• Particle and aerosol research
• /
• v.8 no.2
• /
• pp.89-95
• /
• 2012

Spherical mesoporous silica particles, of which main pore diameter was 3.8 nm, were successfully prepared by spray pyrolysis from aqueous silicic acid. The effect of precursor concentration, reaction temperature, and the addition of urea and PEG on the particle diameter and pore properties such as pore diameter, total pore volume, and specific surface area were investigated by using FE-SEM, particle size analyzer, and nitrogen absorption-desorption analysis. With an increase of the precursor concentration from 0.2 M to 0.7 M, the average particle diameter, total pore volume, and specific surface area of the porous silica particles increased from 0.56 to $0.96\;{\mu}m$, 0.434 to $0.486\;cm^3/g$, 467.8 to $610.4\;m^2/g$, respectively. Within the temperature range $(600\;^{\circ}C{\sim}800\;^{\circ}C)$, there was no significant difference in the pore diameter, total pore volume, and specific surface area. In addition, the addition of urea as an expansion aid led to slight increases in particle diameter, pore diameter, and specific surface area. However, when the polyethylene glycol (PEG) as an organic template was used, the total pore volume of porous particles increased dramatically.

• Journal of Powder Materials
• /
• v.24 no.1
• /
• pp.6-10
• /
• 2017

This study investigates the main growth mechanism of InP during InP/ZnS reaction of quantum dots (QDs). The size of the InP core, considering a synthesis time of 1-30 min, increased from the initial 2.56 nm to 3.97 nm. As a result of applying the proposed particle growth model, the migration mechanism, with time index 7, was found to be the main reaction. In addition, after the removal of unreacted In and P precursors from bath, further InP growth (of up to 4.19 nm (5%)), was observed when ZnS was added. The full width at half maximum (FWHM) of the synthesized InP/ZnS quantum dots was found to be relatively uniform, measuring about 59 nm. However, kinetic growth mechanism provides limited information for InP / ZnS core shell QDs, because the surface state of InP changes with reaction time. Further study is necessary, in order to clearly determine the kinetic growth mechanism of InP / ZnS core shell QDs.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.115-121
• /
• 2017

In this work, p-type Bi-Sb-Te alloys powders are prepared using gas atomization, a mass production powder preparation method involving rapid solidification. To study the effect of the sintering temperature on the microstructure and thermoelectric properties, gas-atomized powders are consolidated at different temperatures (623, 703, and 743 K) using spark plasma sintering. The crystal structures of the gas-atomized powders and sintered bulks are identified using an X-ray diffraction technique. Texture analysis by electron backscatter diffraction reveals that the grains are randomly oriented in the entire matrix, and no preferred orientation in any unique direction is observed. The hardness values decrease with increasing sintering temperature owing to a decrease in grain size. The conductivity increases gradually with increasing sintering temperature, whereas the Seebeck coefficient decreases owing to increases in the carrier mobility with grain size. The lowest thermal conductivity is obtained for the bulk sintered at a low temperature (603 K), mainly because of its fine-grained microstructure. A peak ZT of 1.06 is achieved for the sample sintered at 703 K owing to its moderate electrical conductivity and sustainable thermal conductivity.

• Journal of Powder Materials
• /
• v.18 no.5
• /
• pp.449-455
• /
• 2011

In this study, p-type $(AgSbTe_2)_{15}(GeTe)_{85}$: TAGS-85 compound powders were prepared by gas atomization process, and then their microstructures and mechanical properties were investigated. The fabricated powders were of spherical shape, had clean surface, and illustrated fine microstructure and homogeneous $AgSbTe_2$ + GeTe solid solution. Powder X-ray diffraction results revealed that the crystal structure of the TAGS-85 sample was single rhombohedral GeTe phase, which with a space group $R_{3m}$. The grain size of the powder particles increased while the micro Vickers hardness decreased with increasing annealing temperature within the range of 573 K and 723 K due to grain growth and loss of Te. In addition, the crystal structure of the powder went through a phase transformation from rhombohedral ($R_{3m}$) at low-temperature to cubic ($F_{m-3m}$) at high-temperature with increasing annealing temperature. The micro Vickers hardness of the as-atomized powder was around 165 Hv, while it decreased gradually to 130 Hv after annealing at 673K, which is still higher than most other fabrication processes.

• Journal of Powder Materials
• /
• v.30 no.1
• /
• pp.22-28
• /
• 2023

The global demand for raw lithium materials is rapidly increasing, accompanied by the demand for lithiumion batteries for next-generation mobility. The batch-type method, which selectively separates and concentrates lithium from seawater rich in reserves, could be an alternative to mining, which is limited owing to low extraction rates. Therefore, research on selectively separating and concentrating lithium using an electrodialysis technique, which is reported to have a recovery rate 100 times faster than the conventional methods, is actively being conducted. In this study, a lithium ion selective membrane is prepared using lithium lanthanum titanate, an oxide-based solid electrolyte material, to extract lithium from seawater, and a large-area membrane manufacturing process is conducted to extract a large amount of lithium per unit time. Through the developed manufacturing process, a large-area membrane with a diameter of approximately 20 mm and relative density of 96% or more is manufactured. The lithium extraction behavior from seawater is predicted by measuring the ionic conductivity of the membrane through electrochemical analysis.

