• 한국산업융합학회 논문집
• /
• 제24권6_2호
• /
• pp.909-917
• /
• 2021

This study was carried out experimentally on the production and properties of silicon nanopowders characteristics using a transferred type arc plasma apparatus. To investigate the properties of silicon nanopowder, the purity of argon gas(99.999%, 99.9%) and the partial pressure ratio of nitrogen gas(0~90%) were varied. The total pressure in chamber is 400Torr and the silicon chunk amount used as raw material is 300g. The power supplied to the cathode to generate arc plasma was 9~12kW/h, and the electrode was made of tungsten and graphite with a diameter of 13mm. The particle size, impurity elements and powder evaporation rate of the silicon powder were analyzed using the XRD, FE-SEM, TEM and electronic scale. According to the purity of argon gas, the silicon evaporation rate and the particle size were similar, and impurities were generated more in the case of 99.9% purity than 99.999%. When argon gas and nitrogen gas were mixed in the chamber, the silicon evaporation rate and particle size increased as the partial pressure ratio of nitrogen gas increased. In particular, when the partial pressure ratio of nitrogen gas was 80%, the silicon evaporation rate 80g/h, and the particle size was about 80~100nm.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1041-1042
• /
• 2006

High heat-resistant Al-Fe-V-Si and Al-Fe-V-Si-X rapidly solidified powder metallurgy (RS P/M) alloys have been developed under well-controlled high purity argon gas atmosphere. The $Al_{90.49}Fe_{6.45}V_{0.68}Si_{2.38}$ (at. %) RS P/M alloy exhibited high elevated-temperature strength exceeding 300 MPa and good ductility with elongation of 6 % at 573 K. Reduction of $H_2O$ partical pressure in P/M processing atmosphere led to improvement in mechanical properties of the powder-consolidated alloys under elevated-temperature service conditions. Ti addition to the Al-Fe-V-Si conduced to enhancement of the strength at room temperature. The tensile yeild strength and ultimate strenght were 545 MPa and 722 MPa, respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.179-179
• /
• 2016

A radio-frequency (RF) Inductively Coupled Plasma (ICP) torch system was used for boron-nitride nano-tube (BNNT) synthesis. Because of electrodeless plasma generation, no electrode pollution and effective heating transfer during nano-material synthesis can be realized. For stable plasma generation, argon and nitrogen gases were injected with 60 kW grid power in the difference pressure from 200 Torr to 630 Torr. Varying hydrogen gas flow rate from 0 to 20 slpm, the electrical and optical plasma properties were investigated. Through the spectroscopic analysis of atomic argon line, hydrogen line and nitrogen molecular band, we investigated the plasma electron excitation temperature, gas temperature and electron density. Based on the plasma characterization, we performed the synthesis of BNNT by inserting 0.5~1 um hexagonal-boron nitride (h-BN) powder into the plasma. We analysis the structure characterization of BNNT by SEM (Scanning Electron Microscopy) and TEM (Transmission Electron Microscopy), also grasp the ingredient of BNNT by EELS (Electron Energy Loss Spectroscopy) and Raman spectroscopy. We treated bundles of BNNT with the atmospheric pressure plasma, so that we grow the surface morphology in the water attachment of BNNT. We reduce the advancing contact angle to purity bundles of BNNT.

• 대한화학회지
• /
• 제39권4호
• /
• pp.252-256
• /
• 1995

고순도 구리 금속중에 존재하는 미량의 안티몬을 사전 분리시키지 않고 직접 분석할 수 있는 GFAAS 조건을 조사하였다. 과량 존재하는 구리가 안티몬의 감도를 향상시키는 matrix modifier의 역할을 하고 있음을 알았다. 희화 온도는 $600^{\circ}C(20s){\sim}700^{\circ}C(10s)$를 이용할 때에 $1000^{\circ}C(20s){\sim}1100^{\circ}C(10s)$보다 감도가 향상되며, 원자화 온도는 $2200^{\circ}C$에서 가장 좋은 Sb의 흡광도를 보였다. Ar 기체의 압력은 $2.0\; kg/cm^2$일때에 최적임을 확인하였으며, 20 ppb에서 200 ppb Sb 범위에서 변화율(coefficient of variation)이 5% 미만이며 직선 관계를 보였다.

• 한국연소학회지
• /
• 제15권2호
• /
• pp.1-11
• /
• 2010

Power generation systems based on the oxy-coal combustion with carbon dioxide capture and storage (CCS) capability are being proposed and discussed lately. Although a large number of lab scale studies for oxy-coal power plant have been made, studies of pilot scale or commercial scale power plant are not enough. Only a few demonstration projects for oxy-coal power plant are publicized recently. The proposed systems are evolving and various alternatives are to be comparatively evaluated. This paper presents a proposed approach for performance evaluation of a commercial 100 MWe class power plant, which is currently being considered for 'retrofitting' for the demonstration of the concept. The system is configurated based on design and operating conditions with proper assumptions. System components to be included in the discussion are listed. Evaluation criteria in terms of performance are summarized based on the system heat and mass balance and simple performance parameters, such as the fuel to power efficiency and brief introduction of the second law analysis. Also, gas composition is identified for additional analysis to impurities in the system including the purity of oxygen and unwanted gaseous components of nitrogen, argon and oxygen in air separation unit and $CO_2$ processing unit.

