• Korean Chemical Engineering Research
• /
• v.47 no.3
• /
• pp.316-320
• /
• 2009

UV curable hard and color coatings were formed on polycarbonate(PC) films. The coating materials were composed of a commercially available end-capped polyester(EB830), diacrylate monomer(HDDA), silicon acrylate, photoinitiator, and organic dye as a coloring agent. The surface properties of coating films were evaluated, and the influences of the compositions of coating materials were investigated. The coating films showed high transmission and good adhesion between coating layer and PC substrate. And the coating films exhibited higher hardness than bare PC film. The coating films with various colors were obtained by wet process, and the clear and color window lenses for mobile phone were prepared successfully.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.739-744
• /
• 1996

Lanthanide diphthalocyanines have interesting properties on electrochemical and chemical redox reactions. It is however, difficult to use because of thier short device life. Plasma-polymerization attends to improvement thier device life. Yb-diphthalocyanine ($YbPc_2$) polymer film was deposited in a parallel plate electrodes-type RF plasma reactor. $YbPc_2$ was sublimed into the argon plasma, and polymer film was obtained on a substrate. Radio frequency was constant of 13.56MHz. Pressure of argon gas, sublimation rate of $YbPc_2$ and RF power were variable parameters depending on film quality. Surface of polymer films include a lot of sub-micron order lumps. It was indicated that size of lumps depends on polymerization degree controled by parameters. Size of lumps and polymerization degree are increased with RF power. However, by the high RF power over 40W, polymerization degree is decreased with RF power and surface of film is rough. In condition of RF power is high, polymerization will compete with etching of film. We obtained good films for electrochromic display with RF power of 20W, argon gas pressure of 8.0 Pa and sublimationrate of $1.2 \times 10$ mol/min, and good films for gas sensor with RF power of 30W, argon gas pressure of 10.6Pa and sublimation rate of $1.2 \times 10$ mol/min.

• Journal of Microbiology and Biotechnology
• /
• v.13 no.1
• /
• pp.77-84
• /
• 2003

Chitinase was purified from an antagonistic bacterium Bacillus sp. 7079 by ammonium sulfate precipitation, QAE-Sephadex anion exchange chromatography, Sephadex G-100 gel filtration, and SP-Sephadex cation exchange chromatography. The molecula. weight of purified chitinase (PC-1) was approximately 66.5 kDa on SDS-PACE. PC-1 exhibited optimum pH and temperature of pH 7.5 and $45^{\circ}C$, respectively. More than $80\%$ of PC-1 was stable at pH 5.0 to 9.0, and more than $90\%$ at $40^{\circ}C$. $Fe^2+\;and\;Ca^2+$ inhibited the chitinase activity about $20\%$, and EDTA and p-CMB by about $30\%$, whereas $Ag^+$ inhibited the activity up to $65\%$. The $K_m$ value of PC-1 was 1.215 mg/ml with colloidal chitin as a substrate. We also investigated the effect of PC-1 treated chitin (PCTC) on the pro-inflammatory cytokine gene expression in macrophage RAW 264.7 cells. The expression of IL-$1{\alpha}$ and IL-$1{\beta}$ mRNA gene was investigated using reverse transcriptase polymerase chain reaction (RT-PCR). IL-$1{\alpha}$ and IL-$1{\beta}$ mRNA were induced by the treatment of PCTC and chitin only in RAW 264.7 cells. These expressions were induced as early as 2 h and sustained up to 24 h in RAW 264.7 cells. IL-$1{\alpha}$ and IL-$1{\beta}$ mRNA were more strongly expressed by the treatment of PCTC than chitin treatment alone in RAW 264.7 cells.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.12
• /
• pp.1115-1120
• /
• 2003

In this paper, we investigated the position dependent stress distribution of indium-tin-oxide (ITO) film on Polycarbonate (PC) substrate by external bending force. It was found that there are the maximum crack density at the center position and decreasing crack density as goes to the edge, In accordance with crack distribution, it was observed that the change of electrical resistivity of ITO islands is maximum at the center and decrease as goes to the edge. From the result that crack density is increasing at same island position as face plate distance (L) decreases, it is evident that the more stress is imposed on same island position as L decreases.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.334-334
• /
• 2011

