• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.886-890
• /
• 2003

The etching characteristics of a LiNbO$_3$ single crystal have been investigated using helicon wave plasma source with bias power and the mixture of CF$_4$, HBr, SF$_{6}$ gas parameters. The etching rate of LiNbO$_3$ with etching parameters was evaluated by surface profiler. The etching surface was evaluated by Atomic Force Microscopy (AFM). The surface morphology of the etched LiNbO$_3$ changed with bias power and the mixture of CF$_4$/Ar/Cl$_2$, HBr/Ar/Cl$_2$, and SF$_{6}$/Ar/Cl$_2$ parameters. Optimum etching conditions, considering both the surface flatness and etch rate were determined.

• Journal of the Korean Chemical Society
• /
• v.45 no.4
• /
• pp.351-356
• /
• 2001

Planarization of the free-standing diamond film surface as smooth as possible could be obtained by using the hydrogen plasma etching with the diffusion of the carbon species into the metal alloy (Fe, Cr, Ni). For this process, we placed the free-standing diamond film between the metal alloy and the Mo substrate like a metal-diamond-molybdenum (MDM) sandwich. We set the sandwich-type MDM in a microwave-plasma-enhanced chemical vapor deposition (MPECVD) system. The sandwich-type MDM was heated over ca. 1000 $^{\circ}C$ by using the hydrogen plasma. We call this process as the hydrogen plasma etching with carbon diffusion process. After etching the free-standing diamond film surface, we investigated surface roughness, morphologies, and the incorporated impurities on the etched diamond film surface. Finally, we suggest that the hydrogen plasma etching with carbon diffusion process is an adequate etching technique for the fabrication of the diamond film surface applicable to electronic devices.

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.570-575
• /
• 2002

The present tendency of electrical and electronics is concentrated on MEMS devices for advantage of miniaturization, intergration, low electric power and low cost. Therefore it is essential that high aspect ratio and high etch rate by HDP technology development, so that silicon deep trench etching reactions was studied by ICP equipment. Deep trench etching of silicon was investigated as function of platen power, etch step time of etch/passivation cycle time and SF$\_$6/:C$_4$F$\_$8/ flow rate. Their effects on etch profile, scallops, etch rate, uniformity and selectivity were also studied.

• Journal of Magnetics
• /
• v.12 no.2
• /
• pp.81-83
• /
• 2007

Etching of NiFe films covered with an organic photo-resist or Ti was successfully performed by an inductively coupled plasma-reactive ion etching (ICP-RIE) system using $CHF_3/O_2/NH_3$ discharges exchanging $CHF_3$ for $CH_4$ gas gradually. Experimental results showed that the organic photo-resist mask can be applied to the NiFe etching. In the case of the Ti metal mask, it was found that the etching-selectivity Ti against NiFe was significantly varied from 7.3 to ${\sim}0$ by changing $CHF_3/CH_4/O_2/NH_3$ to $CH_4/O_2/NH_3$ discharges used in the ICP-RIE system. These results show that the present RIE of NiFe was dominated by a chemical reaction rather than a physical sputtering.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.182-182
• /
• 2012

Plasma etching is used in various semiconductor processing steps. In plasma etcher, optical- emission spectroscopy (OES) is widely used for in-situ endpoint detection. However, the sensitivity of OES is decreased if polymer is deposited on viewport or the proportion of exposed area on the wafer is too small. Because of these problems, the object is to investigate the suitability of using plasma impedance monitoring (PIM) and self plasma optical emission spectrocopy (SPOES) with statistical approach for in-situ endpoint detection. The endpoint was determined by impedance signal variation from I-V monitor (VI probe) and optical emission signal from SPOES. However, the signal variation at the endpoint is too weak to determine endpoint when $SiO_2$ and SiNx layers are etched by fluorocarbon on inductive coupled plasma (ICP) etcher, if the proportion of $SiO_2$ and SiNx area on Si wafer are small. Therefore, modified principal component analysis (mPCA) is applied to them for increasing sensitivity. For verifying this method, detected endpoint from impedance monitoring is compared with optical emission spectroscopy.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.516-521
• /
• 2001

Dry etching of Si wafer and $SiO_2$ layers was performed using He/Cl$_2$ mixture plasma by diode-type reactive ion etcher (RIE) system. For Si etching, the Cl molecules react with the Si molecules on the surface and become chemically stable, indicating that the reactants need energetic ion bombardment. During the ion assisted desorption, energetic ions would damage the photoresist (PR) and produce the bad etch Si-profile. Moreover, we have examined the characteristics of the Cl-Si reaction system, and developed the new fabrication procedures with a $Cl_2$/He mixture for Si and $SiO_2$-etching. The developed novel fabrication procedure allows the RIE to be unexpensive and useful a Si deep etching system. Since the etch rate was proved to increase linearly with fHe and the selectivity of Si to $SiO_2$ etch rate was observed to be inversely proportional to fHe.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.32-42
• /
• 2004

