• Membrane Journal
• /
• v.21 no.2
• /
• pp.118-126
• /
• 2011

A method of light pre-irradiation, one of methods modifying hydrophobic surface to hydrophilic surface in a membrane, was proposed to overcome the drawback of previous methods such as blending, chemical treatment and post-irradiation, Process of membrane preparation in the study was comprised of 4 parts as follows: firstly process of precursor preparation to introduce hydrophilic nature under atmosphere and aqueous vapor by irradiating electron beam (EB), secondly process of dope solution preparation to cast on non-woven fabrics, thirdly process of casting to prepare membrane and finally process of coagulation in non-solvent to form porous structure. The merit of this method might show simple process as well as homogenous modification compared to previous methods. To carry it out, precursor was prepared by irradiating EB to powder PVDF at 75~125 K Gray dose. Precursor prepared was analyzed by FTIR, EDS and DSC to confirm the introduction of hydrophilic function and its mechanism. From their results, it was inferred I conformed that hydrophilic function was hydroxy1 and it was introduced by dehydrozenation. Hydrophilicity of membranes prepared was evaluated by contact angle (pristine PVDF : $62^{\circ}$, 125 K Gray-PVDF$13^{\circ}$). Porosity was evaluated by mercury intrusion method, simultaneously morpholoy and surface pore size were observed by SEM phothographs. The result showed the trend that more dose of EB led to smaller pore size and to lower porosity (pristine PVDF : 82%, 125 K Gray-PVDF : 63%). Trend of water permeability was similar to result above (pristine PVDF : 892 LMH, 125 K Gray-PVDF : 355 LMH).

• Applied Chemistry for Engineering
• /
• v.19 no.5
• /
• pp.477-483
• /
• 2008

$La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ oxide was synthesized by a citrate method and a typical dense membrane of perovskite oxide has been prepared using as-prepared powder by pressing and sintering at $1300^{\circ}C$. Precursor of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ prepared by citrate method was investigated by TGA and XRD. Metal-citrate complex in precursor was decomposed into perovskite oxide in the temperature range of $260{\sim}410^{\circ}C$ but XRD results showed $SrCO_3$ existed as impurity at less than $900^{\circ}C$. Electrical conductivity of membrane increased with increasing temperature but then decreased over $700^{\circ}C$ in air atmosphere ($Po_2=0.2atm$) and $600^{\circ}C$ in He atmosphere ($Po_2=0.01atm$) respectively due to oxygen loss from the crystal lattice. The oxygen permeation flux increased with increasing temperature and maximum oxygen permeation flux of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ membrane with 1.6 mm thickness was about $0.31cm^3/cm^2{\cdot}min$ at $950^{\circ}C$. The activation energy for oxygen permeation was 88.4 kJ/mol in the temperature range of $750{\sim}950^{\circ}C$. Perovskite structure of membrane was not changed after permeation test of 40 h and the membrane was stable without secondary phase change with 0.3 mol Sr addition.

• Resources Recycling
• /
• v.23 no.1
• /
• pp.40-47
• /
• 2014

Feasibility of utilizing unburned carbon residue in coal ash as a potential precursor for the production of activated carbon was assessed to seek for solution to recycle unburned carbon residue. The unburned carbon concentrate generated from the 4 stages of cleaner flotation has a grade of 87% carbon. The crystalline impurities in the concentrate included quartz and mullite. Unburned carbon had a low specific surface area of $10m^2/g$, which might be related to a high degree of coalification of domestic anthracite coal. Carbon particles were mostly porous and have a turbostratic structure. When 1g of carbon was activated with 6g of KOH powder, the highest specific surface area value of $670m^2/g$ was achieved. Low wettability of unburned carbon particles, which was resulted from high temperature combustion in a boiler, might cause poor pore formation when they were activated by KOH solution. The activated carbon produced in this study developed micropores, with an equivalent quality of general-purpose activated carbon made from coal. Hence, it is concluded that chemically treated unburned carbon can be used for water purification or an alternative to carbon black as it is.

• Journal of the Korean Vacuum Society
• /
• v.22 no.6
• /
• pp.306-312
• /
• 2013

Single-crystalline InSb nanowire was synthesized on $SiO_2$ wafer via vapor-liquid-solid (VLS) mechanism using chemical vapor deposition method. According to the source container system (open or close) which contain InSb powder and $SiO_2$ wafer, the single-crystalline InSb nanowires have different growth mechanisms. Structural characterization of the InSb nanowires was examined by scanning electron microscope (SEM). Composition of the nanowires was investigated using x-ray diffraction (XRD) and energy dispersive x-ray spectroscopy (EDS). This study demonstrates that length and diameter of the InSb nanowires are long and thick using open-boat system by VLS and additional vapor-solid (VS) mechanisms, because open-boat system can carry a large amount of vapor-phase InSb precursor than close-boat system.

