• Restorative Dentistry and Endodontics
• /
• v.23 no.2
• /
• pp.656-669
• /
• 1998

Hydrogen peroxide at high concentration during walking bleaching may cause damage to the tooth structure and to the surrounding periodontal tissues and may develop external root resorption. Clinically, It is so important to find a method of prevention or minimization of these complications. The efficacy of various chamber-irrigating agents to eliminate residual hydrogen peroxide after walking bleaching was examined and compared with water rinse in this study. Extracted human 46 premolars without any cementoenamel junction defects were treated endodontically and based with IRM to 1 mm below CEJ and totally bleached 3 times for each tooth with 30% hydrogen peroxide and sodium perborate. Upon completion of the 3rd walking bleaching procedure, the cervical portion and pulp chamber of each group of teeth were irrigated with catalase, 70% ethylalcohol, acetone, and distilled water. And then, a radicular hydrogen peroxide penetration was measured with spectrophotometer immediately after each bleaching and following treatment with each chamber-irrigating agents, and the significance of their eliminating efficacy of residual hydrogen peroxide was analyzed by Kruskal-Wallis test. The results were obtained as follows. 1. Cervical root penetration of hydrogen peroxide was increased as the bleaching procedure was repeated(P<.01). 2. The most effective irrigant that removed residual hydrogen peroxide was the catalase, and the least effective one was water rinsing (P<.01).; there was no significant difference between the acetone and ethanol group. 3. The Irrigation with antioxidant enzyme or water-displacement solutions can eliminate residual oxygen radicals from the pulp chamber effectively after walking bleaching. So, these agents can reduce adverse effects such as cervical external resorption and periapical inflammation and prevent residual $O_2$ from impeding composite resin polymerization, thus increase the bonding strength of composite resin. This, in turn reduces microleakage and discoloration of the esthetic restoration, extending its service-life.

• Restorative Dentistry and Endodontics
• /
• v.34 no.3
• /
• pp.199-207
• /
• 2009

The objective of this study was to evaluate the effect of color measuring instrument by measuring the color of dental composite resins. Nine shade light cured composite resin disks were prepared (diameter : 15 mm, thickness : 4 mm). CIE $L^*a^*b^*$ color scale of each disk was measured with 3 different types of spectrophotometer [MiniScan XE plus (Model 4000S, Hunter Lab, USA), CM-3500d (Minolta, Japan) and Specbos 2100 Miniature VIS Reflection spectrometer (Serial No: 319416, JETI Technishe VIS Instrumentic GmbH. Germany)]. Miniscan XE Plus and CM-3500d using identical measuring geometry with different size of viewing aperture. But Specbos 2100 using different measuring geometry. Within the limitation of this study, there were color difference (${\Delta}E^*$) from 2.4 to 7.8 between Miniscan XE Plus and CM-3500d, but $L^*$, $a^*$, $b^*$ values showed the high correlation. However, there were great color difference (${\Delta}E^*$) in the extent of about 20 between instruments with the different measuring geometry. Therefore, color scale measured by color measuring instrument should be used as a relative value rather than an absolute value in the field of dentistry.

• Restorative Dentistry and Endodontics
• /
• v.27 no.2
• /
• pp.158-174
• /
• 2002

