Microwave dielectric properties of (1-x)ZnW $O_4$-xTi $O_2$ ceramic systems were investigated with calcination temperatures and Ti $O_2$ contents. The ZnW $O_4$ ceramic could be suitably sintered at 1075$^{\circ}C$ and showed the dielectric constant of 13.6, quality factor(Q$\times$ $f_{O}$value) of 22,000 and temperature coefficient of resonant frequency($\tau$$_{f}$) of -65$\pm$2ppm/$^{\circ}C$. Increasing the amount of Ti $O_2$ in the range of 0.25 to 0.45 mol, the dielectric constant and $\tau$$_{f}$ increased due to the role of Ti $O_2$ but the quality factor decreased due to the increase of phase boundaries. The 0.7ZnW $O_4$-0.3Ti $O_2$ ceramic showed the dielectric constant of 19.8, qualify factor(Q$\times$ $f_{0}$) of 20,000 and $\tau$$_{f}$ of -3$\pm$1ppm/$^{\circ}C$.>.EX>.>.>.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.6
• /
• pp.524-530
• /
• 2006

$xCa(Li_{1/4}Nb_{3/4})O_{3}-(1-x)CaTiO_{3}$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to low-temperature co-fired ceramic(LTCC) technology. The addition of $5{\sim}15wt%$ ZBS glass ensured successful sintering below $900\;^{\circ}C$. In general, increased addition of ZBS glass increased sinterability but it decreased the quality factor($Q{\times}f_{0}$) significantly due to the formation of an excessive liquid and second phases. As for the addition of $CaTiO_3$, the dielectric constant(${\epsilon}_r$) and temperature coefficient of resonant frequency(${\tau}_f$) increased, while the quality factor($Q{\times}f_{0}$) did not show an apparent change. The sintered $0.9Ca(Li_{1/4}Nb_{3/4})O_{3}-0.1CaTiO_{3}$ specimen at $900\;^{\circ}C$ with 10 wt% ZBS glass demonstrated 39.6 in dielectric constant(${\epsilon}_r$), 4,400 in quality factor$(Q{\times}f_{0}),\;and\;-11ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.2
• /
• pp.67-72
• /
• 2004

The microwave dielectric properties and microstructure of the (1-x)$Mg_4Ta_2O_{9-x}TiO_2$(X=0, 0.3, 0.4) ceramic were, investigated. The specimens were prepared by the conventional mixed oxide method with sintering temperature of $1350^{\circ}C$∼$1425^{\circ}C$. According to the XRD patterns, the (1-x)$Mg_4Ta_2O_{9-x}TiO_2$(X=0, 0.3, 0.4) ceramics have the $Mg_4Ta_2O_{9}$ phase(hexagonal). The dielectric constant($\varepsilon$$_{\gamma}$) and density increased with sintering temperature and mole fraction of x. To improve the quality factor and the temperature coefficient of resonant frequency, TiO$_2$($\varepsilon_{r}$=100, $Q{\times}f_{r}$=40,000GHz, $\tau$$_{f}$=＋450 ppm/$^{\circ}C$) was added in $Mg_4Ta_2O_{9}$ ceramics. In the case of the $0.7Mg_4Ta_2O_{9}$-$0.3TiO_2$ and the $0.6Mg_4Ta_2O_{9}$-$0.4TiO_2$ceramics sintered at $1400^{\circ}C$ for 5hr., the microwave dielectric properties were $\varepsilon$$_{\gamma}$=11.72, $Q{\times}f_{r}$=126,419GHz, $\tau_{f}$=-31.82 ppm/$^{\circ}C$ and $\varepsilon_{r}$=12.19, $Q{\times}f_{r}$=109,411GHZ, $\tau$$_{f}$= -17.21 ppm/$^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.139-142
• /
• 2003