• Journal of Magnetics
• /
• 제12권4호
• /
• pp.133-136
• /
• 2007

We have carried out the study of magnetocaloric effect for as-quenched and annealed $Fe_{91-x}Y_xZr_9$ alloys. Samples were prepared by arc melting the high-purity elemental constituents under argon gas atmosphere and by single roller melt spinning. These alloys were annealed one hour at 773 K in vacuum chamber. The magnetization behaviours of the samples were measured by vibrating sample magnetometer. The Curie temperature increases with increasing Y concentration (x=0 to 8). Temperature dependence of the entropy variation ${\Delta}S_M$ was found to appear in the vicinity of the Curie temperature. The results show that annealed $Fe_{86}Y_5Zr_9$ and $Fe_{83}Y_8Zr_9$ alloys a bigger magnetocaloric effect than that those in as-quenched alloys. The value is 1.23 J/kg K for annealed $Fe_{86}Y_5Zr_9$ alloy and 0.89 J/kg K for as-quenched alloy, respectively. In addition, the values of ${\Delta}S_M$ for $Fe_{83}Y_8Zr_9$ alloy is 0.72 J/Kg K for as-quenched and 1.09 J/Kg K for annealed alloy, respectively.

• 한국전기전자재료학회논문지
• /
• 제18권2호
• /
• pp.164-168
• /
• 2005

Piezoelectric ZnO thin films were for the first time formed on SiO$_2$/Si(100) substrate using 2-step deposition, atomic layer deposition(ALD) and RF magnetron sputtering deposition, for film bulk acoustic resonator(FBAR) applications. The ZnO buffer layer by ALD was deposited using alternating diethyl zinc(DEZn)/$H_2O$ exposures and ultrahigh purity argon gas for purging. The ZnO films by 2-step deposition revealed stronger c-axis-preferred orientation and smoother surface than those by the conventional RF sputtering method. The solidly mounted resonator(SMR)-typed FBAR fabricated by using 2-step deposition method revealed higher quality factor of 580 and lower return loss of -17.35dB. Therefore the 2-step deposition method in this study could be applied to the FBAR device fabrication.

• Carbon letters
• /
• 제1권2호
• /
• pp.53-59
• /
• 2000

The synthetic methods for high yield of multiwalled carbon nanotube (MWNT) and singlewalled carbon nanotube (SWNT) with high purity by arc discharge have been investigated. MWNTs were synthesized under different pressures of helium and the gas mixture of argon and hydrogen. Relatively high pressure of 300-400 torr was required for high yield MWNTs synthesis at low bias voltage of about 20 V and 55 A, whereas low pressure of about 100 torr was required for SWNTs. The introduction of hydrogen gases during the synthesis of MWNTs improved the yield and purity of the samples. The SWNTs were synthesized by the assistance of a small amount of mixture of transition metals, which played as a catalyst during the formation process. The purity and yield of SWNTs were higher at a lower pressure and enhanced by mixing more components of the transition metals.

• 한국표면공학회지
• /
• 제46권4호
• /
• pp.139-144
• /
• 2013

c-BN(cubic boron nitride) is known to have extremely high hardness next to diamond, as well as very high thermal and chemical stability. The c-BN in the form of film is useful for wear resistant coatings where the application of diamond film is restricted. However, there is less practical application because of difficult control of processing variables for synthesis of c-BN film as well as unclear mechanism on formation of c-BN. Therefore, in the present study, the structural characterization of c-BN thin film were investigated using $B_4C$ target in r.f. magnetron sputtering system as a function of processing variables. c-BN films were coated on Si(100) substrate using $B_4C$ (99.5% purity). The mixture of nitrogen and argon was used for carrier gas. The deposition processing conditions were changed with substrate bias voltage, substrate temperature and base pressure. Fourier transform infrared microscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) were used to analyze crystal structures and chemical binding energy of the films. In the case of the BN film deposited at room temperature, c-BN was formed in the substrate bias voltage range of -400 V~ -600 V. Less c-BN fraction was observed as deposition temperature increased and more c-BN fraction was observed as base pressure increased.

• Progress in Superconductivity
• /
• 제7권1호
• /
• pp.58-63
• /
• 2005

We investigated the surface oxidation behavior of cube-textured polycrystalline nickel at various oxidation conditions. Cube-textured NiO film was formed on a cube-textured polycrystalline nickel regardless of oxidation conditions but different growth behavior of NiO crystals was observed depending on the oxidation conditions. The introduction of water vapor into $O_2$ did not affect the texture evolution, but rough and porous microstructure was developed. Microstructure of NiO film tends to be denser as the oxygen partial pressure increases. It is interesting that (111) peak of theta - two theta diffraction pattern started to get stronger in air atmosphere and (111) plane became the major texture in the substrate oxidized in high purity argon gas. Small amount of high index crystallographic plane NiO peak crystal was observed when $N_{2}O$ was used as an oxidant while only (200) plane crystal was formed in dry $O_2$ atmosphere. Flat and smooth surface was changed into rough faceted one when ramping rate to oxidation temperature was faster. The grain size of NiO was decreased when the oxygen partial pressure was low. It was also observed that the modification of nickel surface suppressed the development of (200) texture.