The aim of this study was to investigate the effect of light irradiation modes on polymerization shrinkage, degree of cure and microleakage of a composite resin. VIP$^{TM}$ (Bisco Dental Products, Schaumburg, IL, USA) and Optilux 501$^{TM}$ (Demetron/Kerr, Danbury, CT, USA) were used for curing Filtek$^{TM}$ Z-250 (3M Dental Products, St. Paul., MN, USA) composite resin using following irradiation modes: VIP$^{TM}$ (Bisco) 200mW/$\textrm{cm}^2$ (V2), 400mW/$\textrm{cm}^2$ (V4), 600mW/$\textrm{cm}^2$ (V6), Pulse-delay (200 mW/$\textrm{cm}^2$ 3 seconds, 5 minutes wait, 600mW/$\textrm{cm}^2$ 30seconds, VPD) and Optilux 501$^{TM}$ (Demetron/Kerr) C-mode (OC), R-mode (OR). Linear polymerization shrinkage of the composite specimens were measured using Linometer (R&B, Daejeon, Korea) for 90 seconds for V2, V4, V6, OC, OR groups and for up to 363 seconds for VPD group (n=10, each). Degree of conversion was measured using FTIR spectrometer (IFS 120 HR, Bruker Karlsruhe, Germany) at the bottom surface of 2 mm thick composite specimens V2, Y4, V6, OC groups were measured separately at five irradiation times (5, 10, 20, 40, 60 seconds) and OR, VPD groups were measured in the above mentioned irradiation modes (n=5 each). Microhardness was measured using Digital microhardness tester (FM7, Future-Tech Co., Tokyo, Japan) at the top and bottom surfaces of 2mm thick composite specimens after exposure to the same irradiation modes as the test of degree of conversion(n=3, each). For the microleakage test, class V cavities were prepared on the distal surface of the ninety extracted human third molars. The cavities were restored with one of the following irradiation modes : V2/60 seconds, V4/40 seconds, V6/30 seconds, VPD , OC and OR. Microleakage was assessed by dye penetration along enamel and dentin margins of cavities. Mean polymerization shrinkage, mean degree of conversion and mean microhardness values for all groups at each time were analyzed using one-way ANOVA and Duncan's multiple range test, and using chi-square test far microleakage values. The results were as follows : . Polymerization shrinkage was increased with higher light intensity in groups using VIP$^{TM}$ (Bisco) : the highest with 600mW/$\textrm{cm}^2$, followed by Pulse-delay, 400mW/$\textrm{cm}^2$ and 200mW/$\textrm{cm}^2$ groups, The degree of polymerization shrinkage was higher with Continuous mode than with Ramp mode in groups using Optilux 501$^{TM}$ (Demetron/Kerr). . Degree of conversion and microhardness values were higher with higher light intensity. The final degree of conversion was in the range of 44.7 to 54.98% and the final microhardness value in the range of 34.10 to 56.30. . Microleakage was greater in dentin margin than in enamel margin. Higher light intensity showed more microleakage in dentin margin in groups using VIP$^{TM}$ (Bisco). The microleakage was the lowest with Continuous mode in enamel margin and with Ramp mode in dentin margin when Optilux 501$^{TM}$ (Demetron/Kerr) was used.

• Proceedings of the KACD Conference
• /
• 2008.05a
• /
• pp.246-257
• /
• 2008

The purpose of this study was to investigate the influence of various occlusal loading sites and directions on the stress distribution of the cervical composite resin restorations of maxillary second premolar, using 3 dimensional (3D) finite element (FE) analysis. Extracted maxillary second premolar was scanned serially with Micro-CT (SkyScan1072; SkyScan, Aartselaar, Belgium). The 3D images were processed by 3D-DOCTOR (Able Software Co., Lexington, MA, USA). HyperMesh (Altair Engineering. Inc., Troy, USA) and ANSYS (Swanson Analysis Systems. Inc., Houston, USA) was used to mesh and analyze 3D FE model. Notch shaped cavity was filled with hybrid (Z100, 3M Dental Products, St. Paul, MN, USA) or flowable resin (Tetric Flow, Viva dent Ets., FL-9494-Schaan, Liechtenstein) and each restoration was simulated with adhesive layer thickness ($40{\mu}m$). A static load of 200 N was applied on the three points of the buccal incline of the palatal cusp and oriented in $20^{\circ}$ increments, from vertical (long axis of the tooth) to oblique $40^{\circ}$ direction towards the buccal. The maximum principal stresses in the occlusal and cervical cavosurface margin and vertical section of buccal surfaces of notch-shaped class V cavity were analyzed using ANSYS. As the angle of loading direction increased, tensile stress increased. Loading site had little effect on it. Under same loading condition. Tetric Flow showed relatively lower stress than Z100 overall, except both point angles. Loading direction and the elastic modulus of restorative material seem to be important factor on the cervical restoration.

• Restorative Dentistry and Endodontics
• /
• v.35 no.6
• /
• pp.445-452
• /
• 2010

