• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2005년도 춘계학술대회 논문집
• /
• pp.391-396
• /
• 2005

Salt water spray test and salt water immersion test were experimentally conducted in order to investigate the durability of fiber reinforced composites under salt water environment. The specimens were made of glass fabric reinforcement and phenolic resin. Mechanical test was performed to obtain mechanical properties such as tensile properties, flexural properties, and shear properties by varying with exposure times. Also dynamic mechanical test and FTIR were conducted to investigate a change in chemical structure as well as thermal analysis properties such as storage shear modulus, loss shear moduls, and tan ${\delta}$. According to the results, salt water environment has effected on mechanical properties and thermal analysis properties and especially the durability of glass fabric/phenolic composites were severely affected on salt water immersion environment rather than salt water spray environment.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.852-858
• /
• 2007

The durability of carbon/epoxy composites under salt water environment was investigated through salt water spray tester. Salt water environment was obtained through salt spray and salt immersion. 5% NaCl solution was used for salt water as natural salt water. Mechanical test was performed to obtain tensile properties, flexural properties, and shear properties of carbon/epoxy composite over 12 months under salt water environment. Dynamic mechanical analyzer was used to investigate thermal analysis properties such storage modulus, loss modulus, and tan ${\delta}$. Also FT/IR test was conducted to investigate a change in chemical structure. According to the results, mechanical properties were found to be slowly degraded as a function of exposure times. Regarding to thermal analysis properties, storage modulus was insensitive to exposure times, but loss modulus was shown to be slightly decreased. Although the shape and location of peak in FT/IR were not much changed, the intensity of peak in FT/IR was affected on exposure times. We also found that salt water immersion was more severe to the durability of carbon/epoxy composite rather than salt water spray.

• Composites Research
• /
• 제21권6호
• /
• pp.1-7
• /
• 2008

본 연구에서는 염수환경이 고강성 탄소-에폭시 복합재의 기계적 특성에 미치는 영향을 살펴보았다. 시편은 UPN139B 탄소-에폭시 복합재로 제작하였고, 3.5% 염수에 0, 1, 3, 6, 9, 12개월 간의 침수 후 면내 인장시험과 전단시험을 수행하였다. 실험에서 온도 조절과 같이 흡수 시간을 절약하기 위한 특별한 가속방법은 사용하지 않았다. 섬유방향 및 기지방향 인장강도와 강성의 경우 12개월 동안의 침수에도 불구하고 특별한 변화를 발견할 수 없었다. 반면 12개월 침수 후 전단강도와 강성은 염수에 노출되지 않은 시편에 비해 약 10% 내외의 감소를 보였다. 본 연구를 통하여 UPN139B가 우수한 섬유방향 강성과 내부식성으로 인하여 염수환경에서 외부수압에 의한 좌굴을 지지해야 하는 구조물의 설계에 효과적으로 사용될 수 있음을 확인하였다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.722-727
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.56mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability

• 한국군사과학기술학회지
• /
• 제7권1호
• /
• pp.5-12
• /
• 2004

This paper includes the comparative study between Cr plating and nitriding process with an aim at improving corrosion, wear and maintainability for KNR(Korean Next Generation Rifle) 5.5mm barrel. The endurance test was conducted to compare the performance of standard barrel, Cr plating barrel and nitriding barrel. Main activities are described as follows; optimal Cr plating and nitriding process set-up for KNR 5.56mm barrel; durability test of each barrel(20,000 rounds); salt water immersion test; dispersion, initial velocity, inner diameter data acquisition. According to the results of this firing test, Cr plating barrel is superior to standard barrel and nitriding barrel in view of corrosion, wear and maintainability.

• 대한기계학회논문집A
• /
• 제36권10호
• /
• pp.1261-1266
• /
• 2012

본 연구에서는 최대 12개월 동안 염수침수시험을 수행하여 염수환경의 열습조건이 복합재의 특성에 미치는 영향을 조사하였다. 복합재 시편은 직물 형태의 탄소섬유와 에폭시로 구성된 프리프레그를 적층하여 제작하였으며, 노출온도 $35^{\circ}C$, $55^{\circ}C$, $75^{\circ}C$가 적용된 염수환경에 완전 침수시키는 조건을 적용하였다. 연구결과에 따르면 복합재의 인장강성과 인장강도는 노출온도와 노출시간이 증가할수록 노출전에 비해 감소 정도가 크지 않았지만 이에 비해 압축강성과 압축강도는 감소 정도가 크게 나타났다. 특히 압축강도는 노출온도가 증가할수록 염수침투가 가속화되어 감소 정도가 크게 나타났다.

