• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.360-364
• /
• 2003

$Sr_{l}$ $\pm$x/$Bi_{2}$ $\pm$y/$Ta_2$ $O_{9}$ and $Sr_{l}$ $\pm$$Bi_{x}$ $2\pm$y$Nb_2$$O_{9}$ ceramics were prepared by a solid state reaction method. X-ray diffraction analysis indicated that single-phase of Bi-layered perovskite was obtained. According to Sr/Bi content ratio, Curie temperature( $T_{c}$), electromechanical factor($K_{p}$ ) and mechanical quality factor($Q_{m}$ ) were measured. The Curie temperature of SBN(SBT) rose from $414^{\circ}C$(314$^{\circ}C$) to $494^{\circ}C$(426$^{\circ}C$) when Sr/Bi content ratio was increased. In the case of Sr/Bi content ratio = 0.55/2.3, the maximum value of the mechanical quality factor $Q_{m}$ of SBT and SBN were obtained 3320 and 1010, respectively.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.992-999
• /
• 1999

Due to the inherently poor adhesion strength of Cu-based leadframe/EMC(Epoxy Molding Compound) interface, popcorn-cracking phenomena of thin plastic packages frequently occur during the solder reflow process. In this study, in order to enhance the adhesion strength of Cu-based leadframe/EMC interface, brown-oxide layer was formed on the leadframe surface by immersing of leadframe sheets in hot alkaline solution, and the adhesion strength of leadframe/EMC interface was measured by using SDCB(Sandwiched Double Cantilever Beam) and SBN(Sandwiched Brazil-Nut) specimens. Results showed that brown oxide treatment of leadframe introduced fine acicular CuO crystals on the leadframe surface and improved the adhesion strength of leadframe/EMC interface. Enhancement of adhesion strength was directly related to the thickening kinetics of oxide layer. This might be due to the mechanical interlocking of fine acicular CuO crystals into EMC.

• 프린팅코리아
• /
• v.11 no.1
• /
• pp.112-115
• /
• 2012

국립중앙도서관(관장 우진영)은 최근 국립중앙도서관 국제회의장에서 대한출판문화협회와 공동으로 '도서관과 출판계의 상호발전과 협력'을 주제로 세미나를 개최했다. 김기태 교수(세명대학교)사회로 진행된 이번 세미나는 표정훈 출판평론가의 '최근 우리 출판계 동향과 전망' 발표를 시작으로 곽철완 교수의 '납본제도 현황과 발전', 최성구 출판유통진흥원 기획팀장의 '국제표준도서번호(SBN)제도운영 활성화: 전자출판물, 정부간행물 ISBN 부여 중심으로', 오혜영 국가서지정보센터추진단 사무관의 '출판시도서목록(CIP)제도운영 현황과 신청안내'에 대한 주제발표와 참석자들의 질의 응답 순으로 진행됐다. 본지는 표정훈 출판평론가가 발표한 '최근 우리 출판계 동향과 전망' 발표를 요약 정리한다.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2002.05a
• /
• pp.942-947
• /
• 2002

In this study, reduction of airborne and structure-borne noise of naval ship pump is presented. Since piping system arrangement such as valve location, flexible joint, pipe diameter and elbow location, discharge basin affect greatly on the noise measurement, care must be taken to minimize the unnecessary noise from the piping system. It is shown that structure-borne noise of the motor with single resilient mount system exceeds criterion. Therefore, it is concluded that double resilient mount system is inevitable. Two kinds of mount is studied for upper mount; spring and rubber type. Although both mounts show good performance at low frequency including rpm frequency, 63Hz, spring mount is found to be inadequate at high frequency, because spring coil acts as a path for SBN.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2003.11a
• /
• pp.751-755
• /
• 2003

In this paper, floor impact noise reduction in a steel structure is studied. A mock-up is built by using 6t steel plate, and two identical cabins are made where 25t panel is used to construct wall and ceiling inside the steel structure. Various floating floor systems are tested for which normalized impact noise is measured according to ISO 140-7. In addition, floor SBN(Structure-borne Noise) and floor damping are measured to study the effect of floating floor. structure. It is shown that VL(Visco-elastic Layer) is more effective when hard plates are added above the VL.

• Journal of the Society of Naval Architects of Korea
• /
• v.41 no.5
• /
• pp.41-47
• /
• 2004

In this paper, floor impact noise reduction in cruise ship cabin is studied. A mock-up is built by using 6t steel plate, and two identical cabins are made where 25t panel is used to construct wall and ceiling inside the steel structure. Various floating floor systems are tested for which normalized impact noise is measured according to ISO 140-7. In addition, floor SBN (Structure-borne Noise) and floor damping are measured to study the effect of floating floor structure. It is shown that VL(Visco-elastic Layer) is more effective when hard plates are added above the VL.

• Journal of the Korean Physical Society
• /
• v.73 no.10
• /
• pp.1561-1565
• /
• 2018

The dielectric properties of the uniaxial relaxor ferroelectric $Sr_xBa_{1-x}Nb_2O_6$ with x = 0.75 were investigated along the polar [001] direction as a function of temperature. The capacitance maximum showed the frequency dispersion commonly observed in relaxors. Additional weak dielectric anomalies were observed in the paraelectric phase; they were only seen during the heating process and disappeared upon subsequent cooling. These were attributed to the existence of large polar clusters strongly pinned at defects and/or to random fields and their metastable characters. Aligning the ferroelectric domains along the polar axis at room temperature removed the high-temperature dielectric anomalies. The dependences of the capacitance and the dielectric maximum temperature on the magnitude of the poling field were investigated.