Microwave dielectric properties of $Ca(Li_{1/4}Nb_{3/4})O_3-CaTiO_3$ ceramic systems were investigated with calcination temperatures and amounts of $CaTiO_3$ in the range of 0.2 to 0.4mol. $Ca(Li_{1/4}Nb_{3/4})O_3$ ceramics having orthorhombic crystal structure could be synthesized at $750^{\circ}C$ and sintered well at $1250^{\circ}C$. They showed the dielectric constant of 26, quality factor($Q{\times}f_o$) of 13,000 and temperature coefficient of resonant frequency(${\tau}_f$) of $-49{\pm}2ppm/^{\circ}C$ With adding the $CaTiO_3$ amount the dielectric constant and ${\tau}_f$ increased due to the solute of $CaTiO_3$ but the quality factor decreased. The 0.7$Ca(Li_{1/4}Nb_{3/4})O_3-0.3CaTiO_3$ ceramic showed the dielectric constant of 44, quality factor($Q{\times}f_o$) of 12,000 and ${\tau}_f$ of $-9{\pm}1ppm/^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.313-314
• /
• 2006

$BiNbO_4$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to LTCC technology. The addition of 5~20 wt% ZBS glass ensured successful sintering below $900^{\circ}C$. In general, increased addition of ZBS glass increased sinterability and temperature coefficient of resonant frequency(${\tau}_f$), but it decreased the dielectric constant(${\varepsilon}_r$) and quality factor($Q{\times}f_0$) significantly due to the formation of an excessive liquid. The sintered $BiNbO_4$ ceramics at $900^{\circ}C$ with 15 wt% ZBS glass demonstrated 25 in dielectric constant(${\varepsilon}_r$), 3,700 in quality factor($Q{\times}f_0$), and -32 $ppm/{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.143-148
• /
• 2001

PbWO$_4$ can be densified at 85$0^{\circ}C$ and it shows fairy good microwave dielectric properties; dielectric constant($\varepsilon$$_{r}$) of 21.5, quality factor(Q $\times$f$_{0}$) of 37,224 GHz, and temperature coefficient of resonant frequency($\tau$/suf f/) of -31ppm/$^{\circ}C$. Due to its low sintering temperature, PbWO$_4$ can be used as a multilayered chip component at microwave frequency with high electrical performance by using high conductive electrode metals such as Ag and Cu. However, in order to use this material for microwave communication devices, the $\tau$$_{f}$ of PbWO$_4$ must be stabilized to near zero with high Q$\times$f$_{0}$. In present study, PbWO$_4$ was modified by adding TiO$_2$, B$_2$O$_3$, and CuO in order to improve the microwave dielectric properties without increasing the sintering temperature. The addition of TiO$_2$ increased the $\tau$$_{f}$ and $\varepsilon$$_{r}$, due to its high rr(200ppm/$^{\circ}C$) and $\varepsilon$$_{r}$(100). However, the addition of TiO$_2$ reduced the Q$\times$f$_{0}$ value. When the mot ratio of PbWO$_4$ and TiO$_2$ was 0.913:7.087, near zero $\tau$$_{f}$(0.2ppm/$^{\circ}C$) was obtaibed with $\varepsilon$$_{r}$=22.3, and Q$\times$f/$_{0}$=21,443GHz. With this composition, various amount of B$_2$O$_3$ and CuO were added in order to improve the quality factor. The addition, of B$_2$O$_3$ decreased the $\varepsilon$$_{r}$. However, increased Q$\times$f$_{0}$ and $\tau$$_{f}$. When 2.5 wt% of B$_2$O$_3$ was added to the 0.913PbWO$_4$-0.087TiO$_2$ ceramic, $\tau$$_{f}$ =8.2, $\varepsilon$$_{r}$=20.3, Q$\times$f$_{0}$=54784 GHz. When CuO added to the 0.913PbWO$_4$-0.087TiO$_2$ ceramic, $\tau$$_{f}$ was continuously decreased. And $\varepsilon$$_{r}$ . and Q$\times$f$_{0}$ were increased up to 1.0 wt% then decreased. At 0.1 wt% of CuO addition, the 0.913PbWO$_4$-7.087Ti0$_2$ Ceramic Showed $\varepsilon$$_{r}$=23.5, $\tau$$_{f}$=4.4ppm/$^{\circ}C$, and Q$\times$f$_{0}$=32,932 GHz.> 0/=32,932 GHz.X>=32,932 GHz.> 0/=32,932 GHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.476-479
• /
• 2001