• Composites Research
• /
• 제21권3호
• /
• pp.1-8
• /
• 2008

본 연구에서는 염수환경이 탄소-에폭시 복합재의 기계적 물성치에 미치는 영향을 살펴보았다. 시편은 USN125 복합재로 제작하였고, 3.5% 염수에 0, 0.5. 1, 2, 3, 6, 9, 12 개월간의 침수 후 면내 인장시험과 전단시험을 수행하였다. 실험에서 염수로부터 시편을 보호하기 위한 방수페인트나 시간을 절약하기 인한 특별한 가속방법은 사용하지 않았다. 섬유방향 및 기지방향 인장강도와 강성의 경우 12개월 동안의 침수에도 불구하고 특별한 물성치의 변화를 발견할 수 없었다. 반면 전단강도와 강성은 염수환경에 민감하게 반응하며. 12개월 침수 후의 물성치는 염수에 노출되지 않은 시편에 비해 전단강도 30%, 전단강성 46%의 저하를 보였다.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.395-400
• /
• 2016

This article reports improved corrosion resistance and adhesion of electro-paint (E-paint) with fluoride conversion coating (FCC) on AZ31 Mg alloy for the first time. These improvements were observed in comparison to chemically polished samples with no chemical conversion coating and samples with cerium conversion coatings (CeCC). FCCs were prepared in a hydrofluoric acid (HF) solution for four different times; 10, 30, 60, and 120 s. The colour of the samples changed from light gold to brown with increasing immersion time, indicating the formation of thicker FCC coatings with increasing immersion time. The adhesion of the E-paint on FCC-coated AZ31 Mg alloy was tested after 500 h of immersion in deionized (DI) water. Salt spray test (SST) results revealed delamination of E-paint on the chemically polished sample, severe blistering on the samples with CeCC, but no delamination and no blistering on the samples with FCC.

• Composites Research
• /
• 제18권4호
• /
• pp.27-34
• /
• 2005

염수시험기를 통해 6개월 동안 염수분무시험과 염수침수시험을 수행함으로써 염수환경에 노출된 유리섬유직물페놀 복합재의 내구성을 실험적으로 조사하였다. 이때 염수환경에 노출된 시간에 따른 인장특성, 굽힘특성, 전단특성 등의 기계적 특성을 평가하고 동역학 측정장치를 적용하여 저장전단탄성계수. 손실전단탄성계수, tan $\delta$ 등의 열분석 특성을 측정하였다. 또한 적외선 분광분석기를 적용하여 염수환경에의 노출시간에 따른 화학구조의 변화를 분석하였다. 연구결과에 따르면 기계적 특성과 열분성 특성은 노출시간에 민감하게 변하며 노출시간이 길어짐에 따라 점차 감소되는 양상을 나타낸다. 그러나 강성의 경우에는 염수환경에 노출되면 복합재의 가소화로 인해 노출의 초기에는 감소하기 시작하고 노출시간이 길어짐에 따라 복합재의 팽창, 수지의 소성화, 가교 결합의 증가 등으로 인해 다소 증가하는 양상을 나타내지만 노출시간이 더욱 더 길어지면 점차 감소할 것으로 추측된다. 또한 FT-IR 선도에서의 피크 형상과 위치는 노출시간에 큰 영향을 받지 않으며 피크 세기는 노출시간에 따라 달라진다. 마지막으로 염수침수환경은 염수분무환경에 비해 유리섬유직물/복합재의 내구성에 더욱 심각한 영향을 미침을 알 수 있었다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제27권5호
• /
• pp.16-22
• /
• 2023

이 연구는 원전 콘크리트 배합설계를 모사한 콘크리트 시험체에 대하여 염수침지 실험을 수행하였으며, 시험체 깊이에 따른 염화물량과 XRF 성분의 상관관계를 분석하였다. 원전 콘크리트의 표면부의 염화물량은 염수 침지기간이 증가함에 따라 소폭 증가하였으나, 깊이 5.5 mm 이상의 콘크리트 시험체 내부 염화물량은 염수 침지기간이 증가함에 증가하는 경향이 뚜렷하게 나타났다. 콘크리트의 염화물량과 XRF 성분의 상관관계 분석결과, OPC 배합과 비교하여 FA가 20% 치환된 배합은 XRF 성분분석을 통한 Cl 이온의 구성비율과 염해저항성 평가결과의 상관관계가 매우 높게 나타났다. 이에 따라 FA가 20% 치환된 원전 콘크리트 배합에서는 반복적인 데이터 누적을 통해 XRF 성분분석을 통하여 염소이온분석 및 염해저항성능 평가가 가능함을 확인하였다.