window. The C-V and leakage current characteristics of the$Pt/SBT(260nm)/ZrO_2(20nm)/Si$structure were better than those of$Pt/SBT(260nm)/Si$ structure. These results showed that$ZrO_2$films took a role of buffer layer effectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.307-314
• /
• 1998

PZT thin films were fabricated by the Sol-gel method. Starting materials used for the preparation of the stock solution were Pb-acetate trihydrate, Zr-normal propoxide and Ti-isopropoxide. 2-Methoxyethanol and iso-propanol were used for solution. For studying the diffusion of Pb ion into the substrates. We used bare Si substrate, $SiO_2/Si$ substrates which was produced by thermal oxidation and $TiO_2/SiO_2/Si$ which was mad by Sol-gel method. Densification and adhesion of thin films were observed by SEM. Phase formation of thin films and diffusion of Pb ion into the substrate were examined by XRD and ESCA, respectively. In the case of bare Si and $SiO_2/Si$ substrate, we obtained the perovskite phase at $700^{\circ}C$ and restricted a little the diffusion of Si ion into the film with $SiO_2$ buffer layer. In the case of $TiO_2/SiO_2/Si$, perovskite phase were obtained at $500^{\circ}C$ and the diffusion of Pb ion and Si ion were restriced.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.165-165
• /
• 2003

The growth of GaN on Si is of great interest due to the several advantages low cost, large size and high-quality wafer availability as well as its matured technology. The crystal quality of GaN is known to be much influenced by the surface pretreatment of Si substrate [1]. In this work, the properties of GaN overlayer grown on ion implanted Si(111)and bare Si(111) have been investigated. Si(111) surface was treated ion implantation with 60KeV and dose 1${\times}$10$\^$16//$\textrm{cm}^2$ prior to film growth. GaN epilayers were grown at 1100$^{\circ}C$ for 1 hour after growing AlN buffer layers for 15-30 minutes at 1100$^{\circ}C$ with metal organic chemical vapor deposition (MOCVD). The properties of GaN epilayers were evaluated by X-Ray Diffraction (XRD), Scanning electron microscope (SEM) Photoluminescence (PL) at room temperature and Hall measurement The results showed that the GaN on ion implanted Si(111) markedly affected to the structural, optical and electrical characteristic of GaN layers.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.23 no.6
• /
• pp.656-662
• /
• 2015

In the present study, multi-layered Si DLC (Silicon Diamond-Like Carbon) coatings with HMDSO (Hexamethyldisiloxane) buffer layers are applied on SKD 11 substrates by PECVD (Plasma Enhanced Chemical Vapor Deposition) with different HMDSO gas flow rates, while the gas flow rate of $C_2H_2$ is fixed to enhance the electric resistivity of forming dies for electrically assisted forming. The HMDSO buffer layer is introduced to increase adhesion between the base metal and Si-DLC layers. The result of evaluation of electric resistivity and adhesion strength shows that the properties are affected by the flow rate of HMDSO, while the flow rate of 80 sccm results in the coating with the highest electric resistivity and adhesion strength among the selected flow rates.

• Journal of the Korean Ceramic Society
• /
• v.54 no.6
• /
• pp.492-498
• /
• 2017

A thermal barrier coating (TBC) with self-healing property for cracks was proposed to improve reliability during gas turbine operation, including structural design. Effect of healing agent on crack propagation behavior in TBCs with and without buffer layer was investigated through furnace cyclic test (FCT). Molybdenum disilicide ($MoSi_2$) was used as the healing agent; it was encapsulated using a mixture of tetraethyl orthosilicate and sodium methoxide. Buffer layers with composition ratios of 90 : 10 and 80 : 20 wt%, using yttria stabilized zirconia and $MoSi_2$, respectively, were prepared by air plasma spray process. After generating artificial cracks in TBC samples by using Vickers indentation, FCTs were conducted at $1100^{\circ}C$ for a dwell time of 40 min., followed by natural air cooling for 20 min. at room temperature. The cracks were healed in the buffer layer with the healing agent of $MoSi_2$, and it was found that the thermal reliability of TBC can be enhanced by introducing the buffer layer with healing agent in the top coat.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.67-69
• /
• 2004

