• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.897-900
• /
• 2001

Space charge distributions in silane crosslinked polyethylene (SXLPE)/ crosslinked polyethylene (XLPE) laminates was investigated using a pulsed electroacoustic (PEA) method. XLPE shows heterocharge while SXLPE shows homocharge. Positive charge is accumulated at the interface of SXLPE/XLPE laminate when applied electric field is more than 20 kV/mm. The charge profile at various temperatures was also acquired using temperature-controllable PEA system. Although applied electric field is only 8.6 kV/mm, positive interfacial charge starts to appear near 50$^{\circ}C$.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.1
• /
• pp.42-49
• /
• 1992

Charge accumulation characteristics in low density polyethylene (LDPE) has been discussed based upon the internal charge distrubution measured by the pulsed electroacoustic technique. When the negative voltage with respect to earth is applied to the upper electrode, the negative charges near the anode and the positive charges near the cathode are accumulated in LDPE. Also, there was an asymmetric behavior of charge accumulation exhibiting that the charge accumulation near the anode keeps increasing whereas that near the cathode increases first and then decreases. Besides, under the present test conditions the internal charge distrubution becomes stabilized eventually. When the positive voltage with respect to earth is applied to the upper electrode, on the other hand, no such asymmetric charge accumulation was found. Therefore, it can be concluded that the heterocharges are accumulated at the surface region of LDPE subjected to high do voltages and that the begavior of charge accumulation depends on the polarity of do voltage and the position of charge accumulation.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.2
• /
• pp.127-132
• /
• 2002

Space charge distributions and behaviors in silane crosslinked polyethylene(SXLPE)/ crosslinked polyethylene(XLPE) laminates were investigated using a pulsed electroacoustic (PEA) method. In case of monolayer, XLPE shows heterocharge while SXLPE shows homocharge. It was observed that charges were accumulated at the interface of SXLPE/XLPE laminate when applied electric field was more than 20kV/mm. The charge profile at various temperatures was also acquired using temperature-controllable PEA system. Although applied electric field is only 8.6 kV.mm, positive interfacial charge starts to appear near 50$^{\circ}C$. It was found that the interfacial charge behavior of SXLPE/XLPE laminate under low voltage at high temperature is corresponding to that under high voltage at room temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.107-110
• /
• 1995

Space charge formation in epoxy/silica composites has been investigated by the pulsed electroacoustic (PEA) method. The addition of silica resulted in homocharge formation, which attributed to the interfacial trapping of injected charge at epoxy/silica interfaces, Homocharge accumulation with increase of voltage and silica content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.287-290
• /
• 1996

The behaviour of interfacial charge in EPDM/XLPE laminates has been investigated by measuring charge distributions using a pulsed electroacoustic (PEA) method. Homocharge develops in EPDM while heterocharge develops in XLPE. A broadly interfacial charge peak is observed at EPDM/XLPE interface. When EPDM /XLPE laminates are treated in high temperature for different times, the amount and polarity of interfacial charge are changed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.536-539
• /
• 1999

Physical properties of glass fiber-reinforced nylon 6,6 and ionomer blends were investigated in variation of ionomer and glass fiber content. With the increase of ionomer content, tensile strength, impact strength and flexural strength decreased, whereas increasing glass fiber content, these properties were improves. Both permittivity and tan $\delta$ remain unchanged. Space charge distribution was investigated by PEA (Pulsed electroacoustic) method. Heterocharge was found in nylon 6,6 and 히ass fiber composites, whereas composites, whereas when ionomer is blended.

• Journal of Electrical Engineering and Technology
• /
• v.10 no.3
• /
• pp.1124-1130
• /
• 2015

Moisture and high temperature are the most important factors that lead to the ageing of oil-paper insulation, but the research about space charge characteristics of oil-paper insulation does not take the combined effect of ambient temperature, moisture and thermal ageing into account. The pulsed electroacoustic (PEA) method was used to investigate the influence of moisture and temperature on space charge characteristics of oil paper at different ageing stages. The results showed that moisture could speed up formation of space charge in oil paper when water concentration was low, but the formation was restrained if the water concentration was high. At the beginning of thermal ageing, heterogeneous charge accumulation had predominance, but it gradually changed to homogeneous charge injection with ageing. It was believed that moisture concentration could speed up ageing and enhance charge accumulation on one hand, and accelerate or slow down the establishment speed of space charge on the other hand, therefore, charge accumulation type changed with ageing. The more seriously the oil-paper insulation was thermally aged, the deeper the trap energy level was, hence more space charge was trapped, which could be speeded up by increasing the ageing temperature, but the effect of ambient temperature did not fit the Arrhenius law.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.77-80
• /
• 2000

In order to determine what influences the interfacial charge in EPDM/XLPE laminates, We used PEA (pulsed electroacoustic) method. Interfacial properties such as space charge accumulation and breakdown strength in crosslinked polyethylene (XLPE)/ethylene-propylene-diene monomer (EPDM) laminates were investigated. Interfacial charge develops when the EPDM is laminated with XLPE. It showed the positive polarity same as the simulation in case on intercase of EPDM/XLPE. In case of coupling agent added silicone oil, as increasing the content of coupling agent, the interfacial charge decreased. Details of the results are given and their origins discussed.

• Proceedings of the KIEE Conference
• /
• 2003.10a
• /
• pp.95-97
• /
• 2003

This paper describes electrical properties such as electrical conduction characteristics and space charge distributions of polyaniline/polystyrene conducting blends. It is interesting to note that the charging current decreased as the temperature was elevated when DC voltage was applied, and also the hopping distance decreased with the increase of temperature for the PANI/HIPS blends, while generally, the hopping distance decreases as the charging current increases. It is exposed that this result is opposed to widely known phenomenon. It could be examined viewing space charge distributions by a pulsed electroacoustic (PEA) method.

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1457-1459
• /
• 2003

Space charge distributions and behaviors of polystyrene/polyaniline conducting blends were investigated using a pulsed electroacoustic(PEA) method. It was found that positive charges were accumulated near the cathode with increasing polyaniline content in polystyrene/polyaniline when electric field was applied. Breakdown phenomena was investigated by breakdown test and it was observed that dielectric strength was diminished as polyaniline content was increased. By Scanning Electron Microscopy, corss-sectional views of polystyrene/polyaniline conducting blends were observed that the particles of polyaniline were well distributed in polystyrene.