• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.205-207
• /
• 2009

아크이온플래이팅 기술과 스퍼터링 기술이 결합된 하이브리드 코팅 시스템을 이용하여 STS 304와 Si 기판에 4성분계 Cr-Al-Mo-N 코팅을 증착하였다. $N_2$/Ar 혼합가스 분위기하에 아크 타겟은 Cr을 사용하였고 스퍼터링 타겟은 Al과 Mo를 사용하였으며 합성된 Cr-Al-Mo-N 코팅은 주로 치환고용된 (Cr, Al, Mo)N으로 구성되었다. 최고 경도값은 Mo 함량이 24.2 at.%일 때 35 GPa을 나타냈으며 마찰계수는 Mo의 함량이 0에서 33.2 at.%로 증가함에 따라 0.9에서 0.48로 감소하였다. 이는 $MoO_3$가 코팅면과 스틸볼 계면에서 고체 윤활제로 작용한 것으로 사료된다. 그러나 Cr-Al-Mo-N 코팅은 MoN의 낮은 내산화온도로 인하여 Cr-Al-N에 비하여 더 낮은 온도에서 산화되었다.

• Applied Chemistry for Engineering
• /
• v.31 no.1
• /
• pp.57-60
• /
• 2020

An acetaldehyde, a representative food waste odor, was decomposed using a hybrid system comprised of a non-thermal plasma and catalyst at an ambient temperature under high humidity. A five wt.% Mn was impregnated on two differently structured microporous zeolites, namely Beta and ZSM-5, with a different molar ratio of SiO₂/Al₂O₃. Under high humidity conditions, the acetaldehyde degradation was higher in zeolites with the high ratio of SiO₂/Al₂O₃. Among studied catalysts, a five wt.% Mn/Beta (SiO₂/Al₂O₃ = 300) showed the highest acetaldehyde removal activity owing to its high hydrophobicity and reducibility. During long term stability test using the same catalyst for 110 hours, the acetaldehyde removal activity was relatively well-maintained.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.4
• /
• pp.79-84
• /
• 2017

The solar cells should be protected from the moisture and oxygen in order to sustain the properties and reliability of the devices. In this research, we prepared the protection films on the flexible plastic substrates by spray coating method using organic-inorganic hybrid solutions. The protection characteristics were studied depending on the various process conditions (nozzle distance, thicknesses of the coatings, film structures). The organic-inorganic solutions for the protection film layer were synthesized by addition of $Al_2O_3$ ($P.S+Al_2O_3$) and $SiO_2$ ($P.S+SiO_2$) nano-powders into PVA (polyvinyl alcohol) and SA (sodium alginate) (P.S) organic solution. The optical transmittances of the protection film with the thicknesses of $5{\mu}m$ showed 91%. The optical transmittance decreased from 81.6% to 73.6% with the film thickness increased from $78{\mu}m$ to $178{\mu}m$. In addition, the protective films were prepared on the PEN (polyethylene naphthalate), PC (polycarbonate) single plastic substrates as well as the Acrylate film coated on PC substrate (Acrylate film/PC double layer), and $Al_2O_3$ film coated on PEN substrate ($Al_2O_3$ film/PEN double layer) using the $P.S+Al_2O_3$ organic-inorganic hybrid solutions. The optimum protection film structure was studied by means of the measurements of water vapor transmittance rate (WVTR) and surface morphology. The protective film on PEN/$Al_2O_3$ double layer substrate showed the best water protective property, indicating the WVTR value of $0.004gm/m^2-day$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.200-200
• /
• 2009

아크이온플래이팅 기술과 DC 마그네트론 스퍼터링 기술이 결합된 하이브리드 코팅 시스템을 이용하여 STS 304와 Si 기판에 4성분계 CrAlCxN1-x 코팅을 증착하였다. 합성된 CrAlCxN1-x 코팅은 주로 유도결합형로 f구성되었다. CrAlCxN1-x 코팅의 carbon 함량이 0.17 at.%일 때 약 34 GPa을 나타내었으며 마찰계수는 carbon 함량이 0에서 1 at.%로 증가함에 따라 0.82에서 0.38까지 크게 감소하였다. 이는 코팅 표면과 steel 볼 사이에 amorphous carbon layer가 형성되어 고체윤활제로 작용한 것으로 사료된다.

• Computers and Concrete
• /
• v.21 no.1
• /
• pp.103-110
• /
• 2018

This study introduces the supervised committee fuzzy model as a hybrid fuzzy model to predict compressive strength (CS) of geopolymers prepared from alumina-silica products. For this purpose, more than 50 experimental data that evaluated the effect of $Al_2O_3/SiO_2$, $Na_2O/Al_2O_3$, $Na_2O/H_2O$ and Na/[Na+K] on (CS) of geopolymers were collected from the literature. Then, three different Fuzzy Logic (FL) models (Sugeno fuzzy logic (SFL), Mamdani fuzzy logic (MFL), and Larsen fuzzy logic (LFL)) were adopted to overcome the inherent uncertainty of geochemical parameters and to predict CS. After validating the model, it was found that the SFL model is superior to MFL and LFL models, but each of the FL models has advantages to predict CS. Therefore, to achieve the optimal performance, the supervised committee fuzzy logic (SCFL) model was developed as a hybrid method to combine the benefits of individual FL models. The SCFL employs an artificial neural network (ANN) model to re-predict the CS of three FL model predictions. The results also show significant fitting improvement in comparison with individual FL models.

