• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2000.05a
• /
• pp.115-121
• /
• 2000

As the development of industry water quality of river is going to bad because of waste water of an industrial complex and general home agricultural chemicals exhaust of $SO_3$ and CO gas acid rain and so on. Corrosion damage of boiler factory equipment and so forth occur quickly due to using of the polluted water resulting in increasing leak accident. Especially working life of hot water boiler using the polluted water becomes more short and energy loss increases. The cathodic protection method is the most economical and reliable one to prevent corrosion damage of steel structures. Mg-base alloys galvanic anode protection of cathodic protection method is suitable for than application of hot water boiler using water with high specific resistance such as tap water. This paper is studied on the cathodic protection characteristics of how water boiler. In tap water and 0.001mol/$\ell$ NaCl solution the characteristics of anodic polarization of Mg-base alloys galvanic anode and tube material is investigated the measurement of cathodic protection potential according to the time elaspsed is carried out.

• Corrosion Science and Technology
• /
• v.17 no.4
• /
• pp.166-175
• /
• 2018

In this study, the electrochemical properties of CP-Ti (commercially pure titanium) and Ti-64 (Ti-6Al-4V) were evaluated and the effect of hydrofluoric acid on corrosion resistance and electrochemical properties was elucidated. Additive manufactured materials were made by DMT (Directed Metal Tooling) method. Samples were heat-treated for 1 hour at $760^{\circ}C$ and then air cooled. Surface morphologies were studied by optical microscope and SEM. Electrochemical properties were evaluated by anodic polarization method and AC-impedance measurement. The oxide film formed on the surface was analyzed using an XPS. The addition of HF led to an increase in the passive current density and critical current density and decreased the polarization resistance regardless of the alloys employed. Based on the composition of the oxide film, the compositional difference observed by the addition of HF was little, regardless of the nature of alloys. The Warburg impedance obtained by AC-impedance measurement indicates the dissolution of the constituents of CP-Ti and Ti-64 through a porous oxide film.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.682-687
• /
• 2000

In this research the remaining service life of the concrete due to the steel corrosion was predicted by three cases; causing carbonation, using sea sand, using deicing salts. In case of deterioration by carbonation, effective carbonation depth, effective coverage depth and relative humidity are considered for predicting method. In case of using sea sand, predicting method is made of rust growth equation from polarization resistance method. In case of using deicing salts, predicting method is made of transformation of Fick's law. Three methods are very useful in predicting service life of concrete.

• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.292-299
• /
• 2019

The hull material of a high-speed ship may cause erosion damage from fluid impact. When physical erosion and electrochemical corrosion combine, erosion corrosion damage occurs. The aluminum ship is vulnerable to erosion corrosion because it can be operated at high speed. Thus, in this study, Al5052-O and Al6061-T6 aluminum alloys for the marine environment were selected as experimental materials. The erosion corrosion resistance of Al5052-O and Al6061-T6 aluminum alloys in seawater was investigated by an erosion test and potentiodynamic polarization test at the various flow rate (0 m/s, 5 m/s, 10 m/s, 15 m/s, 20 m/s). Erosion corrosion characteristics were evaluated by surface analysis, 3D analysis, SEM analysis, and the Tafel extrapolation method. The results of surface damage analysis after the erosion test showed that Al6061-T6 presented better erosion resistance than Al5052-O. The results of the potentiodynamic polarization test at the various flow rate, corrosion current density by Tafel extrapolation presented lower values of Al6061-T6 than Al5052-O. Al5052-O showed more surface damage than Al6061-T6 at all flow rates. Consequently, Al6061-T6 presented better erosion corrosion resistance than Al5052-O. The results of this study are valuable data for selecting hull material for an aluminum alloy vessel.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.4
• /
• pp.1177-1182
• /
• 2012

The corrosion resistance of 316L stainless steel coated with NiO-YSZ (Ni added yttria stabilized zirconia) was examined in a proton exchange membrane fuel cell (PEMFC) environment. The NiO-YSZ coating was carried out using a sol-gel dip coating method, and the corrosion resistance and interfacial contact resistance (ICR) were determined by the composition and morphology of the NiO-YSZ film. The corrosion resistance increased with increasing Ni content in the NiO-YSZ film, but rapid corrosion was observed when the YSZ film contained more than 15 wt % Ni due to surface cracks. The polarization resistance was improved by several orders of magnitude when 316L stainless steel was coated with a 15 wt % NiO-YSZ film compared to bare 316L. The ICR of the NiO-YSZ film was decreased to that of bare 316L when the YSZ film contained 25 wt % NiO, suggesting the possible application of NiO-YSZ coated stainless steel for a bipolar plate.

• Corrosion Science and Technology
• /
• v.21 no.6
• /
• pp.495-502
• /
• 2022

Anodization is a representative electrochemical surface treatment method that can improve both heat resistance and corrosion resistance by forming an anodization film on the surface of the aluminum. However, these properties can be changed after an additional heat treatment process. In this study, Al 6061 was subjected to an anodization process at 60 V for 1 hour, 5 hours, or 9 hours. An additional heat treatment process was performed at 500 ℃ for 30 minutes. Field emission scanning electron microscopy (FE-SEM) analysis revealed that the thickness of the anodized film was increased in proportion to the anodization time. Both pore size and pore diameter of the anodized film was also increased after anodization. After an additional heat treatment process, there were no significant changes in the thickness, pore size, or pore diameter of the anodized film. Heat resistance was confirmed through thermal analysis and chemical resistance was evaluated with a potentiodynamic polarization test.