Recently, plasma surface-cleaning or surface-etching techniques have been focused in respect of the decontamination of spent or used nuclear parts and equipment. In this study the removal rate of metallic cobalt surface is experimentally investigated via its surface etching rate with a $CF_4-o_2$mixed gas plasma. Experimental results reveal that a mixed etchant gas with about 80% $CF_4$-20% $O_2$ (molar) gives the highest reaction rate and the rate reaches 0.06 ${\mu}m$/min at $380^{\circ}C$ and ion-assisted etching dramatically enhances the surface reaction rate. With a negative 300 V DC bias voltage applied to the substrate, the surface reaction initiation temperature lowers and the rate increases about 20 times at $350^{\circ}C$ and up to 0.43 ${\mu}m$/min at $380^{\circ}C$, respectively. Surface morphology analysis confirms the etching rate measurements. Auger spectrum analysis clearly shows the adsorption of fluorine atoms on the reacted surface. From the current experimental findings and the results discussed in previous studies, mechanistic understanding of the surface reaction, fluorination and/or fluoro-carbonylation reaction, is provided.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.12
• /
• pp.996-1002
• /
• 2000

Ferroelectric (Ba, Sr) TiO$_3$(BST) thin films have attracted much attention for use in new capacitor materials of dynamic random access memories (DRAMs). In order to apply BST to the DRAMs, the etching process for BST thin film with high etch rate and vertical profile must be developed. However, the former studies have the problem of low etch rate. In this study, in order to increase the etch rate, BST thin films were etched with a magnetically enhanced inductively coupled plasma(MEICP) that have much higher plasma density than RIE (reactive ion etching) and ICP (inductively coupled plasma). Experiment was done by varying the etching parameters such as CF$_4$/(CF$_4$+Ar) gas mixing ratio, rf power, dc bias voltage and chamber pressure. The maximum etch rate of the BST films was 170nm/min under CF$_4$/CF$_4$+Ar) of 0.1, 600 W/-350 V and 5 mTorr. The selectivities of BST to Pt and PR were 0.6 and 0.7, respectively. Chemical reaction and residue of the etched surface were investigated with X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.391-392
• /
• 2012

In these days, the desire for the precise and tiny displays in mobile application has been increased strongly. Currently, laser displays ranging from large-size laser TV to mobile projectors, are commercially available or due to appear on the market [1]. In order to achieve a mobile projectors, the semiconductor laser diodes should be used as a laser source due to their size and weight. In this presentation, the continuous etch characteristics of Pd and AlGaN/GaN superlattice for the fabrication of blue laser diodes were investigated by using inductively coupled $CHF_3$ and $Cl_2$ -based plasma. The GaN laser diode samples were grown on the sapphire (0001) substrate using a metal organic chemical vapor deposition system. A Si-doped GaN layer was grown on the substrate, followed by growth of LD structures, including the active layers of InGaN/GaN quantum well and barriers layer, as shown in other literature [2], and the palladium was used as a p-type ohmic contact metal. The etch rate of AlGaN/GaN superlattice (2.5/2.5 nm for 100 periods) and n-GaN by using $Cl_2$ (90%)/Ar (10%) and $Cl_2$ (50%)/$CHF_3$ (50%) plasma chemistry, respectively. While when the $Cl_2$/Ar plasma were used, the etch rate of AlGaN/GaN superlattice shows a similar etch rate as that of n-GaN, the $Cl_2/CHF_3$ plasma shows decreased etch rate, compared with that of $Cl_2$/Ar plasma, especially for AlGaN/GaN superlattice. Furthermore, it was also found that the Pd which is deposited on top of the superlattice couldn't be etched with $Cl_2$/Ar plasma. It was indicating that the etching step should be separated into 2 steps for the Pd etching and the superlattice etching, respectively. The etched surface of stacked Pd/superlattice as a result of 2-step etching process including Pd etching ($Cl_2/CHF_3$) and SLs ($Cl_2$/Ar) etching, respectively. EDX results shows that the etched surface is a GaN waveguide free from the Al, indicating the SLs were fully removed by etching. Furthermore, the optical and electrical properties will be also investigated in this presentation. In summary, Pd/AlGaN/GaN SLs were successfully etched exploiting noble 2-step etching processes.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2005.11b
• /
• pp.300-315
• /
• 2005

Recently plasma surface-cleaning or surface-etching techniques have been focused in the respect of decontamination of spent or used nuclear parts and equipment. In this study decontamination rate of metallic cobalt surface was experimentally investigated via its surface etching rate with a $CF_4-O_2$ mixed gas plasma and metallic surface wastes of cobalt oxides were simulated and decontaminated with $NF_3$ - Ar mixed gas plasma. Experimental results revealed that a mixed etchant gas with about $80{\%}\;CF_4-20{\%}\;O_2$ gives the highest reaction rate of cobalt disk and the rate reaches with a negative 300 DC bias voltage up to $0.43\;{\mu}m$/min at $380^{\circ}C$ and $20{\%}\;NF_3-80\%$ Ar mixed gas gives $0.2\;{\mu}m$/min of reaction rate of cobalt oxide film.