• Economic and Environmental Geology
• /
• v.43 no.5
• /
• pp.455-466
• /
• 2010

Seabed mineral resources explored by Korea are categorized into major three types of deposit; manganese nodule, manganese crust and polymetallic sulfides. Pt displays high enrichment factors (400, ore/crust ratios) in manganese nodule. Rare earth oxide content in manganese nodule ranges from 0.037 to 0.302 REO % with mean value of 0.12 REO %. Both of Te and Pt are enriched elements in manganese crust, displaying enrichment factors of 10800 and 150, respectively. Rare earth oxide's contents of manganese crust are slightly higher than manganese nodule's (0.013~0.387 REO %, average = 0.18 REO %). Se and In are outstanding rare metals from seabed polymetallic sulfides, showing enrichment factors of 1300 and 110, respectively. Au (0.8~26.3 g/t) and Ag (0.9~348.0 g/t) are another enriched elements in polymetallic sulfides. The main concern at exploiting seabed mineral resource will be a securing rare metals for high-technology industries and rare metals from subsea mineral deposits will add economic values to commodity candidates such like Co, Ni and Cu.

• Korean Journal of Materials Research
• /
• v.15 no.4
• /
• pp.217-223
• /
• 2005

Thermal, electrical and mechanical properties of high purity niobium and tantalum refractory rare metals were investigated tn evaluate the physical purity. Higher purity niobium and tantalum metals showed lower hardness due to smaller solution hardening effect. Temperature dependence of electrical resistivity showed a typical metallic behavior. Remarkable decrease in electrical resistivity was observed for a high purity specimen at low temperature. However, thermal conductivity increased for a high purity specimen, and abrupt increase in thermal conductivity was observed at very low temperature, indicating typical temperature dependence of thermal conductivity for high purity metals. It can be known that reduction of electron-phonon scattering leads to increase in thermal conductivity of high purity niobium and tantalum metals at low temperature.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1047-1051
• /
• 2001

Purity tantalum powder has been produced by sodium reduction of potassium tantalum fluoride($K_2TaF_7$)in a stainless steel bomb. The influence of experimental variable, such as excess of reductant and temperature of reduction on the yield and quality of the Ta powder has been studied. The excesses of reductant were varied from -20%, -10%, 0%, 5%, 10%, 20%. When -20% excess of sodium was used, the un-reacted sodium remained in the reacted product. The yield of 81% of Ta powder has been achieved by reducing 50g of$K_TaF_7$with 5% sodium in excess of stoichiometric amount in presence of 16.8g of sodium chloride in the charge at a reduction temperature of$905{\circ}C$. The proportion of fine fraction(~325mesh) decreased appreciably with the increase of sodium excess, and the yield of tantalum powder improved from 65% to 94%. The average particle size of Ta Powder is improved from 3 microns to 4 microns in the 5% excess sodium.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1052-1056
• /
• 2001

Pure tantalum powder has been produced by sodium as a reluctant, $K_2TaF_7$as a feed material and KCl/KF as a diluent in an inconel stainless steel bomb by the metallothermic reduction. The influence of experimental variable, such as temperature of reduction on the yield and characteristics of the Ta powder has been studied. As the temperature of the reduction was varied from$ 800{\circ}C~980{\circ}C$, the yield of tantalum powder increased from 41% to 56%. However no appreciable improvement was observed above$920{\circ}C$. The fraction of fine Ta Powder decreased appreciably with the increase of temperature, and particle size was$2~3{\mu}m$at reduction temperature of$920{\circ}C$.Therefore a reduction temperature of$920{\circ}C$was optimally fixed for subsequent runs.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.146-152
• /
• 2002

Effect of polyaniline and additives on surface appearance of Zn electrodeposition was investigated by SEM and XRD analyzing. We carried out the experiment from sulfate Zinc bath containing sulfonated polyaniline, gelatin and thiourea by EG(Electrogalvanizing) simulator. Addition of polyaniline and gelatin in bath, crystal size and shape of hexagonal plane of Zn crystal reduced. Mixing of thiourea, however, brittle deposits were observed because of the difference between vertical growth and parallel growth. (1011) peak appeared with polyaniline and gelatin in XRD analysis. In case of mixing of polyaniline, gelatin and thiourea, (1011) peak appeared and intensity of Zn basal plane decreased. These results suggested that overpotential increased with addition of polyaniline and additives In bath.