• Corrosion Science and Technology
• /
• v.17 no.3
• /
• pp.101-108
• /
• 2018

AA7010 is an Al-Zn-Mg-Cu alloy containing Zr, developed as an alternate to traditional AA7075 alloy owing to their high strength combined with better fracture toughness. It is necessary to improve the corrosion resistance and surface properties of the alloy by incorporating plasma electrolytic oxidation (PEO) method. AA7010-T7452 aluminum alloy has been processed through the forging route with multi-stage working operations, and was coated with $10{\mu}m$ thick $Al_2O_3$ ceramic aluminina coating using the plasma electrolytic oxidation (PEO) method. The corrosion, stress corrosion cracking (SCC) and nano-mechanical behaviours were examined by means of potentiodynamic polarization, slow strain rate test (SSRT) and nano-indentation tests. The results indicated that the additional thermomechanical treatment during the forging process caused a fully recrystallized microstructure, which lead to the poor environmental cracking resistance of the alloy in 3.5% NaCl solution, despite the overaging treatment. Although the fabricated PEO coating improved general corrosion resistance, the brittle nature of the coating did not provide any improvement in SCC resistance of the alloy. However, the hardness and elastic modulus of the coating were significantly higher than the base alloy.

• Journal of Advanced Marine Engineering and Technology
• /
• v.31 no.6
• /
• pp.744-752
• /
• 2007

Recently a fuel oil of the diesel engine in the ship is being changed with low quality as the oil price is higher more and more. Therefore the wear and corrosion in all parts of the engine like cylinder liner ring groove of piston crown, spindle and seat ring of exhaust valve are increased with using of heavy oil of low quality In particular the degree of wear and corrosion in between valve spindle and seat ring are more serious compared to the other parts of the engine due to operating in severe environment such as the high temperature of exhaust gas and repeating impact. Thus the repair weld to the valve spindle and seat ring is a unique method to prolong the life of the exhaust valve in an economical point of view In this study. corrosion property of both weld metal zone and base metal was investigated with some electrochemical methods such as measurement of corrosion potential, cathodic and anodic polarization curves, cyclic voltammogram and polarization resistance etc. in 5% $H_2SO_4$ solution. in the case of being welded with some welding methods and welding materials to the exhaust valve specimen as the base metal. In all cases. the values of hardness of the weld metal zone were more high than that of the base metal. And their corrosion resistance were also superior to the base metal. The weld metal of A2F(AC SMAW: 2 pass welding with foreign electrode) showed a relatively good results to the corrosion resistance as well as the hardness compared to the ether welding methods and welding materials. Moreover it indicated that hardness of the weld metal by the domestic electrode was considerably high compared to that of the foreign electrode.

• Corrosion Science and Technology
• /
• v.2 no.6
• /
• pp.289-295
• /
• 2003

The corrosion behavior of Cr-N coated steels with different phases (${\alpha}-Cr$, CrN and $Cr_2N$) deposited by cathodic arc deposition on Hl3 steel was investigated in 3.5% NaCl solution at ambient temperature. Potentiodynamic polarization test, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) were the techniques applied to characterize the corrosion behavior. It was found that the CrN coating had a lower current density from potentiodynamic polarization test than others. The porosity, corresponding to the ratio of the polarization resistance of the uncoated and the coated substrate, was higher in the $Cr_2N$ coating than in the other Cr-N coated steels. EIS measurements showed, for the most of Cr-N coated steels, that the Bode plot presented two time constants. Also, the $Cr_2N$ coating represents the characteristic of Warburg behavior after 72hr of immersion. The coating morphologies were examined in planar view and cross-section by SEM analyses and the results were compared with those of the electrochemical measurement. The CrN coating had a dense, columnar grain-sized microstructure with minor intergranular porosity. From the above results, the CrN coating provided a better corrosion protection than the other Cr-N coated steels.

• Journal of Ocean Engineering and Technology
• /
• v.21 no.3 s.76
• /
• pp.65-70
• /
• 2007

There are many kinds of protection methods for marine structures, with varyingeconomical and environmental advantages. The coating protection method is being widely used in both continental and marine structures. In this study, by adding some additives, such as Zn powder(Zn), carbon black(CB) to epoxy anti-corrosive paint, the effect on the corrosion resistance was investigated throughan electrochemical method. The additive of Zn(20)+CB(10) showed the lowest passivity current density. Polarization resistance in both cyclic voltammogram and impedance measurement of an additive of Zn(20)+CB(10) was also the largest value, compared to other additives. Furthermore, rusting and bubbling was not observed on the surface of the test specimen with the additive of Zn(20)+CB(10), compared to other specimens. It is suggested that the corrosion resistance of the anti-corrosive paint can be improved by using some additives.