We applied N-ion bombardment and heat treatment to the Cu thin films deposited on aluminum oxide layer for the enhancement of adhesion. With e-beam evaporation method. $1,000{\AA}$ thick Cu pre-bombardment layer was deposited on the aluminum oxide surface and then N-ion beam was bombared in order to mix the atoms at the film/substrate interface. Additional $4,000{\AA}$-thick Cu film was the coated. Subsequently, the ion mixide Cu on aluminum oxide was annealed at $200^{\circ}C$ and $300^{\circ}C$ in vacuum.

• Journal of information and communication convergence engineering
• /
• v.5 no.3
• /
• pp.219-222
• /
• 2007

Highly conductive and transparent aluminum doped ZnO thin films (AZO) films have been prepared by r.f. magnetron sputtering processes on poly carbonate (PC) and onto glass as reference. In addition, the electrical, optical properties of the films prepared at various sputtering powers were investigated. The XRD measurements revealed that all of the obtained films were polycrystalline with the hexagonal structure and had a preferred orientation with the c-axis perpendicular to the substrate. The ZnO:Al films were increasingly dark gray colored as the sputter power increased, resulting in the loss of transmittance. High quality films with the resistivity as low as $9.7{\times}10^{-4}\;{\Omega}-cm$ and transmittance over 90% have been obtained by suitably controlling the r.f. power.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.364-366
• /
• 2009

We successfully fabricated flexible electronic paper display (EPD) by using toner particles on plastic (PC) substrate. It has high resolution (WVGA : 800 ${\times}$ 480) and 7 inch diagonal viewable image size. The response time was about 0.25 msec at 90 V, a contrast ratio of about 2, a driving voltage of 60 V which we successfully demonstrated to display several images at.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08a
• /
• pp.659-662
• /
• 2007

The characteristics of a $SiN_x$ passivation layer grown by a specially designed catalyzer enhanced chemical vapor deposition (CECVD) system and electrical and optical properties of OLEDs passivated with the $SiN_x$ layer are described. Despite the low substrate temperature, the single $SiN_x$ passivation layer, grown on the PC substrate, exhibited a low water vapor transmission rate of $2{\sim}6{\times}10^{-2}\;g/m^2/day$ and a high transmittance of 87 %. In addition, current-voltage-luminescence results of an OLED passivated with a 150 nm-thick $SiN_x$ film compared to nonpassivated sample were identical indicating that the performance of an OLED is not critically affected by radiation from tungsten catalyzer during the $SiN_x$ deposition.

• Design & Manufacturing
• /
• v.13 no.1
• /
• pp.48-54
• /
• 2019

Analytical and experimental study were carried out in order to achieve simultaneous coating and injection molding of an automotive armrest. A mold was designed to be included one core and two cavities, which were composed of a substrate cavity and a coating cavity. The materials used were PC/ABS for substrate and 2-component Polyurethane for coating. The predicted flow patterns were in good agreement with experimental results in injection molding and in-mold coating. Based on analysis and experiment, it was found that the optimal processing conditions were packing pressure of 90MPa and holding time of 7sec.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.22 no.5
• /
• pp.282-288
• /
• 2010

Experiment on the surface characteristics of polymer films treated by atmospheric pressure plasma has been conducted. We chose the process parameters as frequency, gas flow, treatment time, and scrutinized the effects of the process parameters on the surface characteristics of polymer materials by measuring the contact angle and examining SEM. As the result, the surface characteristics highly depends on frequency, reaction gas and treatment time. In the case of PC substrate, the contact angle was changed from $83.5^{\circ}$ (before plasma treatment) to $30^{\circ}$ (after plasma treatment) at 30 kHz, CDA 0.6%, and number of repeat 7. In the case of PET substrate, the contact angle change was found from $59^{\circ}$ to $23.5^{\circ}$ at 20 kHz, CDA 0.6%, and number of repeat 7. In the case of EVA substrate, it shows from $84^{\circ}$ to $44.2^{\circ}$ at 30 kHz, CDA 0.6%, and number of repeat 7.