The microwave dielectric properties of $[(Pb_{1-x}Ba_{x})_{1/2}La_{1/2}](Mg_{1/2}Nb_{1/2})O_{3}$ ceramics were investigated. When $[(Pb_{0.9}Ba_{0.1})_{1/2}La_{1/2}](Mg_{1/2}Nb_{1/2})O_{3}$ ceramics were sintered at $1250^{\circ}C$ and $1350^{\circ}C$ for 2hr, the microwave dielectric properties were obtained $\varepsilon_{r}=64\sim80$, $Q{\times}f=11,800\sim18,000$. As a result, $[(Pb_{0.9}Ba_{0.1})_{1/2}La_{1/2}](Mg_{1/2}Nb_{1/2})O_{3}$ having $\varepsilon_{r}=80$, $Q{\times}f=11,800$ (at 4 GHz) was developed.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.7
• /
• pp.305-310
• /
• 2002

The microwave dielectric properties of Ba(Mg$_{1}$3/Ta$_{2}$3/O$_3$-Ba(Co$_{1}$3/Nb$_{2}$3/O$_3$[BMT-BCN] ceramics were investigated. The specimens were prepared by the conventional mixed oxide method with the sintering temperature of 15$25^{\circ}C$~1575$^{\circ}C$. It was found that Ba(Mg$_{1}$3/Ta$_{2}$3/O$_3$[BMT] and BCN formed a solid solution with complex perovskite structure. As increasing the mole fraction of BCN, dielectric constant increased while the temperature coefficient of resonant frequency was changed from positive to negative value. The highest value of quality factor, Q$\times$f$_{0}$=138,205GHz, obtained in the 0.9BMT-0.1BCN ceramics sintered at 1575$^{\circ}C$. In the range of x$\geq$0.4, the dielectric constant was about 30. The 0.55BMT-0.45BCN ceramics sintered at 15$25^{\circ}C$ for 5 hours showed the microwave dielectric properties of $\varepsilon$$_{r}$=30.21, Q$\times$f$_{0}$=85,789GHz and $\tau$$_{f}$=2.9015ppm/$^{\circ}C$.EX>.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.289-294
• /
• 2010

For the aim of low-temperature co-fired ceramic microwave components, sintering behavior and microwave properties (dielectric constant ${\varepsilon}_r$, quality factor Q, and temperature coefficient of resonant frequency ${\tau}_f$) are investigated in $Bi_{18}O(Ca_{0.725}Zn_{0.275})_8Nb_{12}O_{65}$ [BCZN] ceramics with addition of $V_2O_5$. The specimens are prepared by conventional ceramic processing technique. As the main result, it is demonstrated that the additives ($V_2O_5$) show the effect of lowering of sintering temperature and improvement of microwave properties at the optimum additive content. The addition of 0.25 wt% $V_2O_5$ lowers the sintering temperature to $890^{\circ}C$ utilizing liquidphase sintering and show the microwave dielectric properties (dielectric constant ${\varepsilon}_r$ = 75, quality factor $Q{\times}f$ = 572 GHz, temperature coefficient of resonance frequency ${\tau}_f\;=\;-10\;ppm/^{\circ}C$). The estimated microwave dielectric properties with $V_2O_5$ addition (increase of ${\varepsilon}_r$, decrease of $Q{\times}f$, shift of ${\tau}_f$ to negative values) can be explained by the observed microstrucure (sintered density, abnormal grain structure) and possibly high-permittivity $Bi_{18}Zn_8Nb_{12}O_{65}$ (BZN) phase determined by X-ray diffraction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.642-645
• /
• 2002

Microwave dielectric properties of $ZnWO_4$ ceramic were investigated with calcination and sintering temperatures. The dielectric properties required for such application are high dielectric constant$(\varepsilon_r)$, high $Q{\times}f_o$ value and low temperature coefficient of resonant frequency$(\tau_f)$. These requirement correspond to necessities for size reduction, excellent frequency selectivity, good temperature stability of devices. $ZnWO_4$ ceramics could be sintered at low $1075^{\circ}C$, which was comparatively low temperature for microwave dielectrics. As a result, $ZnWO_4$ showed the dielectric constant of 13, quality factor($Q{\times}f_o$ value) of 22000 and 'temperature coefficient of resonant frequency$(\tau_f)$ of $-65{\pm}5ppm/^{\circ}C$.