• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.15-19
• /
• 2012

Both electrogalvanized and hot-dip galvanized steel sheets have been finally produced via organic-inorganic surface coating process on the zinc surface to enhance corrosion resistance and afford additional functional properties. Recently, POSCO has been developed a variety of chromate-free coated steels that are widely used in household, construction and automotive applications. New organic-inorganic hybrid coating solutions as chromate alternatives are comprised of surface modified silicate with silane coupling agent and inorganic corrosion inhibitors as an aqueous formulation. In this paper we have prepared new type of hybrid coatings and evaluated quality performances such as corrosion resistance, spot weldability, thermal tolerance, and paint adhesion property etc. The electrogalvanized steels with these coating solutions exhibit good anti-corrosion property compared to those of chromate coated steels. Detailed components composition of coating solutions and experimental results suggest that strong binding between organic-inorganic hybrid coating layer and zinc surface plays a key role in the advanced quality performances.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.2
• /
• pp.240-246
• /
• 2011

UV-Curable hybrid coatings were synthesized to improve the surface properties of plastic film. Organic-inorganic coating solutions were prepared by the sol-gel method using urethane-acrylate oligomer, acrylate monomer, photo initiator and tetraethoxysilane (TEOS). Methacryloyloxypropyltrimethoxysilane(MPTMS) was used as a silane coupling agent to improve chemical interaction between inorganic phases and UV curable acrylate. In this study, the surface hardness and adhesive properties were improved with the use of inorganic component. The experimental results showed that UV-Curable hybrid films containing aliphatic urethane oligomer, hexanedioldiacrylate, trimethylolpropanetriacrylate, hydroxy dimethyl acetophenone exhibited good surface properties. Also, the optimum curing conditions were investigated.

• Korean Chemical Engineering Research
• /
• v.52 no.3
• /
• pp.388-394
• /
• 2014

Inorganic-organic hybrid coating solutions were synthesized using titania sol from titanium isopropoxide (TTIP) as an inorganic component and mixture of two or three types of silane coupling agents, such as methacryloxypropyl trimethoxysilane (MPTMS), aminopropyl triethoxysilane (APS), glycidoxypropyl trimethoxysilane (GPTMS) and vinyltriethoxysilane (VTES) as an organic component. The hard coating films were obtained by spin-coating on the polycarbonate sheets and curing the inorganic-organic hybrid coating solutions. The coating films made from the mixture of two types of silane coupling agents showed poor pencil hardness and adhesion, while those from the mixture of three types of silane coupling agents exhibited an improved pencil hardness of 2H~4H and adhesion of 5B. The refractive indexes of coating films were increased from 1.56 to 1.63 at 550 nm by increasing the content of titania sols from 20 to 30 g.

• Korean Chemical Engineering Research
• /
• v.49 no.3
• /
• pp.277-284
• /
• 2011

In this study, UV-curing type organic - inorganic hybrid hard coating solutions were prepared from alumina sols and acrylate monomers. The mixture of alumina sols, prepared from aluminum isopropoxide, and a silane coupling agent, methacryloxypropyl trimethoxysilane(MPTMS), was used as an inorganic component. Also, the mixture of acrylate monomers, pentaerythritol triacrylate(PETA), 1,6-hexanediol diacrylate(HDDA) and dipentaerythritol hexaacrylate (DPEHA), was used as an organic component. The organic-inorganic hybrid coating solutions were obtained by mixing the inorganic component and organic component, deposited on polycarbonate substrates by spin coating and densified by UV-curing. The effect of the amount of MPTMS in the inorganic component and the irradiation time during UV-curing was studied on the properties of coating films. As a result, when 0.20 mole of MPTMS was used, the pencil hardness of coated films showed an excellent pencil hardness of 3H and also exhibited a good abrasion resistance of 2% in haze.

• Korean Chemical Engineering Research
• /
• v.50 no.3
• /
• pp.421-426
• /
• 2012

The effect of synthesis conditions such as various organic material and composition of organic-inorganic material in ozone resistance and surface characteristic of ultraviolet cured organic-inorganic hybrid coating film has been investigated. Organic-inorganic hybrid coating solution was prepared using tetraethoxysilane (TEOS), silane coupling agent methacryloyloxypropyltrimethoxysilane (MPTMS), 2,2,2-trifluoroethylmethacrylate, and various organic materials with acrylate group, bar-coated on substrates using applicator and densified by UV-curing. It was found that ozone resistance and surface hardness of the coating film was increased with contents of TEOS. It was also found that ozone resistance of coating film was increased with contents of 2,2,2-trifluoroethylmethacrylate. On the other hand, surface hardness was decreased with increase of 2,2,2-trifluoroethylmethacrylate. In addition, Surface hardness of coating film was increased with the addition of aliphatic urethane acrylate. It was also found that the transmittance of coating films was not influenced by content of TEOS and 2,2,2-trifluoroethylmethacrylate. In addition, the coating film exhibited high transmittance of above 90%.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.16-21
• /
• 2012

Organic-inorganic hybrid coating film using 1,2-bis(2,4-dimethyl-5-phenyl-3-thienyl)-3,3,4,4,5,5-hexafluoro-1-cyclopentene (BTHFC) as a photochromic material was prepared under various reaction conditions such as the amounts of tetramethoxysilane (TMOS), various silane coupling agents, and solvent. It was found that color-fading speed and absorbance of the coating film was strongly dependent upon the polarity of silane coupling agent and solvent. In addition, the mole ratio of TMOS and methacryloyloxypropyltrimethoxysilane (MPTMS) was an important factor to determine color-fading speed and absorbance of the coating film. With increasing TMOS contents in coating film, the pencil hardness was increased. On the other hands, the transmittance of coating film was relatively decreased with the increase of TMOS.