• Composites Research
• /
• v.33 no.5
• /
• pp.235-240
• /
• 2020

In this study, in order to improve the impact resistance of the B₄C tile-inserted B₄C_p/Al7075 hybrid composite, a control method of the B₄C/Al7075 interface was developed and the characteristics of the controlled interface were analyzed. B₂O₃, Ni, and Si were coated on the B₄C tile surface using additional thermal oxidation, electroless plating, and plasma spraying. The coated B₄C tile is inserted into the B₄C_p/Al7075 composite material using the liquid pressurization method. Interfacial energy, bonding strength, and impact resistance were measured to analyze the effect of the coating. All coatings enhanced interfacial energy, bonding strength, and impact resistance, and in particular, it was confirmed that the impact resistance increased by 86.8% when B₂O₃ coating was used. This study is significant in developing and analyzing a core surface treatment method that improves the performance of B₄C/Al series composites, which are attracting attention as next-generation lightweight amour and bulletproof materials.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.467-473
• /
• 2010

The objective of this study is to prepare lead-free thick film resistor (TFR) paste compatible with AlN substrate for hybrid microelectronics. For this purpose, CaO-ZnO-$B_2O_3-Al_2O_3-SiO_2$ glass system was chosen as a sintering aid of $RuO_2$. The effects of the weight ratio of CaO to ZnO in glass composition, the glass content and the sintering temperature on the electrical properties of TFR were investigated. $RuO_2$ as a conductive and glass powder were dispersed in an organic binder to obtain printable paste and then thick-film was formed by screen printing, followed by sintering at the range between $750^{\circ}C$ and $900^{\circ}C$ for 10 min with a heating rate of $50^{\circ}C$/min in an ambient atmosphere. The addition of ZnO to glass composition and sintering at higher temperature resulted in increasing sheet resistance and decreasing temperature coefficient of resistance. Using $RuO_2$-based resistor paste containing 40 wt%glass of CaO-20.5%ZnO-25%$B_2O_3$-7%$Al_2O_3$-15%$SiO_2$ composition, it is possible to produce thick film resistor on AlN substrate with sheet resistance of $10.6\Omega/\spuare$ and the temperature coefficient of resistance of 702ppm/$^{\circ}C$ after sintering at $850^{\circ}C$.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.4_2
• /
• pp.591-598
• /
• 2023

In this study, the corrosion resistance by salt spray was evaluated using A6061-T6 for an electric vehicle battery pack case coated with an organic/inorganic hybrid solution. The lowest curing temperature of 190 ℃ resulted in significant corrosion and pitting. Meanwhile, no corrosion was observed in the coated specimens at 210 ℃ and 230 ℃ except at 210 ℃ - 6 min and 8 min. The surface of the as-received coating specimen observed by FE-SEM exhibited streaks and dents in the rolling direction, but the coating surface was clean. On the 190 ℃ - 6 min coating specimen, which had a lot of corrosion, rolling streaks spread, and dents were caused by corrosion. The 200 ℃ - 12 min coating specimen did not show corrosion, but it showed an etched surface. In the line profile, Si, the main component of the coating solution, was detected the most, and Ti was also detected. In the coating specimens with salt spray, O increased and Si decreased, regardless of corrosion. The peeling rate by adhesion evaluation was 26 - 87% for the 190 ℃ coating specimen, 4 - 83% for the 210 ℃ coating specimen, and 94 - 100% for the 230 ℃ coating specimen. The optimal curing conditions for the coating solution used in this study were 210 ℃ for 10 min.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.79-79
• /
• 2012

A high temperature and a low temperature plasma process technologies were developed and demonstrated for synthesis, hybrid formation, surface treatment and CVD engineering of nano powder. RF thermal plasma is used for synthesis of spherical nano particles in a diameter ranged from 10 nm to 100 nm. A variety of nano particules such as Si, Ni, has been synthesized. The diameter of the nano-particles can be controlled by RF plasma power, pressure, gas flow rate and raw material feed rate. A modified RF thermal plasma also produces nano hybrid materials with graphene. Hemispherical nano-materials such as Ag, Ni, Si, SiO2, Al2O3, size ranged from 30 to 100 nm, has been grown on graphene nanoplatelet surface. The coverage ranged from 0.1 to 0.7 has been achieved uniformly over the graphene surface. Low temperature AC plasma is developed for surface modification of nano-powder. In order to have a three dimensional and lengthy plasma treatment, a spiral type of reactor has been developed. A similar plasma reactor has been modfied for nano plasma CVD process. The reactor can be heated with halogen lamp.

• Composites Research
• /
• v.23 no.2
• /
• pp.10-16
• /
• 2010

$Al_2O_3$ fiber and SiC particle hybrid metal matrix composites (MMCs) were manufactured by squeeze casting method investigated for their tribological properties. The pin specimens had different ratios of fiber to particle content but their total weight fraction was constant at 20 wt. %. Tribological tests were performed with a pin-on-disk friction and wear tester. The investigation of the dry tribological characteristics of hybrid MMCs were carried out at room temperature and elevated temperature of$100^{\circ}C$ and$150^{\circ}C$. The morphologies of worn surfaces were examined by scanning electron microscope (SEM) to observe tribological characteristics and investigate wear behavior. The results revealed that the wear resistance improved with the content of SiCp increased of the planar random (PR) MMCs at room temperature. At the elevated temperature, it revealed that the wear resistance of normal (N) MMCs was superior to that of the PR-MMCs due to PR-fibers were easily pulled out holistically from the worn surface. Meanwhile, the coefficient of friction decreased with the temperature increasing.