Objectives: The aim of this study was to compare apical sealing ability and physical properties of MTA, MTA - AH-plus mixture (AMTA) and experimental Portland cement - Epoxy resin mixture (EPPC) for a development of a novel retro-filling material. Materials and Methods: Forty-nine extracted roots were instrumented and filled with gutta-percha. Apical root was resected at 3 mm and the retro-filling cavity was prepared for 3 mm depth. Roots were randomly divided into 3 groups of 15 roots each. The retro-filling was done using MTA, AMTA, and EPPC as the groups divided. Four roots were used as control groups. After setting in humid condition for 24 hours, the roots were immersed in 1% methylene blue dye solution for 72 hours to test the apical leakage. After immersion, the roots were vertically sectioned and photos were taken to evaluate microleakage. Setting times were measured with Vicat apparatus and digital radiographs were taken to evaluate aluminum equivalent thickness using aluminum step wedge. The results of microleakage and setting time were compared between groups using one-way ANOVA and Scheffe's post-hoc comparison at the significance level of 95%. Results: AMTA and EPPC showed less microleakage than MTA group (p < 0.05). AMTA showed the highest radio-opacity than other groups and the novel EPPC showed 5 mm aluminum thickness radio-opacity. EPPC showed the shortest initial and final setting times than other groups while the MTA showed the longest (p < 0.05). Conclusions: Under the condition of this study, the novel composite using Portland cement-Epoxy resin mixture may useful for retro-filling with the properties of favorable leakage resistance, radio-opacity and short setting time.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.2
• /
• pp.370-378
• /
• 2000

The composite restorative resins have their insufficient resistance to wear. The subsurface degradation within the restoration is considered to be associated with wear. The aim of this study was to evaluate the resistance to degradation of six commercial composite resins in an alkaline solution. The brands studied were Clearfil APX(Kuraray), Heliomolar(Vivadent), Surefil(Dentsply), TPH(Dentsply), Tetric Ceram(Vivadent), and Z100(3M). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCL, washed with water and dried to constant mass at $60^{\circ}C$. Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights; (b) Si loss (ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({\mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The mass loss was in descending order by Z100, TC H, S, CL, TPH and in the range of $0.45\sim3.64%$ 2. The degradation layer depth was in descending order by H, Z100, S, TC, TPH, CL and in the range of $10.85\sim73.38{\mu}m$ 3. For the Si concentration, Z100 was the highest of all 4. The highly significant correlation(r=0.81, p<0.05) was observed between mass loss and degradation depth. 5. Under scanning electronmicroscopy, the degradation of connection between resin matrix and fillers was observed 2 weeks after soaking in NaOH solution.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.3
• /
• pp.469-477
• /
• 2002

One of the major deficiencies of composite restorative resins is their insufficient resistance to wear. Of the multitude of factors that have been associated with wear, subsurface degradation within the restoration is considered to be one. The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. The brands studied were Z100(3M), Clearfil AP-X(Kuraray), Tetric Ceram(Vivadent), Aelit flo(Bisco). Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights: (b) Si loss(ppm) - obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth(${\mu}m$) - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The sequence of the mass loss was in ascending order by AE, EL, TC, Z100. There was statistically significant difference of mass loss between AE, CL group and TC, Z100 group(p<0.05). 2. The sequence of the degree of degradation layer depth was in ascending order by AE, CL, TC, Z100. But there was no statistically significant difference of degree of degradation layer depth between AE and CL(p<0.05). 3. For the Si concentration, Z100 was the highest of all. 4. The correlation coefficient between mass loss and degradation depth was relatively high(r=0.71 p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.23 no.2
• /
• pp.618-629
• /
• 1998

CAD/CAM-fabricated ceramic restorations nowadays are used as alternatives of amlagam and posterior composite resin restorations, especially in the cases of inlay restorations. But the reported results on marginal and internal fit of CAD/CAM-fabricated ceramic inlay have showed considerable difference. In this study, to evaluate the marginal and internal fit of CEREC2-fabricated ceramic inlay restoration and to compare with the fit of gold inlay and amalgam restoration, standardized Class II MO cavities were prepared in forty extracted caries-free human premolars. The teeth with prepared cavities were divided into 4 groups of ten teeth each. In group 1, CEREC2-fabricated ceramic inlays were treated with Scotchbond Multi-Purpose Plus(SMP plus) and cemented with Scotchbond Resin Cement. In group 2, casted gold inlays were cemented in the same method as in group 1. In group 3, casted gold inlays were cemented with zinc-phosphate cement. And in group 4, the prepared cavities were restored with amalgam. Restored teeth were thermocycled, stored in 1% methylene blue for 24 hours, and sectioned faciolingually and mesiodistally using EXAKT. Sectioned surfaces were observed with stereomicroscope and the gaps were measured at 9 points of mesiodistally sectioned surface and 7 points of faciolingually sectioned surface. The measured data were treated by Kruskal-Wallis one way ANOVA and Student-Newman-Keuls test. 1. The differences among measured gaps at each points were statistically significant for 4 experimental groups (P<0.05). 2. There were statistically significant differences in the measured gaps at each points between group 1 and group 2, group 1 and group 3, group 1 and group 4, group 2 and group 4, and group 3 and group 4 (P<0.05). 3. There were not statistically significant differences in the measured gaps at each points between group 2 and group 3 (P>0.05). 4. In the cases of inlay restorations(group 1, group 2, group 3), the gaps at internal line angle(distopulpal, axiogingival, faciopulpal, linguopulpal line angle) had a tendency to increase. In the cases of amalgam restorations(group 4), the gaps at occlusal margin, gingival margin and axiogingival line angle were greater than those at the other parts of cavities. 5. In CEREC2-fabricated ceramic inlays which were treated with Scotchbond Multi-Purpose Plus and cemented with Scotchbond Resin Cement, the mean gaps were $111{\mu}m$ at cavity margins, $168{\mu}m$ at vertical walls of cavities, $225{\mu}m$ at internal line angles and $123{\mu}m$ at cavity floors.

• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.125-133
• /
• 2010

Objectives: Rapid polymerization of overlying composite resin causes high polymerization shrinkage stress at the adhesive layer. In order to alleviate the shrinkage stress, increasing the light intensity over the first 5 seconds was suggested as an exponential curing mode by an LED light curing unit (Elipar FreeLight2, 3M ESPE). In this study, the effectiveness of the exponential curing mode on reducing stress was evaluated with measuring microtensile bond strength of three adhesives after the overlying composite resin was polymerized with either continuous or exponential curing mode. Methods: Scotchbond Multipurpose Plus (MP, 3M ESPE), Single Bond 2 (SB, 3M ESPE), and Adper Prompt (AP, 3M ESPE) were applied onto the flat occlusal dentin of extracted human molar. The overlying hybrid composite (Denfil, Vericom, Korea) was cured under one of two exposing modes of the curing unit. At 48h from bonding, microtensile bond strength was measured at a crosshead speed of 1.0 mm/min. The fractured surfaces were observed under FE-SEM. Results: There was no statistically significant difference in the microtensile bond strengths of each adhesive between curing methods (Two-way ANOVA, p > 0.05). The microtensile bond strengths of MP and SB were significantly higher than that of AP (p < 0.05). Mixed failures were observed in most of the fractured surfaces, and differences in the failure mode were not observed among groups. Conclusion: The exponential curing method had no beneficial effect on the microtensile dentin bond strengths of three adhesives compared to continuous curing method.

• Restorative Dentistry and Endodontics
• /
• v.32 no.3
• /
• pp.208-221
• /
• 2007

The fracture toughness test is believed as a clinically relevant method for assessing the fracture resistance of the dentinal restoratives. The objectives of this study were to measure the fracture toughness $(K_{1C})$ and microtensile bond strength of dentin-resin composite interface and compare their relationship for their use in evaluation of the integrity of the dentin-resin bond. A minimum of six short-rod specimens for fracture toughness test and fifteen specimens for microtensile bond strength test was fabricated for each group of materials used. After all specimens storing for 24 hours in distilled water at $37^{\circ}C$, they were tensile-loaded with an EZ tester universal testing machin. Statistical analysis was performed using ANOVA and Tukey's test at the 95% confidence level, Pearson's coefficient was used to verify the correlation between the mean of fracture toughness and microtensile bond strength. FE-SEM was employed on fractured surface to describe the crack propagation. Fracture toughness value of Clearfil SE Bond (SE) was the highest, followed by Adper Single Bond 2 (SB), OptiBond Solo (OB), ONE-STEP PLUS (0S), ScotchBond Multi-purpose (SM) and there was significant difference between SE and other 4 groups (p < 0.05). There were, however, no significant difference among SB, OB, OS, SM (p > 0.05). Microtensile bond strength of SE was the highest, followed by SB, OB, SM, OS and OS only showed significant lower value (p < 0.05). There was no correlation between fracture toughness and microtensile bond strength values. FE-SEM examination revealed that dentin bonding agent showed different film thickness and different failure pattern according to the film thickness. From the limited results of this study, it was noted that there was statistically no correlation between K1C and ${\mu}TBS$. We can conclude that for obtaining the reliability of bond strength test of dentin bonding agent, we must pay more attention to the test procedure and its profound scrutiny.