• Polymer(Korea)
• /
• v.24 no.3
• /
• pp.389-398
• /
• 2000

Transparent, abrasion resistant coatings with 4~13 ${\mu}{\textrm}{m}$ thickness were prepared by spin-coating on polycarbonates with organic/inorganic hybrid solutions, followed by UV curing and heat treatment at 12$0^{\circ}C$ for 12 hours. The coating solutions were composed of inorganic phase and organic phase in 0:100, 20:80, 30:70, 50:50, 80:20 wt% ratios, respectively, mixed with photoinitiator, senaitizer and surfactant. The inorganic phase was formed by sol-gel reaction of TEOS and silane coupling agent MPTMS in 1 : 2 or 2 : 1 molar ratios, the organic phase consisted of difunctional urethane acrylate oligomeric resin, multifunctional acrylate TMPTA and HDDA in 4 : 3 : 3 wt% ratio. The coating systems were investigated by FT-IR, $^{29}$ Si-NMR spectra. In addition, TGA/DSC for thermal analysis and SEM, AFM observation for coated surface were examined. Gererally, the homogeneity of phases, the surface smoothness of coating and abrasion resistance were improved with the higher content of inorganic component. Namely, coating system with below 10 $\AA$ surface roughness and T$_{g}$ of 15$0^{\circ}C$ showed only 10% decrease in light transmittance after abrasion test, whereas uncoated polycarbonate substrate exhibited 46% decrease..

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.573-579
• /
• 2014

The effect of synthesis conditions such as carbon nanotube (CNT), 2,2,2-trifluoroethylmethacrylate (3FMA), and composition of organic-inorganic material in ozone resistance and surface characteristics of ultraviolet cured organic-inorganic hybrid coating film has been investigated. Coating solution was prepared using tetraethoxysilane (TEOS), silane coupling agent methacryloyloxypropyltrimethoxysilane (MPTMS), 3FMA, various organic materials with acrylate group, and CNT, then bar-coated on substrates using applicator, and densified by UV-curing. It was found that ozone resistance and adhesion of the coating film were strongly dependent upon contents of TEOS, 3FMA, and CNT. Especially, ozone resistance, adhesion, and surface hardness of coating film with CNT were improved, relatively. Ozone resistance of coating film with a high TEOS content was increased, but adhesion was decreased. In addition, it was also found that ozone resistance of coating film was increased with contents of 3FMA. On the other hand, surface hardness was decreased with increase of 3FMA.

• Journal of Adhesion and Interface
• /
• v.20 no.4
• /
• pp.146-154
• /
• 2019

In this study, alkoxysilane-functionalized amphiphilic polymer (AFAP), which have hydrophilic segment and hydrophobic segment functionalized by alkoxysilane group at the same backbone, was synthesized and used as a dispersant and control agent for reaction rate in the preparation of colloidally stable organic-inorganic (O-I) hybrid sols. After reaction with fluorosilane compounds, fluorinated O-I hybrid sols were prepared and coated onto glass substrate to form hydrophobic O-I hybrid coating films through low-temperature curing process. Surface hardness and hydrophobicity of cured coating films were varied with type of solvent and composition of AFAP and fluorinated alkoxysilane compounds. At appropriate solvent and composition of fluorinated alkoxysilane compounds, O-I hybrid coating film having high transparency and surface hardness could be prepared, which could be applicable to cover window of solar cell and displays.

• Journal of the Korean Applied Science and Technology
• /
• v.26 no.3
• /
• pp.288-296
• /
• 2009

In this study, the silica-based hybrid material with high barrier property was prepared by incorporating ethylene-vinyl alcohol (EVOH) copolymer, which has been utilized as packaging materials due to its superior gas permeation resistance, during sol-gel process. In preparation of this EVOH/$SiO_2$ hybrid coating materials, the (3-glycidoxy-propyl)-trimethoxysilane (GPTMS) as a silane coupling agent was employed to promote interfacial adhesion between organic and inorganic phases. As confirmed from FT-IR analysis, the physical interaction between two phases was improved due to the increased hydrogen bonding, resulting in homogeneous microstructure with dispersion of nano-sized silica particles. However, depending on the range of content of added silane coupling agent (GPTMS), micro-phase separated microstructure in the hybrid could be observed due to insufficient interfacial attraction or possibility of polymerization reaction of epoxide ring in GPTMS. The oxygen barrier property of the mono-layer coated BOPP (biaxially oriented polypropylene) film was examined for the hybrids containing various GPTMS contents. Consequently, it is revealed that GPTMS should be used in an optimum level of content to produce the high barrier EVOH/$SiO_2$ hybrid material with an improved optical transparency and homogeneous phase morphology.