• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.305-305
• /
• 2010

In this study, in order to develop excellent lead free piezoelectric ceramics for piezoelectric transformer application (Na,K)(Nb,Sb)$O_3$ ceramics were fabricated using conventional oxides mixed method and their piezoelectric and dielectric characteristics were investigated according to the amount of $Bi_2O_3$ addition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.216-217
• /
• 2005

In this paper, in order to develop Pb-free piezoelectric ceramics, $(Li_{0.05}Na_{0.57}K_{0.38})NbO_3$ ceramic was fabricated with the variation of $Bi_2O_3$ addition. Piezoelectric properties of the ceramic were varied with the amount of $Bi_2O_3$ addition and showed the maximum kp value at.0.2 wt% $Bi_2O_3$ addition. Qm of $Bi_2O_3$ added ceramics showed lower values than the non-added ceramics, however, the kp was increased by the addition of $Bi_2O_3$ up to 0.2 wt%. At the sintering temperature of 1110$^{\circ}C$ and the calcination temperature of 850$^{\circ}C$, the optimal values of density=4.52g/$cm^3$, kp=0.47, $\varepsilon_r$=400 were obtained.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1320-1325
• /
• 2004

In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, PCW-PMN-PZT ceramics added with Li$_2$CO$_3$, Bi$_2$O$_3$ and CuO as sintering aids were manufactured, and their microstructural, dielectric and piezoelectric properties were investigated. When the only CuO was added, specimens could not be sintered below 98$0^{\circ}C$. However, when Li$_2$CO$_3$ and Bi$_2$O$_3$ were added, specimens could be sintered below 98$0^{\circ}C$. Li$_2$CO$_3$ and Bi$_2$O$_3$ addition were proved to lower sintering temperature of piezoelectric ceramics due to the effect of Li$_2$O-Bi$_2$O$_3$ liquid phase. Li$_2$CO$_3$ and Bi$_2$O$_3$ added specimens showed higher piezoelectric properties than those of the only CuO added specimens. At 0.2 wt% Li$_2$CO$_3$ and 0.3 wt% Bi$_2$O$_3$ added specimen sintered at 92$0^{\circ}C$, the dielectric constant of 1457, electromechanical coupling factor of 0.56 and mechanical quality factor of 1000 were shown, respectively. These values are suitable for multilayer piezoelectric transformer application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.9
• /
• pp.692-701
• /
• 2012

Recently, many lead-free piezoelectric materials have been investigated for the replacement of existing Pb-based piezoelectric ceramics because of globally increasing environmental interest. There has been remarkable improvement in piezoelectric properties of some lead-free ceramics such as $(Bi,Na)TiO_3-(Bi,K)TiO_3-BaTiO_3$, $(Na,K)NbO_3-LiSbO_3$, and so on. However, no one still has comparable piezoelectric properties to lead-based materials. Therefore, new lead-free piezoelectric ceramics are required. $BiFeO_3$ has a rhombohedrally distorted perovskite structure at room temperature and a very high Curie temperature ($T_C$= 1,100 K). And a very large electric polarization of 50 ~ 60 ${\mu}C/cm^2$ has been reported both in epitaxial thin film and single crystal $BiFeO_3$. Therefore, a high piezoelectric effect is expected also in a $BiFeO_3$ ceramics. The recent research activities on $BiFeO_3$ or $BiFeO_3$-based solid solutions are reviewed in this article.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.292-293
• /
• 2007

In the study, in order to develop low temperature sintering ceramics for multilayer piezoelectric transformer, $(Pb,Ca,Sr)Ti(Mn,Sb)O_3$ ceramics were fabricated using $Na_2CO_3$, $Li_2CO_3$, $MnO_2$ and $Bi_2O_3$ as sintering aids and their dielectric and piezoelectric properties were investigated according to the amount of $Bi_2O_3$ addition. At the sintering temperature of $900^{\circ}C$, density, thickness vibration mode electromechanical coupling factor ($k_t$), thickness vibration mode mechanical quality factor ($Q_{mt}$) and dielecteic constant (${\varepsilon}_r$) showed the optimum value of $6.94[g/cm^3]$, 0.497, 3,162 and 209, respectively, for multilayer piezoelectric transformer application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.9
• /
• pp.771-775
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for thickness vibration mode multilayer piezoelectric transformer, $PbTiO_3$ system ceramics were fabricated using $Na_2CO_3,\;Li_2CO_3,\;MnO_2\;and\;Bi_2O_3$ as sintering aids and their dielectric and piezoeletric properties were investigated according to the amount of $Bi_2O_3$ addition. At the sintering temperature of $900^{\circ}C\;and\;Bi_2O_3$ addition of 0.1 wt%, density, grain size, thickness vibration mode eletromechanical coupling factor($k_t$), thickness vibration mode mechanical quality factor($Q_{mt}$) and dielecteic constant(${\varepsilon}_r$) showed the optimum value of $6.94g/cm^3,\;2.413{\mu}m$, 0.497, 3,162 and 209, respectively, for thickness vibration mode multilayer piezoelectric transformer application.