• Special Issue of the Society of Naval Architects of Korea
• /
• 2011.09a
• /
• pp.112-116
• /
• 2011

The noise analysis is usually carried out in the early structure design stage for the main areas in a vessel such as an accommodation, an engine room, HVAC System and etc. If the analysis results are higher than the noise limits based on guideline, appropriate countermeasures are established to reduce noise levels and applied to the vessel. But excessive noise induced the main or auxiliary equipment and high pressure steam system is very difficult to check in the initial design stage, and local noise problems frequently appear in actual vessels. This paper deals with excessive noise of the engine control room on LNG carrier. It includes the cause analysis of excessive noise, the countermeasure, and verification. Also, it proves suitability of the countermeasure through the on-board test.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.346-347
• /
• 2006

기계적 품질계수(Qm)를 향상시키기 위해 $Y_2O_3$와 $MnO_2$를 첨가함에 따른 $SrBi_2Nb_2O_9$ 세라믹스의 강유전 특성을 알아보았다. 합성분말의 입도를 분석 한 결과 $SrBi_2Nb_2O_9$의 경우 781.27nm였고, $Y_2O_3$와 $MnO_2$를 첨가한 경우 각 각 830.4nm와 981.1nm로 particle size는 증가하였고, 소결 후 소결밀도는 차이가 거의 없었으며, grain size는 $SrBi_2Nb_2O_9$과 $Y_2O_3$를 첨가했을 경우 $1{\mu}m$이하이며 반면, $MnO_2$를 첨가하였을 때 결정립이 성장하여 $3{\sim}4{\mu}m$로 나타났다. 또한, 모두가 $450^{\circ}C$ 이상의 상전이온도를 갖았다.

• Proceedings of the Optical Society of Korea Conference
• /
• 2000.02a
• /
• pp.288-289
• /
• 2000

SBN, BSKNN KNSBN 등의 tungsten-bronze 계열에 속하는 광굴절 결정은 짧은 파장에서 좋은 감광도와 빠른 응답시간을 갖는다. 이중에서도 KNSBN 결정은 큰 크기의 결정 성장 및 도핑이 용이하고 광굴절 결정에서 중요한 특성 중 하나인 열 안정성(thermal stability)이 좋기 때문에 빠른 응답특성이 요구되는 응용분야에서 촉망받는 매질이다. 본 논문에서는 광정보저장, 광정보처리, 광컴퓨터, 광통신과 같은 다양한 분야에서 응용가능성을 가지는 Cu가 0.04wt.%도핑된 5mm$\times$5mm$\times$5mm 크기의 KNSBN 결정을 이용한 광신호의 증폭기술에 대하여 연구하였다. 먼저 Cu-KNSNB 결정의 2광파 결합 특성을 분석하기 위하여, 기록 파장에 따른 지수이득계수의 외부입사각의존성, 최대 지수이득계수를 나타내는 외부입사각에서 입사빔의 세기비에 따른 2광파 결합 이득을 측정하였다. 또한, 632.8nm파장 영역에서 기록 및 삭제시간 상수, 회절 효율의 입사빔 세기비 의존성을 측정하였다. 그리고, 음향-광학 변조기(AOM: acousto-optic modulator)에 의해 진폭 변조된 신호빔을 이용하여 광신호 증폭특성을 분석하고 그 결과를 제시하였다. 이때 두 빔의 입사각은 최대 지수이득계수를 나타내는 입사반각 12$^{\circ}$로 고정하고, 감쇄기를 이용하여 신호빔의 세기를 조절하면서 신호빔의 차동이득을 측정하였다. 투과된 신호빔은 같은 주파수에서 차동 이득(diffrerential gain)을 보였으며, 이는 moving grating과 시간-변조된 신호빔(또는 펌프빔)사이의 새로운 상호작용은 광굴절 결정의 시간 적분 특성에 의한 것이다. (중략) 경우는 상온에서 펌프 펄스의 유지시간이 0.5% 인 경우 레이저가 동작하는 것을 보여주었다. 이는 구조내에서 열전도가 문제가 된다는 것을 의미하는데 위아래가 공기로 둘러 싸여 있어 발생한 열이 가는 유전체 네트웍을 통해서만 전달 될 수 있기 때문이다. (중략)$^4$A$_2$에 의한 nophonon line R$_1$, R$_2$(680.4, 678.5 nm) 및 $^2$T$_1$$\longrightarrow$$^4$A$_2$(655.7, 649.3, 645.2 nm)의 형광방출 스펙트럼을 얻었으며, 형광수명은 0.264 ms로 조사되었다. 제조된 레이저 발진봉은 직경 6.3 m, 길이 45 nm이었다.\pm$0.06kHz Ge $F_4$; -1.84$\pm$0.04kHz$0.04kHz/TEX>0.04kHz 모국어 및 관련 외국어의 음운규칙만 알면 어느 학습대상 외국어에라도 적용할 수 있는 보편성을 지니는 것으로 사료된다.없다. 그렇다면 겹의문사를 [-wh]의리를 지 닌 의문사의 병렬로 분석할 수 없다. 예를 들어 누구누구를 [주구-이-ν가] [누구누구-이- ν가]로부터 생성되었다고 볼 수 없다. 그러므로 [-wh] 겹의문사는 복수 의미를 지닐 수 없 다. 그러면 단수 의미는 어떻게 생성되는가\ulcorner 본 논문에서는 표면적 형태에도 불구하고 [-wh]의미의 겹의문사는 병렬적 관계의 합성어가 아니라 내부구조를 지니지 않은 단순한 단어(minimal $X^{0}$ elements)로 가정한다.