HYDROLYTIC DEGRADATION OF DENIAL COMPOSITE RESINS

수종 치과용 복합레진의 가수분해

The composite restorative resins have their insufficient resistance to wear. The subsurface degradation within the restoration is considered to be associated with wear. The aim of this study was to evaluate the resistance to degradation of six commercial composite resins in an alkaline solution. The brands studied were Clearfil APX(Kuraray), Heliomolar(Vivadent), Surefil(Dentsply), TPH(Dentsply), Tetric Ceram(Vivadent), and Z100(3M). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCL, washed with water and dried to constant mass at $60^{\circ}C$. Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights; (b) Si loss (ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({\mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The mass loss was in descending order by Z100, TC H, S, CL, TPH and in the range of $0.45\sim3.64%$ 2. The degradation layer depth was in descending order by H, Z100, S, TC, TPH, CL and in the range of $10.85\sim73.38{\mu}m$ 3. For the Si concentration, Z100 was the highest of all 4. The highly significant correlation(r=0.81, p<0.05) was observed between mass loss and degradation depth. 5. Under scanning electronmicroscopy, the degradation of connection between resin matrix and fillers was observed 2 weeks after soaking in NaOH solution.

심미성 수복재로서 임상에서 널리 사용되는 복합레진은 구강내에서 장기간 유지되도록 하기 위하여 그 물성을 향상시킬 필요가 있다. 복합레진의 단점 중 하나로 낮은 마모저항성을 들수 있으며, 이와 관련된 하나의 인자로 수복물의 표면하 분해(subsurface degradation)가 고려되고 있다. 본 연구에서는 알카리성 용액(0.1N NaOH)에 현재 임상에서 많이 이용되는 Clearfil APX (CL, Kuraray). Heliomolar (H,Vivadent), Surefil (S, Dentsply), Tetric Ceram (TC, Vivadent), TPH (Dentsply), Z100 (3M)의 6종의 복합레진을 보관하였을 때 각 제품의 분해저항성을 평가하고자 하였다. 각 제품당 3개의 시편을 제작하여 무게측정을 한 후 0.1N NaOH용액에 저장하여 $60^{\circ}C$에서 보관하였다. 2주후 제거하여 HCl로 중화, 세척 후 $60^{\circ}C$에서 건조하였다. 무게손실, 분해층 깊이, Si 농도등을 기준으로 분해저항성을 평가하여 다음과 같은 결과를 얻었다. 1. 각 제품의 무게손실량은 $0.45\sim3.64%$ 까지 다양하며 Z100, TC, H, S, CL, TPH 순으로 많았다. 2. 각 제품의 표면하 분해층 깊이는 제품마다 다양하여, $10.85\sim73.38{\mu}m$의 범위였고, H, Z100, S, TC, TPH, CL 순으로 깊었다. 3. 각 제품으로부터 용출된 Si 양은 Z100군 2060ppm으로 가장 많고, H, TPH, CL, TC, S순으로 많았다. 4. 무게손실량과 표면하 분해층 깊이사이에 높은 상관관계를 보였다. (r=0.81, p,0.05) 5. 주사전자현미경하 관찰시 NaOH 용액에 보관한 후 레진기질과 필러사이의 결합의 파괴를 관찰할 수 있었다.