• Journal of the Korean Ceramic Society
• /
• v.53 no.2
• /
• pp.162-166
• /
• 2016

0.75BF-0.25BT ceramics were prepared by sintering at $980-1040^{\circ}C$ in air or under atmosphere powder. A sample with 1 mole %-excess $Bi_2O_3$ was also prepared to compensate for $Bi_2O_3$-evaporation. Physical and piezoelectric properties of these three samples were compared. When the sintering temperature increased from $980^{\circ}C$ to $1040^{\circ}C$, the density of the sample sintered in air decreased continuously due to Bi-evaporation. Due to the suppression of Bi-evaporation, the sample sintered under atmosphere powder had a higher density at sintering temperatures above $1000^{\circ}C$ than did the sample sintered in air. The addition of 1 mole %-excess $Bi_2O_3$ successfully compensated for Bi-evaporation and kept the density at the higher value until $1020^{\circ}C$. Grain size increased continuously when the sintering temperature increased from 980 to $1040^{\circ}C$, irrespective of the sintering atmosphere. When the sintering temperature increased, the piezoelectric constant ($d_{33}$) and the electromechanical coupling factor ($k_p$) increased for all samples. The sample with 1 mole % excess-$Bi_2O_3$ showed the highest density and the best piezoelectric properties at sintering temperature of $1020^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.9
• /
• pp.577-580
• /
• 2015

In this paper, in order to develop the composition ceramics with the outstanding piezoelectric properties, $Pb(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.09}(Zr_{0.5}Ti_{0.5})_{0.88}O_3$ ceramics substituted with $BiFeO_3$ were prepared by the conventional solid-state reaction method. The addition of small amount of $Li_2CO_3$ and $CaCO_3$ as sintering aids decreased the sintering temperature of the ceramics. The effects of $BiFeO_3$ substitution on their piezoelectric and dielectric properties were investigated. when 0.015 mol $BiFeO_3$ was substituted, the optimal physical properties of $d_{33}=590pC/N$, $E_c=8.78kV/mm$ were obtained.

• Journal of the Korean Ceramic Society
• /
• v.45 no.5
• /
• pp.263-267
• /
• 2008

$(Bi_{1/2}Na_{1/2})TiO_3$-based ceramics have been intensively studied as lead-free piezoelectric ceramics. In this study, the piezoelectric properties and phase transition behaviors of BNT based solid solution $(Bi_{0.5}Na_{0.5})_{1-x}Ca_xTiO_3$ ($X=0.01{\sim}0.25$) were investigated. The morphotropic phase boundary(MPB) zone which BNT is transformed from rhombohedral to cubic structure was appeared by adding $CaTiO_3$ with 0.12 mol by the measurement of permittivity and X-ray diffraction. The behavior which ferroelectric BNT with adding $CaTiO_3$ was changed to antiferroelectric and paraelectric state was confirmed by the measurement ofhysterisis loop and depolarization temperature as a function of temperature. As $CaTiO_3$ concentration was increased, the phase transition temperature was decreased. The piezoelectric properties were highest at 0.01 mol of $CaTiO_3$ concentration. The electromechanical coupling factor($K_t$) and mechanical quality factor($Q_m$) were 42% and 254, respectively.

• Journal of Powder Materials
• /
• v.26 no.5
• /
• pp.405-409
• /
• 2019

Piezoelectric ceramic specimens with the $Pb(Mg_{1/3}Nb_{2/3})_{0.65}Ti_{0.35}O_3$ (PMN-PT) composition are prepared by the solid state reaction method known as the "columbite precursor" method. Moreover, the effects of the $Li_2O-Bi_2O_3$ additive on the microstructure, crystal structure, and piezoelectric properties of sintered PMN-PT ceramic samples are investigated. The addition of $Li_2O-Bi_2O_3$ lowers the sintering temperature from $1,200^{\circ}C$ to $950^{\circ}C$. Moreover, with the addition of >5 wt.% additive, the crystal structure changes from tetragonal to rhombohedral. Notably, the sample with 3 wt.% additive exhibits excellent piezoelectric properties ($d_{33}=596pC/N$ and Kp = 57%) and a sintered density of $7.92g/cm^3$ after sintering at $950^{\circ}C$. In addition, the sample exhibits a curie temperature of $138.6^{\circ}C$ at 1 kHz. Finally, the compatibility of the sample with a Cu electrode is examined, because the energy-dispersive X-ray spectroscopy data indicate the absence of interdiffusion between Cu and the ceramic material.