• Journal of the Korean Ceramic Society
• /
• v.33 no.4
• /
• pp.391-398
• /
• 1996

In order to understand the electrostrictive behavior of Pb(Mg1/3Nb2/3)O3-PbTiO3(PMN-PT) solid solutions the dielectric constants and the electric-field-induced strains in (1-x)PMN-xPT (x=0.0-0.4) were investigated in the temperature range -5$0^{\circ}C$-20$0^{\circ}C$. Powder of (1-x)Pb(Mg2/3Nb2/3)O3-xPbTiO3 (x=0.0, 0.1, 0.2, 0.3, 0.35, and 0.4) were prepared from the oxide forms of Pb, Mg, Nb and Ti via a columbite precursor method As the amount of PbTiO3 increases the temperature of maximum dielectric constant(T$\varepsilon$max) increases and the phase transition become less diffusive. The strain maximum occurs only when the diffuse phase transition occurs from rhombohedral to cubic or rhombohedral to tetragonal as in x=0.1-0.35 The strains monotonically decrease with temperature in the materials in which phase transition occurs from tetragonal to cubic as in x=0.4.

• Microbiology and Biotechnology Letters
• /
• v.45 no.4
• /
• pp.291-298
• /
• 2017

We compared the ingredients present in freeze-dried ground food samples with those present in hot air-dried and ambient ground food samples to optimize processing conditions for preserving nutrients in and for improving the ingestion of different foods. The freeze-dried ground sample of black bean showed 4.57% higher retention rate than the ambient ground sample of black bean. Mineral content was also significantly different between these two samples. Moreover, the freeze-dried ground sample of black bean contained 11.54% higher content of ${\beta}$-carotene, a precursor of vitamin A, than the ambient ground sample of black bean. Total anthocyanin content was 453.49 mg in the freeze-dried ground sample of Aronia compared with 158.98 mg in the ambient ground sample of Aronia. Contents of ${\beta}$-carotene and niacin increased by 129.47% and 439.39%, respectively, in the freeze-dried ground sample of grapefruit. Retention rates of proteins, carbohydrates, and niacin were 107.74%, 103.87%, and 156.52%, respectively, in the freeze-dried ground sample of germinated brown rice. Protein digestibility increased by 120.5% and 101.14% in the freeze-dried ground samples of Aronia and black bean, respectively, but did not increase in the freeze-dried ground samples of grapefruit and germinated brown rice.

• Korean Chemical Engineering Research
• /
• v.48 no.1
• /
• pp.75-79
• /
• 2010

The precursor powders with thin wall structure were prepared by spray pyrolysis from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux. The $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution without organic additives and flux material had sizes of $1{\sim}5{\mu}m$ and hollow structure with high thickness at post-treatment temperature of $1,200^{\circ}C$. However, $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux had fine size and plate-like shape. The mean crystallite sizes of the phosphor powders with fine sizes were 23, 35, and 33 nm when the content of $NH_4Cl$ flux were 0, 6, 35 wt% of phosphor. The photoluminescence intensity of the phosphor powders formed from the spray solution with the optimum amount of $NH_4Cl$ flux as 35 wt% was 215% of that of the phosphor powders formed from the spray solution without flux material.

• Korean Chemical Engineering Research
• /
• v.46 no.3
• /
• pp.479-485
• /
• 2008

Porous $TiO_2$ nanostructured particles containing both mesopores and macropores were fabricated by utilizing an aerosol templating method from two kinds of starting materials (colloidal mixture of $TiO_2$ nanoparticles and PS particles, and that of TTIP solution and PS particles). The effects of mixing ratio of PS to $TiO_2$ and reactor temperature on the particle properties were investigated. When $TiO_2$ nanoparticles were used as starting materials, the increase of macropores number was observed by SEM and the specific surface area and total pore volume were increased from $31.6m^2/g$ to $39.1m^2/g$ and $0.068cm^3/g$ to $0.089cm^3/g$, respectively, by increasing the weight mixing ratio of $PS/TiO_2$ from 0.79 to 1.31. When TTIP was used as precursor, the specific surface area and mesopore volume of particles prepared at same condition decreased by 67% and 75%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.284-288
• /
• 2004

To improve mechanical properties of $Al_2$O$_3$/ZrO$_2$composites have been controlled dispersion of ultra low size ZrO$_2$ particles in $Al_2$O$_3$ ceramics by polymeric precursor method (Pechini process). In case of coprecipitation or mechanical mixing of ZrO$_2$ powders with $Al_2$O$_3$, homogeneous dispersion and controlling the ZrO$_2$ size were relatively difficult due to high sintering temperature. So the polyesterization process of Zr/Y(NO$_3$)$_3$-citric acid solution in ethylene glycol with the commercial sub-micron sized o(-alumina powder (Sumitomo AES-11(0.4 ${\mu}{\textrm}{m}$)) was adopted in order to obtain homogeneous dispersion of ZrO$_2$ in A1203. By this partial polyesterization process, the homogeneous dispersion of relatively low sized ZrO$_2$in $Al_2$O$_3$/ZrO$_2$composites was achieved at 1450∼1$600^{\circ}C$ of sintering temperature range and their mechanical properties were measured.

• Korean Chemical Engineering Research
• /
• v.50 no.1
• /
• pp.1-5
• /
• 2012

$Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ hollow fiber with o.d. 1.02 mm and i.d. 0.437 mm were fabricated by a phase-inversion spinning technique.The starting $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ precursor was synthesized by the polymerized complex method and then calcined at $900^{\circ}C$. As-prepared powder was dispersed in a polymer solution, and extruded as form of hollow fiber through a spinneret. Finallydense $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ hollow fiber membrane was obtained by sintering for 2 h at $1,080^{\circ}C$ for the application of oxygen separation. In addition, despite a very thin membrane with 0.58 mm, the BSCF hollow fiber membrane possessed a proper mechanical strength of 602.5 MPa.