The $Pb(Zr,Ti)O_3$ thin films were fabricated with $Pb(La,Ti)O_3$ buffers in-situ onto $Pt/Ti/SiO_2/Si$ substrates by pulsed laser deposition technique using a Nd:YAG laser with energy density of $2.5J/cm^2$, and deposited for 10 minutes at $550^{\circ}C$ of substrate temperature. And then, the films have been annealed at $550^{\circ}C$ in oxygen ambient pressure. The remanent polarization value is increased by using buffer layers but coercive field of films is slightly increased.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.99-99
• /
• 2003

The growth of GaN on Si is of great interest due to the several advantages : low cost, large size and high-quality wafer availability as well as its matured technology. The crystal quality of GaN is known to be much influenced by the surface pretreatment of Si substrate[1]. In this work, the properties of GaN overlayer grown on ion beam modified Si(111) have been investigated. Si(111) surface was treated RIB with 1KeV-N$_2$$\^$+/(at 1.9 ${\times}$ 10$\^$-5/) to dose ranging from 5${\times}$10$\^$15/ to 1${\times}$10$\^$17/ prior to film growth. GaN epilayers were grown at 1100$^{\circ}C$ for 1 hour after growing AlN buffer layers for 5∼30 minutes at 1100$^{\circ}C$ in Metal Organic Chemical Vapor Deposition (MOCVD). The properties of GaN epilayers were evaluated by X-Ray Diffraction(XRD), Raman spectroscopy, Photoluminescence(PL) and Hall measurement. The results showed that the ion modified treatment markedly affected to the structural, optical and electrical characteristic of GaN layers.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.68-69
• /
• 2007

We have prepared p-type ZnO:Al films in pure oxygen ambient on n-type Si (100) and homo buffer layers by RF magnetron sputtering system. Hall effect measurement shows that the film annealed at $600^{\circ}C$ possesses p-type conductivity and the film annealed $800^{\circ}C$ does not. PL spectra show different properties of p- and n-type ZnO film. The corresponding peaks of PL spectra of p- and n-type show at about same positions. The intensities of high photon energy of n-type film on buffer shows decreasing tendency.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.186-189
• /
• 2003

The MFIS capacitors were fabricated using a metalorganic decomposition method. Thin layers of $ZrO_2$ and $CeO_2$ were deposited as a buffer layer on Si substrate and BLT thin films were used as a ferroelectric layer. The electrical and structural properties of the MFIS structure were investigated. X -ray diffraction was used to determine the phase of the BLT thin films and the quality of the $ZrO_2$ and $CeO_2$ layer. AES show no interdiffusion and the formation of amorphous $SiO_2$ layer is suppressed by using the $ZrO_2$ and $CeO_2$ film as buffer layer between the BLT film and Si substrate. The width of the memory window in the C-V curves for the $BLT/ZrO_2/Si$ and $BLT/CeO_2/Si$ structure is 2.94 V and 1.3V, respectively. The experimental results show that the BLT-based MFIS structure is suitable for non-volatile memory FETs with large memory window.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.47-50
• /
• 2000

This paper investigated structural and electrical properties of $Y_2$ $O_3$ as a buffer layer of single transistor FRAM (ferroelectric RAM). $Y_2$ $O_3$ buffer layers were deposited at a low substrate temperature below 40$0^{\circ}C$ and then RTA (rapid thermal anneal) treated. Investigated parameters are substrate temperature, $O_2$ partial pressure, post-annealing temperature, and suppression of interfacial $SiO_2$ layer generation. For a well-fabricated sample, we achieved that leakage current density ( $J_{leak}$) in the order of 10$^{-7}$ A/$\textrm{cm}^2$, breakdown electric field ( $E_{br}$ ) about 2 MV/cm for $Y_2$ $O_3$ film. Capacitance versus voltage analysis illustrated dielectric constants of 7.47. We successfully achieved an interface state density of $Y_2$ $O_3$/Si as low as 8.72x1010 c $m^{-2}$ e $V^{-1}$ . The low interface states were obtained from very low lattice mismatch less than 1.75%.